The development of an efficient artificial H_(2)O_(2) photosynthesis system is a challenging work using H_(2)O and O_(2) as starting materials.Herein,3D In_(2.77)S_(4) nanoflower precursor was in-situ deposited on K^(...The development of an efficient artificial H_(2)O_(2) photosynthesis system is a challenging work using H_(2)O and O_(2) as starting materials.Herein,3D In_(2.77)S_(4) nanoflower precursor was in-situ deposited on K^(+)-doped g-C_(3)N_(4)(KCN)nanosheets using a solvothermal method,then In_(2.77)S_(4)/KCN(IS/KCN)het-erojunction with an intimate interface was obtained after a calcination process.The investigation shows that the photocatalytic H_(2)O_(2) production rate of 50IS/KCN can reach up to 1.36 mmol g^(-1)h^(-1)without any sacrificial reagents under visible light irradiation,which is 9.2 times and 4.1 times higher than that of KCN and In_(2.77)S_(4)/respectively.The enhanced activity of the above composite can be mainly attributed to the S-scheme charge transfer route between KCN and In_(2.77)S_(4) according to density functional theory calculations,electron paramagnetic resonance and free radical capture tests,leading to an expanded light response range and rapid charge separation at their interface,as well as preserving the active electrons and holes for H_(2)O_(2) production.Besides,the unique 3D nanostructure and surface hydrophobicity of IS/KCN facilitate the diffusion and transportation of O_(2) around the active centers,the energy barriers of O_(2) protonation and H_(2)O_(2) desorption steps are ef-fectively reduced over the composite.In addition,this system also exhibits excellent light harvesting ability and stability.This work provides a potential strategy to explore a sustainable H_(2)O_(2) photo-synthesis pathway through the design of heterojunctions with intimate interfaces and desired reac-tion thermodynamics and kinetics.展开更多
A Eu^3＋-doped CaCO3 phosphor with red emission was prepared by microwave synthesis. The scanning electron microscopy （SEM） image and laser particle size analysis show that the CaCO3：Eu^3＋ particles are needle-lik...A Eu^3＋-doped CaCO3 phosphor with red emission was prepared by microwave synthesis. The scanning electron microscopy （SEM） image and laser particle size analysis show that the CaCO3：Eu^3＋ particles are needle-like in the length range of 5.0-10.0 μm. The results of X-ray diffraction （XRD） analysis, Fourier transform infrared spectroscopy （FT-IR）, and Raman spectroscopy indicate that pure aragonite CaCO3：Eu^3＋ is prepared using microwave irradiation and the Eu^3＋ ion as a luminescence center inhabits the site of Ca^2＋. The photoluminescence excitation （PLE） spectrum shows that the strong broad band at around 270 nm and weak sharp lines in 300-550 nm are assigned to the charge transfer band of Eu^3＋-O^2- and intra-configurational 4f-4f transitions of Eu^3＋, respectively. The photoluminescence （PL） spectrum implies that the red luminescence can be attributed to the transitions from the ^5D0 excited level to the ^7FJ （J = 0, 1, 2, 3, 4） levels of Eu^3＋ ions with the mainly electric dipole transition ^5D0 → ^7F2 （614 and 620 nm）, and the Eu^3＋ ions prefer to occupy the low symmetric site in the crystal lattice.展开更多
BaBiO3-doped BaTiO3 （BB-BT） ceramic, as a candidate for lead-free positive temperature coefficient of resistivity （PTCR） materials with a higher Curie temperature, has been synthesized in air by a conventional sin...BaBiO3-doped BaTiO3 （BB-BT） ceramic, as a candidate for lead-free positive temperature coefficient of resistivity （PTCR） materials with a higher Curie temperature, has been synthesized in air by a conventional sintering technique. The temperature dependence of resistivity shows that the phase transition of the PTC thermistor ceramic occurs at the Curie temperature, Tc = 155℃, which is higher than that of BaTiO3 （≤ 130 ℃）. Analysis of ac impedance data using complex impedance spectroscopy gives the alternate current （AC） resistance of the PTCR ceramic. By additional use of the complex electric modulus formalism to analyse the same data, the inhomogeneous nature of the ceramic may be unveiled. The impedance spectra reveal that the grain resistance of the BB-BT sample is slightly influenced by the increase of temperature, indicating that the increase in overall resistivity is entirely due to a grain-boundary effect. Based on the dependence of the extent to which the peaks of the imaginary part of electric modulus and impedance are matched on frequency, the conduction mechanism is also discussed for a BB-BT ceramic system.展开更多
