Fine TiFe series alloy powder was fabricated by magnesothermic reduction of ilmenite as main raw material.Adiabatic temperature of the FeTiO_(3)-Mg system was studied through thermodynamic analysis.Meanwhile,the chara...Fine TiFe series alloy powder was fabricated by magnesothermic reduction of ilmenite as main raw material.Adiabatic temperature of the FeTiO_(3)-Mg system was studied through thermodynamic analysis.Meanwhile,the characteristics of TiFe series alloy were described by XRD,SEM and grading analysis.It is shown that combustion synthesis of the FeTiO_(3)-Mg system can carry out due to its strong exothermic reaction through adiabatic temperature calculate.Ultrafine TiFe series alloy powder after leached for 5 h has reasonable phases and morphology with the particle distribution of 0.2 to 1μm.It indicates that in-situ magnesothermic reduction of natural ilmenite is a feasible way to fabricate ultrafine powder with a relatively lower cost.展开更多
基金This work was financially supported by the Guangxi Science Research and Technology Exploiture Item(05112001-2A4)the Application Basic Research of Guangxi Natural Science Foundation(0575104).
文摘Fine TiFe series alloy powder was fabricated by magnesothermic reduction of ilmenite as main raw material.Adiabatic temperature of the FeTiO_(3)-Mg system was studied through thermodynamic analysis.Meanwhile,the characteristics of TiFe series alloy were described by XRD,SEM and grading analysis.It is shown that combustion synthesis of the FeTiO_(3)-Mg system can carry out due to its strong exothermic reaction through adiabatic temperature calculate.Ultrafine TiFe series alloy powder after leached for 5 h has reasonable phases and morphology with the particle distribution of 0.2 to 1μm.It indicates that in-situ magnesothermic reduction of natural ilmenite is a feasible way to fabricate ultrafine powder with a relatively lower cost.