Anatase TiO2 films were successfully prepared on foam nickel substrates by sol-gel technique using tetrabutyl titanate as precursor. The characteristics of the TiO2 films were investigated by XPS, XRD, FE-SEM, TEM and...Anatase TiO2 films were successfully prepared on foam nickel substrates by sol-gel technique using tetrabutyl titanate as precursor. The characteristics of the TiO2 films were investigated by XPS, XRD, FE-SEM, TEM and UV-Vis absorption spectra. The photocatalytic activities of TiO2 films were investigated by photocatalytic degradation reactions of gaseous acetaldehyde, an indoor pollutant, under ultraviolet light irradiation. It was found that Ni^2+ doping into TiO2 films due to the foam nickel substrates resulted in the extension of absorption edges of TiO2 films from UV region to visible light region. The pre-heating for foam nickel substrates resulted in the formation of NiO layer, which prevented effectively the injection of photogenerated electrons from TiO2 films to metal nickel. The TiO2 films displayed high photocatalytic activity for the degradation of acetaldehyde, and were enhanced by calcining the substrates and coating TiO2 films repeatedly. The high activity was mainly attributed to the improvement of the characteristics of substrate surface and the increase of active sites on photocatalyst.展开更多
TiO2 films were deposited at room temperature by DC pulse magnetron sputtering system.The crystalline structures,morphological features and photocatalytic activity of TiO2 films were systematically investigated by X-r...TiO2 films were deposited at room temperature by DC pulse magnetron sputtering system.The crystalline structures,morphological features and photocatalytic activity of TiO2 films were systematically investigated by X-ray diffraction(XRD),atomic force microscopy(AFM) and ultraviolet spectrophotometer,respectively.The results indicated that working pressure was the key deposition parameter in?uencing the TiO2 film phase composition at room temperature,which directly affected its photocatalytic activity.With increasing working pressure,the target self-bias decreases monotonously.Therefore,low temperature TiO2 phase(anatase) could be deposited with high working pressure.The anatase TiO2 films deposited with 1.4 Pa working pressure displayed the highest photocatalytic activity by the decomposition of Methyl Orange solution,which the degradation rate reached the maximum(35%) after irradiation by ultraviolet light for 1 h.展开更多
Anatase TiO2 sol was synthesized under mild conditions (75℃ and ambient pressure) by hydrolysis of titaniumn-butoxide in abundant acidic aqueous solution and subsequent reflux to enhance crystallization. At room te...Anatase TiO2 sol was synthesized under mild conditions (75℃ and ambient pressure) by hydrolysis of titaniumn-butoxide in abundant acidic aqueous solution and subsequent reflux to enhance crystallization. At room temperature and in ambient atmosphere, crystalline TiO2 thin films were deposited on polymethylmethacrylate (PMMA), SiO2-coated PMMA and SiO2-coated silicone rubber substrates from the as-prepared TiO2 sol by a dip-coating process. SiO2 layers prior to TiO2 thin films on polymer substrates could not only protect the substrates from the photocatalytic decomposition of the TiO2 thin films but also enhance the adhesion of the TiO2 thin films to the substrates. Field-emission type scanning electron microscope (FE-SEM) investigations revealed that the average particle sizes of the nanoparticles composing the TiO2 thin films were about 35-47 nm. The TiO2 thin films exhibited high photocatalytic activities in the degradation of reactive brilliant red dye X-3B in aqueous solution under aerated conditions. The preparation process of photocatalytic TiO2 thin films on the polymer substrates was quite simple and a low temperature route.展开更多
A PANI/TiO2 composite film deposited on the glass surface was successfully prepared using sol-gel dip-coating technique and chemical oxidation method. The film was characterized using XRD, AFM, and UV. The result show...A PANI/TiO2 composite film deposited on the glass surface was successfully prepared using sol-gel dip-coating technique and chemical oxidation method. The film was characterized using XRD, AFM, and UV. The result showed that the TiO2 film consists of both cuboid-shaped and anatase-phased TiO2 nanoparticles. The average grain size of TiO2 in the film was approximately 20 nm. After coating with PANI, the particle was changed into irregular spherical-shaped and the size was increased up to approximately 35 nm in diameter. UV-Vis spectroscopy analysis indicated that the coating of TiO2 with PANI would result in an enhancement of photocatalytic efficiency and an extension of the photoresponse of TiO2. The band gap of the PANI/TiO2 film was 3.18 eV. The photocatalytic property of the film was evaluated by the degradation of rhodamine-B. It was found that 67.1% and 83.2% of rhodamine-B could be degraded under sunlight and UV irradiation within 120 min using the PANI/TiO2 composite t-tim as photocatalyst.展开更多
