A series of SO 2- 4/TiO 2 SiO 2 catalysts with different mass fractions of SiO 2 were prepared by sol gel method. The effect of adding SiO 2 on the crystal structure, specific surface area, oxygen adsorption, and acid...A series of SO 2- 4/TiO 2 SiO 2 catalysts with different mass fractions of SiO 2 were prepared by sol gel method. The effect of adding SiO 2 on the crystal structure, specific surface area, oxygen adsorption, and acidity of SO 2- 4/TiO 2 catalyst and its photocatalytic property for degradation of bromomethane was studied. The results showed that the specific surface area and amount of oxygen adsorption of catalyst were increased by addition of SiO 2, leading to the obvious increase on photocatalytic activity of SO 2- 4/TiO 2 SiO 2 catalysts and mineralization ratio of bromomethane. Comparing with SO 2- 4/TiO 2, the acidic strength and anti moisture ability of SO 2- 4/TiO 2 SiO 2 catalyst were decreased.展开更多
A comparative study on the corrosion resistance of 17Ni/（NiFe2O4-10NiO） cermet inert anode prepared in differentsintering atmospheres was conducted in Na3AlF6-Al2O3 melt. The results indicate that the corrosion rate...A comparative study on the corrosion resistance of 17Ni/（NiFe2O4-10NiO） cermet inert anode prepared in differentsintering atmospheres was conducted in Na3AlF6-Al2O3 melt. The results indicate that the corrosion rates of NiFe2O4-based cermetanodes prepared in the vacuum and the atmosphere with oxygen content of 2×10^-3 （volume fraction） are 6.46 and 2.71 cm/a,respectively. Though there is a transition layer with lots of holes or pores, a densified layer is formed on the surface of anode due tosome reactions producing aluminates. For the anode prepared in the atmosphere with oxygen content of 2×10^-3, the thickness of thedensification layer （about 50 μm） is thicker than that （about 30 μm） formed on the surface of anode prepared in the vacuum. Thecontents of NiO and Fe（II） in NiFe2xO4-y-z increase with the decrease of oxygen content in sintering atmosphere, which reduces thecorrosion resistance of the material.展开更多
Ultra fine SO 2- 4/TiO 2-SiO 2 complex catalysts were synthesized by the one-step calcination method,which used titania sulfate and white carbon as raw materials and polyvinyl alcohol as dispersing agent. Catalysts ar...Ultra fine SO 2- 4/TiO 2-SiO 2 complex catalysts were synthesized by the one-step calcination method,which used titania sulfate and white carbon as raw materials and polyvinyl alcohol as dispersing agent. Catalysts are characterized by XRDIRTDA and BET. Different preparation factors were discussed.The catalysts consisting of SO 2- 43.4% and TiO 2∶SiO 2=1∶6 showed excellent reaction activity and stability for the photocatalytic degradation of phenol.Controlling calcination temperature and time (450℃,2h) could avoid or diminish the formation of Ti-O-Si bond and obtain higher V g and better dispersivity of TiO 2 on the surface of SiO 2.The kinetic study on photocatalytic degradation of phenol with the complex catalysts in a suspension system under 40W UV-lamp showed that apparent rate constant k conformed to a zero-order kinetic model at initial concentration <100mg·L -1 and increased with increasing pH value of phenol solution up to pH=12.When pH=10,k=3.32×10 -1 mg·L -1 ·min -1 . Solar photocatalytic experiment also gave good results.展开更多
NiFe2O4-10NiO-based cermet inert anodes for aluminium electrolysis were prepared and their properties were investigated in a lab-scale electrolysis cell. The results show that the inert anodes exhibit good performance...NiFe2O4-10NiO-based cermet inert anodes for aluminium electrolysis were prepared and their properties were investigated in a lab-scale electrolysis cell. The results show that the inert anodes exhibit good performance during electrolysis in molten salt cryolite at 960 °C, but according to the analyses of phase compositions and microstructures through XRD, SEM/EDX and metallographic analysis, the metal in the anodes is preferentially corroded and many pores are produced on the anode surface after electrolysis. The preferential dissolution of Fe in the NiFe2O4 phase may lead to the non-uniform corrosion of NiFe2O4 grains. Moreover, a dense protective layer of NiFe2O4-NiAl2O4-FeAl2O4 is formed on the anode surface, which originates from the reaction of Al2O3 dissolved in the electrolyte with NiO or FeO, the annexation of NiFe2O4-NiAl2O4-FeAl2O4 to NiO and volume expansion. Thus, the dense NiFe2O4-NiAl2O4-FeAl2O4 layer inhibits the metal loss and ceramic-phase corrosion on the surface of the cermet inert anodes.展开更多
文摘A series of SO 2- 4/TiO 2 SiO 2 catalysts with different mass fractions of SiO 2 were prepared by sol gel method. The effect of adding SiO 2 on the crystal structure, specific surface area, oxygen adsorption, and acidity of SO 2- 4/TiO 2 catalyst and its photocatalytic property for degradation of bromomethane was studied. The results showed that the specific surface area and amount of oxygen adsorption of catalyst were increased by addition of SiO 2, leading to the obvious increase on photocatalytic activity of SO 2- 4/TiO 2 SiO 2 catalysts and mineralization ratio of bromomethane. Comparing with SO 2- 4/TiO 2, the acidic strength and anti moisture ability of SO 2- 4/TiO 2 SiO 2 catalyst were decreased.
