Microfibril angle variability in Masson Pine (Pinus massoniana Lamb.) using X-ray diffraction

The microfibril angle of fiber walls is an ultra-mieroscopic feature affecting the performance of wood products. It is therefore essential to get more definitive information to improve selection and utilization. X-ray diffraction is a rapid method for measuring microfibril angles. In this paper, the variability of microfibril angle in plantation-grown Masson pine was investigated by peak-fitting method. This method was compared with the traditional hand-drawn method, 40% peak height method and half peak height method. X-ray diffraction measurements indicated that the microfibril angle changed as a function of the position in the tree. The mean microfibril angle decreased more gradually as the distance increased from the pith and reached the same level in mature wood. The microfibril angle also seemed to decrease clearly from the base upward. Differences of angle-intensity curves between heartwood and sapwood were also examined.

Small Angle X-ray Scattering Study of Precipitation Kinetics in Al-Zn-Mg-Cu Alloys

The evolution of microstructure parameters （precipitate size and volume fraction） for two types of Al-Zn-Mg-Cu alloys （7075 and 7055） during aging has been studied by synchrotron-radiation small angle X-ray scattering （SAXS）.The results show that the precipitates are only a few nanorneters for both alloys ageing even at higher temperature of 160℃ for 72 h （4.44 and 5.82 nm, respectively）. The maximum of the precipitate volume fraction increases with in creasing Zn content and is about 0.023-0.028 and 0.052-0.054, respectively. The coarsening of precipitate is consistent with LSW （Lifshitz-Slyozov-Wagner） model even at the initial stage where volume fraction is still varying.The activation energy of coarsening regime has been determined to be about 1.22±0.02 eV and 1.25±0.02 eV for alloys 7075 and 7055, respectively.

Small-angle X-ray scattering investigation of aging behavior of Al-Cu-Mg-Ag alloys using synchrotron radiation

The aging behavior of Al-Cu-Mg-Ag alloys with high Cu/Mg was studied by transmission electron microscopy (TEM) and small-angle X-ray scattering (SAXS) using synchrotron radiation. TEM study reveals that the major strengthening phases of the alloy after aging at 160?C for 10 h are Ω and less θ′. SAXS study shows that the scattering patterns are composed of several concentric circles at the beginning of aging process, which is replaced by the butterfly-wings scattering patterns with the increase of aging time. The butterfly-wings scattering patterns are composed of several branches. The angles between the branches are roughly equal to that between the habit planes of precipitates. The evolution of Guinier radius with aging time indicates the good coarsening resistance of the precipitates. The evolution of integrated intensity is consistent with the classical two-step precipitation process.

Growth Kinetics of Nanocrystals and Nanorods by Employing Small-angle X-ray Scattering (SAXS) and Other Techniques

In this article, we report the results of our detailed investigations of the growth kinetics of zero-dimensional nanocrystals as well as one-dimensional nanorods by the combined use of small angel X-ray scattering （SAXS）, transmission electron microscopy （TEM） along with other physical techniques. The study includes growth kinetics of gold nanocrystals formed by the reduction of HAuCl4 by tetrakis（hydroxymethyl） phosphonium chloride in aqueous solution, of CdSe nanocrystals formed by the reaction of cadmium stearate and selenium under solvothermal conditions, and of ZnO nanorods formed by the reaction of zinc acetate with sodium hydroxide under solvothermal conditions in the absence and presence of capping agents. The growth of gold nanocrystals does not follow the diffusion-limited Ostwald ripening, and instead follows a Sigmoidal rate curve. The heat change associated with the growth determined by isothermal titration calorimetry is about 10 kcal·mol^-1 per I nm increase in the diameter of the nanocrystals. In the case of CdSe nanocrystals also, the growth mechanism deviates from diffusion-limited growth and follows a combined model containing both diffusion and surface reaction terms. Our study of the growth kinetics of uncapped and poly（vinyl pyrollidone） （PVP）-capped ZnO nanorods has yielded interesting insights. We observe small nanocrystals next to the ZnO nanorods after a lapse of time in addition to periodic focusing and defocusing of the width of the length distribution. These observations lend support to the diffusion-limited growth model for the growth of uncapped ZnO nanorods. Accordingly, the time dependence on the length of uncapped nanorods follows the L3 law as required for diffusion-limited Ostwald ripening. The PVP-capped nanorods, however, show a time dependence, which is best described by a combination of diffusion （L^3） and surface reaction （L^2） terms.

