High qualityβ-Ga_(2)O_(3)single crystal nanobelts with length of 2−3 mm and width from tens of microns to 132μm were synthesized by carbothermal reduction method.Based on the grown nanobelt with the length of 600μm...High qualityβ-Ga_(2)O_(3)single crystal nanobelts with length of 2−3 mm and width from tens of microns to 132μm were synthesized by carbothermal reduction method.Based on the grown nanobelt with the length of 600μm,the dual-Schottky-junctions coupling device(DSCD)was fabricated.Due to the electrically floating Ga_(2)O_(3)nanobelt region coupling with the double Schottky-junctions,the current I_(S2)increases firstly and rapidly reaches into saturation as increase the voltage V_(S2).The saturation current is about 10 pA,which is two orders of magnitude lower than that of a single Schottky-junction.In the case of solar-blind ultraviolet(UV)light irradiation,the photogenerated electrons further aggravate the coupling physical mechanism in device.I_(S2)increases as the intensity of UV light increases.Under the UV light of 1820μW/cm^(2),I_(S2)quickly enters the saturation state.At V_(S2)=10 V,photo-to-dark current ratio(PDCR)of the device reaches more than 104,the external quantum efficiency(EQE)is 1.6×10^(3)%,and the detectivity(D*)is 7.5×10^(12)Jones.In addition,the device has a very short rise and decay times of 25−54 ms under different positive and negative bias.DSCD shows unique electrical and optical control characteristics,which will open a new way for the application of nanobelt-based devices.展开更多
Five experimental self-shielded flux cored wires are fabricated withdifferent amount of Fe_2O_3 in the flux. The effect of Fe_2O_3 on welding technology and mechanicalproperties of weld metals deposited by these wires...Five experimental self-shielded flux cored wires are fabricated withdifferent amount of Fe_2O_3 in the flux. The effect of Fe_2O_3 on welding technology and mechanicalproperties of weld metals deposited by these wires are studied. The results show that with theincrease of Fe_2O_3 in the mix, the melting point of the pretreated mix is increased. LiBaF_3 andBaFe_(12)O_(19), which are very low in inherent moisture, are formed after the pretreatment. Themechanical properties are evaluated to the weld metals. The low temperature notch toughness of theweld metals is increased linearly with the Fe_2O_3 content in the flux due to the balance betweenFe_2O_3 and residual Al in the weld metal. The optimum Fe_2O_3 content in flux is 2.5 percent approx3.5 percent.展开更多
基金supported by Natural Science Basic Research Program in Shaanxi Province of China(No.2023-JCYB-574)National Natural Science Foundation of China(No.62204203).
文摘High qualityβ-Ga_(2)O_(3)single crystal nanobelts with length of 2−3 mm and width from tens of microns to 132μm were synthesized by carbothermal reduction method.Based on the grown nanobelt with the length of 600μm,the dual-Schottky-junctions coupling device(DSCD)was fabricated.Due to the electrically floating Ga_(2)O_(3)nanobelt region coupling with the double Schottky-junctions,the current I_(S2)increases firstly and rapidly reaches into saturation as increase the voltage V_(S2).The saturation current is about 10 pA,which is two orders of magnitude lower than that of a single Schottky-junction.In the case of solar-blind ultraviolet(UV)light irradiation,the photogenerated electrons further aggravate the coupling physical mechanism in device.I_(S2)increases as the intensity of UV light increases.Under the UV light of 1820μW/cm^(2),I_(S2)quickly enters the saturation state.At V_(S2)=10 V,photo-to-dark current ratio(PDCR)of the device reaches more than 104,the external quantum efficiency(EQE)is 1.6×10^(3)%,and the detectivity(D*)is 7.5×10^(12)Jones.In addition,the device has a very short rise and decay times of 25−54 ms under different positive and negative bias.DSCD shows unique electrical and optical control characteristics,which will open a new way for the application of nanobelt-based devices.
文摘Five experimental self-shielded flux cored wires are fabricated withdifferent amount of Fe_2O_3 in the flux. The effect of Fe_2O_3 on welding technology and mechanicalproperties of weld metals deposited by these wires are studied. The results show that with theincrease of Fe_2O_3 in the mix, the melting point of the pretreated mix is increased. LiBaF_3 andBaFe_(12)O_(19), which are very low in inherent moisture, are formed after the pretreatment. Themechanical properties are evaluated to the weld metals. The low temperature notch toughness of theweld metals is increased linearly with the Fe_2O_3 content in the flux due to the balance betweenFe_2O_3 and residual Al in the weld metal. The optimum Fe_2O_3 content in flux is 2.5 percent approx3.5 percent.