A systematic investigation on the structural, magnetic and magnetocaloric properties of Pr_（0.6）Sr_（0.4-x）Ag_xMnO_3（x=0.05 and 0.1） manganites was reported. Rietveld refinements of the X-ray diffraction patterns...A systematic investigation on the structural, magnetic and magnetocaloric properties of Pr_（0.6）Sr_（0.4-x）Ag_xMnO_3（x=0.05 and 0.1） manganites was reported. Rietveld refinements of the X-ray diffraction patterns confirmed that all samples were single phase and crystallized in the orthorhombic structure with Pnma space group. Magnetic measurements in a magnetic applied field of 0.01T revealed that the ferromagnetic-paramagnetic transition temperature T_C decreased from about 293 to 290 K with increasing silver content from x=0.05 to 0.1. The reported magnetocaloric entropy change and relative cooling power for both samples were considerably remarkable with a △S_（max） value of 1.9 J/（kg·K）and maximum RCP values of 100 J/kg, under a magnetic field change（？μ0H） equal to 1.8T. The analysis of the universal curves gave an evidence of a second order magnetic transition for the studied samples. The magnetic field influence on both the magnetic entropy change and the relative cooling power was also studied and discussed.展开更多
基金supported by the Polish Government and WBI(Belgium)in a Frame of Mutual Scientific Exchange Visits between WBI and Polish Ministry under project with reference numbers 14794/PVB/BE.POL/AN/an/2016/28611 and Rhea 2015/245812
文摘A systematic investigation on the structural, magnetic and magnetocaloric properties of Pr_（0.6）Sr_（0.4-x）Ag_xMnO_3（x=0.05 and 0.1） manganites was reported. Rietveld refinements of the X-ray diffraction patterns confirmed that all samples were single phase and crystallized in the orthorhombic structure with Pnma space group. Magnetic measurements in a magnetic applied field of 0.01T revealed that the ferromagnetic-paramagnetic transition temperature T_C decreased from about 293 to 290 K with increasing silver content from x=0.05 to 0.1. The reported magnetocaloric entropy change and relative cooling power for both samples were considerably remarkable with a △S_（max） value of 1.9 J/（kg·K）and maximum RCP values of 100 J/kg, under a magnetic field change（？μ0H） equal to 1.8T. The analysis of the universal curves gave an evidence of a second order magnetic transition for the studied samples. The magnetic field influence on both the magnetic entropy change and the relative cooling power was also studied and discussed.