The hot ductility of the V-containing micro-alloying steel CC (continuouscasting) slabs and precipitation of vanadium carbide in the tensile specimens were investigated. Theresults indicate that the precipitation rati...The hot ductility of the V-containing micro-alloying steel CC (continuouscasting) slabs and precipitation of vanadium carbide in the tensile specimens were investigated. Theresults indicate that the precipitation ratio and precipitation rate of vanadium in the specimensreach maximum respectively at 900, -825 and 825 deg C. There is still l0 percent-l7 percent ofvanadium precipitated when the deformation temperature decreases to 800-700 deg C. Vanadium largelyaffects the ductility of the steel in the low ductility temperature Region III. Embrittlement ofsteel with higher V content is severer in the region and the embrittlement extends to lowertemperature.展开更多
In order to improve the osseointegration and antibacterial activity of titanium alloys,micro/nano-structured ceramic coatings doped with antibacterial element F were prepared by plasma electrolytic oxidation(PEO)proce...In order to improve the osseointegration and antibacterial activity of titanium alloys,micro/nano-structured ceramic coatings doped with antibacterial element F were prepared by plasma electrolytic oxidation(PEO)process on Ti6Al4V alloy in NaF electrolyte.The influence of NaF concentration(0.15-0.50 mol/L)on the PEO process,microstructure,phase composition,corrosion resistance and thickness of the coatings was investigated using scanning/transmission electron microscopy,energy dispersive spectroscopy,atomic force microscopy,X-ray diffractometer,and potentiodynamic polarization.The results demonstrated that Ti6Al4V alloy had low PEO voltage(less than 200 V)in NaF electrolyte,which decreased further as the NaF concentration increased.A micro/nano-structured coating with 10-15μm pits and 200-800 nm pores was formed in NaF electrolyte;the morphology was different from the typical pancake structure obtained with other electrolytes.The coating formed in NaF electrolyte had low surface roughness and was thin(<4μm).The NaF concentration had a small effect on the phase transition from metastable anatase phase to stable rutile phase,but greatly affected the corrosion resistance.In general,as the NaF concentration increased,the surface roughness,phase(anatase and rutile)contents,corrosion resistance,and thickness of the coating first increased and then decreased,reaching the maximum values at 0.25 mol/L NaF.展开更多
Ti-6AI-4V, among the Ti alloys, is the most widely used. In the present work, the behavior of Ti-6AI-4V alloy has been investigated by the uniaxial hot isothermal compression tests and a series of dilatometric experim...Ti-6AI-4V, among the Ti alloys, is the most widely used. In the present work, the behavior of Ti-6AI-4V alloy has been investigated by the uniaxial hot isothermal compression tests and a series of dilatometric experiments were also carried out to determine the transformation temperatures at different cooling rates. Specimens for hot compression tests were homogenized at 1050℃ for 10 min and then quickly cooled to different straining temperatures from 1050 to 850℃. Cooling rates were chosen fast enough to prevent high temperature transformation during cooling. Compression tests were conducted at temperatures from 1050 to 850℃ in steps of 50℃ at constant true strain rates of 10-3 or 10-2 s-1. The apparent activation energy for compression in two-phase region was calculated 420 kJ·mol-1. Partial globularization of a phase was observed in the specimen deformed at low strain rates and at temperatures near the transformation zone and annealed after deformation.展开更多
Superplastic forming and diffusion bonding (SPF/DB) is a well-established process for the manufacture of components almost exclusively from Ti-6AI-4V sheet material. The sandwich structure of Ti-6AI-4V alloy is invest...Superplastic forming and diffusion bonding (SPF/DB) is a well-established process for the manufacture of components almost exclusively from Ti-6AI-4V sheet material. The sandwich structure of Ti-6AI-4V alloy is investigated. The effects of the microstructure on the SPF/DB process were discussed. The microstructure at the interfaces and the distribution of thickness were researched.展开更多
文摘The hot ductility of the V-containing micro-alloying steel CC (continuouscasting) slabs and precipitation of vanadium carbide in the tensile specimens were investigated. Theresults indicate that the precipitation ratio and precipitation rate of vanadium in the specimensreach maximum respectively at 900, -825 and 825 deg C. There is still l0 percent-l7 percent ofvanadium precipitated when the deformation temperature decreases to 800-700 deg C. Vanadium largelyaffects the ductility of the steel in the low ductility temperature Region III. Embrittlement ofsteel with higher V content is severer in the region and the embrittlement extends to lowertemperature.
文摘In order to improve the osseointegration and antibacterial activity of titanium alloys,micro/nano-structured ceramic coatings doped with antibacterial element F were prepared by plasma electrolytic oxidation(PEO)process on Ti6Al4V alloy in NaF electrolyte.The influence of NaF concentration(0.15-0.50 mol/L)on the PEO process,microstructure,phase composition,corrosion resistance and thickness of the coatings was investigated using scanning/transmission electron microscopy,energy dispersive spectroscopy,atomic force microscopy,X-ray diffractometer,and potentiodynamic polarization.The results demonstrated that Ti6Al4V alloy had low PEO voltage(less than 200 V)in NaF electrolyte,which decreased further as the NaF concentration increased.A micro/nano-structured coating with 10-15μm pits and 200-800 nm pores was formed in NaF electrolyte;the morphology was different from the typical pancake structure obtained with other electrolytes.The coating formed in NaF electrolyte had low surface roughness and was thin(<4μm).The NaF concentration had a small effect on the phase transition from metastable anatase phase to stable rutile phase,but greatly affected the corrosion resistance.In general,as the NaF concentration increased,the surface roughness,phase(anatase and rutile)contents,corrosion resistance,and thickness of the coating first increased and then decreased,reaching the maximum values at 0.25 mol/L NaF.
文摘Ti-6AI-4V, among the Ti alloys, is the most widely used. In the present work, the behavior of Ti-6AI-4V alloy has been investigated by the uniaxial hot isothermal compression tests and a series of dilatometric experiments were also carried out to determine the transformation temperatures at different cooling rates. Specimens for hot compression tests were homogenized at 1050℃ for 10 min and then quickly cooled to different straining temperatures from 1050 to 850℃. Cooling rates were chosen fast enough to prevent high temperature transformation during cooling. Compression tests were conducted at temperatures from 1050 to 850℃ in steps of 50℃ at constant true strain rates of 10-3 or 10-2 s-1. The apparent activation energy for compression in two-phase region was calculated 420 kJ·mol-1. Partial globularization of a phase was observed in the specimen deformed at low strain rates and at temperatures near the transformation zone and annealed after deformation.
文摘Superplastic forming and diffusion bonding (SPF/DB) is a well-established process for the manufacture of components almost exclusively from Ti-6AI-4V sheet material. The sandwich structure of Ti-6AI-4V alloy is investigated. The effects of the microstructure on the SPF/DB process were discussed. The microstructure at the interfaces and the distribution of thickness were researched.