基金Project(51474238)supported by the National Natural Science Foundation of China
文摘A comparative study on the corrosion resistance of 17Ni/（NiFe2O4-10NiO） cermet inert anode prepared in differentsintering atmospheres was conducted in Na3AlF6-Al2O3 melt. The results indicate that the corrosion rates of NiFe2O4-based cermetanodes prepared in the vacuum and the atmosphere with oxygen content of 2×10^-3 （volume fraction） are 6.46 and 2.71 cm/a,respectively. Though there is a transition layer with lots of holes or pores, a densified layer is formed on the surface of anode due tosome reactions producing aluminates. For the anode prepared in the atmosphere with oxygen content of 2×10^-3, the thickness of thedensification layer （about 50 μm） is thicker than that （about 30 μm） formed on the surface of anode prepared in the vacuum. Thecontents of NiO and Fe（II） in NiFe2xO4-y-z increase with the decrease of oxygen content in sintering atmosphere, which reduces thecorrosion resistance of the material.
文摘Ultra fine SO 2- 4/TiO 2-SiO 2 complex catalysts were synthesized by the one-step calcination method,which used titania sulfate and white carbon as raw materials and polyvinyl alcohol as dispersing agent. Catalysts are characterized by XRDIRTDA and BET. Different preparation factors were discussed.The catalysts consisting of SO 2- 43.4% and TiO 2∶SiO 2=1∶6 showed excellent reaction activity and stability for the photocatalytic degradation of phenol.Controlling calcination temperature and time (450℃,2h) could avoid or diminish the formation of Ti-O-Si bond and obtain higher V g and better dispersivity of TiO 2 on the surface of SiO 2.The kinetic study on photocatalytic degradation of phenol with the complex catalysts in a suspension system under 40W UV-lamp showed that apparent rate constant k conformed to a zero-order kinetic model at initial concentration <100mg·L -1 and increased with increasing pH value of phenol solution up to pH=12.When pH=10,k=3.32×10 -1 mg·L -1 ·min -1 . Solar photocatalytic experiment also gave good results.
基金Project (2012FJ6123) supported by the Project of Science and Technology of Hunan Province,ChinaProject supported by Post-Doctoral Foundation of Central South University,China+1 种基金Project (CL12100) supported the Undergraduate Innovative Training of Central South University,ChinaProject (2282013bkso13) supported by Free Exploration Plan of Central South University,China
文摘NiFe2O4-10NiO-based cermet inert anodes for aluminium electrolysis were prepared and their properties were investigated in a lab-scale electrolysis cell. The results show that the inert anodes exhibit good performance during electrolysis in molten salt cryolite at 960 °C, but according to the analyses of phase compositions and microstructures through XRD, SEM/EDX and metallographic analysis, the metal in the anodes is preferentially corroded and many pores are produced on the anode surface after electrolysis. The preferential dissolution of Fe in the NiFe2O4 phase may lead to the non-uniform corrosion of NiFe2O4 grains. Moreover, a dense protective layer of NiFe2O4-NiAl2O4-FeAl2O4 is formed on the anode surface, which originates from the reaction of Al2O3 dissolved in the electrolyte with NiO or FeO, the annexation of NiFe2O4-NiAl2O4-FeAl2O4 to NiO and volume expansion. Thus, the dense NiFe2O4-NiAl2O4-FeAl2O4 layer inhibits the metal loss and ceramic-phase corrosion on the surface of the cermet inert anodes.