Silane coupling agent KH560 was used to modify the surface of nano-α-Al<sub>2</sub>O<sub>3</sub> in ethanol-aqueous solution with different proportions. The particle size of nano-α-Al<sub&...Silane coupling agent KH560 was used to modify the surface of nano-α-Al<sub>2</sub>O<sub>3</sub> in ethanol-aqueous solution with different proportions. The particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> was determined by nano-particle size analyzer, and the effects of nano-α-Al<sub>2</sub>O<sub>3</sub> content, ethanol-aqueous solution ratio and KH560 dosage on the dispersion and particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> were investigated. The material structure before and after modification was determined by Fourier transform infrared spectroscopy (FTIR). Aqueous polyurethane resin and inorganic components are combined with modified nano-α-Al<sub>2</sub>O<sub>3</sub> dispersion to form chromium-free passivation solution. The solution is coated on the galvanized sheet, the adhesion and surface hardness are tested, the bonding strength of the coating and the surface hardness of the substrate are discussed. The corrosion resistance and surface morphology of the matrix were investigated by electrochemical test, neutral salt spray test and scanning electron microscope test. The chromium-free passivation film formed after the modification of nano-α-Al<sub>2</sub>O<sub>3</sub> increases the surface hardness of galvanized sheet by about 85%. The corrosion resistance of the film is better than that of a single polyurethane film. The results show that the surface hardness and corrosion resistance of polyurethane resin composite passivation film are significantly improved by the introduction of nano-α-Al<sub>2</sub>O<sub>3</sub>.展开更多
The thermal shock fatigue behaviors of pure hot-pressed alumina and 30 wt.% TiC/Al2O3 composites were studied. The effect of TiC and Al2O3 starting particle size on the mechanical properties of the composites was disc...The thermal shock fatigue behaviors of pure hot-pressed alumina and 30 wt.% TiC/Al2O3 composites were studied. The effect of TiC and Al2O3 starting particle size on the mechanical properties of the composites was discussed. Indentation-quench test was conducted to evaluate the effect of thermal fatigue temperature difference （ΔT） and number of thermal cycles （Ⅳ） on fatigue crack growth （Δa）. The mechanical properties and thermal fatigue resistance of TiC/Al203 composites are remarkably improved by the addition of TiC. The thermal shock fatigue of monolithic alumina and TiC/Al2O3 composites is due to a ＂true＂ cycling effect （thermal fatigue）. Crack deflection and bridging are the predominant reasons for the improvement of thermal shock fatigue resistance of the composites.展开更多
Al2O3-13%TiO2 （mass fraction） coatings, prepared by laser cladding on nickel-based alloy, were heated using high frequency induction sources. The coating microstructure and the interface between bond coating and cer...Al2O3-13%TiO2 （mass fraction） coatings, prepared by laser cladding on nickel-based alloy, were heated using high frequency induction sources. The coating microstructure and the interface between bond coating and ceramic coating were characterized by SEM, XRD and EDS. The results show that two-layer substructure exists in the ceramic coating： one layer evolving from fully melted region where the sintered grains grow fully; another layer resembling the liquid-phase-sintered structure consisting of three-dimensional net where the melted Al2O3 particles are embedded in the TiO2-rich matrix. The mechanism of the two-layer substructure formation is also explained in terms of the melting and flattening behavior of the powders during laser cladding processing. The spinel compounds NiAl2O4 and acicular compounds Cr2O3 are discovered in the interface between bond coating and ceramic coating. It proves that the chemical reactions in the laser cladding process will significantly enhance the coating adhesion.展开更多
