To meet the performance requirements of hot forging die heat resistant layer, the Ni60-SiC coating, Ni60-Cr3C2 coating, and Ni60-WC coating were prepared using W6Mo5Cr4V2 as substrate material with 30%SiC, 10%Cr3C2, 3...To meet the performance requirements of hot forging die heat resistant layer, the Ni60-SiC coating, Ni60-Cr3C2 coating, and Ni60-WC coating were prepared using W6Mo5Cr4V2 as substrate material with 30%SiC, 10%Cr3C2, 30%WC powder by means of plasma spraying and plasma spray re-melting and plasma spray welding, respectively. Microstructure of each carbide coating was analyzed, micro-hardness was tested, and mainly thermal parameters of coating were detected. The experimental results show that using plasma spray welding, the performance of 70%Ni60/30%SiC powder is the best, and its micro-hardness can achieved 1100HV, showing good thermal-physical property.展开更多
A process parameter optimization method for mold wear during die forging process is proposed and a mold life prediction method based on polynomial fitting is presented,by combining the variance analysis method in the ...A process parameter optimization method for mold wear during die forging process is proposed and a mold life prediction method based on polynomial fitting is presented,by combining the variance analysis method in the orthogonal test with the finite element simulation test in the forging process.The process parameters with the greatest influence on the mold wear during the die forging process and the optimal solution of the process parameters to minimize the wear depth of the mold are derived.The hot die forging process is taken as an example,and a mold wear correction model for hot forging processes is derived based on the Archard wear model.Finite element simulation analysis of die wear process in hot die forging based on deform software is performed to study the relationship between the wear depth of the mold working surface and the die forging process parameters during hot forging process.The optimized process parameters suitable for hot forging are derived by orthogonal experimental design and analysis of variance.The average wear amount of the mold during the die forging process is derived by calculating the wear depth of a plurality of key nodes on the mold surface.Mold life for the entire production process is predicted based on average mold wear depth and polynomial fitting.展开更多
Dry sliding wear tests of a Cr-Mo-V cast hot-forging die steel was carried out within a load range of 50--300 N at 400℃ by a pin-on-disc high temperature wear machine. The effect of heat treatment process on wear res...Dry sliding wear tests of a Cr-Mo-V cast hot-forging die steel was carried out within a load range of 50--300 N at 400℃ by a pin-on-disc high temperature wear machine. The effect of heat treatment process on wear resistance was systematically studied in order to select heat treatment processes of the steel with high wear resistance. The morphology, structure and composition were analyzed using scanning electron microscopy （SEM）, X-ray diffraction （XRD） and energy dispersive spectroscopy （EDS） ; wear mechanism was also discussed. Tribo-oxide layer was found to form on worn surfaces to reduce wear under low loads, but appear inside the matrix to increase wear under high loads. The tribo-oxides were mainly consisted of Fe3O4 and Fe2O3, FeO only appeared under a high load. Oxidative mild wear, transition of mild-severe wear in oxidative wear and extrusive wear took turns to operate with increasing the load. The wear resistance strongly depended on the selection of heat treatment processes or microstructures. It was found that bainite presented a better wear resistance than martensite plus bainite duplex structure, martensite structure was of the poorest wear resistance. The wear resistance increased with increasing austenizing temperature in the range of 920 to 1 120 ℃, then decreased at up to 1 220 ℃. As for tempering temperature and microstructure, the wear resistance increased in following order： 700℃ （tempered sorbite）, 200 ℃ （tempered martensite）, 440 to 650 ℃ （tempered troostite）. An appropriate combination of hardness, toughness, microstructural thermal stability was re- quired for a good wear resistance in high-temperature wear. The optimized heat treatment process was suggested for the cast hot-forging steel to be austenized at 1020 to 1 120 ℃, quenched in oil, then tempered at 440 to 650℃ for 2 h.展开更多
文摘To meet the performance requirements of hot forging die heat resistant layer, the Ni60-SiC coating, Ni60-Cr3C2 coating, and Ni60-WC coating were prepared using W6Mo5Cr4V2 as substrate material with 30%SiC, 10%Cr3C2, 30%WC powder by means of plasma spraying and plasma spray re-melting and plasma spray welding, respectively. Microstructure of each carbide coating was analyzed, micro-hardness was tested, and mainly thermal parameters of coating were detected. The experimental results show that using plasma spray welding, the performance of 70%Ni60/30%SiC powder is the best, and its micro-hardness can achieved 1100HV, showing good thermal-physical property.
基金This work was supported in part by the National Natural Science Foundation of China(No.51575008).
文摘A process parameter optimization method for mold wear during die forging process is proposed and a mold life prediction method based on polynomial fitting is presented,by combining the variance analysis method in the orthogonal test with the finite element simulation test in the forging process.The process parameters with the greatest influence on the mold wear during the die forging process and the optimal solution of the process parameters to minimize the wear depth of the mold are derived.The hot die forging process is taken as an example,and a mold wear correction model for hot forging processes is derived based on the Archard wear model.Finite element simulation analysis of die wear process in hot die forging based on deform software is performed to study the relationship between the wear depth of the mold working surface and the die forging process parameters during hot forging process.The optimized process parameters suitable for hot forging are derived by orthogonal experimental design and analysis of variance.The average wear amount of the mold during the die forging process is derived by calculating the wear depth of a plurality of key nodes on the mold surface.Mold life for the entire production process is predicted based on average mold wear depth and polynomial fitting.
基金Item Sponsored by National Nature Science Foundation of China(51071078)
文摘Dry sliding wear tests of a Cr-Mo-V cast hot-forging die steel was carried out within a load range of 50--300 N at 400℃ by a pin-on-disc high temperature wear machine. The effect of heat treatment process on wear resistance was systematically studied in order to select heat treatment processes of the steel with high wear resistance. The morphology, structure and composition were analyzed using scanning electron microscopy （SEM）, X-ray diffraction （XRD） and energy dispersive spectroscopy （EDS） ; wear mechanism was also discussed. Tribo-oxide layer was found to form on worn surfaces to reduce wear under low loads, but appear inside the matrix to increase wear under high loads. The tribo-oxides were mainly consisted of Fe3O4 and Fe2O3, FeO only appeared under a high load. Oxidative mild wear, transition of mild-severe wear in oxidative wear and extrusive wear took turns to operate with increasing the load. The wear resistance strongly depended on the selection of heat treatment processes or microstructures. It was found that bainite presented a better wear resistance than martensite plus bainite duplex structure, martensite structure was of the poorest wear resistance. The wear resistance increased with increasing austenizing temperature in the range of 920 to 1 120 ℃, then decreased at up to 1 220 ℃. As for tempering temperature and microstructure, the wear resistance increased in following order： 700℃ （tempered sorbite）, 200 ℃ （tempered martensite）, 440 to 650 ℃ （tempered troostite）. An appropriate combination of hardness, toughness, microstructural thermal stability was re- quired for a good wear resistance in high-temperature wear. The optimized heat treatment process was suggested for the cast hot-forging steel to be austenized at 1020 to 1 120 ℃, quenched in oil, then tempered at 440 to 650℃ for 2 h.