YAG： Ce^3 ＋ phosphor particles were prepared using polyacrylamide gel method. The structure evolution of powders during annealing process was followed by X-ray diffraction determination. It is found that some interm...YAG： Ce^3 ＋ phosphor particles were prepared using polyacrylamide gel method. The structure evolution of powders during annealing process was followed by X-ray diffraction determination. It is found that some intermediate phases, including θ-Al2O3, YAM and YAP, are formed when calcining polyacrylamide gel, however, the pure YAG phase can be formed directly when calcining polyacrylamide gel with α-Al2O3 as seed crystal. These facts show that the existence of α- Al2O3 seed crystal can block the formation of θ-Al2O3, YAM and YAP, and accelerate its reaction with Y2O3 to form YAG phase directly at lower temperature. The emission peak of prepared YAG ： Ce^3 ＋ phosphor is wide with maximum at 550 nm and the exitation band has two peaks, the major one is around at 460 nm, which matches the blue emission of GaN LED and is suitable for the assemble of white LED. Some fluxes can enhance the photoluminescence intensity of phosphor particles, that can be attributed both to the improvement of crystallization processes of YAG and to the stabilization of trivalence cerium ion in YAG：Ce^3 ＋.展开更多
The passively Q-switched and mode-locked（QML） characteristics in a diode-pumped Nd∶GdVO4 laser with Cr4+∶YAG saturable absorbers have been demonstrated. A maximum average output power of 710mW has been obtained in...The passively Q-switched and mode-locked（QML） characteristics in a diode-pumped Nd∶GdVO4 laser with Cr4+∶YAG saturable absorbers have been demonstrated. A maximum average output power of 710mW has been obtained in the QML laser. The maximum energy of a single Q-switched pulse is 52.5μJ, with the corresponding pulse width of 30ns and the peak power of 1.75kW, at the incident pump power of 7.75W. The repetition rates of the Q-switched envelope and the mode-locked laser pulse are 16.7kHz and 680MHz, respectively.展开更多
This paper reported the crystal growth and spectroscopy characters of Cr^3＋：Li2Mg2（MoO4）3. The refractive index of Cr^3＋：Li2Mg2（MoO4）3 crystal is 1.87 and the hardness is 270 I-IV. This crystal shows broadband...This paper reported the crystal growth and spectroscopy characters of Cr^3＋：Li2Mg2（MoO4）3. The refractive index of Cr^3＋：Li2Mg2（MoO4）3 crystal is 1.87 and the hardness is 270 I-IV. This crystal shows broadband absorption property with peak wavelength at about 495 and 699 nm. The absorption crosssection is 14.75 × 10^-20 cm^2 at 495 nm and 9.63 ×10^-20 cm^2 at 699 nm, respectively. The crystal field strength and energy levels of Cr^3＋ ion were calculated based on the spectroscopic data. The Cr^3＋：Li2Mg2（MoO4）3 crystal shows broadband emission extending from 750 to 1300 nm even excited at 10 K. The room temperature emission cross section is 72×10^-20 cm^2 at 926 nm. A discussion of the relation between the spectroscopic properties and crystal field parameters of Cr^3＋：Li2Mg2（MoO4）3 crystal was presented based on the solid state spectroscopytheory.展开更多
文摘YAG： Ce^3 ＋ phosphor particles were prepared using polyacrylamide gel method. The structure evolution of powders during annealing process was followed by X-ray diffraction determination. It is found that some intermediate phases, including θ-Al2O3, YAM and YAP, are formed when calcining polyacrylamide gel, however, the pure YAG phase can be formed directly when calcining polyacrylamide gel with α-Al2O3 as seed crystal. These facts show that the existence of α- Al2O3 seed crystal can block the formation of θ-Al2O3, YAM and YAP, and accelerate its reaction with Y2O3 to form YAG phase directly at lower temperature. The emission peak of prepared YAG ： Ce^3 ＋ phosphor is wide with maximum at 550 nm and the exitation band has two peaks, the major one is around at 460 nm, which matches the blue emission of GaN LED and is suitable for the assemble of white LED. Some fluxes can enhance the photoluminescence intensity of phosphor particles, that can be attributed both to the improvement of crystallization processes of YAG and to the stabilization of trivalence cerium ion in YAG：Ce^3 ＋.
文摘The passively Q-switched and mode-locked（QML） characteristics in a diode-pumped Nd∶GdVO4 laser with Cr4+∶YAG saturable absorbers have been demonstrated. A maximum average output power of 710mW has been obtained in the QML laser. The maximum energy of a single Q-switched pulse is 52.5μJ, with the corresponding pulse width of 30ns and the peak power of 1.75kW, at the incident pump power of 7.75W. The repetition rates of the Q-switched envelope and the mode-locked laser pulse are 16.7kHz and 680MHz, respectively.
基金supported by the National Natural Science Foundation of China(Nos.61308085 and 61475158)
文摘This paper reported the crystal growth and spectroscopy characters of Cr^3＋：Li2Mg2（MoO4）3. The refractive index of Cr^3＋：Li2Mg2（MoO4）3 crystal is 1.87 and the hardness is 270 I-IV. This crystal shows broadband absorption property with peak wavelength at about 495 and 699 nm. The absorption crosssection is 14.75 × 10^-20 cm^2 at 495 nm and 9.63 ×10^-20 cm^2 at 699 nm, respectively. The crystal field strength and energy levels of Cr^3＋ ion were calculated based on the spectroscopic data. The Cr^3＋：Li2Mg2（MoO4）3 crystal shows broadband emission extending from 750 to 1300 nm even excited at 10 K. The room temperature emission cross section is 72×10^-20 cm^2 at 926 nm. A discussion of the relation between the spectroscopic properties and crystal field parameters of Cr^3＋：Li2Mg2（MoO4）3 crystal was presented based on the solid state spectroscopytheory.
基金National Natural Science Foundation of China(51872286,51832007)Fujian Science&Technology Innovation Laboratory for Optoelectronic Information of China(2021ZR204)+1 种基金Science and Technology Plan Leading Project of Fujian Province(2022H0043,2020H0036)Natural Science Foundation of Jiangxi Province(20181BAB211009)。