This paper reports that polycrystalline （α-Al2O3：C ceramics are fabricated by conventional ceramics process. The excitation, emission spectra, thermoluminescence （TL） and optical stimulated luminescence （OSL） ...This paper reports that polycrystalline （α-Al2O3：C ceramics are fabricated by conventional ceramics process. The excitation, emission spectra, thermoluminescence （TL） and optical stimulated luminescence （OSL） of α-Al2O3：C polycrystalline ceramics are investigated. There exists 410nm maximum emission peak which is caused by recombination of an electron with F＋ centre to produce an excited F centre. The samples show three clear TL glow peaks at 405, 493 and 610 K. The attenuation constant of exponentially decaying fast component （τ1） and slow component（τ2） of OSL curve are 8.43s and 41.73s, respectively. Those fluorescence and thermoluminescence characteristics are similar with α-Al2O3：C crystal.展开更多
Lu2O3-doped ZnO-Bi2O3-based varistor ceramics samples were prepared by a conventional mixed oxide route and sintered at temperatures in the range of 900-1 000°C,and the microstructures of the varistor ceramics sa...Lu2O3-doped ZnO-Bi2O3-based varistor ceramics samples were prepared by a conventional mixed oxide route and sintered at temperatures in the range of 900-1 000°C,and the microstructures of the varistor ceramics samples were characterized by X-ray diffractometry(XRD)and scanning electron microscopy(SEM);at the same time,the electrical properties and V-I characteristics of the varistor ceramics samples were investigated by a DC parameter instrument for varistors.The results show that the ZnO-Bi2O3-based varistor ceramics with 0.3%Lu2O3(molar fraction)sintered at 950°C exhibit comparatively ideal comprehensive electrical properties.The XRD analysis of the samples shows the presence of ZnO,Bi-rich,spinel Zn7Sb2O12 and Lu2O3-based phases.展开更多
Through measuring the coefficient of linear expansion, the structure and properties of the Li2O-Al2O3-SiO2 low expansion glass ceramics containing B2O3 are studied by JR and XRD. It is shoutn that the IR method is eff...Through measuring the coefficient of linear expansion, the structure and properties of the Li2O-Al2O3-SiO2 low expansion glass ceramics containing B2O3 are studied by JR and XRD. It is shoutn that the IR method is efficient in the study of the glass-ceramics structure. There is a " Boron abnormality" in the system which has an important influence on the properties of the glass-ceramics.展开更多
The effects of Al2O3 addition on both the sintering behavior and microwave dielectric properties of PbO-B203-SiO2 glass ceramics were investigated by Fourier transform infrared spectroscope （FTIR）, differential ther...The effects of Al2O3 addition on both the sintering behavior and microwave dielectric properties of PbO-B203-SiO2 glass ceramics were investigated by Fourier transform infrared spectroscope （FTIR）, differential thermal analysis （DTA）, X-ray diffraction （XRD） and scanning electron microscopy （SEM）. The results show that with the increase of Al2O3 content the bands assigned to [SiO4] nearly disappear. Aluminum replaces silicon in the glass network, which is helpful for the formation of boron-oxygen rings. The increase of the transition temperature Tg and softening temperature Tf of PbO-B2O3-SiO2 glass ceramics leads to the increase of liquid phase precipitation temperature and promotes the structure stability in the glasses, and consequently contributes to the decreasing trend of crystallization. Densification and dielectric constants increase with the increase of Al2O3 content, but the dielectric loss is worsened. By contrast, the 3% （mass fraction） Al2O3-doped glass ceramics sintered at 725℃ have better properties of density p=2.72 g/cm3, dielectric constant Er=6.78, dielectric loss tan8=2.6×10^-3 （measured at 9.8 GHz）, which suggest that the glass ceramics can be applied in multilayer microwave devices requiring low sintering temperatures.展开更多
Optically transparent alumina ceramics were fabricated by conventional process and sintered without pressure in H2 atmosphere. The results indicate that relative densities of alumina specimens increase to theoretical ...Optically transparent alumina ceramics were fabricated by conventional process and sintered without pressure in H2 atmosphere. The results indicate that relative densities of alumina specimens increase to theoretical densities （T. D. ） with increasing content of La2O3. With increasing holding time during sintering, much less pores and larger grains were found in the sintered alumina samples. Higher transmittance was achieved in alumina codoped with MgO and La2O3 as compared with that doped with MgO only. The total-transmittance of alumina sample is up to 86% at twavelength range of 300 - 800 nm.展开更多
