3D flower-like hierarchical mesoporous Bi_(4)O_(5)I_(2)/MoS_(2)Z-scheme layered heterojunction photocatalyst was fabricated by oil bath and hydrothermal methods.The heterojunction with narrow band gap of~1.95 eV exten...3D flower-like hierarchical mesoporous Bi_(4)O_(5)I_(2)/MoS_(2)Z-scheme layered heterojunction photocatalyst was fabricated by oil bath and hydrothermal methods.The heterojunction with narrow band gap of~1.95 eV extended the photoresponse to near-infrared region,which showed obvious photothermal effect due to the introduction of MoS_(2) with broad spectrum response.MoS_(2) nanosheets were anchored onto the surface of flower-like hierarchical mesoporous Bi_(4)O_(5)I_(2) nanosheets,thereby forming efficient layered heterojunctions,the solar-driven photocatalytic efficiency in degradation of highly toxic dichlorophenol and reduction of hexavalent chromium was improved to 98.5%and 99.2%,which was~4 and 7 times higher than that of the pristine Bi_(4)O_(5)I_(2),respectively.In addition,the photocatalytic hydrogen production rate reached 496.78 μmol h^(-1)g^(-1),which was~6 times higher than that of the pristine Bi_(4)O_(5)I_(2).The excellent photocatalytic performance can be ascribed to the promoted photothermal effect,as well as,the formation of compact Z-scheme layered heterojunctions.The 3D flower-like hierarchical mesoporous structure provided adequate surface active-sites,which was conducive to the mass transfer.Moreover,the high stability of the prepared photocatalyst further promoted its potential practical application.This strategy also provides new insights for fabricating layered Zscheme heterojunctions photocatalysts with highly photothermal-photocatalytic efficiency.展开更多
Catalytic oxidation of benzene with N_(2)O to phenol over the hierarchical and microporous Fe/ZSM-5-based catalysts in a continuous fixedbed reactor was investigated.The spent catalyst was in-situ regenerated by an ox...Catalytic oxidation of benzene with N_(2)O to phenol over the hierarchical and microporous Fe/ZSM-5-based catalysts in a continuous fixedbed reactor was investigated.The spent catalyst was in-situ regenerated by an oxidative treatment using N_(2)O and in total 10 reaction-regeneration cycles were performed.A 100% N_(2)O conversion,93.3% phenol selectivity,and high initial phenol formation rate of 16.49±0.06mmol_(phenol gcatalyst)^(-1)h^(-1)at time on stream(TOS) of 5 min,and a good phenol productivity of 147.06 mmol_(phenol gcatalyst)^(-1)during catalyst lifetime of 1800 min were obtained on a fresh hierarchical Fe/ZSM-5-Hi2.8 catalyst.With the reaction-regeneration cycle,N_(2)O conversion is fully recovered within TOS of 3 h,moreover,the phenol productivity was decreased ca.2.2±0.8% after each cycle,leading to a total phenol productivity of ca.0.44 ton_(pheol kg_(catalyst)^(-1)estimated for 300 cycles.Catalyst characterizations imply that the coke is rapidly deposited on catalyst surface in the initial TOS of 3 h(0.28 mgc_(gcatalyst)^(-1)min^(-1)) and gradually becomes graphitic during the TOS of 30 h with a slow formation rate of 0.06 mgc g_(catalyst)^(-1)min^(-1).Among others(e.g.,the decrease of textural property and acidity),the nearly complete coverage of the active Fe-O-Al sites by coke accounts for the main catalyst deactivation.Besides these reversible deactivation characteristics related to coking,the irreversible catalyst deactivation is also observed with the reaction-regeneration cycle.The latter is reflected by a further decreased amount of the active Fe-O-Al sites,which agglomerate on catalyst surface with the cycle,likely associated with the hard coke residue that is not completely removed by the regeneration.展开更多
The preparation and electrocatalytic activity for oxygen evolution of the thermally prepared Ti anodes coated with IrO2-Ta2O5 were studied. The structure and morphologies of the oxide films with different contents of ...The preparation and electrocatalytic activity for oxygen evolution of the thermally prepared Ti anodes coated with IrO2-Ta2O5 were studied. The structure and morphologies of the oxide films with different contents of IrO2 were determined by XRD and SEM respectively. Their electrochemical properties were studied by Linear Sweep Voltammetry, Tafel Plot and Cyclic Voltammetry. The results show that iridium and tantalum can form solid solution and the mutual solubility is affected by the ratio of Ir to Ta in coating solution. With increasing IrO2 content in the coatings, the amount of fine crystallites of IrO2 is increased and the electrocatalytic capability of oxygen evolution is strengthened. The coating adhesion and rigidity decrease, which affects electrochemical activity of the anode when the content of IrO2 is too high. The electrochemically active surface area is determined not only by the content of IrO2but also the structure and morphology of the anode coatings. It is probably due to the existence of proper quantities of inert Ta2O5 which results in a typical morphology of cracks and solid solution structure.展开更多
基金support of this research by the National Natural Science Foundation of China(21871078)the Natural Science Foundation of Heilongjiang Province(JQ2019B001 and B2018010)+3 种基金the Heilongjiang Postdoctoral Startup Fund(LBH-Q14135)the Heilongjiang University Science Fund for Distinguished Young Scholars(JCL201802)the Heilongjiang Provincial Institutions of Higher Learning Basic Research Funds Basic Research Projects(KJCX201909)the Heilongjiang Touyan Innovation Team Program.