Steel-cemented WC was prepared by ball milling, cold compacting and microwave sintering with Fe powder as the matrix, WC as the hard phase and the addition of rare earth Y2O3. The results show that the interface of th...Steel-cemented WC was prepared by ball milling, cold compacting and microwave sintering with Fe powder as the matrix, WC as the hard phase and the addition of rare earth Y2O3. The results show that the interface of the WC particles and Fe matrix exhibits excellent wettability and liquidity when the microwave sintering temperature reaches 1,280℃. The density and mechanical properties of the steel bonded WC carbides could be greatly improved, the hard phases become finer and more uniform dispersed owing to the addition of Y2O3. With the increase of the Y2O3 contents, the grain becomes uniform and fine first, and then gathers and grows up. The relative density, microhardness and bending strength all rise first, reaching the maximum values of 97.29 %, HV1024 and 1,267.60 MPa at 0.5 % Y2O3, respectively, and then decrease. Moreover, the relative density and mechanical properties of the steel-cemented WC with nano-Y2O3 are higher than that with micron-Y2O3, which indicates that the effect of nano-Y2O3 is better than that of the micron-Y2O3.展开更多
A near infrared to visible blue, green, and red upconversion luminescence in a Tb^3＋-doped CaO-Al2O3-SiO2 glass was studied, which was excited using 800 nm femtosecond laser irradiation. The upconversion luminescence...A near infrared to visible blue, green, and red upconversion luminescence in a Tb^3＋-doped CaO-Al2O3-SiO2 glass was studied, which was excited using 800 nm femtosecond laser irradiation. The upconversion luminescence was attributed to ^5D3→^7F5, ^5D3→^7F4, ^5D3→^7F3, ^5D4→^7F6, ^5D4→^7F5, ^5D4→^7F4, and ^5D4→^7F3 transitions of Tb^3＋. The relationship between upconversion luminescence intensity and the pump power indicated that a three-photon simultaneous absorption process was dominant in this upconversion luminescence. The intense red, green, and blue upconversion luminescence of Tb^3＋-doped CaO-Al2O3-SiO2 glass may be potentially useful in developing three-dimensional display applications.展开更多
Chemical-looping oxidative dehydrogenation(CL-ODH)is a process designed for the conversion of alkanes into olefins through cyclic redox reactions,eliminating the need for gaseous O_(2).In this work,we investigated the...Chemical-looping oxidative dehydrogenation(CL-ODH)is a process designed for the conversion of alkanes into olefins through cyclic redox reactions,eliminating the need for gaseous O_(2).In this work,we investigated the use of Ca_(2)MnO_(4)-layered perovskites modified with NaNO_(3) dopants,serving as redox catalysts(also known as oxygen carriers),for the CL-ODH of ethane within a temperature range of 700-780℃.Our findings revealed that the incorporation of NaNO_(3) as a modifier significantly-nhanced the selectivity for-thylene generation from Ca_(2)MnO_(4).At 750℃and a gas hourly space velocity of 1300 h^(-1),we achieved an-thane conversion up to 68.17%,accompanied by a corresponding-thylene yield of 57.39%.X-ray photoelectron spectroscopy analysis unveiled that the doping NaNO_(3) onto Ca_(2)MnO_(4) not only played a role in reducing the oxidation state of Mn ions but also increased the lattice oxygen content of the redox catalyst.Furthermore,formation of NaNO_(3) shell on the surface of Ca_(2)MnO_(4) led to a reduction in the concentration of manganese sites and modulated the oxygen-releasing behavior in a step-wise manner.This modulation contributed significantly to the enhanced selectivity for ethylene of the NaNO_(3)-doped Ca_(2)MnO_(4) catalyst.These findings provide compelling evidence for the potential of Ca_(2)MnO_(4)-layered perovskites as promising redox catalysts in the context of CL-ODH reactions.展开更多