The Al2O3 abrasion-resistant ceramics is successfully prepared by using waste aluminum sludge as the main raw material with the addition of a little clay, talc and barium carbonate. The crystal structure and microstru...The Al2O3 abrasion-resistant ceramics is successfully prepared by using waste aluminum sludge as the main raw material with the addition of a little clay, talc and barium carbonate. The crystal structure and microstructure of ceramic are characterized by means of XRD, SEM, etc., and the physical and mechanical properties are also tested. The results show that besides the phase of corundum, a little mullite, Mg-Al spinel and hyalophane phases also exist in the product. These phases are produced via reaction in-situ, which can inhibit the overgrowth of Al2O3 grain in grain boundary, and improve the integral property of the material.展开更多
In recent decades, many additives with different characteristics have been applied to strengthen and toughen Al2O3-based ceramic cutting tool materials. Among them, SiC whiskers and SiC nanoparticles showed excellent ...In recent decades, many additives with different characteristics have been applied to strengthen and toughen Al2O3-based ceramic cutting tool materials. Among them, SiC whiskers and SiC nanoparticles showed excellent performance in improving the material properties. While no attempts have been made to add SiC whiskers and SiC nanoparticles together into the ceramic matrix and the synergistically toughening effects of them have not been studied. An Al2O3-SiCw-SiC np advanced ceramic cutting tool material is fabricated by adding both one-dimensional SiC whiskers and zero-dimensional SiC nanoparticles into the Al2O3 matrix with an effective dispersing and mixing process. The composites with 25 vol% SiC whiskers and 25 vol% SiC nanoparticles alone are also investegated for comparison purposes. Results show that the Al2O3-SiCw-SiCnp composite with both 20 vo1% SiC whiskers and 5 vol% SiC nanoparticles additives have much improved mechanical properties. The flexural strength of Al2O3-SiCw-SiCnp is 730＋ 95 MPa and fracture toughness is 5.6 ± 0.6 MPa.m1/2. The toughening and strengthening mechanisms of SiC whiskers and nanoparticles are studied when they are added either individually or in combination. It is indicated that when SiC whiskers and nanoparticles are added together, the grains are further refined and homogenized, so that the microstructure and fracture mode ratio is modified. The SiC nanoparticles are found helpful to enhance the toughening effects of the SiC whiskers. The proposed research helps to enrich the types of ceramic cutting tool and is benefit to expand the application range of ceramic cutting tool.展开更多
BNp/Al2O3-SiO2 system ceramic matrix composites with different volume fractions （10%-60%） of hexagonal BN particulates （BNp） were prepared by hot-press sintering technique. Phase components, microstructure, mechan...BNp/Al2O3-SiO2 system ceramic matrix composites with different volume fractions （10%-60%） of hexagonal BN particulates （BNp） were prepared by hot-press sintering technique. Phase components, microstructure, mechanical properties and plasma erosion resistance were also investigated. With the increase of h-BNp content, relative density and Vickers＇ hardness of the composite ceramics decrease, while the flexural strength, elastic modulus and fracture toughness increase and then decrease. The plasma erosion resistance linearly deteriorated with the increase of BNp content which is mainly determined by the density, crystal structure and atomic number of the elements.展开更多
The Al2O3-ZrO2（3Y）-SiC composite ceramics used in solar thermal power were prepared by micrometric Al2O3,nano-ZrO2 and SiC powders under the condition of pressureless sintering.The bulk density and bending strength ...The Al2O3-ZrO2（3Y）-SiC composite ceramics used in solar thermal power were prepared by micrometric Al2O3,nano-ZrO2 and SiC powders under the condition of pressureless sintering.The bulk density and bending strength of samples with 10vol% nano-ZrO2 sintered at 1480℃ were 3.222 g/cm3 and 160.4MPa,respectively.The bending strength of samples after 7 times thermal shock tests （quenching from 1000℃ to 25℃ in air medium） is 132.0MPa,loss rate of bending strength is only 17%.The effect of nano-ZrO2 content on the microstructure and performance of Al2O3-ZrO2（3Y）-SiC composite ceramic was investigated.The experimental results show that the bending strength of samples with above 10vol% nano-ZrO2 content has decreased,because the volume expansion resulting from t-ZrO2 to m-ZrO2 phase transformation is excessive;Adding proper nano-ZrO2 would be contributed to improve the thermal shock resistance of the composite ceramics.The Al2O3-ZrO2（3Y）-SiC composite ceramic has promising potential application in solar thermal power.展开更多