TiO2 thin film has attracted considerable attention in recent years, due to its different refractive index and transparency with amorphous and different crysta ls in the visible and near-infrared wavelength region, hi...TiO2 thin film has attracted considerable attention in recent years, due to its different refractive index and transparency with amorphous and different crysta ls in the visible and near-infrared wavelength region, high dielectric constant, wide band gap, high wear resistance and stability, etc, for which make it being used in many fields. This paper aims to investigate the optical characterizatio n of thin film TiO2 on silicon wafer. The TiO2 thin films were prepared by DC re active magnetron sputtering process from Ti target. The reflectivity of the film s was measured by UV-3101PC, and the index of refraction (n) and extinction coef ficient (k) were measured by n & k Analyzer 1200.展开更多
A NiP/TiO2 composite film on carbon steel was prepared by electroless plating and sol-gel composite process. An artificial neural network was applied to optimize the prepared condition of the composite film. Corrosion...A NiP/TiO2 composite film on carbon steel was prepared by electroless plating and sol-gel composite process. An artificial neural network was applied to optimize the prepared condition of the composite film. Corrosion behavior of the NiP/TiO2 composite film was investigated by polarization resistance measurement, anode polarization, ESEM (environmental scanning electron microscopy) and EIS (electrochemical impedance spectroscopy) measurements. Results showed that the NiP/ TiO2 composite film has a good corrosion resistance in 0.5mol/L H2SO4 solution. The element valence of the composite film was characterized by XPS (X-ray photoelectron spectroscopy) spectrum, and an anticorrosion mechanism of the composite film was discussed.展开更多
Pb-doped TiO2 photocatalytic thin films were prepared on a soda-lime glass substrate via sol-gel method using TiO2 sol solution containing lead and characterized by X-ray photoelectron spectroscopy (XPS). The results ...Pb-doped TiO2 photocatalytic thin films were prepared on a soda-lime glass substrate via sol-gel method using TiO2 sol solution containing lead and characterized by X-ray photoelectron spectroscopy (XPS). The results showed that besides oxides of Ti(IV) there is a certain amount of oxides of To(?) and Ti(?) and Pb exists in the forms of PbTiO3 and PbO. The photocatalytic activity of the Pb-doped TiO2 films was evaluated by the photocatalytic decolorization of aqueous methyl orange and photocatalytic mechanism mas also analyzed.展开更多
A new technique for preparing TiO2 modified film on carbon steel was accomplished by electroless plating and sol-gel composite process. The artificial neural network was applied to optimize the preparing condition of ...A new technique for preparing TiO2 modified film on carbon steel was accomplished by electroless plating and sol-gel composite process. The artificial neural network was applied to optimize the preparing condition of TiO2 modified film. The optimized condition for forming TiO2 modified film on carbon steel was that NiP plating for 50 min, dip-coating times as 4, heat treatment time for 2 h, and the molar ratio of complexing agent and Ti(OC4HZ9)4 kept 1.5:1. The results showed that TiO2 modified film have good corrosion resistance. The result conformed that it is feasible to design the preparing conditions of TiO2 modified film by artificial neural network.展开更多
A new TiO2 modified film on carbon steel was prepared by electroless plating and sol gel composite process. An artificial neural net was used to optimize the preparing condition of the film. The optimized condition of...A new TiO2 modified film on carbon steel was prepared by electroless plating and sol gel composite process. An artificial neural net was used to optimize the preparing condition of the film. The optimized condition of the TiO2-modified film on carbon steel is as follows: plating time of NiP is 50 min, number of dip coating is 4, heat treatment time is 2 h, and the molar ratio of complexing reagent to Ti(OC4 H9)4 is 1.5 : 1. Corrosion behavior of carbon steel with coating was investigated by polarization resistance measurement, anode polarization, EIS and ESEM measurement. XPS was used to characterize the element valence of the modified film. Results show that carbon steel with TiO2 modified film has good corrosion resistance in 0.5 mol/L of H2SO4 solution and 0.5 mol/L of NaCl solution. It is also found that the preparing condition of forming TiO2-modified film can be obtained easily by the artificial neural net.展开更多