Small Angle X-ray Scattering Study of PS Conformation in Tetrahydrofuran Solvent with Gas Anti-solvent

Small angle X-ray scattering (SAXS) was used to study the effect of dissolved CO2 on the conformation of polystyrene (PS) in PS/tetrahydrofuran(THF) solution at 308.15 K and at pressures up to 3 MPa. The cloud pressure and the expansion curve of the solution were also determined. The dependence of the conformation on pressure was discussed.

Scanning Microfocus Small Angle X-ray Scattering Study of the Avian Eggshell

Synchrotron microfocus small angle X-ray scattering was used to investigate the nanostructure and microscopic variation of eggshells. It uses a microbeam allowing the ability to probe interactions between the organic and inorganic components at nanometer level and is ideal for mapping over small areas to obtain a detailed analysis of structural variations. Thin sections of eggshells were scanned from the shell membrane （inner） to the cuticle （outer） surface. The data collected was used to produce two-dimensional maps showing microscopic changes within the different layers of the eggshell. The structural alterations ap- parently could have implications at the macroscopic level of the resulting eggshell. As the organic matrix is embedded within the eggshell this may contribute to the variations observed in calcite crystal form and texture, Structural information obtained about a biomaterial at different length scales is important in relating the structure to its functional properties. This knowledge and the principles behind the formation of biomaterials could be used in the attempt of bioengineering new systems.

Characteristics of AOT Microemulsion Structure: a Small Angle X-ray Scattering Study

The method of synchrotron radiation small-angle X-ray scattering (SR-SAXS) has been used to obtain structural information on the system of bis (2-ethylhexyl) sulfosuccinate (AOT)/H2O/isooctane. By using the Guinier plot (Ln I (q) versus q(2)) on the data sets in a defined small q range (0.03-0.06 Angstrom (-1)), the gyration radius at different water/surfactant molar ratio, W-0, was obtained. With the increase of W-0, the gyration radius (R-g) increased at the range of 23.2 similar to 52.7 Angstrom.

Probing Nanoscale Morphology of PS/PMMA/CdS &PS/PVC/CdS Polymeric Nanocomposites through Small Angle X-Ray Scattering Analysis

Polymeric nanocomposites of PS/PMMA/CdS and PS/PVC/CdS samples have been synthesized through dispersion solution casting technique. The nanoparrticles of CdS were prepared by simple chemical method using CdCl2 and H2S gas produced from thiourea. The nanoscale morphology of the prepared polymeric nanocomposite samples is probed through small angle X-ray scattering (SAXS). The SAXS study reveals that CdS nanoparticles take place at voids position in the respective plymer blend matrix and exhibit their nano nature with very little tendency to agglomerates.

Stability of the Dividing Distribution Function Method for ParticleSize Distribution Analysis in Small Angle X－Ray Scattering

The Dividing Distribution Function (DDF) method is one of the methods by which the particle size distribution of ultrafine powder can be evaluated from its small angle X-ray scattering data. In this paper, the stability of the solution obtained from DDF method has been investigated through optimizing the coefficient matrix, introducing a damping factor and a least square treatment. All calculations were accomplished with a microcomputer. It was shown that the average deviations of the size distribution obtained are not larger than the assigned random errors to the scattering intensities as long as the corresponding requirements are satisfied.

Characterization of Thin Films by Low Incidence X-Ray Diffraction

Glancing Angle X-ray Diffraction (GAXRD) is introduced as a direct, non-destructive, surface-sensitive technique for analysis of thin films. The method was applied to polycrystalline thin films (namely, titanium oxide, zinc selenide, cadmium selenide and combinations thereof) obtained by electrochemical growth, in order to determine the composition of ultra-thin surface layers, to estimate film thickness, and perform depth profiling of multilayered heterostructures. The experimental data are treated on the basis of a simple absorption-diffraction model involving the glancing angle of X-ray incidence.