CaO-B203-SiO2 （CBS） glass powders are prepared by conventional glass melting method at different melting temperatures whose properties and microstructures are characterized by X-ray diffraction （XRD） and scanning ...CaO-B203-SiO2 （CBS） glass powders are prepared by conventional glass melting method at different melting temperatures whose properties and microstructures are characterized by X-ray diffraction （XRD） and scanning electron microscopy （SEM）. It is found that there are SiO2 and some unknown phases in CBS glass melting liquid from 1 300 ℃ to 1 500 ℃ and the amount of these phases decreases with the increase of the melting temperature. The CBS glass melted at 1 450 ℃ could be sintered from 830 ℃ to 930 ℃ and the bulk densities of the samples are all higher than 2.4 g/cm^3. From the points of the properties and energy conservation, the melting temperature of 1 450 ℃ is the optimal melting temperature. The glass ceramic sintered at 850 ℃ exhibits better dielectric properties： er=6.33, tan6=2.2×10^-3 at 10 GHz, and the major phases of the samples are CaSiO3, CaB2O4 and SiO2.展开更多
ZrO2-Y2O3 ceramic coating was produced by plasma electrolytic oxidation （PEO） on ZAlSil2Cu3Ni2 alloy. The microstructure and phase composition of the coating were investigated by SEM and XRD.： The results show that...ZrO2-Y2O3 ceramic coating was produced by plasma electrolytic oxidation （PEO） on ZAlSil2Cu3Ni2 alloy. The microstructure and phase composition of the coating were investigated by SEM and XRD.： The results show that adding an appropriate amount of yttrium ion can improve the growing rate of ceramic coating at different oxidation stages and decrease arc voltage. The thickness of ZrO2-Y2O3 coating is 16 μn thicker than that of ZrO2 coating and the maximum oxidation rate improves by 0.6 μm/min. In addition, the arc voltage decreases from 227 to 172 V. It can be seen that the rate of oxidation firstly increases to some extent and then decreases with the content of yttrium ion increasing. The growth rate reaches the maximum while the content of yttrium ion is 0.05 g-L-1The maximum thickness is 90 μm.Compared to ZrO2 coating, the micropores of ZrO2-Y2O3 coating are less and the ceramic layer is repeatedly deposited by ZrO2 and Y2O3 ceramic particles. Meanwhile, the binding force between coating and substrate is better and the coating is uniform and compact. The ceramic layer is mainly composed of c-Y0.15Zr0.85O1.93□0.07, m-ZrO2, α-Al2O3, ,γ-Al2O3 and Y2O3. It is indicated that ZrO2 has beert fully stabilized by yttrium ion through the formation of solid solution.展开更多
A Y2O3 particle enhanced Ni/TiC composite coating was fabricated in-situ on a TC4 Ti alloy by laser surface cladding. The phase component, microstructure, composition distribution and properties of the composite layer...A Y2O3 particle enhanced Ni/TiC composite coating was fabricated in-situ on a TC4 Ti alloy by laser surface cladding. The phase component, microstructure, composition distribution and properties of the composite layer were investigated. The composite layer has graded microstructures and compositions, due to the fast melting followed by rapid solidification and cooling during laser cladding. The TiC powders are completely dissolved into the melted layer during melting and segregated as fine dendrites when solidified. The size of TiC dendrites decreases with increasing depth. Y2O3 fine particles distribute in the whole clad layer. The Y2O3 particle enhanced Ni/TiC composite layer has a quite uniform hardness along depth with a maximum value of HV1380, which is 4 times higher than the initial hardness. The wear resistance of the Ti alloy is significantly improved after laser cladding due to the high hardness of the composite coating.展开更多
