The total conductivity,oxygen sorption property,oxygen permeability and stability of pure perovskite-type oxide BaCo0.7Fe0.2Nb0.1O3-δ (BCFNO) in real operating conditions were investigated. Its total conductivity was...The total conductivity,oxygen sorption property,oxygen permeability and stability of pure perovskite-type oxide BaCo0.7Fe0.2Nb0.1O3-δ (BCFNO) in real operating conditions were investigated. Its total conductivity was measured to be 3.6 S·cm-1 at 600°C. Though the total conductivity of the BCFNO membrane is much smaller than that of the Ba0.5Sr0.5Co0.8Fe0.2O3-δ (BSCFO) membrane,the oxygen permeability of the BCFNO membrane is similar to that of the BSCFO membrane. SEM observation and EDX analysis of the BCFN...展开更多
The La0.7Sr0.3CryMnzCo(1-y-z)O3-δ samples were prepared by solid state reaction.The phases,microstructure and properties of the samples were investigated by XRD,SEM,DC four-probe method and iodometry method.The singl...The La0.7Sr0.3CryMnzCo(1-y-z)O3-δ samples were prepared by solid state reaction.The phases,microstructure and properties of the samples were investigated by XRD,SEM,DC four-probe method and iodometry method.The single orthorhombic phase La0.7Sr0.3CryMnzCo(1-y-z)O3-δ perovskite oxides were obtained when sintered at l350 °C for 10 h.The oxygen nonstoichiometry of the materials varied inversely with the total electronic conductivity.The sample with composition of La0.7Sr0.3Cr0.5Mn0.35 Co0.15O3-δ had the maxima...展开更多
基金the National High-Tech Research and Development Program of China (No. 2006AA11A189)the Science and Technology Commission of Shanghai Municipality (No. 07DZ12036)+1 种基金the National Engineering Research Center of Advanced Steel Technology (NERCAST, No. 050209)the Education Commission of Shanghai Municipality.
文摘The total conductivity,oxygen sorption property,oxygen permeability and stability of pure perovskite-type oxide BaCo0.7Fe0.2Nb0.1O3-δ (BCFNO) in real operating conditions were investigated. Its total conductivity was measured to be 3.6 S·cm-1 at 600°C. Though the total conductivity of the BCFNO membrane is much smaller than that of the Ba0.5Sr0.5Co0.8Fe0.2O3-δ (BSCFO) membrane,the oxygen permeability of the BCFNO membrane is similar to that of the BSCFO membrane. SEM observation and EDX analysis of the BCFN...
基金supported by the National Natural Science Foundation of China (50204007)Program for New Century Excellent Talents in University (NCET-07-0387)
文摘The La0.7Sr0.3CryMnzCo(1-y-z)O3-δ samples were prepared by solid state reaction.The phases,microstructure and properties of the samples were investigated by XRD,SEM,DC four-probe method and iodometry method.The single orthorhombic phase La0.7Sr0.3CryMnzCo(1-y-z)O3-δ perovskite oxides were obtained when sintered at l350 °C for 10 h.The oxygen nonstoichiometry of the materials varied inversely with the total electronic conductivity.The sample with composition of La0.7Sr0.3Cr0.5Mn0.35 Co0.15O3-δ had the maxima...