Aluminum(Al)powder is widely used in solid propellants.In particular,nano-Al has attracted extensive scholarly attention in the field of energetic materials due to its higher reactivity than micro-Al.However,the exist...Aluminum(Al)powder is widely used in solid propellants.In particular,nano-Al has attracted extensive scholarly attention in the field of energetic materials due to its higher reactivity than micro-Al.However,the existence of aluminum oxide film on its surface reduces the heat release performance of the aluminum powder,which greatly limits its application.Hence,this paper used iron,a component of solid propellant,to coat micron-Al and nano-Al to improve the heat release efficiency and reactivity of Al powder.SEM,TEM,EDS,XRD,XPS,and BET were used to investigate the morphological structure and properties of pure Al and Fe/Al composite fuels of different sizes.The results show that Fe was uniformly coated on the surface of Al powder.There was no reaction between Fe and Al,and Fe/Al composite fuels had a larger specific surface area than pure Al,which could better improve the reactivity of pure Al.Besides,the catalytic effects of pure Al and Fe/Al composite fuels of different sizes on ammonium perchlorate and ammonium nitrate were explored.The results show that the catalysis of pure Al powder could be greatly improved by coating Fe on the surface of Al powder.Especially,the micron-Fe/Al composite fuel had a higher catalytic effect than the pure nano-Al powder.Hence,Fe/Al composite fuels are expected to be widely used in solid propellants.展开更多
To improve the mechanical properties of WC-Al2O3 composites, the effects of trace amount of CeO2 additives on the microstructure and mechanical properties of the WC-Al2O3 composites prepared by hot pressing were inves...To improve the mechanical properties of WC-Al2O3 composites, the effects of trace amount of CeO2 additives on the microstructure and mechanical properties of the WC-Al2O3 composites prepared by hot pressing were investigated. The results revealed that the WC-Al2O3 composites doped with 0.1% CeOz possessed refined microstructure and enhanced mechanical properties compared with that of the undoped WC-Al2O3composites. Trace CeO2 suppressed the decarburization of WC, promoted the microstructural refinement, and improved the interface coherence of the WC matrix and Al2O3. When 0.1% CeO2 was added to the WC-Al2O3 composites, the effect of CeO2 resulted in the achievement of a relative density of 98.82% with an excellent Vickers hardness of 16.89 GPa, combining a fracture toughness of 9.85 MPa. m1/2 with an acceptable flexural strength of 1 024.05 MPa.展开更多
Magnetic Cu^0/Fe3O4 submicron composites were prepared using a hydrothermal method and used as heterogeneous catalysts for the activation of peroxymonosulfate（PMS） and the degradation of organic pollutants.The as-pr...Magnetic Cu^0/Fe3O4 submicron composites were prepared using a hydrothermal method and used as heterogeneous catalysts for the activation of peroxymonosulfate（PMS） and the degradation of organic pollutants.The as-prepared magnetic Cu^0/Fe3O4 submicron composites were composed of Cu^0 and Fe3O4 crystals and had an average size of approximately 220 nm.The Cu^0/Fe3O4 composites could efficiently catalyze the activation of PMS to generate singlet oxygen,and thus induced the rapid degradation of rhodamine B,methylene blue,orange Ⅱ,phenol and 4-chlorophenol.The use of0.1 g/L of the Cu^0/Fe3O4 composites induced the complete removal of rhodamine B（20 μmol/L） in15 min,methylene blue（20 μmol/L） in 5 min,orange Ⅱ（20 μmol/L） in 10 min,phenol（0.1mmol/L） in 30 min and 4-chlorophenol（0.1 mmol/L） in 15 min with an initial pH value of 7.0 and a PMS concentration of 0.5 mmol/L.The total organic carbon（TOC） removal higher than 85%for all of these five pollutants was obtained in 30 min when the PMS concentration was 2.5 mmol/L.The rate of degradation was considerably higher than that obtained with Cu^0 or Fe3O4 particles alone.The enhanced catalytic activity of the Cu^0/Fe3O4 composites in the activation of PMS was attributed to the synergistic effect of the Cu^0 and Fe3O4 crystals in the composites.Singlet oxygen was identified as the primary reactive oxygen species responsible for pollutant degradation by electron spin resonance and radical quenching experiments.A possible mechanism for the activation of PMS by Cu^0/Fe3O4 composites is proposed as electron transfer from the organic pollutants to PMS induces the activation of PMS to generate ^1O2,which induces the degradation of the organic pollutants.As a magnetic catalyst,the Cu^0/Fe3O4 composites were easily recovered by magnetic separation,and exhibited excellent stability over five successive degradation cycles.The present study provides a facile and green heterogeneous catalysis method for the oxidative removal of organic pollutants.展开更多
The base structure of in situ TiCp/Fe composites fabricated under industrial condition was changed by different heat treatments. Erosive wear tests were carried out and the results were compared with that of wear-resi...The base structure of in situ TiCp/Fe composites fabricated under industrial condition was changed by different heat treatments. Erosive wear tests were carried out and the results were compared with that of wear-resistant white cast iron. The results suggest that the wear resistance of the in situ TiCp/Fe composite is higher than that of wear-resistant white cast iron under the sand erosive wear condition. The wear mechanism of the wear-resistant white cast iron was a cycle process that base surface was worn and carbides were exposed, then carbides was broken and wear pits appeared. While the wear mechanism of in situ TiCp/Fe composite was a cycle process that base surface was worn and TiC grains were exposed and dropped. The wear resistance of in situ TiCp/Fe composite was lower than that of wear-resistant white cast iron under the slurry erosive wear condition. Under such circumstance, the material was not only undergone erosive wear but also electrochemistry erosion due to the contact with water in the medium. The wear behaviours can be a combination of two kinds of wear and the sand erosive wear is worse than slurry erosive wear.展开更多