The microstructure properties of the sol-gel derived TiO2 films were studied by the atomic force microscopy (AFM). The films were prepared by dip coating process. The optical properties of the films were explained on ...The microstructure properties of the sol-gel derived TiO2 films were studied by the atomic force microscopy (AFM). The films were prepared by dip coating process. The optical properties of the films were explained on the basis of the microstructure of the films.展开更多
TiO2 is a promising photocatalyst. However, the low photocatalytic efficiency calls for the modification of TiO2. Metal- and nonmetal-doping of TiO2 have been proved to be effective ways to enhance photocatalytic prop...TiO2 is a promising photocatalyst. However, the low photocatalytic efficiency calls for the modification of TiO2. Metal- and nonmetal-doping of TiO2 have been proved to be effective ways to enhance photocatalytic properties. This review provides a deep insight into the understanding of the metal- and nonmetal-doped TiO2 photocatalysts. This article begins with the introduction of the crystal structures of TiO2 and applications of TiO2 materials. We then reviewed the doped-TiO2 system in two categories: (1) metal-doped TiO2 photocatalysts system, and (2) nonmetal-doped TiO2 photocatalysts system. Both experimental results and theoretical analyses are elaborated in this section. In the following part, for the advantages of TiO2 thin films over particles, various preparation methods to obtain TiO2 thin films are briefly discussed. Finally, this review ends with a concise conclusion and outlook of new trends in the development of TiO2-based photocatalysts.展开更多
In order to clarify the respective role of the UV light, catalyst, external bias as well as their combined effects on the photodegradation process and to clarify the photocatalytic mechanism under different experiment...In order to clarify the respective role of the UV light, catalyst, external bias as well as their combined effects on the photodegradation process and to clarify the photocatalytic mechanism under different experimental conditions, a series of experiments were conducted in a shallow pond photoreactor with an effective volume of 100 mL using TiO 2/Ti thin film prepared by anodization as photocatalyst. A 300W UV lamp( E max =365 nm)was used as side light source. The effect of light intensity on photocatalysis was also conducted. The results show that photocatalytic oxidation is an effective method for phenol removal from waters. The degradation rate can be improved by applying an anodic bias to the TiO 2/Ti film electrode, phenol can not be decomposed under only 365 nm UV light irradiation even in the presence of hydrogen peroxide. In the range of our research, the phenol removal rate can be described in terms of pseudo first order kinetics.展开更多
Ag TiO 2 thin films were prepared on glasses.The morphology and structure of Ag TiO 2 films were investigated by XRD, SEM and FT IR.The photocatalytic and hydrophilic properties of Ag TiO 2 thin films were also...Ag TiO 2 thin films were prepared on glasses.The morphology and structure of Ag TiO 2 films were investigated by XRD, SEM and FT IR.The photocatalytic and hydrophilic properties of Ag TiO 2 thin films were also evaluated by examining photocatalytic degradation dichlorophos under sunlight illumination and the change of contact angle respectively.The research results show that the Ag TiO 2 thin film is mainly composed of 20-100nm Ag and TiO 2 particles.The Ag TiO 2 thin films possess a super hydrophilic ability and higher photocatalytic activity than that of pure TiO 2 thin film.展开更多
The transparent C-doped TiO2 nanostructure films were fabricated on the silicate glass substrates by sol-gel spin-coated method. The as-prepared films were characterized by X-ray diffraction (XRD), scanning electron...The transparent C-doped TiO2 nanostructure films were fabricated on the silicate glass substrates by sol-gel spin-coated method. The as-prepared films were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), UV-visible absorption spectra (UV-vis) and X-ray photoelectron spectroscopy (XPS). The photocatalytic activity was evaluated via the photocatalytic oxidation of methylene blue in aqueous under daylight irradiation at room temperature. The results show that the daylight-induced photocatalytic activities of the as-prepared films are improved by the C-doping. The calcination temperatures significantly affect the morphology, microstructure and photocatalytic activity of the as-prepared samples. At 723 K, the C-doped TiO2 films exhibit the highest photocatalytic activity due to the synergetic effects of good crystallization, appropriate oxygen vacancies and strong absorption in the near UV and visible-light region.展开更多