Tetragonal structural(t-NdVO4)nanorod-arrays were fabricated by simple one-pot hydrothermal method.The phase,morphology and microstructure of NdVO4 were characterized by X-ray diffractometer,scanning electron microsco...Tetragonal structural(t-NdVO4)nanorod-arrays were fabricated by simple one-pot hydrothermal method.The phase,morphology and microstructure of NdVO4 were characterized by X-ray diffractometer,scanning electron microscope(SEM),transmission electron microscope(TEM),dispersive X-ray spectrometer(EDS)and selected area electron diffraction(SAED)techniques.t-NdVO4 nanorods are single-crystalline with a length of 100 nm and a diameter of 25 nm,which grow orientally along the direction of(112)crystalline plane and self-assemble to form nanorod-arrays.The results show that Eu^3+-doping interrupts the formation of NdVO4 nanorod-arrays,and then leads to the red-shift of the strongest luminescence emission of Nd3+transition from 4D3/2 state to 4I11/2 and decreases its intensity of the fluorescence emission at 400 nm sharply.The research results have some reference values to optimize the photoluminescence performance of rare earth vanadates.展开更多
A kind of novel experiment was disclosed as it possessed two bands of fluorescence emission at 1.4 and 1.6 μm, which were perfectly complimentary to the current C band of optic communication. The fluorescence was bas...A kind of novel experiment was disclosed as it possessed two bands of fluorescence emission at 1.4 and 1.6 μm, which were perfectly complimentary to the current C band of optic communication. The fluorescence was based on energy transfer and up-conversion processes between Tm^3＋ and Yb^3＋ under direct pumping of 975 nm LD. The spectra and lifetimes of Tm^3＋ fluorescence in the tellurite glass were described. The corresponding fluorescence characteristics and energy migration process were analyzed by the method of lifetime and intensity comparison. The mechanism of the up-conversion based IR fluorescence was presented upon analyzing the multi-photon pumping process. The potential advantages of Tm^3＋/Yb^3＋ co-doped tellurite glass as amplifier material were concluded.展开更多
The fluorozirconate glasses ZBLANP( ZrF\-4-BaF\-2-LaF\-3-AlF\-3-NaF-PbF\-2) doped with different Yb\+ 3+ concentration were prepared. The Raman spectra and absorption spectra are measured to substantiate the existenc...The fluorozirconate glasses ZBLANP( ZrF\-4-BaF\-2-LaF\-3-AlF\-3-NaF-PbF\-2) doped with different Yb\+ 3+ concentration were prepared. The Raman spectra and absorption spectra are measured to substantiate the existence of phonon-assisted emission. After analyzing the normalized absorption spectra of samples with different Yb\+ 3+-doped concentration, we calculated the maximum cooling effect in the 3 wt% Yb\+ 3+-doped sample pumped at 1 012.5 nm. The corresponding cooling capability is about -4.09 ℃/W and the cooling efficiency reaches 1.76%.展开更多
Y2O3：Eu3＋ phosphors co-doped with different metal cations （Li＋, Na＋, K＋, Mg2＋, Ca2＋） are prepared by the gel- combustion method with Y2O3：Eu3＋, and R（NO3）x （R = Li, Na, K, Mg, Ca） serving as raw materi...Y2O3：Eu3＋ phosphors co-doped with different metal cations （Li＋, Na＋, K＋, Mg2＋, Ca2＋） are prepared by the gel- combustion method with Y2O3：Eu3＋, and R（NO3）x （R = Li, Na, K, Mg, Ca） serving as raw materials and glycine as fuel, calcined at 1000 ℃ for 2 h. The synthesized Y203 ：Eu3＋ phosphors doped with different metal cations and doping ratios are characterized by x-ray diffractometry （XRD）, fluorescence and phosphorescent spectrophotometer. The co-doping metal cations are advantageous to the development of Y203：Eu3＋ lattice. All the samples can emit red light peaked at 611 nm under 254-nm excited. The luminescence intensities of co-doping samples are increased because the cations increase the electron transition probability of Eu3＋ from 5D0 level to 7F level. The fluorescence lifetime of Eu3＋ （SD0 --＋7F2） is increased by doping metal cations.展开更多
The bismuth and europium activated Y2O3 red phosphors and were investigated their structure and optical properties. Adding bismuth ions enhance the energy absorption between 300 nm and 400 nm of Eu-doped Y2O3 excitati...The bismuth and europium activated Y2O3 red phosphors and were investigated their structure and optical properties. Adding bismuth ions enhance the energy absorption between 300 nm and 400 nm of Eu-doped Y2O3 excitation spectra. The reason may be the energy transfer from bismuth to europium ions.展开更多
