The characters of dense dispersion managed soliton in optical fiber transmission systems

The properties of ultra-short dense dispersion-managed soliton (DBMS) in optical fiber links are investigated. They show some excellent characters, such as, reducing pulse's breathing extent greatly, facing fewer mutual interactions and tolerating larger local dispersion. In general, DBMS is more stable than a conventional dispersion-managed soliton in high-capacity systems. Excessively dense dispersion compensation is more suitable for systems with weak nonlinear effect.

Ternary Pt/Re/SnO2/C catalyst for EOR:Electrocatalytic activity and durability enhancement

Carbon-supported Pt/C,Pt/Re/C,Pt/SnO2/C and Pt/Re/SnO2/C,with 20 wt.%overall metal loading were prepared and their electrochemical activity towards ethanol oxidation reaction(EOR)was investigated.Transmission electron microscopy(TEM)combined with energy dispersive X-ray spectroscopy(EDS)revealed,that indeed binary and ternary combinations of the designed nanoparticles(NPs)were formed and successfully uniformly deposited on a carbon support.Fourier transform infrared spectroscopy(FTIR)allowed to assess the chemical composition of the nanocatalysts and X-ray diffraction(XRD)allowed to determine the catalyst structure.Potentiodynamic and chronoamperometric measurements were used to establish its catalytic activity and stability.The influence of Re addition on the electrochemical activity towards ethanol oxidation reaction(EOR)was verified.Indeed,the addition of Re to the binary Pt/SnO2/C catalyst leads to the formation of ternary Pt/Re/SnO2/C with physical contact between the individual NPs,enhancing the EOR.Furthermore,the onset potential of the synthesized ternary catalyst is shifted to more negative potentials and the current densities and specific activity are nearly 11 and 5 times higher,respectively,than for commercial Pt catalyst.Additionally ternary Pt/Re/SnO2/C catalyst retained 96%of its electrochemical surface area.

Synthesis of Single-Crystal TiO_2 Nanowire Using Titanium Monoxide Powder by Thermal Evaporation

TiO 2 nanowires were synthesized successfully in a large quantity by thermal evaporation using titanium monoxide powder as precursor. X-ray diffraction results showed that all the products were pure rutile phase of TiO 2 . According to microstructural observations, the nanowires have two typical morphologies, a long straight type and a short tortuous type. The straight nanowires were obtained at a wide temperature range of 900–1050 ℃, while the tortuous ones were formed below 900 ℃. Transmission electron microscopy characterization revealed that both the straight and the tortuous nanowires are single-crystal rutile TiO 2 . The preferential growth direction of the nanowires was determined as [110] orientation according to electron diffraction and high-resolution image analyses. The morphological change of TiO 2 nanowires was discussed by considering the different atomic diffusion rates of Ti atoms caused by the phase transformation in Ti substrate at around 900 ℃.