VINYL POLYMERIZATION OF NORBORNENE CATALYZED BY [2-(2-BENZIMIDAZOLYL)-6-((1-ARYLIMINOETHYL)PYRIDYL)]NICKEL CHLORIDE/MAO SYSTEM

The catalytic system of[2-(2-benzimidazolyl)-6-((1-aryliminoethyl)pyridyl)]nickel chloride/MAO(methylalu- minoxane)was found to be good active for vinyl polymerization of norbornene and provided polymers with relative narrow molecular distributions.Various reaction parameters,such as the ratios of nickel precursor to MAO or monomer norbornene, and the nature of the ligands in complexes were carefully investigated to realize their effects on the catalytic activities, polymer molecular weight and molecular we...

PARTICLE MORPHOLOGY OF POLY(VINYL CHLORIDE)RESIN PREPARED BY SUSPENDED EMULSION POLYMERIZATION

Suspended emulsion polymerization was used to prepare poly(vinyl chloride) (PVC) resin. Fine PVC particleswere formed at low polymerization conversions. The amount of fine panicles decreases as conversion increases anddisappears at conversions greater than 30%. Scanning electron micrographs show that PVC grains are composed of looselycoalesced primary particles, especially for PVC resins prepared in the presence of poly(vinyl alcohol) dispersant. The size ofprimary particles increases and porosity decreases with the increase of conversion. In view of the particle features of PVCresin, a particle formation mechanism including the formation of primary particles and grains is proposed. The formationprocess of primary particles includes the formation of particle nuclei, coalescence of particle nuclei to form primary particles,and growth of primary particles. PVC grains are formed by the coagulation of primary particles. The loose coalescence ofprimary particles is caused by the colloidal stability of primary particles and the low swelling degree of vinyl chloride in the primary particles.

Influence of Suspended Emulsion Polymerization Conditions on Particle Characteristics of Polyvinyl Chloride Resin

Suspended emulsion polymerization of vinyl chloride was carried out in a 5 L autoclave. The influence of agitation, polymerization conversion, dispersant and surfactant on the average particle size (PS) and particle size distribution (PSD), particle morphology and porosity of polyvinyl chloride (PVC) resin was investigated. It showed that the agitator had great influence on the smooth operation of polymerization, PS and PSD. The PS increased and PSD became narrow as polymerization conversion became high. The porosity decreased with the increase of conversion. A convenient choice of additives, both dispersants and non-ionic surfactants, allows one to adjust PS and PSD. The PS decreased with the addition of polyvinyl alcohol or hydroxypropyl methylcellulose dispersants,and increased with the addition of Span surfactants. The addition of dispersants or surfactants also affected the morphology and porosity of resin, and PVC resin with looser agglomeration and homogeneous distribution of primary particles was prepared.

Enzymatic Regioselective Synthesis of Vinyl Lactose Ester and Its Chemical Polymerization

Transesterification reaction of lactose with divinyladipate in pyridine catalyzed by an alkaline protease from Bacillus subtilis at 50C for 3 days gave 6-O-vinyladipoyl-lactose (yield 35%). Poly(6-O-vinyladipoyl-lactose) with Mn = 21,200, Mw = 32,900, Mw/Mn = 1.56 could be obtained by chemical polymerization. Poly(vinyl alcohol) containing lactose branch was biodegradable. After 6 days in aqueous buffer (PH 7), this alkaline protease could degrade the polymer to an Mn of ca. 2100, Mw/Mn = 2.56.

Graft co-polymerization of maleic acid and vinyl acetate onto poly(vinylidene fluoride) powder by pre-irradiation technique

Binary monomers of maleic acid and vinyl acetate are grafted onto poly(vinylidene fluoride) (PVDF) powder by pre-irradiation induced graft polymerization technique in emulsion solution. The co-grafting of binary monomers is successfully proved by FT-IR spectroscopy analysis. The influences of the absorbed dose, reaction temperature, reaction time, total concentration of monomers, and feed ratio of binary monomers on the degree of grafting are investigated. The thermal property of grafted PVDF powder was characterized by differential scanning calorimetry (DSC) and thermo-gravimetry analysis (TGA).