This study delves into the charge transfer mechanism of boron (B)-doped 3C-SiC through first-principles investigations. We explore the effects of B doping on the electronic properties of 3C-SiC, focusing on a 12.5% im...This study delves into the charge transfer mechanism of boron (B)-doped 3C-SiC through first-principles investigations. We explore the effects of B doping on the electronic properties of 3C-SiC, focusing on a 12.5% impurity concentration. Our comprehensive analysis encompasses structural properties, electronic band structures, and charge density distributions. The optimized lattice constant and band gap energy of 3C-SiC were found to be 4.373 Å and 1.36 eV respectively, which is in agreement with previous research (Bui, 2012;Muchiri et al., 2018). Our results show that B doping narrows the band gap, enhances electrical conductivity, and influences charge transfer interactions. The charge density analysis reveals substantial interactions between B dopants and surrounding carbon atoms. This work not only enhances our understanding of the material’s electronic properties, but also highlights the importance of charge density analysis for characterizing charge transfer mechanisms and their implications in the 3C-SiC semiconductors.展开更多
Peroxidase plays an important role in living systems;however,its storage difficulty and easy inactivation have limited its applications in complex environments.To address these problems,herein,we proposed a method to ...Peroxidase plays an important role in living systems;however,its storage difficulty and easy inactivation have limited its applications in complex environments.To address these problems,herein,we proposed a method to synthesize peroxidase mimics by amination,carbonization,and Fe^(3+)-doping of industrial alkali lignin.The Fe^(3+)-doped lignin-based peroxidase mimic(Fe-LPM),with active centers of coordination between Fe^(3+)and N atoms,showed higher tolerance to pH value and temperature than natural peroxidase.Using Fe-LPM,10-100 mmol/L of H_(2)O_(2) and glucose could be colorimetrically detected with the lowest detection limits of 80μmol/L and 1.5 mmol/L and visual detection limits of 1.0 mmol/L and 10 mmol/L,respectively.The Fe-LPM maintained peroxidase-like activity after 10 cycles and could even be used for H_(2)O_(2) detection in practical samples.This work not only provides a new approach to synthesize peroxidase mimics using biomass materials but also promotes the high-value utilization of lignin.展开更多
文摘The development of an efficient artificial H_(2)O_(2) photosynthesis system is a challenging work using H_(2)O and O_(2) as starting materials.Herein,3D In_(2.77)S_(4) nanoflower precursor was in-situ deposited on K^(+)-doped g-C_(3)N_(4)(KCN)nanosheets using a solvothermal method,then In_(2.77)S_(4)/KCN(IS/KCN)het-erojunction with an intimate interface was obtained after a calcination process.The investigation shows that the photocatalytic H_(2)O_(2) production rate of 50IS/KCN can reach up to 1.36 mmol g^(-1)h^(-1)without any sacrificial reagents under visible light irradiation,which is 9.2 times and 4.1 times higher than that of KCN and In_(2.77)S_(4)/respectively.The enhanced activity of the above composite can be mainly attributed to the S-scheme charge transfer route between KCN and In_(2.77)S_(4) according to density functional theory calculations,electron paramagnetic resonance and free radical capture tests,leading to an expanded light response range and rapid charge separation at their interface,as well as preserving the active electrons and holes for H_(2)O_(2) production.Besides,the unique 3D nanostructure and surface hydrophobicity of IS/KCN facilitate the diffusion and transportation of O_(2) around the active centers,the energy barriers of O_(2) protonation and H_(2)O_(2) desorption steps are ef-fectively reduced over the composite.In addition,this system also exhibits excellent light harvesting ability and stability.This work provides a potential strategy to explore a sustainable H_(2)O_(2) photo-synthesis pathway through the design of heterojunctions with intimate interfaces and desired reac-tion thermodynamics and kinetics.