The effects of the reactive temperature, time and the cooling rate of an Fe Ti C alloy melt on the microstructures and mechanical properties of in situ TiC p/Fe composites were investigated. The results show that the ...The effects of the reactive temperature, time and the cooling rate of an Fe Ti C alloy melt on the microstructures and mechanical properties of in situ TiC p/Fe composites were investigated. The results show that the hardness and impact toughness of the prepared composites increase with increasing the reactive temperature, because more and finer TiC particles are formed in the higher temperature melt. However, after the TiC synthesis reaction in the melt completed, the impact toughness of the composites will decrease if the melt reactive time is further prolonged, owing to the coarsening of the formed TiC particles. Under the present experimental condition, the cooling rate of the melt containing dispersions has little influence on the number, size and distribution of the particles in the composites.展开更多
FeS2/Fe composites were mechanochemically prepared with iron powder and pyrite for the stabilization of ferrite arsenate sludge(FAS).The effects of preparation parameters on stabilization performance were investigated...FeS2/Fe composites were mechanochemically prepared with iron powder and pyrite for the stabilization of ferrite arsenate sludge(FAS).The effects of preparation parameters on stabilization performance were investigated.The results show that the optimum conditions are FeS2/Fe molar ratio of 5:5,milling time of 2 h,ball-to-material mass ratio of 15:1 and milling with stainless steel ball.Then,the composites were characterized by XRD,SEM,FTIR,etc.The physicochemical properties of FeS2/Fe mixture change dramatically,which is responsible for its excellent performance.Finally,the stabilization process of FAS was optimized.When the FAS is mixed with composites at mass ratio of 4:1 and milled for 30 min,the As leaching concentration of FAS can be reduced from 639.15 to 4.74 mg/L with the stabilization ratio of 99.2%.展开更多
The electromagnetic and microwave absorbing properties of FeCoB powder composites prepared by sin- gle-roller melt-spinning and mechanical milling processes were investigated in this paper. The result indicates that t...The electromagnetic and microwave absorbing properties of FeCoB powder composites prepared by sin- gle-roller melt-spinning and mechanical milling processes were investigated in this paper. The result indicates that the flake-like powders are obtained. As milling time increases, the flake-like powder particles tend to agglomerate, causing the flake-like powders decrease gradually. The milling time plays an important role in the electromagnetic parameters which relates to the shape and size of the powder particles. The calculation shows that the sample milled for 6 h could achieve an optimal reflection loss of -11.5 dB at 5.8 GHz, with mass fraction of 83 % and a matching thickness of 1.8 mm. The result also indicates that the microwave absorbing properties of the FeCoB powder composites are adjustable by changing their thickness, and can be applied as a thinner microwave absorbing material in the range of 2-8 GHz.展开更多
The Fe-Al/WC intermetallic composite coatings have been prepared by high velocity arc spraying(HVAS) technology on 20G steel and the oxidation performance of Fe-Al/WC composite coatings has been studied by means of th...The Fe-Al/WC intermetallic composite coatings have been prepared by high velocity arc spraying(HVAS) technology on 20G steel and the oxidation performance of Fe-Al/WC composite coatings has been studied by means of thermogrativmetic analyzer. The results demonstrate that the kinetics curve of oxidation approximately follows the logarithmic law. The composition of the oxidized coating surface mainly is composed of A12O3, Fe2O3, Fe3O4 and FeO which distribute unevenly. The protective A12O3 film firstly forms and preserves the coatings from further oxidation.展开更多
文摘Aluminum(Al)powder is widely used in solid propellants.In particular,nano-Al has attracted extensive scholarly attention in the field of energetic materials due to its higher reactivity than micro-Al.However,the existence of aluminum oxide film on its surface reduces the heat release performance of the aluminum powder,which greatly limits its application.Hence,this paper used iron,a component of solid propellant,to coat micron-Al and nano-Al to improve the heat release efficiency and reactivity of Al powder.SEM,TEM,EDS,XRD,XPS,and BET were used to investigate the morphological structure and properties of pure Al and Fe/Al composite fuels of different sizes.The results show that Fe was uniformly coated on the surface of Al powder.There was no reaction between Fe and Al,and Fe/Al composite fuels had a larger specific surface area than pure Al,which could better improve the reactivity of pure Al.Besides,the catalytic effects of pure Al and Fe/Al composite fuels of different sizes on ammonium perchlorate and ammonium nitrate were explored.The results show that the catalysis of pure Al powder could be greatly improved by coating Fe on the surface of Al powder.Especially,the micron-Fe/Al composite fuel had a higher catalytic effect than the pure nano-Al powder.Hence,Fe/Al composite fuels are expected to be widely used in solid propellants.