Bifurcation control and eigenstructure assignment in continuous solution polymerization of vinyl acetate

The major difficulty in achieving good performance of industrial polymerization reactors lies in the lack of understanding of their nonlinear dynamics and the lack of well-developed techniques for the control of nonlinear processes, which are usually accompanied with bifurcation phenomenon. This work aims at investigating the nonlinear behavior of the parameterized nonlinear system of vinyl acetate polymerization and further modifying the bifurcation characteristics of this process via a washout filter-aid controller, with all the original steady state equilibria preserved. Advantages and possible extensions of the proposed methodology are discussed to provide scientific guide for further controller design and operation improvement.

RADICAL DESORPTION IN EMULSION POLYMERIZATION OF VINYL ACETATE

In the present paper a model equation for calculating the radical desorption rate constant,k0,in the emulsion polymerization of vinyl acetate was suggested and the various parameters forevaluating k0 were determined.Effects of reaction temperature,emulsifier concentration,initiator con-centration,monomer conversion and phase ratio on k0 were studied.It indicates that the desorptionof radicals from latex particles to aqueous phase must be taken into account in the modelling ofemulsion polymerization for the monomers with higher hydrophilicity such as vinyl acetate.

Studies on the Self-condensing Vinyl Polymerization of a Novel Maleimide Inimer

The self-condensing vinyl polymerization(SCVP) of a novel maleimide inimer(initiator-monomer) 1, N-(4-α-bromobutyryloxy phenyl) maleimide with the complex of CuBr/Bipy(2, 2′-bipyridine) as the catalyst was studied. GPC was used to determine the molecular weight and the results show that the molecular weight increases exponentially with polymerization time during the first hour, and then the rate of increase molecular weight slows down. The molecular weight also increases with increasing dosage of the catalyst. The coincidence of the molecular weights determined by 1H NMR and GPC proves that the polymer obtained from the SCVP of inimer 1 has a linear structure, which is further verified by 13C NMR spectrum. A hyperbranched polymer was obtained by the copolymerization of inimer 1 and styrene.

Studies on the Self-condensing Vinyl Living Radical Polymerization of a Novel Acrylate Inimer

A novel acrylate inimer, 2-（2-chloroacetyloxy） ethyl acrylate, was prepared by the reaction of 2-hydroxyethyl acrylate with chloroacetyl chloride in the presence of triethylamine. The self-condensing vinyl living radical polymerization of the inimer was studied and the hyperbranched macromolecules containing ester linkages on their backbone were prepared. All the polymerization products were characterized by 1H NMR. The polymerization degree and the branching parameter were calculated based on the 1H NMR spectra. It has been shown that this inimer exhibits a very distinctive polymerization behavior. Similar to step-growth polymerization, the polymerization degree of the products formed increased exponentially during the early stage of the polymerization, and then the increasing rate slowed down. However, the inimer remained present throughout the polymerization consistent with conventional free radical polymerization. Also, if much longer polymerization time was used, the polymerization system would become gel due to the crosslinking reaction derived from radical-radical recombination. As a result of the unequal reactivity of -CH2Cl and >CHCl, an almost linear product was obtained at a molar ratio of bipy to inimer=0.05, while a relatively high ratio of bipy to inimer 1 favored the formation of the branched structure. The macromolecules formed at a high ratio of bipy to inimer 1 exhibited an excellent solubility in organic solvents such as acetone.

POLYMERIZATION OF ISOBUTYL VINYL ETHER CATALYSED BY DINUCLEAR HALF-TITANOCENES

Polymerization of isobutyl vinyl ether(IBVE)has been studied with mononuclear half-titanocene,CpTiCl_3[1]and dinuclear half-titanocenes,[(C_5H_4)_2(CH_2)_n][(TiCl_3)_2][2(n=3),3(n=6)],and[(C_5H_4)_2(CH_2)_n[(TiCl_2OR_2](R=2,6- diisopropylphenoxyl)[4(n=3),5(n=6)],in the presence of methyl aluminoxanes(MAO)as cocatalyst in methylene chloride.The influences of the length of polymethylene brigde and the substitution of aryloxy group at the metal center have been investigated at three polymerization temperature(...

