Wear resistance of Zr/WC composite coatings on Cr12MoV steel surface by electric spark deposition

Zr/WC composite coating was prepared on the surface of Cr12MoV steel by electric spark deposition technology to change its surface properties. The surface and worn surface morphology of the coating were observed using scanning electron microscope. Dry friction and wear tests of the coatings were carried out at room temperature. The results show that the coating is continuous and uniform, and the thickness was about 50-60 μm. The microhardness of the coating surface was highest at 1140 HV_(200g), which was significantly higher than that of the substrate. The ear tests results show that the wear weight loss, wear volume and wear rate follow the following rules: Cr12MoV>WC coating> Zr/WC composite coating.

等离子喷涂纳米WC-12％Co涂层与陶瓷和不锈钢配副时的摩擦磨损性能对比研究

利用大气等离子喷涂技术制备了纳米和微米WC-12% Co涂层,采用SRV摩擦磨损试验机考察了纳米和微米WC-12%Co涂层在干摩擦条件下分别与Si3N4陶瓷球和不锈钢球配副时的摩擦磨损性能.结果表明:在相同试验条件下,纳米和微米WC-12% Co涂层分别与Si3N4陶瓷球和不锈钢球配副时的摩擦系数相差不大,但纳米WC-12% Co涂层的抗磨性能明显优于微米WC-12% Co涂层;2种涂层的磨损机制差异亦较小,纳米涂层在低载荷下的主要磨损机制为微断裂和轻微磨粒磨损,而在较高载荷下的磨损机制为硬质相的剥落和磨粒磨损;微米涂层在较低载荷下的磨损机制为微断裂和磨粒磨损,在较高载荷下为疲劳磨损.在相同试验条件下,纳米WC-12% Co涂层的磨损表面损伤明显较轻微.

爆炸喷涂WC-12%Co涂层的滑动磨损性能

采用爆炸喷涂技术制备纳米和普通WC-12%Co涂层,用往复试验机对涂层的干滑动磨损性能进行了研究,分析了涂层磨损前后的形貌、结构及成分变化。结果表明:相同的喷涂条件下,WC-12%Co纳米涂层比普通涂层结构均匀、致密,但碳化物分解严重。尽管纳米涂层与普通涂层具有相近的硬度,但普通涂层的耐磨性优于纳米涂层,尤其是在重载条件下。普通涂层的磨损机制为微切削;纳米涂层在轻载(10 N)下,以塑性变形为主要磨损机制,随载荷增加至30 N,纳米WC粒子不能起到阻抗陶瓷球对磨副的磨削作用,而是随粘结相一起被去除,同时由于纳米涂层脱碳导致的层间结合薄弱,在滑动磨损中易发生成片剥落,耐磨性大幅下降。

HVOF喷涂超细结构WC-12Co涂层磨粒磨损性能

以喷雾转换法制备的球壳形WC-12Co复合粉为原料,采用超音速火焰喷涂(HVOF)在45#钢上制备超细结构WC-12Co涂层,并测试涂层的显微硬度、开裂韧性。利用XRD、SEM和磨损试验机分析涂层物相组成、微观结构和耐磨损性能。结果表明:多孔球壳形WC-12Co复合粉在HVOF喷涂过程中发生了中度脱碳,涂层中不仅含有WC、W2C相,还有少量W相;涂层微观结构致密,组织呈岩层状,截面平均显微硬度HV0.3为1 205.5、平均开裂韧性为4.96 MPa·m^1/2;磨损过程中,粘结相被SiO2犁削出非连续状槽沟,WC晶粒剥离或裂解出的细小WC晶粒成为新的磨粒,对粗大晶粒产生磨削或积于裂纹处加剧开裂。

超音速火焰喷涂WC-12Co涂层抗磨粒磨损性能研究

采用超音速火焰（HVOF）喷涂工艺在316L不锈钢基体上制备了WC-12Co涂层，测试了涂层的结合强度、显微硬度、气孔率以及抗磨粒磨损性能。并利用XRD对喷涂粉末及涂层进行了相结构分析，用扫描电子显微镜对喷涂粉末、磨粒磨损前后的涂层表面形貌进行了观察。结果表明：在喷涂过程中，仅有很少量的WC粒子发生氧化脱碳。涂层的结合强度和显微硬度高，组织结构致密。在相同的实验条件下，316L的磨粒磨损量是WC-12Co涂层的95倍，这表明HVOF制备的WC-12Co涂层具有优异的抗磨粒磨损性能。

纳米结构WC/12Co涂层精密磨削的磨削力研究

本文对金刚石砂轮平面磨削纳米结构WC/ 12Co涂层材料时得到的磨削力进行了试验研究 ,研究了涂层材料的磨削力与磨削工艺参数以及砂轮特性之间的关系。通过各项试验研究得出 ,用金刚石砂轮磨削纳米结构WC/ 12Co涂层时 ,磨削力与当量磨削厚度基本成一元线性关系 ,它随磨削深度、工件速度的增加而增加。当磨粒尺寸减小时 ,总磨削力增加 ,但单颗磨粒磨削力减小。材料以非弹性变形的材料去除方式为主。通过试验采集的数据 。