Preparation of TiO<sub>2</sub> thin films by MOCVD method is presented in this paper. A MOCVD system has been designed and built. A wide range of processing conditions are investigated to deposit TiO<su...Preparation of TiO<sub>2</sub> thin films by MOCVD method is presented in this paper. A MOCVD system has been designed and built. A wide range of processing conditions are investigated to deposit TiO<sub>2</sub> films on Si wafers starting from metal-organic precursor tetrabutyl titanate. Activation energy of the film formation (E) is obtained to be 23.6 kJ/mol. Structure of films is pure anatase when deposit temperatures are low, rutile forms at 700℃. The films also exhibit preferred crystallographic orientations which strongly depend on deposit conditions. Refractive index increases with increasing of film thickness and decreasing of deposit temperature.展开更多
TiO2 thin films were prepared by DC magnetron sputtering with the oxygen flow rate higher than the threshold. The film deposited for 5 h was of anatase phase with a preferred orientation along the <220> directio...TiO2 thin films were prepared by DC magnetron sputtering with the oxygen flow rate higher than the threshold. The film deposited for 5 h was of anatase phase with a preferred orientation along the <220> direction, but the films deposited for 2 and 3 h were amorphous. The transmittance and photocatalytic activity of the TiO2 films increased constantly with increasing film thickness. When the annealing temperature was lower than 700℃, only anatase grew in the TiO2 film. TiO2 phase changed from anatase to rutile when the annealing temperature was above 800℃. The photocatalytic activity decreased with increasing annealing temperature.展开更多
Unique and various microstructures of titanium oxide(TiO_2 ) film including macroporous structure, chromatic veins and rings, have been easily fabricated by mist deposition method on silicon substrate with mild prepar...Unique and various microstructures of titanium oxide(TiO_2 ) film including macroporous structure, chromatic veins and rings, have been easily fabricated by mist deposition method on silicon substrate with mild preparation conditions. Rutile phase TiO_2 nanoparticles were directly used as starting material to prepare film and led to a simple preparation process. It was found that several different microstructures existed in the sample and changed with the varied positions from the center to the edge of the film when the concentration of the TiO_2 suspension is 0.06 mol/l, the deposition time is 30 min, the flow rate is 1 l/min and the temperature is150. The surface texturing shows apparent distinction as the concentration of the TiO_2 suspension decreased to 0.03 mol/l and 0.01 mol/l.展开更多
The nano-ZnFe2O4/TiO2 films possess the functions of desulfurization and degradation for organic pollutants. The sols of ZnFe2O4/TiO2 were prepared by sol-gel method and coated on glass and porous ceramic by vertical ...The nano-ZnFe2O4/TiO2 films possess the functions of desulfurization and degradation for organic pollutants. The sols of ZnFe2O4/TiO2 were prepared by sol-gel method and coated on glass and porous ceramic by vertical coating and dipping-lift processes, respectively, and the samples were obtained after drying and sintering. The composition, appearance, absorption spectrum of the films, and the influence of the film on porous ceramic performances were analyzed using SEM, AFM, UVVis spectrometer, and mercury porosimeter, respectively, to determine the operation parameters of the multifunction porous ceramic elements for gas-purification.展开更多
基金Project supported by the Special Foundation of Nanometer Technology from Shanghai Municipal Science and Technology Commis-sion(STCSM) (No. 0552nm002).
文摘Anatase TiO2 films were successfully prepared on foam nickel substrates by sol-gel technique using tetrabutyl titanate as precursor. The characteristics of the TiO2 films were investigated by XPS, XRD, FE-SEM, TEM and UV-Vis absorption spectra. The photocatalytic activities of TiO2 films were investigated by photocatalytic degradation reactions of gaseous acetaldehyde, an indoor pollutant, under ultraviolet light irradiation. It was found that Ni^2+ doping into TiO2 films due to the foam nickel substrates resulted in the extension of absorption edges of TiO2 films from UV region to visible light region. The pre-heating for foam nickel substrates resulted in the formation of NiO layer, which prevented effectively the injection of photogenerated electrons from TiO2 films to metal nickel. The TiO2 films displayed high photocatalytic activity for the degradation of acetaldehyde, and were enhanced by calcining the substrates and coating TiO2 films repeatedly. The high activity was mainly attributed to the improvement of the characteristics of substrate surface and the increase of active sites on photocatalyst.
