The hot deformation characteristics of GH738 superalloy over the temperature range of 1000 °C to 1 200 °C and strain range of 0.01 s^-1 to 10.0 s^-1 under a strain of 1.0 s^-1 were investigated through hot c...The hot deformation characteristics of GH738 superalloy over the temperature range of 1000 °C to 1 200 °C and strain range of 0.01 s^-1 to 10.0 s^-1 under a strain of 1.0 s^-1 were investigated through hot compression tests with a Gleeble-1500 simulation machine. The flow stress reached peak value before flow softening occurred. The average apparent activation energy（Q） of GH738 was calculated to be 430 k J/mol, and the stress index（n） is approximately 4.08. The processing map was developed based on flow stress data and dynamic materials model（DMM）. The map shows a dynamic recrystallization（DRX） domain in 1 050 °C to 1150 °C and 0.01 s^-1 to 1.0 s^-1 strain rate range with a peak efficiency of 45%, which is considered to be the optimum region for hot working. Moreover, the materials undergo flow instability in the temperature range of 1000 °C to 1050 °C and strain range of 1.0 s^-1 to 10.0 s^-1, and adiabatic shear bands can be observed in this domain.展开更多
基金Item Sponsored by National High Technology Research and Development Program(863 Program)of China(2012AA03A502)
文摘The hot deformation characteristics of GH738 superalloy over the temperature range of 1000 °C to 1 200 °C and strain range of 0.01 s^-1 to 10.0 s^-1 under a strain of 1.0 s^-1 were investigated through hot compression tests with a Gleeble-1500 simulation machine. The flow stress reached peak value before flow softening occurred. The average apparent activation energy（Q） of GH738 was calculated to be 430 k J/mol, and the stress index（n） is approximately 4.08. The processing map was developed based on flow stress data and dynamic materials model（DMM）. The map shows a dynamic recrystallization（DRX） domain in 1 050 °C to 1150 °C and 0.01 s^-1 to 1.0 s^-1 strain rate range with a peak efficiency of 45%, which is considered to be the optimum region for hot working. Moreover, the materials undergo flow instability in the temperature range of 1000 °C to 1050 °C and strain range of 1.0 s^-1 to 10.0 s^-1, and adiabatic shear bands can be observed in this domain.