基金supported by the National Natural Science Foundation of China (No. 10476024) the Science and Technology Bureau of Sichuan Province, China (No. 2006J13-059)
文摘A Eu^3＋-doped CaCO3 phosphor with red emission was prepared by microwave synthesis. The scanning electron microscopy （SEM） image and laser particle size analysis show that the CaCO3：Eu^3＋ particles are needle-like in the length range of 5.0-10.0 μm. The results of X-ray diffraction （XRD） analysis, Fourier transform infrared spectroscopy （FT-IR）, and Raman spectroscopy indicate that pure aragonite CaCO3：Eu^3＋ is prepared using microwave irradiation and the Eu^3＋ ion as a luminescence center inhabits the site of Ca^2＋. The photoluminescence excitation （PLE） spectrum shows that the strong broad band at around 270 nm and weak sharp lines in 300-550 nm are assigned to the charge transfer band of Eu^3＋-O^2- and intra-configurational 4f-4f transitions of Eu^3＋, respectively. The photoluminescence （PL） spectrum implies that the red luminescence can be attributed to the transitions from the ^5D0 excited level to the ^7FJ （J = 0, 1, 2, 3, 4） levels of Eu^3＋ ions with the mainly electric dipole transition ^5D0 → ^7F2 （614 and 620 nm）, and the Eu^3＋ ions prefer to occupy the low symmetric site in the crystal lattice.
基金supported by the Research Funds of the Guangxi Key Laboratory of Information Materials at the School of Material Science and Engineering,China (Grant No. 0710908-07-Z)
文摘BaBiO3-doped BaTiO3 （BB-BT） ceramic, as a candidate for lead-free positive temperature coefficient of resistivity （PTCR） materials with a higher Curie temperature, has been synthesized in air by a conventional sintering technique. The temperature dependence of resistivity shows that the phase transition of the PTC thermistor ceramic occurs at the Curie temperature, Tc = 155℃, which is higher than that of BaTiO3 （≤ 130 ℃）. Analysis of ac impedance data using complex impedance spectroscopy gives the alternate current （AC） resistance of the PTCR ceramic. By additional use of the complex electric modulus formalism to analyse the same data, the inhomogeneous nature of the ceramic may be unveiled. The impedance spectra reveal that the grain resistance of the BB-BT sample is slightly influenced by the increase of temperature, indicating that the increase in overall resistivity is entirely due to a grain-boundary effect. Based on the dependence of the extent to which the peaks of the imaginary part of electric modulus and impedance are matched on frequency, the conduction mechanism is also discussed for a BB-BT ceramic system.
基金supported by the Science and Technology Plan Projects of Jiangxi Province (No. 2011BBE50010)the Project from the Jiangxi Province Key Laboratory of Copper Tungsten New Materials (No. 2011-TW-08)
文摘Steel-cemented WC was prepared by ball milling, cold compacting and microwave sintering with Fe powder as the matrix, WC as the hard phase and the addition of rare earth Y2O3. The results show that the interface of the WC particles and Fe matrix exhibits excellent wettability and liquidity when the microwave sintering temperature reaches 1,280℃. The density and mechanical properties of the steel bonded WC carbides could be greatly improved, the hard phases become finer and more uniform dispersed owing to the addition of Y2O3. With the increase of the Y2O3 contents, the grain becomes uniform and fine first, and then gathers and grows up. The relative density, microhardness and bending strength all rise first, reaching the maximum values of 97.29 %, HV1024 and 1,267.60 MPa at 0.5 % Y2O3, respectively, and then decrease. Moreover, the relative density and mechanical properties of the steel-cemented WC with nano-Y2O3 are higher than that with micron-Y2O3, which indicates that the effect of nano-Y2O3 is better than that of the micron-Y2O3.