基金supported by the Dalian Foundation for Development of Science and Technology (No.2006A13GX029)
文摘TiO2 films were deposited at room temperature by DC pulse magnetron sputtering system.The crystalline structures,morphological features and photocatalytic activity of TiO2 films were systematically investigated by X-ray diffraction(XRD),atomic force microscopy(AFM) and ultraviolet spectrophotometer,respectively.The results indicated that working pressure was the key deposition parameter in?uencing the TiO2 film phase composition at room temperature,which directly affected its photocatalytic activity.With increasing working pressure,the target self-bias decreases monotonously.Therefore,low temperature TiO2 phase(anatase) could be deposited with high working pressure.The anatase TiO2 films deposited with 1.4 Pa working pressure displayed the highest photocatalytic activity by the decomposition of Methyl Orange solution,which the degradation rate reached the maximum(35%) after irradiation by ultraviolet light for 1 h.
文摘Anatase TiO2 sol was synthesized under mild conditions (75℃ and ambient pressure) by hydrolysis of titaniumn-butoxide in abundant acidic aqueous solution and subsequent reflux to enhance crystallization. At room temperature and in ambient atmosphere, crystalline TiO2 thin films were deposited on polymethylmethacrylate (PMMA), SiO2-coated PMMA and SiO2-coated silicone rubber substrates from the as-prepared TiO2 sol by a dip-coating process. SiO2 layers prior to TiO2 thin films on polymer substrates could not only protect the substrates from the photocatalytic decomposition of the TiO2 thin films but also enhance the adhesion of the TiO2 thin films to the substrates. Field-emission type scanning electron microscope (FE-SEM) investigations revealed that the average particle sizes of the nanoparticles composing the TiO2 thin films were about 35-47 nm. The TiO2 thin films exhibited high photocatalytic activities in the degradation of reactive brilliant red dye X-3B in aqueous solution under aerated conditions. The preparation process of photocatalytic TiO2 thin films on the polymer substrates was quite simple and a low temperature route.
基金This work was financially supported by the Combined Project between the Educational Commission and the Economic Commission of Gansu Province (Nos. 99CX-04, 0310B-08)the Natural Science Foundation of Gansu Province (No. 3ZS041-A25-028)the Invention Project of Science & Technology (No. KJCXGC-01, NWNU), China.
文摘A PANI/TiO2 composite film deposited on the glass surface was successfully prepared using sol-gel dip-coating technique and chemical oxidation method. The film was characterized using XRD, AFM, and UV. The result showed that the TiO2 film consists of both cuboid-shaped and anatase-phased TiO2 nanoparticles. The average grain size of TiO2 in the film was approximately 20 nm. After coating with PANI, the particle was changed into irregular spherical-shaped and the size was increased up to approximately 35 nm in diameter. UV-Vis spectroscopy analysis indicated that the coating of TiO2 with PANI would result in an enhancement of photocatalytic efficiency and an extension of the photoresponse of TiO2. The band gap of the PANI/TiO2 film was 3.18 eV. The photocatalytic property of the film was evaluated by the degradation of rhodamine-B. It was found that 67.1% and 83.2% of rhodamine-B could be degraded under sunlight and UV irradiation within 120 min using the PANI/TiO2 composite t-tim as photocatalyst.
基金This work was supported by the National Natural Science Foundation of China(No,50376067)the Plan for Science&Technology Development of Guangzhou(2001-Z-117-01).
文摘TiO2 thin film has attracted considerable attention in recent years, due to its different refractive index and transparency with amorphous and different crysta ls in the visible and near-infrared wavelength region, high dielectric constant, wide band gap, high wear resistance and stability, etc, for which make it being used in many fields. This paper aims to investigate the optical characterizatio n of thin film TiO2 on silicon wafer. The TiO2 thin films were prepared by DC re active magnetron sputtering process from Ti target. The reflectivity of the film s was measured by UV-3101PC, and the index of refraction (n) and extinction coef ficient (k) were measured by n & k Analyzer 1200.
文摘A NiP/TiO2 composite film on carbon steel was prepared by electroless plating and sol-gel composite process. An artificial neural network was applied to optimize the prepared condition of the composite film. Corrosion behavior of the NiP/TiO2 composite film was investigated by polarization resistance measurement, anode polarization, ESEM (environmental scanning electron microscopy) and EIS (electrochemical impedance spectroscopy) measurements. Results showed that the NiP/ TiO2 composite film has a good corrosion resistance in 0.5mol/L H2SO4 solution. The element valence of the composite film was characterized by XPS (X-ray photoelectron spectroscopy) spectrum, and an anticorrosion mechanism of the composite film was discussed.