Variation of microfibril angle and its correlation to wood properties in poplars

The microfibril angle of seven poplar clones was determined by using X-ray diffraction technique. Microfibril angle, wood basic density, fiber length, fiber width and cellulose content were assessed for every growth ring at breast height for all sample trees. Significant variation in microfibril angle was observed among growth rings. Mean microfibril angle (MFA) at breast height varied from 7.8?to 28?between growth rings with cambial age and showed a consistent pith-to-bark trend of decline an-gles. Analysis of variance also indicated that there were significant differences in wood basic density, fiber length, fiber width and cellulose content between the growth rings, which had an increasing tendency from pith to bark. Correlations between MFA and examined wood properties were predominantly large and significant negative (?0.01), and the coefficients were -0.660 for cellulose content, -0.586 for fiber length, -0.516 for fiber width and -0.450 for wood basic density, respectively. Regression analysis with linear and curve estimation indicated that a quadratic function showed the largest R2 and the least standard error for describing the relationships between microfibril angle and measured wood properties, and the correlation coefficients were over -0.45 (n=125). The results from this study suggested that microfibril angle would be a good characteristic for improvement in the future breeding program of poplars.

Nano-scale pore distribution characterisation of coal using small angle X-ray scattering

In the process of coal seam fracturing with liquid nitrogen(LN_(2)),the change of coal pore structure has an important influence on the efficiency of coalbed methane(CBM)extraction.The nano-scale pore size distribution(PSD)in coal particles before and after freezing with LN_(2) are experimentally studied in this work.Coal samples are collected from four coal mines,where coal and gas outburst accidents have occurred.Small angle X-ray scattering technology(SAXS)and scanning electron microscopy(SEM)are used to study the pore structure changes of coal samples quantitatively and qualitatively.It is found that the scattering intensity of coal samples increases after freezing.The PSD of all samples significantly changes in the range of 0.8–7 nm,showing new pore spaces in 0.8–4 nm and fewer pores in the 4–7 nm range.Both the pore fractal dimension and the radius of gyration of coal samples increase after freezing and are mainly affected by the changes in pores and the anisotropy of the coal matrix.Crack expansion and pore connections are observed in the surface structure of the coal sample using SEM.This study provides a better understanding of the nano-scale mechanism of coal seam fracturing with LN_(2) for the prevention of coal and gas outbursts.

Small angle X-ray scattering of the colloidal crystal

The monodisperse polystyrene spheres are assembled into the colloidal crystal on the glass substrate by vertical deposition method, which is aimed at the so-called photonic crystal applications. The structural information of the bulk colloidal crystal is crucial for understanding the crystal growth mechanism and devel- oping the various applications of colloidal crystal. Small-angle X-ray scattering （SAXS） technique was used to obtain the bulk structure of the colloidal crystal at Beamline lW2A of BSRF. It is found that the SAXS pattern is sensitive to the relative orientation between the colloidal sample and the incident X-ray direction. The crystal lattice was well distinguished and determined by the SAXS data.

DETERMINATION OF SIZE DISTRIBUTION OF THE CRYSTALLINE PARTICLE IN AGED METALLIC GLASS BY SMALL ANGLE X-RAY SCATTERING

Ⅰ. INTRODUCTIONAlthough many authors have investigated the structure of annealed metallic glass by means of small angle X-ray scattering (SAXS), there has been no report in which size distribution of the crystalline particle in aged metallic glass is determined. Determining size distribution of the crystalline particle will be beneficial to understanding the nucleation and growth process of the crystalline particle. In this note, size distribution of the crystalline parti-

DETERMINATION OF THE SHAPE AND DIMENSION OF PRECIPITATE FROM AGED Lc4 ALUMINIUM ALLOY BY SMALL ANGLE X-RAY SCATTERING

Small angle X-ray scattering (SAXS) is extensively used for determining the dimension of a particle, but rarely used for determining its shape. The difficulty is that it needs to do extensive calculations. In addition, it can only be carried out for the mono-dispersion system. In re cent years, Reuther et al. succeeded in determining the shape and dimension of the particle of a polymer gel.