基金supported by the Education Department of Zhejiang Province (20050359)
文摘A near infrared to visible blue, green, and red upconversion luminescence in a Tb^3＋-doped CaO-Al2O3-SiO2 glass was studied, which was excited using 800 nm femtosecond laser irradiation. The upconversion luminescence was attributed to ^5D3→^7F5, ^5D3→^7F4, ^5D3→^7F3, ^5D4→^7F6, ^5D4→^7F5, ^5D4→^7F4, and ^5D4→^7F3 transitions of Tb^3＋. The relationship between upconversion luminescence intensity and the pump power indicated that a three-photon simultaneous absorption process was dominant in this upconversion luminescence. The intense red, green, and blue upconversion luminescence of Tb^3＋-doped CaO-Al2O3-SiO2 glass may be potentially useful in developing three-dimensional display applications.
基金support of National Natural Science Foundation of China(22179027)gratefully acknowledged.This work was also supported by the Natural Science Foundation of Guangxi Province(2021GXNSFAA075063,2018GXNSFDA281005)+1 种基金the National Key Research and Development Program of China(2017YFE0105500)Science&Technology Research Project of Guangdong Province(2017A020216009).
文摘Chemical-looping oxidative dehydrogenation(CL-ODH)is a process designed for the conversion of alkanes into olefins through cyclic redox reactions,eliminating the need for gaseous O_(2).In this work,we investigated the use of Ca_(2)MnO_(4)-layered perovskites modified with NaNO_(3) dopants,serving as redox catalysts(also known as oxygen carriers),for the CL-ODH of ethane within a temperature range of 700-780℃.Our findings revealed that the incorporation of NaNO_(3) as a modifier significantly-nhanced the selectivity for-thylene generation from Ca_(2)MnO_(4).At 750℃and a gas hourly space velocity of 1300 h^(-1),we achieved an-thane conversion up to 68.17%,accompanied by a corresponding-thylene yield of 57.39%.X-ray photoelectron spectroscopy analysis unveiled that the doping NaNO_(3) onto Ca_(2)MnO_(4) not only played a role in reducing the oxidation state of Mn ions but also increased the lattice oxygen content of the redox catalyst.Furthermore,formation of NaNO_(3) shell on the surface of Ca_(2)MnO_(4) led to a reduction in the concentration of manganese sites and modulated the oxygen-releasing behavior in a step-wise manner.This modulation contributed significantly to the enhanced selectivity for ethylene of the NaNO_(3)-doped Ca_(2)MnO_(4) catalyst.These findings provide compelling evidence for the potential of Ca_(2)MnO_(4)-layered perovskites as promising redox catalysts in the context of CL-ODH reactions.
基金Project(51202066)supported by the National Natural Science Foundation of ChinaProject(NCET-13-0784)supported by the Program for New Century Excellent Talents of the Education Ministry,China。
文摘Tetragonal structural(t-NdVO4)nanorod-arrays were fabricated by simple one-pot hydrothermal method.The phase,morphology and microstructure of NdVO4 were characterized by X-ray diffractometer,scanning electron microscope(SEM),transmission electron microscope(TEM),dispersive X-ray spectrometer(EDS)and selected area electron diffraction(SAED)techniques.t-NdVO4 nanorods are single-crystalline with a length of 100 nm and a diameter of 25 nm,which grow orientally along the direction of(112)crystalline plane and self-assemble to form nanorod-arrays.The results show that Eu^3+-doping interrupts the formation of NdVO4 nanorod-arrays,and then leads to the red-shift of the strongest luminescence emission of Nd3+transition from 4D3/2 state to 4I11/2 and decreases its intensity of the fluorescence emission at 400 nm sharply.The research results have some reference values to optimize the photoluminescence performance of rare earth vanadates.
基金supported by the Natural Science Foundation of Zhejiang Provience, China (2006C21082)National Natural Science Foundation of China (60677015)+1 种基金Foundation of Ningbo University (XR0710018)sponsored by KC Wong Magna Fund in NingBo University
文摘A kind of novel experiment was disclosed as it possessed two bands of fluorescence emission at 1.4 and 1.6 μm, which were perfectly complimentary to the current C band of optic communication. The fluorescence was based on energy transfer and up-conversion processes between Tm^3＋ and Yb^3＋ under direct pumping of 975 nm LD. The spectra and lifetimes of Tm^3＋ fluorescence in the tellurite glass were described. The corresponding fluorescence characteristics and energy migration process were analyzed by the method of lifetime and intensity comparison. The mechanism of the up-conversion based IR fluorescence was presented upon analyzing the multi-photon pumping process. The potential advantages of Tm^3＋/Yb^3＋ co-doped tellurite glass as amplifier material were concluded.
