YAG： Ce^3 ＋ phosphor particles were prepared using polyacrylamide gel method. The structure evolution of powders during annealing process was followed by X-ray diffraction determination. It is found that some interm...YAG： Ce^3 ＋ phosphor particles were prepared using polyacrylamide gel method. The structure evolution of powders during annealing process was followed by X-ray diffraction determination. It is found that some intermediate phases, including θ-Al2O3, YAM and YAP, are formed when calcining polyacrylamide gel, however, the pure YAG phase can be formed directly when calcining polyacrylamide gel with α-Al2O3 as seed crystal. These facts show that the existence of α- Al2O3 seed crystal can block the formation of θ-Al2O3, YAM and YAP, and accelerate its reaction with Y2O3 to form YAG phase directly at lower temperature. The emission peak of prepared YAG ： Ce^3 ＋ phosphor is wide with maximum at 550 nm and the exitation band has two peaks, the major one is around at 460 nm, which matches the blue emission of GaN LED and is suitable for the assemble of white LED. Some fluxes can enhance the photoluminescence intensity of phosphor particles, that can be attributed both to the improvement of crystallization processes of YAG and to the stabilization of trivalence cerium ion in YAG：Ce^3 ＋.展开更多
The well crystalline YAG：Ce^3＋ phosphor was synthesized by sold-state method, and the temperature dependence of excitation and emission spectra of YAG：Ce^3＋ phosphor were investigated in the temperature range from...The well crystalline YAG：Ce^3＋ phosphor was synthesized by sold-state method, and the temperature dependence of excitation and emission spectra of YAG：Ce^3＋ phosphor were investigated in the temperature range from room temperature to 573 K. With temperature increasing, it was noted that the emission intensity of as-repared phosphors decreased considerably more rapidly when pumped by 460 nm than by 340 nm. The temperature-intensity curves under different excitation wavelengths were obtained using an Arrhenius function, and the corresponding activation energies were also obtained respectively. Thus, the experimental phenomenon was discussed in terms of nonradiative decay rate. The effects of as-prepared phosphors on the performance of the white LED with changing temperature were also studied.展开更多
A series of YAG：Ce,Tb phosphors were synthesized by vacuum sintering method.Moreover,their spectral properties,thermal quenching behaviors and color rendering properties were investigated systematically.The photolumi...A series of YAG：Ce,Tb phosphors were synthesized by vacuum sintering method.Moreover,their spectral properties,thermal quenching behaviors and color rendering properties were investigated systematically.The photoluminescence emission spectra of YAG：Ce,Tb show a great red shift compared with that of YAG：Ce.Direct energy transfer from Tb^（3＋） to Ce^（3＋） ions is verified based on the analysis of different photoluminescence spectra.The quenching temperature for Tb^（3＋）-doped YAG：Ce phosphors is about 490 K.The thermal activation energy is estimated to be 0.18 and 0.291 eV for Tb^（3＋）-doped YAG：Ce and YAG：Ce phosphors,respectively.The smaller activation energy for Tb^（3＋）-doped YAG：Ce means a more rapid nonradiative transition from 5d to 4f state,thus resulting in the lower quenching temperature.In addition,white LEDs with improved color rendering properties are achieved by using modified YAG：Ce,Tb phosphors.展开更多