文摘Silane coupling agent KH560 was used to modify the surface of nano-α-Al<sub>2</sub>O<sub>3</sub> in ethanol-aqueous solution with different proportions. The particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> was determined by nano-particle size analyzer, and the effects of nano-α-Al<sub>2</sub>O<sub>3</sub> content, ethanol-aqueous solution ratio and KH560 dosage on the dispersion and particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> were investigated. The material structure before and after modification was determined by Fourier transform infrared spectroscopy (FTIR). Aqueous polyurethane resin and inorganic components are combined with modified nano-α-Al<sub>2</sub>O<sub>3</sub> dispersion to form chromium-free passivation solution. The solution is coated on the galvanized sheet, the adhesion and surface hardness are tested, the bonding strength of the coating and the surface hardness of the substrate are discussed. The corrosion resistance and surface morphology of the matrix were investigated by electrochemical test, neutral salt spray test and scanning electron microscope test. The chromium-free passivation film formed after the modification of nano-α-Al<sub>2</sub>O<sub>3</sub> increases the surface hardness of galvanized sheet by about 85%. The corrosion resistance of the film is better than that of a single polyurethane film. The results show that the surface hardness and corrosion resistance of polyurethane resin composite passivation film are significantly improved by the introduction of nano-α-Al<sub>2</sub>O<sub>3</sub>.
文摘The thermal shock fatigue behaviors of pure hot-pressed alumina and 30 wt.% TiC/Al2O3 composites were studied. The effect of TiC and Al2O3 starting particle size on the mechanical properties of the composites was discussed. Indentation-quench test was conducted to evaluate the effect of thermal fatigue temperature difference （ΔT） and number of thermal cycles （Ⅳ） on fatigue crack growth （Δa）. The mechanical properties and thermal fatigue resistance of TiC/Al203 composites are remarkably improved by the addition of TiC. The thermal shock fatigue of monolithic alumina and TiC/Al2O3 composites is due to a ＂true＂ cycling effect （thermal fatigue）. Crack deflection and bridging are the predominant reasons for the improvement of thermal shock fatigue resistance of the composites.
基金Project (59975046) supported by the National Natural Science Foundation of China
文摘Al2O3-13%TiO2 （mass fraction） coatings, prepared by laser cladding on nickel-based alloy, were heated using high frequency induction sources. The coating microstructure and the interface between bond coating and ceramic coating were characterized by SEM, XRD and EDS. The results show that two-layer substructure exists in the ceramic coating： one layer evolving from fully melted region where the sintered grains grow fully; another layer resembling the liquid-phase-sintered structure consisting of three-dimensional net where the melted Al2O3 particles are embedded in the TiO2-rich matrix. The mechanism of the two-layer substructure formation is also explained in terms of the melting and flattening behavior of the powders during laser cladding processing. The spinel compounds NiAl2O4 and acicular compounds Cr2O3 are discovered in the interface between bond coating and ceramic coating. It proves that the chemical reactions in the laser cladding process will significantly enhance the coating adhesion.
基金supported by the National Natural Science Foundation of China (Grant No. 60578041)the Sciences and Technology Commission Foundation of Shanghai,China (Grant No. 08520707300)the Key Basic Research Project of Science and Technology of Shanghai (Grant No. 09JC1406500)
文摘This paper reports that polycrystalline （α-Al2O3：C ceramics are fabricated by conventional ceramics process. The excitation, emission spectra, thermoluminescence （TL） and optical stimulated luminescence （OSL） of α-Al2O3：C polycrystalline ceramics are investigated. There exists 410nm maximum emission peak which is caused by recombination of an electron with F＋ centre to produce an excited F centre. The samples show three clear TL glow peaks at 405, 493 and 610 K. The attenuation constant of exponentially decaying fast component （τ1） and slow component（τ2） of OSL curve are 8.43s and 41.73s, respectively. Those fluorescence and thermoluminescence characteristics are similar with α-Al2O3：C crystal.