Characterization of the nanopore structures of PAN-based carbon fiber precursors by small angle X-ray scattering

The nanopore structures in precursors Four carbon-fiber precursors are prepared. They are crucial to the performance of PAN-based carbon fibers are bath-fed filaments （A）, water-washing filaments （B） hot-stretching filaments （C） and drying-densification filaments （D）. Synchrotron radiation small angle X-ray scattering is used to probe and compare the nanopore structures of the four fibers. The nanopore size, discrete volume distribution, nanopore orientation degree along the fiber axis and the porosity are obtained. The results demonstrate that the nanopores are mainly formed in the water-washing stage. During the processes of the subsequent production technologies, the slenderness ratio of nanopores and their orientation degree along the fiber axis increase further and simultaneously, the porosity decreases. These results are helpful for improving the performance of the final carbon fibers.

Influence of energy bandwidth of pink beam on small angle X-ray scattering

Background Compared with the traditional monochromatic synchrotron radiation beam,a pink beam is a quasimonochromatic beam which can be obtained by screening a harmonic of the undulator.The energy bandwidth(E/E)of a pink beam is about 10−2.Despite the intensity gain from the quasi-monochromatic beam,the decrease in the energy resolution will lead the collected data to be smeared.Purpose To study the influence of the energy bandwidth on the small angle X-ray scattering(SAXS)by experiments and verify the feasibility of SAXS with a pink beam.Method Firstly,the influence of different energy bandwidths on SAXS has been studied by simulation and experiment.Then,TEM tests have been performed and compared with the experimental results.Result It has been shown that the scattering curves deviate slightly from the traditional monochromatic ones.This deviation does not influence the data processing for the maximum deviation of the results is just less than 2%.In return,the gain in the intensity(one to two orders of magnitude)makes the pink beam very important for the time-resolved SAXS.Further,the results of TEM and SAXS have shown an excellent agreement.Conclusion Thiswork proves that the pink beam could be used for SAXS directly without a desmearing procedure.Benefiting from the increase in the beam intensity,the exposure time can be greatly shortened,thus enhancing the utilization efficiency of the synchrotron radiation.

热定形工艺对高强型聚酯工业丝结构性能的影响

为探究不同热定形温度获得的高强型聚酯工业丝性能差异的内在结构因素,对3种高强型聚酯工业丝的结构性能进行对比。采用小角X射线散射和广角X射线衍射方法对其多尺度微观结构进行研究,结合力学性能及热收缩等结果,明确不同热定形工艺对高强型工业丝结构性能的影响。结果表明:热定形温度主要影响聚酯工业丝非晶区取向和片晶结构;相比于高强中缩(HTMS)和高强(HT)聚酯工业丝,高强低伸型(HTLE)聚酯工业丝的热定形温度低,高倍牵伸产生的伸直非晶区分子链在较低热定形温度下并未及时排入晶格形成结晶,而发生了小幅的回复,导致HTLE聚酯工业丝表现出非晶区取向高、结晶度低、晶粒尺寸小与片层倾斜角较大的结构特点,从而使断裂伸长率最小、初始弹性模量最大、尺寸稳定性差。

光诱导聚合蒙脱土插层纳米复合材料的研究

用两种光聚合法研究了蒙脱土插层复合材料的制备 .用小角X光衍射技术对产物内蒙脱土的结构进行表征 ,结果表明 ,蒙脱土经改性后能很好地使聚合单体及预聚物插入黏土层内并在光照下“就地”聚合生成光聚合复合材料 .

胆固醇对脂双层结构影响的SAXS和STM研究

用小角X射线散射(SAXS)和扫描隧道显微镜(STM)技术分别研究了模拟生物膜脂质体的结构以及胆固醇对生物膜双层结构的影响 .结果表明 ,在扫描隧道显微镜照片中 ,磷脂分子在石墨表面形成规则的二维点状排列图像 ;磷脂胆固醇脂质体在石墨表面形成规则的二维波纹状排列图像。用小角X射线散射研究结果表明 ,DPPC脂质体是片层相结构 ,DPPC +Chol脂质体是复相片层结构 ,DPPE +Chol脂质体是片层立方相结构 ,DPPC +DPPE +Chol脂质体是立方六角形相结构。