基金Natural Science Foundation of Hubei Province, China (No. 98J029)
文摘Pb-doped TiO2 photocatalytic thin films were prepared on a soda-lime glass substrate via sol-gel method using TiO2 sol solution containing lead and characterized by X-ray photoelectron spectroscopy (XPS). The results showed that besides oxides of Ti(IV) there is a certain amount of oxides of To(?) and Ti(?) and Pb exists in the forms of PbTiO3 and PbO. The photocatalytic activity of the Pb-doped TiO2 films was evaluated by the photocatalytic decolorization of aqueous methyl orange and photocatalytic mechanism mas also analyzed.
文摘A new technique for preparing TiO2 modified film on carbon steel was accomplished by electroless plating and sol-gel composite process. The artificial neural network was applied to optimize the preparing condition of TiO2 modified film. The optimized condition for forming TiO2 modified film on carbon steel was that NiP plating for 50 min, dip-coating times as 4, heat treatment time for 2 h, and the molar ratio of complexing agent and Ti(OC4HZ9)4 kept 1.5:1. The results showed that TiO2 modified film have good corrosion resistance. The result conformed that it is feasible to design the preparing conditions of TiO2 modified film by artificial neural network.
文摘A new TiO2 modified film on carbon steel was prepared by electroless plating and sol gel composite process. An artificial neural net was used to optimize the preparing condition of the film. The optimized condition of the TiO2-modified film on carbon steel is as follows: plating time of NiP is 50 min, number of dip coating is 4, heat treatment time is 2 h, and the molar ratio of complexing reagent to Ti(OC4 H9)4 is 1.5 : 1. Corrosion behavior of carbon steel with coating was investigated by polarization resistance measurement, anode polarization, EIS and ESEM measurement. XPS was used to characterize the element valence of the modified film. Results show that carbon steel with TiO2 modified film has good corrosion resistance in 0.5 mol/L of H2SO4 solution and 0.5 mol/L of NaCl solution. It is also found that the preparing condition of forming TiO2-modified film can be obtained easily by the artificial neural net.
基金We are very grateful to the National Natural Science of Foundation of China(No.69978017,59802007)Shanghai Education Committee(No JW99-TJ-03)for their help and financial supports
文摘The microstructure properties of the sol-gel derived TiO2 films were studied by the atomic force microscopy (AFM). The films were prepared by dip coating process. The optical properties of the films were explained on the basis of the microstructure of the films.
文摘TiO2 is a promising photocatalyst. However, the low photocatalytic efficiency calls for the modification of TiO2. Metal- and nonmetal-doping of TiO2 have been proved to be effective ways to enhance photocatalytic properties. This review provides a deep insight into the understanding of the metal- and nonmetal-doped TiO2 photocatalysts. This article begins with the introduction of the crystal structures of TiO2 and applications of TiO2 materials. We then reviewed the doped-TiO2 system in two categories: (1) metal-doped TiO2 photocatalysts system, and (2) nonmetal-doped TiO2 photocatalysts system. Both experimental results and theoretical analyses are elaborated in this section. In the following part, for the advantages of TiO2 thin films over particles, various preparation methods to obtain TiO2 thin films are briefly discussed. Finally, this review ends with a concise conclusion and outlook of new trends in the development of TiO2-based photocatalysts.
文摘In order to clarify the respective role of the UV light, catalyst, external bias as well as their combined effects on the photodegradation process and to clarify the photocatalytic mechanism under different experimental conditions, a series of experiments were conducted in a shallow pond photoreactor with an effective volume of 100 mL using TiO 2/Ti thin film prepared by anodization as photocatalyst. A 300W UV lamp( E max =365 nm)was used as side light source. The effect of light intensity on photocatalysis was also conducted. The results show that photocatalytic oxidation is an effective method for phenol removal from waters. The degradation rate can be improved by applying an anodic bias to the TiO 2/Ti film electrode, phenol can not be decomposed under only 365 nm UV light irradiation even in the presence of hydrogen peroxide. In the range of our research, the phenol removal rate can be described in terms of pseudo first order kinetics.