基金Project(50902061)supported by the National Natural Science Foundation of ChinaProject(2011-22)supported by the State Key Laboratory of Inorganic Synthesis and Preparative Chemistry of Jilin University,China+3 种基金Project(20100471380)supported by the China Postdoctoral Science FoundationProject(J50102)supported by the Leading Academic Discipline Program of Shanghai Municipal Education Commission,ChinaProject(10KJD430002)supported by the Universities Natural Science Research Program of Jiangsu Province,ChinaProject(2010002)supported by the Jiangsu University Undergraduate Practice-Innovation Training Program,China
文摘Lu2O3-doped ZnO-Bi2O3-based varistor ceramics samples were prepared by a conventional mixed oxide route and sintered at temperatures in the range of 900-1 000°C,and the microstructures of the varistor ceramics samples were characterized by X-ray diffractometry(XRD)and scanning electron microscopy(SEM);at the same time,the electrical properties and V-I characteristics of the varistor ceramics samples were investigated by a DC parameter instrument for varistors.The results show that the ZnO-Bi2O3-based varistor ceramics with 0.3%Lu2O3(molar fraction)sintered at 950°C exhibit comparatively ideal comprehensive electrical properties.The XRD analysis of the samples shows the presence of ZnO,Bi-rich,spinel Zn7Sb2O12 and Lu2O3-based phases.
文摘Through measuring the coefficient of linear expansion, the structure and properties of the Li2O-Al2O3-SiO2 low expansion glass ceramics containing B2O3 are studied by JR and XRD. It is shoutn that the IR method is efficient in the study of the glass-ceramics structure. There is a " Boron abnormality" in the system which has an important influence on the properties of the glass-ceramics.
基金Project(2007AA03Z0455) supported by the National High Technology Research and Development Program of ChinaProject supported by the Priority Academic Program Development of Jiangsu Higher Education Institution, China
文摘The effects of Al2O3 addition on both the sintering behavior and microwave dielectric properties of PbO-B203-SiO2 glass ceramics were investigated by Fourier transform infrared spectroscope （FTIR）, differential thermal analysis （DTA）, X-ray diffraction （XRD） and scanning electron microscopy （SEM）. The results show that with the increase of Al2O3 content the bands assigned to [SiO4] nearly disappear. Aluminum replaces silicon in the glass network, which is helpful for the formation of boron-oxygen rings. The increase of the transition temperature Tg and softening temperature Tf of PbO-B2O3-SiO2 glass ceramics leads to the increase of liquid phase precipitation temperature and promotes the structure stability in the glasses, and consequently contributes to the decreasing trend of crystallization. Densification and dielectric constants increase with the increase of Al2O3 content, but the dielectric loss is worsened. By contrast, the 3% （mass fraction） Al2O3-doped glass ceramics sintered at 725℃ have better properties of density p=2.72 g/cm3, dielectric constant Er=6.78, dielectric loss tan8=2.6×10^-3 （measured at 9.8 GHz）, which suggest that the glass ceramics can be applied in multilayer microwave devices requiring low sintering temperatures.
文摘Optically transparent alumina ceramics were fabricated by conventional process and sintered without pressure in H2 atmosphere. The results indicate that relative densities of alumina specimens increase to theoretical densities （T. D. ） with increasing content of La2O3. With increasing holding time during sintering, much less pores and larger grains were found in the sintered alumina samples. Higher transmittance was achieved in alumina codoped with MgO and La2O3 as compared with that doped with MgO only. The total-transmittance of alumina sample is up to 86% at twavelength range of 300 - 800 nm.
