A novel micro fused-casting(MFC)process is developed for semisolid aluminum alloy slurry.The microstructure evolution and properties of semisolid ZL101 aluminum alloy slurry with difierent pouring temperature by MFC a...A novel micro fused-casting(MFC)process is developed for semisolid aluminum alloy slurry.The microstructure evolution and properties of semisolid ZL101 aluminum alloy slurry with difierent pouring temperature by MFC are investigated in this paper.During the cooling process,the effects of the pouring temperature on microstructure and properties is primarily analyzed.The microstructure of the semisolid ZL101 aluminum alloy is more homogeneous and the grain is smaller under proper pouring temperature.Temperature of liquids and solids of ZL101 aluminum alloy is measured by difierential scanning calorimetry(DSC).Distribution and characteristics of the microstructure of samples are examined by optical microscope(OM),scanning electron microscopy(SEM)equipped with energy dispersive spectrometer(EDS).The results show that the ZL101 semisolid slurry fabricated by MFC presents uniform shape and good grain size under the pouring temperature of 594°C and the stirring velocity of 600 r/min,and the fine grains of the primary a-Al phase with average grain size of 55μm and shape factor up to 0.67 were obtained.Besides,the ultimate tensile strength and the average Vickers hardness for semisolid ZL101 aluminum slurry are 178.19±1.37 MPa and 86.15±1.16 HV,respectively.展开更多
基金Funded by the National Natural Science Foundation of China(No.51341009)。
文摘A novel micro fused-casting(MFC)process is developed for semisolid aluminum alloy slurry.The microstructure evolution and properties of semisolid ZL101 aluminum alloy slurry with difierent pouring temperature by MFC are investigated in this paper.During the cooling process,the effects of the pouring temperature on microstructure and properties is primarily analyzed.The microstructure of the semisolid ZL101 aluminum alloy is more homogeneous and the grain is smaller under proper pouring temperature.Temperature of liquids and solids of ZL101 aluminum alloy is measured by difierential scanning calorimetry(DSC).Distribution and characteristics of the microstructure of samples are examined by optical microscope(OM),scanning electron microscopy(SEM)equipped with energy dispersive spectrometer(EDS).The results show that the ZL101 semisolid slurry fabricated by MFC presents uniform shape and good grain size under the pouring temperature of 594°C and the stirring velocity of 600 r/min,and the fine grains of the primary a-Al phase with average grain size of 55μm and shape factor up to 0.67 were obtained.Besides,the ultimate tensile strength and the average Vickers hardness for semisolid ZL101 aluminum slurry are 178.19±1.37 MPa and 86.15±1.16 HV,respectively.