Single crystal Dy3＋ doped YNbO4phosphors were prepared via a high-temperature high-pressure hydrothermal procedure. Under excitation at 270 nm, the Dy3＋-doped YNbO4 phosphor shows bright white emission, which is com...Single crystal Dy3＋ doped YNbO4phosphors were prepared via a high-temperature high-pressure hydrothermal procedure. Under excitation at 270 nm, the Dy3＋-doped YNbO4 phosphor shows bright white emission, which is composed of two strong bands at 492 and 576 nm corresponding to the characteristic 4F9/2→6H15/2 and aF9/2→6H13/2 transitions of Dy3＋, respectively. The dominant band was observed at 352 nm, which corresponds to the 6H15/2→6p7/2 transition of Dy3＋. Nearly white light was achieved at 2ex 270, 310 and 388 nm and the CIE（International Commission on Illumination） values were （0.3135, 0.3421）, （0.3088, 0.3380） and （0.3146, 0.3296）, respectively.展开更多
Eu3＋-doped （Y,Gd）NbO4 phosphor was synthesized by solid-state reaction for possible application in cold cathode fluorescent lamps. A broad absorption band with peak maximum at 272 nm was observed which was due to t...Eu3＋-doped （Y,Gd）NbO4 phosphor was synthesized by solid-state reaction for possible application in cold cathode fluorescent lamps. A broad absorption band with peak maximum at 272 nm was observed which was due to the charge transfer between Eu3＋ ions and neighboring oxygen anions. A deep red emission at the peak wavelength of 612 nm was observed which could be attributed to the 5D0→7F2 transition in Eu3＋ ions. The highest luminance for Y1-x-yGdyNbO4：Eux3＋ under 254 nm excitation was achieved at Eu3＋ concentration of 18 mol.% （x=0.18） and Gd3＋ concentration of 8.2 mol.% （y=0.082）. The luminance of Y0.738Gd0.082NbO4：Eu3＋0.18 was higher than that of a typical commercial phosphor Y2O3：Eu3＋ and the CIE chromaticity coordinate was （0.6490, 0.3506）, which was deeper than that of Y2O3：Eu3＋. The particle size of the synthesized phosphors was controlled by the NaCl flux and particle size as high as 8 μm with uniform size distribution of particles was obtained.展开更多
基金the National Natural Science Foundation of China
文摘Single crystal Dy3＋ doped YNbO4phosphors were prepared via a high-temperature high-pressure hydrothermal procedure. Under excitation at 270 nm, the Dy3＋-doped YNbO4 phosphor shows bright white emission, which is composed of two strong bands at 492 and 576 nm corresponding to the characteristic 4F9/2→6H15/2 and aF9/2→6H13/2 transitions of Dy3＋, respectively. The dominant band was observed at 352 nm, which corresponds to the 6H15/2→6p7/2 transition of Dy3＋. Nearly white light was achieved at 2ex 270, 310 and 388 nm and the CIE（International Commission on Illumination） values were （0.3135, 0.3421）, （0.3088, 0.3380） and （0.3146, 0.3296）, respectively.
基金supported by the Chung-Ang University Research Scholarship Grants in 2008 (Sung Hwan Choi)
文摘Eu3＋-doped （Y,Gd）NbO4 phosphor was synthesized by solid-state reaction for possible application in cold cathode fluorescent lamps. A broad absorption band with peak maximum at 272 nm was observed which was due to the charge transfer between Eu3＋ ions and neighboring oxygen anions. A deep red emission at the peak wavelength of 612 nm was observed which could be attributed to the 5D0→7F2 transition in Eu3＋ ions. The highest luminance for Y1-x-yGdyNbO4：Eux3＋ under 254 nm excitation was achieved at Eu3＋ concentration of 18 mol.% （x=0.18） and Gd3＋ concentration of 8.2 mol.% （y=0.082）. The luminance of Y0.738Gd0.082NbO4：Eu3＋0.18 was higher than that of a typical commercial phosphor Y2O3：Eu3＋ and the CIE chromaticity coordinate was （0.6490, 0.3506）, which was deeper than that of Y2O3：Eu3＋. The particle size of the synthesized phosphors was controlled by the NaCl flux and particle size as high as 8 μm with uniform size distribution of particles was obtained.