基金This project was sponsored by "863" Project (No. 2003AA322020)
文摘The Al2O3 abrasion-resistant ceramics is successfully prepared by using waste aluminum sludge as the main raw material with the addition of a little clay, talc and barium carbonate. The crystal structure and microstructure of ceramic are characterized by means of XRD, SEM, etc., and the physical and mechanical properties are also tested. The results show that besides the phase of corundum, a little mullite, Mg-Al spinel and hyalophane phases also exist in the product. These phases are produced via reaction in-situ, which can inhibit the overgrowth of Al2O3 grain in grain boundary, and improve the integral property of the material.
基金Supported by National Natural Science Foundation of China(Grant No.51175305)
文摘In recent decades, many additives with different characteristics have been applied to strengthen and toughen Al2O3-based ceramic cutting tool materials. Among them, SiC whiskers and SiC nanoparticles showed excellent performance in improving the material properties. While no attempts have been made to add SiC whiskers and SiC nanoparticles together into the ceramic matrix and the synergistically toughening effects of them have not been studied. An Al2O3-SiCw-SiC np advanced ceramic cutting tool material is fabricated by adding both one-dimensional SiC whiskers and zero-dimensional SiC nanoparticles into the Al2O3 matrix with an effective dispersing and mixing process. The composites with 25 vol% SiC whiskers and 25 vol% SiC nanoparticles alone are also investegated for comparison purposes. Results show that the Al2O3-SiCw-SiCnp composite with both 20 vo1% SiC whiskers and 5 vol% SiC nanoparticles additives have much improved mechanical properties. The flexural strength of Al2O3-SiCw-SiCnp is 730＋ 95 MPa and fracture toughness is 5.6 ± 0.6 MPa.m1/2. The toughening and strengthening mechanisms of SiC whiskers and nanoparticles are studied when they are added either individually or in combination. It is indicated that when SiC whiskers and nanoparticles are added together, the grains are further refined and homogenized, so that the microstructure and fracture mode ratio is modified. The SiC nanoparticles are found helpful to enhance the toughening effects of the SiC whiskers. The proposed research helps to enrich the types of ceramic cutting tool and is benefit to expand the application range of ceramic cutting tool.
基金Project(HIT.NSRIF.2010112)supported by the Fundamental Research Fund for the Central Universities,ChinaProjects(50902030,51021002)supported by the National Natural Science Foundation of China
文摘BNp/Al2O3-SiO2 system ceramic matrix composites with different volume fractions （10%-60%） of hexagonal BN particulates （BNp） were prepared by hot-press sintering technique. Phase components, microstructure, mechanical properties and plasma erosion resistance were also investigated. With the increase of h-BNp content, relative density and Vickers＇ hardness of the composite ceramics decrease, while the flexural strength, elastic modulus and fracture toughness increase and then decrease. The plasma erosion resistance linearly deteriorated with the increase of BNp content which is mainly determined by the density, crystal structure and atomic number of the elements.
文摘The Al2O3-ZrO2（3Y）-SiC composite ceramics used in solar thermal power were prepared by micrometric Al2O3,nano-ZrO2 and SiC powders under the condition of pressureless sintering.The bulk density and bending strength of samples with 10vol% nano-ZrO2 sintered at 1480℃ were 3.222 g/cm3 and 160.4MPa,respectively.The bending strength of samples after 7 times thermal shock tests （quenching from 1000℃ to 25℃ in air medium） is 132.0MPa,loss rate of bending strength is only 17%.The effect of nano-ZrO2 content on the microstructure and performance of Al2O3-ZrO2（3Y）-SiC composite ceramic was investigated.The experimental results show that the bending strength of samples with above 10vol% nano-ZrO2 content has decreased,because the volume expansion resulting from t-ZrO2 to m-ZrO2 phase transformation is excessive;Adding proper nano-ZrO2 would be contributed to improve the thermal shock resistance of the composite ceramics.The Al2O3-ZrO2（3Y）-SiC composite ceramic has promising potential application in solar thermal power.