文摘The fluorozirconate glasses ZBLANP( ZrF\-4-BaF\-2-LaF\-3-AlF\-3-NaF-PbF\-2) doped with different Yb\+ 3+ concentration were prepared. The Raman spectra and absorption spectra are measured to substantiate the existence of phonon-assisted emission. After analyzing the normalized absorption spectra of samples with different Yb\+ 3+-doped concentration, we calculated the maximum cooling effect in the 3 wt% Yb\+ 3+-doped sample pumped at 1 012.5 nm. The corresponding cooling capability is about -4.09 ℃/W and the cooling efficiency reaches 1.76%.
文摘Y2O3：Eu3＋ phosphors co-doped with different metal cations （Li＋, Na＋, K＋, Mg2＋, Ca2＋） are prepared by the gel- combustion method with Y2O3：Eu3＋, and R（NO3）x （R = Li, Na, K, Mg, Ca） serving as raw materials and glycine as fuel, calcined at 1000 ℃ for 2 h. The synthesized Y203 ：Eu3＋ phosphors doped with different metal cations and doping ratios are characterized by x-ray diffractometry （XRD）, fluorescence and phosphorescent spectrophotometer. The co-doping metal cations are advantageous to the development of Y203：Eu3＋ lattice. All the samples can emit red light peaked at 611 nm under 254-nm excited. The luminescence intensities of co-doping samples are increased because the cations increase the electron transition probability of Eu3＋ from 5D0 level to 7F level. The fluorescence lifetime of Eu3＋ （SD0 --＋7F2） is increased by doping metal cations.
文摘The bismuth and europium activated Y2O3 red phosphors and were investigated their structure and optical properties. Adding bismuth ions enhance the energy absorption between 300 nm and 400 nm of Eu-doped Y2O3 excitation spectra. The reason may be the energy transfer from bismuth to europium ions.
文摘This study delves into the charge transfer mechanism of boron (B)-doped 3C-SiC through first-principles investigations. We explore the effects of B doping on the electronic properties of 3C-SiC, focusing on a 12.5% impurity concentration. Our comprehensive analysis encompasses structural properties, electronic band structures, and charge density distributions. The optimized lattice constant and band gap energy of 3C-SiC were found to be 4.373 Å and 1.36 eV respectively, which is in agreement with previous research (Bui, 2012;Muchiri et al., 2018). Our results show that B doping narrows the band gap, enhances electrical conductivity, and influences charge transfer interactions. The charge density analysis reveals substantial interactions between B dopants and surrounding carbon atoms. This work not only enhances our understanding of the material’s electronic properties, but also highlights the importance of charge density analysis for characterizing charge transfer mechanisms and their implications in the 3C-SiC semiconductors.
基金The authors are grateful for the financial support by the
文摘Peroxidase plays an important role in living systems;however,its storage difficulty and easy inactivation have limited its applications in complex environments.To address these problems,herein,we proposed a method to synthesize peroxidase mimics by amination,carbonization,and Fe^(3+)-doping of industrial alkali lignin.The Fe^(3+)-doped lignin-based peroxidase mimic(Fe-LPM),with active centers of coordination between Fe^(3+)and N atoms,showed higher tolerance to pH value and temperature than natural peroxidase.Using Fe-LPM,10-100 mmol/L of H_(2)O_(2) and glucose could be colorimetrically detected with the lowest detection limits of 80μmol/L and 1.5 mmol/L and visual detection limits of 1.0 mmol/L and 10 mmol/L,respectively.The Fe-LPM maintained peroxidase-like activity after 10 cycles and could even be used for H_(2)O_(2) detection in practical samples.This work not only provides a new approach to synthesize peroxidase mimics using biomass materials but also promotes the high-value utilization of lignin.