文摘3D flower-like hierarchical mesoporous Bi_(4)O_(5)I_(2)/MoS_(2)Z-scheme layered heterojunction photocatalyst was fabricated by oil bath and hydrothermal methods.The heterojunction with narrow band gap of~1.95 eV extended the photoresponse to near-infrared region,which showed obvious photothermal effect due to the introduction of MoS_(2) with broad spectrum response.MoS_(2) nanosheets were anchored onto the surface of flower-like hierarchical mesoporous Bi_(4)O_(5)I_(2) nanosheets,thereby forming efficient layered heterojunctions,the solar-driven photocatalytic efficiency in degradation of highly toxic dichlorophenol and reduction of hexavalent chromium was improved to 98.5%and 99.2%,which was~4 and 7 times higher than that of the pristine Bi_(4)O_(5)I_(2),respectively.In addition,the photocatalytic hydrogen production rate reached 496.78 μmol h^(-1)g^(-1),which was~6 times higher than that of the pristine Bi_(4)O_(5)I_(2).The excellent photocatalytic performance can be ascribed to the promoted photothermal effect,as well as,the formation of compact Z-scheme layered heterojunctions.The 3D flower-like hierarchical mesoporous structure provided adequate surface active-sites,which was conducive to the mass transfer.Moreover,the high stability of the prepared photocatalyst further promoted its potential practical application.This strategy also provides new insights for fabricating layered Zscheme heterojunctions photocatalysts with highly photothermal-photocatalytic efficiency.
基金Financial support by the Specialized Research Fund for Doctoral Program of Higher Education,China (No.20120010110003)。
文摘Catalytic oxidation of benzene with N_(2)O to phenol over the hierarchical and microporous Fe/ZSM-5-based catalysts in a continuous fixedbed reactor was investigated.The spent catalyst was in-situ regenerated by an oxidative treatment using N_(2)O and in total 10 reaction-regeneration cycles were performed.A 100% N_(2)O conversion,93.3% phenol selectivity,and high initial phenol formation rate of 16.49±0.06mmol_(phenol gcatalyst)^(-1)h^(-1)at time on stream(TOS) of 5 min,and a good phenol productivity of 147.06 mmol_(phenol gcatalyst)^(-1)during catalyst lifetime of 1800 min were obtained on a fresh hierarchical Fe/ZSM-5-Hi2.8 catalyst.With the reaction-regeneration cycle,N_(2)O conversion is fully recovered within TOS of 3 h,moreover,the phenol productivity was decreased ca.2.2±0.8% after each cycle,leading to a total phenol productivity of ca.0.44 ton_(pheol kg_(catalyst)^(-1)estimated for 300 cycles.Catalyst characterizations imply that the coke is rapidly deposited on catalyst surface in the initial TOS of 3 h(0.28 mgc_(gcatalyst)^(-1)min^(-1)) and gradually becomes graphitic during the TOS of 30 h with a slow formation rate of 0.06 mgc g_(catalyst)^(-1)min^(-1).Among others(e.g.,the decrease of textural property and acidity),the nearly complete coverage of the active Fe-O-Al sites by coke accounts for the main catalyst deactivation.Besides these reversible deactivation characteristics related to coking,the irreversible catalyst deactivation is also observed with the reaction-regeneration cycle.The latter is reflected by a further decreased amount of the active Fe-O-Al sites,which agglomerate on catalyst surface with the cycle,likely associated with the hard coke residue that is not completely removed by the regeneration.
基金Project(50499330) supported by the National Natural Science Foundation of China
文摘The preparation and electrocatalytic activity for oxygen evolution of the thermally prepared Ti anodes coated with IrO2-Ta2O5 were studied. The structure and morphologies of the oxide films with different contents of IrO2 were determined by XRD and SEM respectively. Their electrochemical properties were studied by Linear Sweep Voltammetry, Tafel Plot and Cyclic Voltammetry. The results show that iridium and tantalum can form solid solution and the mutual solubility is affected by the ratio of Ir to Ta in coating solution. With increasing IrO2 content in the coatings, the amount of fine crystallites of IrO2 is increased and the electrocatalytic capability of oxygen evolution is strengthened. The coating adhesion and rigidity decrease, which affects electrochemical activity of the anode when the content of IrO2 is too high. The electrochemically active surface area is determined not only by the content of IrO2but also the structure and morphology of the anode coatings. It is probably due to the existence of proper quantities of inert Ta2O5 which results in a typical morphology of cracks and solid solution structure.