基金Project(2007AA03Z0455) supported by the National High Technology Research and Development Program of ChinaProject(BE2010194) supported by Science&Technology Pillar Program of Jiangsu Province, China+1 种基金Project(KF201103) supported by the State Key Laboratory of New Ceramic and Fine Processing, Tsinghua University, ChinaProject supported by the Priority Academic Development of Jiangsu Higher Education Institutions, China
文摘CaO-B203-SiO2 （CBS） glass powders are prepared by conventional glass melting method at different melting temperatures whose properties and microstructures are characterized by X-ray diffraction （XRD） and scanning electron microscopy （SEM）. It is found that there are SiO2 and some unknown phases in CBS glass melting liquid from 1 300 ℃ to 1 500 ℃ and the amount of these phases decreases with the increase of the melting temperature. The CBS glass melted at 1 450 ℃ could be sintered from 830 ℃ to 930 ℃ and the bulk densities of the samples are all higher than 2.4 g/cm^3. From the points of the properties and energy conservation, the melting temperature of 1 450 ℃ is the optimal melting temperature. The glass ceramic sintered at 850 ℃ exhibits better dielectric properties： er=6.33, tan6=2.2×10^-3 at 10 GHz, and the major phases of the samples are CaSiO3, CaB2O4 and SiO2.
基金Funded by the National Natural Science Foundation of China(No.51401155)the School Foundation(No.XAGDXJJ1012)The Open Fund of Shaanxi Key Laboratory of Photoelectric Functional Materials and Devices(No.ZSKJ201416)
文摘ZrO2-Y2O3 ceramic coating was produced by plasma electrolytic oxidation （PEO） on ZAlSil2Cu3Ni2 alloy. The microstructure and phase composition of the coating were investigated by SEM and XRD.： The results show that adding an appropriate amount of yttrium ion can improve the growing rate of ceramic coating at different oxidation stages and decrease arc voltage. The thickness of ZrO2-Y2O3 coating is 16 μn thicker than that of ZrO2 coating and the maximum oxidation rate improves by 0.6 μm/min. In addition, the arc voltage decreases from 227 to 172 V. It can be seen that the rate of oxidation firstly increases to some extent and then decreases with the content of yttrium ion increasing. The growth rate reaches the maximum while the content of yttrium ion is 0.05 g-L-1The maximum thickness is 90 μm.Compared to ZrO2 coating, the micropores of ZrO2-Y2O3 coating are less and the ceramic layer is repeatedly deposited by ZrO2 and Y2O3 ceramic particles. Meanwhile, the binding force between coating and substrate is better and the coating is uniform and compact. The ceramic layer is mainly composed of c-Y0.15Zr0.85O1.93□0.07, m-ZrO2, α-Al2O3, ,γ-Al2O3 and Y2O3. It is indicated that ZrO2 has beert fully stabilized by yttrium ion through the formation of solid solution.
基金Projects (51101096, 51002093) supported by the National Natural Science Foundation of ChinaProject (1052nm05000) supported by Special Foundation of the Shanghai Science and Technology Commission for Nano-Materials ResearchProject (J51042) supported by Leading Academic Discipline Project of the Shanghai Education Commission, China
文摘A Y2O3 particle enhanced Ni/TiC composite coating was fabricated in-situ on a TC4 Ti alloy by laser surface cladding. The phase component, microstructure, composition distribution and properties of the composite layer were investigated. The composite layer has graded microstructures and compositions, due to the fast melting followed by rapid solidification and cooling during laser cladding. The TiC powders are completely dissolved into the melted layer during melting and segregated as fine dendrites when solidified. The size of TiC dendrites decreases with increasing depth. Y2O3 fine particles distribute in the whole clad layer. The Y2O3 particle enhanced Ni/TiC composite layer has a quite uniform hardness along depth with a maximum value of HV1380, which is 4 times higher than the initial hardness. The wear resistance of the Ti alloy is significantly improved after laser cladding due to the high hardness of the composite coating.