Preparation of Macroporous Poly (vinyl alcohol-co-triallyl isocyanurate) Beads Bearing Aminocarboxylic Acid as Functional Groups by Suspension Polymerization

Macroporous poly (vinyl acetate-co-triallyl isocyanurate) beads were prepared with suspension polymerization method. The copolymer beads were then transformed into poly (vinyl alcohol-co-triallyl isocyanurate) by ester exchange reaction. Aminocarboxylic acids were immobilized on the copolymer beads by the esterification of hydroxyl groups with diethyl-lenetriaminepentaacetic bisanhydride. The weak acid exchange capacities, specific surface areas and mean pore diameters of the resultant resin beads were measured.

Kinetics of Vinyl Chloride Polymerization with Mixture of Initiators

Kinetic models for the rate constants of vinyl chloride polymerization in the presence of initiator mixtures were proposed. They may be used to design the initiator recipes for the vinyl chloride polymerization with uniform rate at different temperatures at which various grades of poly(vinyl chloride) will be prepared.

RADICAL POLYMERIZATION OF VINYL MONOMER INITIATED BY CERIC ION/TARTARIC ACID

The polymerization of acrylamide and acrylonitrile using ceric ion as initiator can be promoted greatly by the tartaric acid. The kinetics of acrylamide polymerization initiated by ceric ion/tartaric acid has been studied. The presence of the species of tartaric acid in Polyacrylonitrile produced by using ceric ion/tartaric acid as niitiator has been confirmed by FT-IR analysis.

Living/controlled polymerization of vinylpyridines into sequence-regulated copolymers by Lewis pair

The poly(vinylpyridine)(PVP) based(co)polymers are of particular interest in materials science, due to their multifunctionality and diverse applications. So far, there is no report on the sequence-regulated copolymerization of vinylpyridines(VPs) and methacrylate monomer in one-step manner yet. Here we designed and synthesized a series of guanidine phosphines as Lewis base(LB), which is combined with bulky organoaluminium to construct Lewis pairs(LPs) for polymerization of VPs. The living/controlled polymerization of 4-vinylpyridine(4-VP) or 2-vinylpyridine(2-VP) can be accomplished with remarkable efficiency by such Lewis pair polymerization(LPP), furnishing polymers with high molecular weight(up to 288 kg/mol) and narrow molecular weight distribution(as low as 1.17). Mechanistic studies reveal the interaction of LPs and formation of zwitterionic intermediates, providing solid evidences to support the proposed polymerization mechanism. More importantly, by simply adjusting the LA dosage, this LPP strategy realizes the unprecedented control over the sequence regulation of 2-VP-based copolymers from gradient to block in one-step manner, regardless of the monomer ratio, which greatly expands the versatility of the LPP.

Synthesis and properties of acrylate latex modified by vinyl alkoxy siloxane

Acrylate latex modified by vinyl triisopropoxy silane (C-1706) was synthesized by seeded emulsion polymerization with anionic emulsifier sodium dodecyl sulphonate(SDS) and nonionic emulsifier OP-10 as the multiple emulsifiers at (78±2) ℃. The effects of different factors, such as the emulsifier, C-1706 monomer and its feeding manner on the properties of acrylate latex modified by C-1706 were investigated. The particle size distribution and the structure, the configuration, the weather durability and stain resistance of copolymer latex were characterized by particle size analyzer, Fourier transform infrared spectroscopy (FT-IR), transmission electron microscope(TEM), scanning electron microscope(SEM) and ultraviolet aging instrument respectively. The results show that SDS to OP-10 as multiple emulsifiers can lead to coordinated efficiency, the optimal emulsifier dosage is 2.4%?3.2%(mass fraction), and the mass ratio of SDS to OP-10 is 1?1? 1?2. The seeded emulsion polymerization can effectively introduce a organic-siloxane bonding in a macromolecule inter polymer, and the obtained acrylate latex modified by organic-siloxane possesses narrow distribution of particle size with mean diameter of 51.8?76.6 nm and has the excellent properties in weather durability and stain-resistance especially.