文摘Ag TiO 2 thin films were prepared on glasses.The morphology and structure of Ag TiO 2 films were investigated by XRD, SEM and FT IR.The photocatalytic and hydrophilic properties of Ag TiO 2 thin films were also evaluated by examining photocatalytic degradation dichlorophos under sunlight illumination and the change of contact angle respectively.The research results show that the Ag TiO 2 thin film is mainly composed of 20-100nm Ag and TiO 2 particles.The Ag TiO 2 thin films possess a super hydrophilic ability and higher photocatalytic activity than that of pure TiO 2 thin film.
基金Funded by Shan Xi Research Fund for Returned Scholars (No.2007-25)Shan Xi Open Fund for Key Laboratory(No.2008012013-7)The Specialized Fund for The Innovative of College Students of Tai Yuan City(No.09122018)
文摘The transparent C-doped TiO2 nanostructure films were fabricated on the silicate glass substrates by sol-gel spin-coated method. The as-prepared films were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), UV-visible absorption spectra (UV-vis) and X-ray photoelectron spectroscopy (XPS). The photocatalytic activity was evaluated via the photocatalytic oxidation of methylene blue in aqueous under daylight irradiation at room temperature. The results show that the daylight-induced photocatalytic activities of the as-prepared films are improved by the C-doping. The calcination temperatures significantly affect the morphology, microstructure and photocatalytic activity of the as-prepared samples. At 723 K, the C-doped TiO2 films exhibit the highest photocatalytic activity due to the synergetic effects of good crystallization, appropriate oxygen vacancies and strong absorption in the near UV and visible-light region.
文摘Preparation of TiO<sub>2</sub> thin films by MOCVD method is presented in this paper. A MOCVD system has been designed and built. A wide range of processing conditions are investigated to deposit TiO<sub>2</sub> films on Si wafers starting from metal-organic precursor tetrabutyl titanate. Activation energy of the film formation (E) is obtained to be 23.6 kJ/mol. Structure of films is pure anatase when deposit temperatures are low, rutile forms at 700℃. The films also exhibit preferred crystallographic orientations which strongly depend on deposit conditions. Refractive index increases with increasing of film thickness and decreasing of deposit temperature.
基金supported by the National Natural Science Foundation of China(No.50001013)Hundred-Talent Project of CAS and the NSFC for Outstanding Young Scientists(No.59625103).
文摘TiO2 thin films were prepared by DC magnetron sputtering with the oxygen flow rate higher than the threshold. The film deposited for 5 h was of anatase phase with a preferred orientation along the <220> direction, but the films deposited for 2 and 3 h were amorphous. The transmittance and photocatalytic activity of the TiO2 films increased constantly with increasing film thickness. When the annealing temperature was lower than 700℃, only anatase grew in the TiO2 film. TiO2 phase changed from anatase to rutile when the annealing temperature was above 800℃. The photocatalytic activity decreased with increasing annealing temperature.
基金supported by a Grant-in-Aid for Scientific Research on Innovative Areas "New Polymeric Materials Based on Element-Blocks (No. 2401)" (24102004) of The Ministry of Education, Culture, Sports, Science, and Technology, Japan
文摘Unique and various microstructures of titanium oxide(TiO_2 ) film including macroporous structure, chromatic veins and rings, have been easily fabricated by mist deposition method on silicon substrate with mild preparation conditions. Rutile phase TiO_2 nanoparticles were directly used as starting material to prepare film and led to a simple preparation process. It was found that several different microstructures existed in the sample and changed with the varied positions from the center to the edge of the film when the concentration of the TiO_2 suspension is 0.06 mol/l, the deposition time is 30 min, the flow rate is 1 l/min and the temperature is150. The surface texturing shows apparent distinction as the concentration of the TiO_2 suspension decreased to 0.03 mol/l and 0.01 mol/l.
基金Supported by National 863 Project of China (2001AAA333040).
文摘The nano-ZnFe2O4/TiO2 films possess the functions of desulfurization and degradation for organic pollutants. The sols of ZnFe2O4/TiO2 were prepared by sol-gel method and coated on glass and porous ceramic by vertical coating and dipping-lift processes, respectively, and the samples were obtained after drying and sintering. The composition, appearance, absorption spectrum of the films, and the influence of the film on porous ceramic performances were analyzed using SEM, AFM, UVVis spectrometer, and mercury porosimeter, respectively, to determine the operation parameters of the multifunction porous ceramic elements for gas-purification.