文摘To improve the mechanical properties of WC-Al2O3 composites, the effects of trace amount of CeO2 additives on the microstructure and mechanical properties of the WC-Al2O3 composites prepared by hot pressing were investigated. The results revealed that the WC-Al2O3 composites doped with 0.1% CeOz possessed refined microstructure and enhanced mechanical properties compared with that of the undoped WC-Al2O3composites. Trace CeO2 suppressed the decarburization of WC, promoted the microstructural refinement, and improved the interface coherence of the WC matrix and Al2O3. When 0.1% CeO2 was added to the WC-Al2O3 composites, the effect of CeO2 resulted in the achievement of a relative density of 98.82% with an excellent Vickers hardness of 16.89 GPa, combining a fracture toughness of 9.85 MPa. m1/2 with an acceptable flexural strength of 1 024.05 MPa.
基金supported by the National Natural Science Foundation of China (21377169, 21507168)the Fundamental Research Funds for the Central Universities (CZW15078)the Natural Science Foundation of Hubei Province of China (2014CFC1119, 2015CFB505)~~
文摘Magnetic Cu^0/Fe3O4 submicron composites were prepared using a hydrothermal method and used as heterogeneous catalysts for the activation of peroxymonosulfate（PMS） and the degradation of organic pollutants.The as-prepared magnetic Cu^0/Fe3O4 submicron composites were composed of Cu^0 and Fe3O4 crystals and had an average size of approximately 220 nm.The Cu^0/Fe3O4 composites could efficiently catalyze the activation of PMS to generate singlet oxygen,and thus induced the rapid degradation of rhodamine B,methylene blue,orange Ⅱ,phenol and 4-chlorophenol.The use of0.1 g/L of the Cu^0/Fe3O4 composites induced the complete removal of rhodamine B（20 μmol/L） in15 min,methylene blue（20 μmol/L） in 5 min,orange Ⅱ（20 μmol/L） in 10 min,phenol（0.1mmol/L） in 30 min and 4-chlorophenol（0.1 mmol/L） in 15 min with an initial pH value of 7.0 and a PMS concentration of 0.5 mmol/L.The total organic carbon（TOC） removal higher than 85%for all of these five pollutants was obtained in 30 min when the PMS concentration was 2.5 mmol/L.The rate of degradation was considerably higher than that obtained with Cu^0 or Fe3O4 particles alone.The enhanced catalytic activity of the Cu^0/Fe3O4 composites in the activation of PMS was attributed to the synergistic effect of the Cu^0 and Fe3O4 crystals in the composites.Singlet oxygen was identified as the primary reactive oxygen species responsible for pollutant degradation by electron spin resonance and radical quenching experiments.A possible mechanism for the activation of PMS by Cu^0/Fe3O4 composites is proposed as electron transfer from the organic pollutants to PMS induces the activation of PMS to generate ^1O2,which induces the degradation of the organic pollutants.As a magnetic catalyst,the Cu^0/Fe3O4 composites were easily recovered by magnetic separation,and exhibited excellent stability over five successive degradation cycles.The present study provides a facile and green heterogeneous catalysis method for the oxidative removal of organic pollutants.
