Downconversion （DC） with emission of two near-infrared photons about 1000 nm for each blue photon absorbed was obtained in thulium （Tm3＋） and ytterbium （Yb3＋） codoped yt- trium lithium fluoride （LiYF4） singl...Downconversion （DC） with emission of two near-infrared photons about 1000 nm for each blue photon absorbed was obtained in thulium （Tm3＋） and ytterbium （Yb3＋） codoped yt- trium lithium fluoride （LiYF4） single crystals grown by an improved Bridgman method. The luminescent properties of the crystals were measured through photoluminescence excitation, emission spectra and decay curves. Luminescence between 960 and 1050 nm from yb3＋： 2Fs/2--＋2FT/2 transition, which was originated from the DC from Tm3＋ ions to Yb3＋ ions, was observed under the excitation of blue photon at 465 nm. Moreover, the energy transfer processes were studied based on the Inokuti-Hirayama model, and the results indicated that the energy transfer from Tm3＋ to Yb3＋ was an electric dipole-dipole interaction. The max- imum quantum cutting efficiency approached with 0.49mo1% Tm3＋ and 5.99mo1% Yb3＋. increasing the energy efficiency of crystalline energy part of the solar spectrum. up to 167.5% in LiYF4 single crystal codoped Application of this crystal has prospects for Si solar cells by photon doubling of the high展开更多
文摘Downconversion （DC） with emission of two near-infrared photons about 1000 nm for each blue photon absorbed was obtained in thulium （Tm3＋） and ytterbium （Yb3＋） codoped yt- trium lithium fluoride （LiYF4） single crystals grown by an improved Bridgman method. The luminescent properties of the crystals were measured through photoluminescence excitation, emission spectra and decay curves. Luminescence between 960 and 1050 nm from yb3＋： 2Fs/2--＋2FT/2 transition, which was originated from the DC from Tm3＋ ions to Yb3＋ ions, was observed under the excitation of blue photon at 465 nm. Moreover, the energy transfer processes were studied based on the Inokuti-Hirayama model, and the results indicated that the energy transfer from Tm3＋ to Yb3＋ was an electric dipole-dipole interaction. The max- imum quantum cutting efficiency approached with 0.49mo1% Tm3＋ and 5.99mo1% Yb3＋. increasing the energy efficiency of crystalline energy part of the solar spectrum. up to 167.5% in LiYF4 single crystal codoped Application of this crystal has prospects for Si solar cells by photon doubling of the high