Effect of Polyvinyl Alcohol with a Thiol End Group on the Properties of Polyacrylic Dispersions and Spray-dried Powder

The emulsion polymerization of highly shear-stable copolymer dispersions of methyl methacrylate and butyl acrylate were carried out using poly （vinyl alcohol） with a thiol end group （PVA-SH） as protective colloid. The dispersions can be transformed into corresponding redispersible powder via a spray dryingcooling process. On-line FT-IR monitoring shows that grafting polymer of PVA-g-PMMA was formed mainly at the stage-1 of the emulsion polymerization. TEM images show, the PVA-SH shell was fragmentary when adding SDS at initial stage and integrated when adding at particle growing or final stage. The particle size turns to be smaller when delayed adding SDS surfactant. Triethanolamine, a co-regulator of PVA-SH, controlled the M to 50 000-70 000 and reduced the PDI to 1.5-1.7. The acrylic dispersions with 0.8wt%-1.5wt% PVA-SH1 can be spray-dried into super dispersible polymer powder （SDPP）, which can easily disperse in water and form recon- stituted dispersions with an average particle size smaller than 1 micron.

Polymerization of Norbornene via an Iron-Based Complex/MAO Catalytic System

Polynorbornenes were synthesized in the presence of an iron based catalyst, 2,6-bis[1-(2,6-diisopropyl-phenylimino)ethyl]pyridine iron(Ⅱ) dichloride. The FTIR, 1H NMR and 13C NMR analysis results revealed that the structure of the obtained polynorbornenes consisted of vinyl addition polymer substructures without any ring-opening structures. The polymers were amorphous with a short-range order, displayed in the WAXD(wide angle X-ray diffraction) diagrams. The glass transition temperatures ranged from 200 to 400 ℃. The effects of the polymerization reaction conditions, such as Al/Fe molar ratio and toluene/CH_2Cl_2 volume ratio, on the activity, intrinsic viscosity and T_g were also studied.

UV enhanced gas–solid synthesis of chlorinated poly vinyl chloride characterized by a UV–Vis online analysis method

Dynamic characteristics of UV enhanced gas–solid PVC chlorination process were revealed by a UV–Vis spectral online analysis method. Experimental results showed an instantaneous increase of the chlorination rate as soon as UV light was affiliated, which demonstrated the intensified effect of UV radiation on PVC chlorination directly.Different affiliation methods of UV light were then studied, proving that continuous UV radiation could enhance the chlorination process significantly while intermittent UV radiation was able to initiate the chlorination reaction once it was conducted. Besides, experiments were carried out to study the influences of parameters on the chlorination process such as UV wavelength, chlorination temperature, partial pressure of chlorine gas and PVC raw materials. Among all the parameters, chlorination temperature and partial pressure of chlorine gas were testified as two key factors to determine the chlorination performance. Thermal analysis of CPVC products showed that their corresponding properties such as the glass transition temperature(Tg) and the homogeneity of chlorine distribution in polymer phase were improved with the increase of chlorine content.

The Effect of Polyvinyl Acetate Polymer on Reducing Dust in Arid and Semiarid Areas

Because the large areas of Iran are on arid and semiarid belt of the world, it has many problems due to windstorms. Wind storms cause dust and haze due to a mass of fine sand or silt soil elevated in the atmosphere. It makes heart disease-cardiovascular and respiratory and so is detrimental for the children. These have plagued the residents and so lives of them are disrupted every so often. In this research, the subject soil stabilization using adherence of poly vinyl acetate polymer as a way to reduce the production of dust is defined for prone area. In this paper, the effect of poly vinyl acetate polymer on silt soil has been studied. In this study the samples were uncompacted particles of soil with different amount of water-solvated polymer (0, 5, 10, 15, 20, 25, 30 grams per meter squared) poured over them. These samples are kept in experimental environment for 7 days. After ensuring complete dryness, their stabilities are tested against wind flow with 20 m/s speed. Results showed that adding more polymers to soil would considerably increase its particles’ stabilities. This stability is due to positive reaction of polymer with soil particles. The effect of this stability is maintained during sample drying time in the lab and the soil maintains its characteristics during testing. The best results are obtained for 20 grams polymer per meter squared, where caused an increase in stability to about 15 times that of the soil without polymer.