文摘The base structure of in situ TiCp/Fe composites fabricated under industrial condition was changed by different heat treatments. Erosive wear tests were carried out and the results were compared with that of wear-resistant white cast iron. The results suggest that the wear resistance of the in situ TiCp/Fe composite is higher than that of wear-resistant white cast iron under the sand erosive wear condition. The wear mechanism of the wear-resistant white cast iron was a cycle process that base surface was worn and carbides were exposed, then carbides was broken and wear pits appeared. While the wear mechanism of in situ TiCp/Fe composite was a cycle process that base surface was worn and TiC grains were exposed and dropped. The wear resistance of in situ TiCp/Fe composite was lower than that of wear-resistant white cast iron under the slurry erosive wear condition. Under such circumstance, the material was not only undergone erosive wear but also electrochemistry erosion due to the contact with water in the medium. The wear behaviours can be a combination of two kinds of wear and the sand erosive wear is worse than slurry erosive wear.
文摘The effects of the reactive temperature, time and the cooling rate of an Fe Ti C alloy melt on the microstructures and mechanical properties of in situ TiC p/Fe composites were investigated. The results show that the hardness and impact toughness of the prepared composites increase with increasing the reactive temperature, because more and finer TiC particles are formed in the higher temperature melt. However, after the TiC synthesis reaction in the melt completed, the impact toughness of the composites will decrease if the melt reactive time is further prolonged, owing to the coarsening of the formed TiC particles. Under the present experimental condition, the cooling rate of the melt containing dispersions has little influence on the number, size and distribution of the particles in the composites.
基金Projects(2018YFC1900305,2018YFC1903301)supported by the National Key R&D Program of ChinaProject(51825403)supported by the National Natural Science Foundation for Distinguished Young Scholars of China+1 种基金Project(51634010)supported by the National Natural Science Foundation of ChinaProject(2017RS3010)supported by the Science and Technology Program of Hunan Province,China
文摘FeS2/Fe composites were mechanochemically prepared with iron powder and pyrite for the stabilization of ferrite arsenate sludge(FAS).The effects of preparation parameters on stabilization performance were investigated.The results show that the optimum conditions are FeS2/Fe molar ratio of 5:5,milling time of 2 h,ball-to-material mass ratio of 15:1 and milling with stainless steel ball.Then,the composites were characterized by XRD,SEM,FTIR,etc.The physicochemical properties of FeS2/Fe mixture change dramatically,which is responsible for its excellent performance.Finally,the stabilization process of FAS was optimized.When the FAS is mixed with composites at mass ratio of 4:1 and milled for 30 min,the As leaching concentration of FAS can be reduced from 639.15 to 4.74 mg/L with the stabilization ratio of 99.2%.
基金financially supported by the National Hi-tech R&D Project Supporting Programs Funded by Ministry of Science&Technology of China(No.2012AA063202)the National Natural Science Foundation of China(Nos.50972013,50802008,and 51004011)+1 种基金the National Key Project of Scientific and Technical Supporting Programs Funded by Ministry of Science&Technology of China(Nos.2012BAC02B01,2012BAC12B05,2011BAE13B07,and 2011BAC10B02)the Guangdong Province&Ministry of Education Industry-Study-Research United Project(No.2009A090100017)
文摘The electromagnetic and microwave absorbing properties of FeCoB powder composites prepared by sin- gle-roller melt-spinning and mechanical milling processes were investigated in this paper. The result indicates that the flake-like powders are obtained. As milling time increases, the flake-like powder particles tend to agglomerate, causing the flake-like powders decrease gradually. The milling time plays an important role in the electromagnetic parameters which relates to the shape and size of the powder particles. The calculation shows that the sample milled for 6 h could achieve an optimal reflection loss of -11.5 dB at 5.8 GHz, with mass fraction of 83 % and a matching thickness of 1.8 mm. The result also indicates that the microwave absorbing properties of the FeCoB powder composites are adjustable by changing their thickness, and can be applied as a thinner microwave absorbing material in the range of 2-8 GHz.
基金supports for this work by the National Natural Science Foundation of China(Project No.50235030)Foundation of state economy trade committee of China are grateful acknowledged.
文摘The Fe-Al/WC intermetallic composite coatings have been prepared by high velocity arc spraying(HVAS) technology on 20G steel and the oxidation performance of Fe-Al/WC composite coatings has been studied by means of thermogrativmetic analyzer. The results demonstrate that the kinetics curve of oxidation approximately follows the logarithmic law. The composition of the oxidized coating surface mainly is composed of A12O3, Fe2O3, Fe3O4 and FeO which distribute unevenly. The protective A12O3 film firstly forms and preserves the coatings from further oxidation.