Because of the size limitation of weld joints in different regions, the traditional standard bar specimen is not suitable to investigate the mechanical properties of weld joints. In this study, miniature specimens wer...Because of the size limitation of weld joints in different regions, the traditional standard bar specimen is not suitable to investigate the mechanical properties of weld joints. In this study, miniature specimens were extracted from specific regions(base metal, weld metal, and three heat-affected zones) of API X80 and X70 weld joints. Uniaxial tensile tests were conducted to obtain the mechanical properties of different regions, and then uniaxial ratcheting tests were conducted to investigate the ratcheting behaviors of the different regions under the same peak and nominal stresses. Under both the tensile tests and ratcheting tests, the weld joints exhibit heterogeneous results, such as different mechanical properties and ratcheting behaviors, which were region dependent. Furthermore, the yield strength and yield-to-tensile strength ratio contribute differently to the ratcheting response.展开更多
Fracture parameters of welded joints with different strength matching and crack depth in weld metal are investigated by using the methods of elastoplastic finite element analysis and three point bend specimen test. Th...Fracture parameters of welded joints with different strength matching and crack depth in weld metal are investigated by using the methods of elastoplastic finite element analysis and three point bend specimen test. The results show that for shallow crack, the plastic zone turns large in loading process, and the fracture toughness turns high. The extent of the plastic zone of overmatched joint is larger than that of undermatched joint because it will extends to parent metal from the weld metal in loading process for the same CTOD value. The plastic zone of undermatched joint is restricted within the weld, and the size of that is small. Overmatched joint shows the fracture behaviour of shallow crack may more easily than the undermatched joint, while the two sorts of joint specimens have the same crack depth. Therefore, the fracture-resistant capability of overmatched weld is better than that of undermatched weld. when the toughness of weld metals is similar for both overmatched and undermatched joints.展开更多
Conventional fusion arc welding of high-strength quenched and tempered steel can be improved through the use of non-conventional laser beam welding. This article presents the investigations of autogenous bead on plate...Conventional fusion arc welding of high-strength quenched and tempered steel can be improved through the use of non-conventional laser beam welding. This article presents the investigations of autogenous bead on plate and butt CO<sub>2</sub> Laser Welding (LW) of 7 mm thick high-strength quenched and tempered low alloy SM570 (JIS) steel plates. The influence of laser welding parameters, mainly welding speed, defocusing distance and shielding gas flow rate on the weld profile, i.e., weld zone penetration depth and width, microstructure and mechanical properties of welded joints was determined. All welded joints showed smooth and uniform weld beads free from superficial porosity and undercuts. The selected best welding conditions were a laser power of 5.0 kW, welding speed of 500 mm/min, argon gas shielding flow rate of 30 L/min and a defocusing distance of -0.5 mm. It was observed that these conditions gave complete penetration and minimized the width of the weld bead. The microstructure of the welded joints was evaluated by light optical microscopy. The weld metal (WM) and heat-affected zone (HAZ) near weld metal achieved maximum hardness (355 HV). The tensile fractured samples showed the ductile mode of failure and ultimate tensile strength of 580 MPa.展开更多
Characterization of the microstructure of the fusion zone of an Alloy 600-82 weld joint was conducted, with focus on the weld residual strain distribution and the comparison of the microstructure of heat affected zone...Characterization of the microstructure of the fusion zone of an Alloy 600-82 weld joint was conducted, with focus on the weld residual strain distribution and the comparison of the microstructure of heat affected zone （HAZ） with that of cold worked alloy. Peak of the residual strain was observed to approach to the fusion boundary in HAZ while the strain increased from the top of the weld to the root. Strain distribution in the HAZ was found to be concentrated adjacent to grain boundaries （GBs）, with a peak of approximately three times of that in grain. Further, triple junctions of the GB appear to cause a higher strain concentration than single GBs. The microstructure of HAZ consists of partially tangled dislocations, which is different from slip bands of high density dislocations in cold worked alloy. This may cause a relatively higher intergranular cracking resistance of HAZ due to the difficulty in transferring tangled dislocations to GB in HAZ under deformation.展开更多
基金supported by the National Natural Science Foundation of China (No. 51435012)
文摘Because of the size limitation of weld joints in different regions, the traditional standard bar specimen is not suitable to investigate the mechanical properties of weld joints. In this study, miniature specimens were extracted from specific regions(base metal, weld metal, and three heat-affected zones) of API X80 and X70 weld joints. Uniaxial tensile tests were conducted to obtain the mechanical properties of different regions, and then uniaxial ratcheting tests were conducted to investigate the ratcheting behaviors of the different regions under the same peak and nominal stresses. Under both the tensile tests and ratcheting tests, the weld joints exhibit heterogeneous results, such as different mechanical properties and ratcheting behaviors, which were region dependent. Furthermore, the yield strength and yield-to-tensile strength ratio contribute differently to the ratcheting response.
文摘Fracture parameters of welded joints with different strength matching and crack depth in weld metal are investigated by using the methods of elastoplastic finite element analysis and three point bend specimen test. The results show that for shallow crack, the plastic zone turns large in loading process, and the fracture toughness turns high. The extent of the plastic zone of overmatched joint is larger than that of undermatched joint because it will extends to parent metal from the weld metal in loading process for the same CTOD value. The plastic zone of undermatched joint is restricted within the weld, and the size of that is small. Overmatched joint shows the fracture behaviour of shallow crack may more easily than the undermatched joint, while the two sorts of joint specimens have the same crack depth. Therefore, the fracture-resistant capability of overmatched weld is better than that of undermatched weld. when the toughness of weld metals is similar for both overmatched and undermatched joints.
文摘Conventional fusion arc welding of high-strength quenched and tempered steel can be improved through the use of non-conventional laser beam welding. This article presents the investigations of autogenous bead on plate and butt CO<sub>2</sub> Laser Welding (LW) of 7 mm thick high-strength quenched and tempered low alloy SM570 (JIS) steel plates. The influence of laser welding parameters, mainly welding speed, defocusing distance and shielding gas flow rate on the weld profile, i.e., weld zone penetration depth and width, microstructure and mechanical properties of welded joints was determined. All welded joints showed smooth and uniform weld beads free from superficial porosity and undercuts. The selected best welding conditions were a laser power of 5.0 kW, welding speed of 500 mm/min, argon gas shielding flow rate of 30 L/min and a defocusing distance of -0.5 mm. It was observed that these conditions gave complete penetration and minimized the width of the weld bead. The microstructure of the welded joints was evaluated by light optical microscopy. The weld metal (WM) and heat-affected zone (HAZ) near weld metal achieved maximum hardness (355 HV). The tensile fractured samples showed the ductile mode of failure and ultimate tensile strength of 580 MPa.
基金financially supported by the Hundred-Talent Program of Chinese Academy of Sciences
文摘Characterization of the microstructure of the fusion zone of an Alloy 600-82 weld joint was conducted, with focus on the weld residual strain distribution and the comparison of the microstructure of heat affected zone （HAZ） with that of cold worked alloy. Peak of the residual strain was observed to approach to the fusion boundary in HAZ while the strain increased from the top of the weld to the root. Strain distribution in the HAZ was found to be concentrated adjacent to grain boundaries （GBs）, with a peak of approximately three times of that in grain. Further, triple junctions of the GB appear to cause a higher strain concentration than single GBs. The microstructure of HAZ consists of partially tangled dislocations, which is different from slip bands of high density dislocations in cold worked alloy. This may cause a relatively higher intergranular cracking resistance of HAZ due to the difficulty in transferring tangled dislocations to GB in HAZ under deformation.