The warm-hot deformation behavior of CF53 steel was studied with hot compression tests at temperature of 1 123 ~1 273 K and strain rate of 0.1~20 s -1 . The activation energy for warm-hot deformation is 274.816 kJ/mol...The warm-hot deformation behavior of CF53 steel was studied with hot compression tests at temperature of 1 123 ~1 273 K and strain rate of 0.1~20 s -1 . The activation energy for warm-hot deformation is 274.816 kJ/mol. The influences of Zener-Hollomon parameter, strain and grain size imposing on the flow stress were analyzed in the temperature range of warm-hot forging. Based on the creep theory and mathematic theory of statistics, mathematical models of flow stress were obtained. The results provide a scientific basis for controlling microstructure of forging process through Zener-Hollomon parameter.展开更多
High-temperature compressive deformation behaviors of Mg–6Zn–1.5Y–0.5Ce–0.4Zr alloy were investigated at temperatures and strain rates ranging from 523 to 673 K and from 0.001 to 1 s~(-1),respectively.The studied ...High-temperature compressive deformation behaviors of Mg–6Zn–1.5Y–0.5Ce–0.4Zr alloy were investigated at temperatures and strain rates ranging from 523 to 673 K and from 0.001 to 1 s~(-1),respectively.The studied alloy was mainly composed ofα-Mg,Mg_(3)Zn_(6)Y(I phase),Mg–Zn–Ce and Mg_(3)Zn_(3)Y_(2)(W phase).The constitutive equation of Mg alloy was obtained,and the apparent activation energy(Q)was determined as 200.44 k J/mol,indicating that rare earth phase increases the difficulty of deformation.The work hardening involves three stages:(1)linear hardening stage;(2)strain hardening stage;and(3)softening and steady-state stage.During these three stages,the dislocation aggregation and tangling,dynamic recovery and recrystallization occur sequentially.To characterize the dynamic recrystallization(DRX)volume fraction,the DRX kinetics was investigated using the Avrami-type equation.The deformation mechanism of magnesium alloy under different Zener–Hollomon parameter(Z)value conditions was also studied.At high Z values and intermediate conditions,dislocations rapidly generate and pile up in the alloy.Recrystallization is hardly seen at this time.At low Z condition,the DRX occurs in the alloy.展开更多
基金The Automobile Industry Science and Tech-nology Development Fund (No3040)
文摘The warm-hot deformation behavior of CF53 steel was studied with hot compression tests at temperature of 1 123 ~1 273 K and strain rate of 0.1~20 s -1 . The activation energy for warm-hot deformation is 274.816 kJ/mol. The influences of Zener-Hollomon parameter, strain and grain size imposing on the flow stress were analyzed in the temperature range of warm-hot forging. Based on the creep theory and mathematic theory of statistics, mathematical models of flow stress were obtained. The results provide a scientific basis for controlling microstructure of forging process through Zener-Hollomon parameter.
基金financially supported by the National Key R&D Program of China(2016YFB0301100)the Natural Science Foundation of Chongqing,China(cstc2019jcyj-msxmX0505)the support of the“111 Project”(B16007)by the Ministry of Education and Fundamental Research Fund of Central Universities in China(Grant No.2018CDJDCL0019)。
文摘High-temperature compressive deformation behaviors of Mg–6Zn–1.5Y–0.5Ce–0.4Zr alloy were investigated at temperatures and strain rates ranging from 523 to 673 K and from 0.001 to 1 s~(-1),respectively.The studied alloy was mainly composed ofα-Mg,Mg_(3)Zn_(6)Y(I phase),Mg–Zn–Ce and Mg_(3)Zn_(3)Y_(2)(W phase).The constitutive equation of Mg alloy was obtained,and the apparent activation energy(Q)was determined as 200.44 k J/mol,indicating that rare earth phase increases the difficulty of deformation.The work hardening involves three stages:(1)linear hardening stage;(2)strain hardening stage;and(3)softening and steady-state stage.During these three stages,the dislocation aggregation and tangling,dynamic recovery and recrystallization occur sequentially.To characterize the dynamic recrystallization(DRX)volume fraction,the DRX kinetics was investigated using the Avrami-type equation.The deformation mechanism of magnesium alloy under different Zener–Hollomon parameter(Z)value conditions was also studied.At high Z values and intermediate conditions,dislocations rapidly generate and pile up in the alloy.Recrystallization is hardly seen at this time.At low Z condition,the DRX occurs in the alloy.