In order to confirm the relationship between the luminescence and the ratio of Ce3+/Ce4+ more clearly, a series of YAG:Ce3+ (Yttrium Aluminum Garnet, Y2.94Al5O12:0.06Ce3+) phosphors were pre- pared under different sin...In order to confirm the relationship between the luminescence and the ratio of Ce3+/Ce4+ more clearly, a series of YAG:Ce3+ (Yttrium Aluminum Garnet, Y2.94Al5O12:0.06Ce3+) phosphors were pre- pared under different sintering atmosphere. A semi-quantitative analysis based on X-ray photoe-lectron spectroscopy (XPS) was introduced to study the mole ratio of Ce3+/Ce4+ in the as-synthesized YAG:Ce3+ phosphors. The results indicated that the percentage of Ce3+/(Ce3+ + Ce4+) reached 88.46% under the reduction atmosphere. The emission intensity of YAG:Ce3+ phosphors was in-creased significantly with the increasing of Ce3+ concentration.展开更多
实现高发光效率、高亮度和良好的热稳定性是固态照明的迫切要求。因此,用于高功率发光二极管或激光二极管(LED/LD)的高性能荧光转换材料具有重要的研究意义。在这项工作中,通过将Lu^(3+)离子引入YAG∶Ce荧光陶瓷中方法作为有效策略来改...实现高发光效率、高亮度和良好的热稳定性是固态照明的迫切要求。因此,用于高功率发光二极管或激光二极管(LED/LD)的高性能荧光转换材料具有重要的研究意义。在这项工作中,通过将Lu^(3+)离子引入YAG∶Ce荧光陶瓷中方法作为有效策略来改善YAG∶Ce荧光材料的发光性能。采用固相反应和真空烧结法制Article ID:1000-7032(2023)06-0964^(-1)1收稿日期:2022^(-1)2-31;修订日期:2023-01-30基金项目:中国科学院战略性先导科技专项(XDA22010301)Supported by The Strategic Priority Research Program of The Chinese Academy of Sciences(XDA22010301)第6 HUANG Xinyou期,et al.:LuYAG∶Ce Transparent Ceramic Phosphors for High-brightness Solid-state…备了不同Lu^(3+)含量的(Lu,Y)_(3)Al_(5)O_(12)∶Ce荧光陶瓷(LuYAG∶Ce荧光陶瓷)。随着Lu^(3+)含量的增加,LuYAG∶Ce荧光陶瓷中的Y^(3+)位点被Lu^(3+)位点取代,Ce^(3+)的发射峰呈现从573 nm到563 nm的蓝移现象。当Lu^(3+)含量为60%时,通过将LuYAG∶Ce荧光陶瓷与蓝光LED组合,其发光强度达到最大值,流明效率达到114 lm∙W^(-1)。使用450 nm激光源与LuYAG∶Ce荧光陶瓷构建了透射模式下的激光驱动照明装置。随着功率密度从2.2 W·mm^(-2)增加到39 W·mm^(-2),Lu^(3+)含量为60%的荧光陶瓷光通量从128 lm增加到1874 lm,且没有发光饱和的迹象,最佳发光效率达到128 lm·W^(-1)。因此,LuYAG∶Ce荧光陶瓷有望成为高功率LED/LD照明的潜在荧光转换材料。展开更多
文摘YAG： Ce^3 ＋ phosphor particles were prepared using polyacrylamide gel method. The structure evolution of powders during annealing process was followed by X-ray diffraction determination. It is found that some intermediate phases, including θ-Al2O3, YAM and YAP, are formed when calcining polyacrylamide gel, however, the pure YAG phase can be formed directly when calcining polyacrylamide gel with α-Al2O3 as seed crystal. These facts show that the existence of α- Al2O3 seed crystal can block the formation of θ-Al2O3, YAM and YAP, and accelerate its reaction with Y2O3 to form YAG phase directly at lower temperature. The emission peak of prepared YAG ： Ce^3 ＋ phosphor is wide with maximum at 550 nm and the exitation band has two peaks, the major one is around at 460 nm, which matches the blue emission of GaN LED and is suitable for the assemble of white LED. Some fluxes can enhance the photoluminescence intensity of phosphor particles, that can be attributed both to the improvement of crystallization processes of YAG and to the stabilization of trivalence cerium ion in YAG：Ce^3 ＋.
基金the Key Technologies R&D Program of Shandong Province (2006gg2201014)Tianjin Natural Science Foundation (07JCYBJC06400)Tianjin Education Committee Science and Technology Development Foundation
文摘The well crystalline YAG：Ce^3＋ phosphor was synthesized by sold-state method, and the temperature dependence of excitation and emission spectra of YAG：Ce^3＋ phosphor were investigated in the temperature range from room temperature to 573 K. With temperature increasing, it was noted that the emission intensity of as-repared phosphors decreased considerably more rapidly when pumped by 460 nm than by 340 nm. The temperature-intensity curves under different excitation wavelengths were obtained using an Arrhenius function, and the corresponding activation energies were also obtained respectively. Thus, the experimental phenomenon was discussed in terms of nonradiative decay rate. The effects of as-prepared phosphors on the performance of the white LED with changing temperature were also studied.
基金supported by the National Natural Science Foundation of China(51272282,51302311)the Beijing Committee of Science and Technology(Z13111000280000)the Education Commission of Beijing(2011010329)
文摘A series of YAG：Ce,Tb phosphors were synthesized by vacuum sintering method.Moreover,their spectral properties,thermal quenching behaviors and color rendering properties were investigated systematically.The photoluminescence emission spectra of YAG：Ce,Tb show a great red shift compared with that of YAG：Ce.Direct energy transfer from Tb^（3＋） to Ce^（3＋） ions is verified based on the analysis of different photoluminescence spectra.The quenching temperature for Tb^（3＋）-doped YAG：Ce phosphors is about 490 K.The thermal activation energy is estimated to be 0.18 and 0.291 eV for Tb^（3＋）-doped YAG：Ce and YAG：Ce phosphors,respectively.The smaller activation energy for Tb^（3＋）-doped YAG：Ce means a more rapid nonradiative transition from 5d to 4f state,thus resulting in the lower quenching temperature.In addition,white LEDs with improved color rendering properties are achieved by using modified YAG：Ce,Tb phosphors.
文摘In order to confirm the relationship between the luminescence and the ratio of Ce3+/Ce4+ more clearly, a series of YAG:Ce3+ (Yttrium Aluminum Garnet, Y2.94Al5O12:0.06Ce3+) phosphors were pre- pared under different sintering atmosphere. A semi-quantitative analysis based on X-ray photoe-lectron spectroscopy (XPS) was introduced to study the mole ratio of Ce3+/Ce4+ in the as-synthesized YAG:Ce3+ phosphors. The results indicated that the percentage of Ce3+/(Ce3+ + Ce4+) reached 88.46% under the reduction atmosphere. The emission intensity of YAG:Ce3+ phosphors was in-creased significantly with the increasing of Ce3+ concentration.
文摘实现高发光效率、高亮度和良好的热稳定性是固态照明的迫切要求。因此,用于高功率发光二极管或激光二极管(LED/LD)的高性能荧光转换材料具有重要的研究意义。在这项工作中,通过将Lu^(3+)离子引入YAG∶Ce荧光陶瓷中方法作为有效策略来改善YAG∶Ce荧光材料的发光性能。采用固相反应和真空烧结法制Article ID:1000-7032(2023)06-0964^(-1)1收稿日期:2022^(-1)2-31;修订日期:2023-01-30基金项目:中国科学院战略性先导科技专项(XDA22010301)Supported by The Strategic Priority Research Program of The Chinese Academy of Sciences(XDA22010301)第6 HUANG Xinyou期,et al.:LuYAG∶Ce Transparent Ceramic Phosphors for High-brightness Solid-state…备了不同Lu^(3+)含量的(Lu,Y)_(3)Al_(5)O_(12)∶Ce荧光陶瓷(LuYAG∶Ce荧光陶瓷)。随着Lu^(3+)含量的增加,LuYAG∶Ce荧光陶瓷中的Y^(3+)位点被Lu^(3+)位点取代,Ce^(3+)的发射峰呈现从573 nm到563 nm的蓝移现象。当Lu^(3+)含量为60%时,通过将LuYAG∶Ce荧光陶瓷与蓝光LED组合,其发光强度达到最大值,流明效率达到114 lm∙W^(-1)。使用450 nm激光源与LuYAG∶Ce荧光陶瓷构建了透射模式下的激光驱动照明装置。随着功率密度从2.2 W·mm^(-2)增加到39 W·mm^(-2),Lu^(3+)含量为60%的荧光陶瓷光通量从128 lm增加到1874 lm,且没有发光饱和的迹象,最佳发光效率达到128 lm·W^(-1)。因此,LuYAG∶Ce荧光陶瓷有望成为高功率LED/LD照明的潜在荧光转换材料。