Electrochemical corrosion behavior of arc sprayed Al-Zn-Si-RE coatings on mild steel in 3.5% NaCl solution

Al-Zn-Si-RE coating with high Al content was deposited on mild steel by arc spraying. The electrochemical behavior of Al-Zn-Si-RE coating in 3.5%NaCl solution was systematically studied by potentiodynamic polarization, corrosion potential (φcor ) and electrochemical impedance spectroscopy techniques (EIS). The impedance data were fitted to appropriate equivalent circuits to explain the different electrochemical processes occurring at the electrode-electrolyte interface. The results indicate that Al-Zn-Si-RE coating reveals the similar polarization behavior as Zn-15Al coating. The coating has no passive region in the anodic polarization, but far lower corrosion current and much higher corrosion potential. Al-Zn-Si-RE coating provides effective sacrificial protection for steel substrate and the sacrificial anodic protection plays dominant role during the immersion process. In addition, theφcor evolution and EIS plots indicate that the corrosion process can be divided into five stages: pitting-dissolution-redeposition, activation corrosion, cathodic protection, physical barriers and the coating failure.

Microstructures and Key Properties of Mechanically Deposited Zn-Al Coatings

Zn-Al coatings can provide protection to exposed steel parts in most environments. For this reason, the investigation of Zn-Al coatings become very popular in recent years. In order to study the microstructures and properties of mechanically deposited Zn-Al coating, zinc powders and aluminum powders were used to deposit Zn-AI coating by mechanical plating. The microstruetures, phase constitutes and compositions of the coating were observed and analyzed with optical microscopy （OM）, scanning electron microscopy（SEM）, X-ray diffraction（XRD） and X-ray energy-dispersive spectroscopy（EDS）. The results of observation show that the coating consists of almost spherically shaped zinc particles point contacting with each other; the coatings are composed of zinc particles, aluminum particles, interstice, and tin; extra fine zinc powders and some smaller interspersed inclusions are positioned in the interstices. Porosity and thickness of the coating were tested by ferroxyl test and magnetic method. The corrosion resistance of coatings was studied by neutral salt spraying test（NSS）, immersion test and electrochemical polarization. It is found that the thickness of the coating dose lacks uniformity, with an uneven thickness distribution and an average variation of approximately 2-5gm; the coating can afford cathodic protection to the steel substrate; the corrosion resistance of Zn-Al coatings is better than that of the mechanically plated zinc coatings with same thickness. These conclusions can be applied to improve anti-corrosion performance by mechanically deposit Zn-Al coatings.

Surface Modification With Zinc and Zn-Ni Alloy Compositionally Modulated Multilayer Coatings

Zinc and Zn-Ni alloy compositionally modulated multilayer （CMM） coatings were electrodeposited on to a steel substrate by the successive deposition of zinc and Zn-Ni alloy sublayers from dual baths. The coated samples were evaluated in terms of the surface appearance, surface and cross-sectional morphologies, as well as corrosion resistance. The microstructural characteristics that were examined using the field emission gun scanning electron microscopy （FEGSEM） confirmed the layered structure, grain refinement of the zinc and Zn-Ni alloy CMM coatings, and revealed the existence of microcracks caused by the internal stress in the thick Zn-Ni alloy sublayers. The corrosion resistance that was evaluated by means of the salt spray test shows that the zinc and Zn-Ni alloy CMM coatings were more corrosion-resistant than the monolithic coatings of zinc or Zn-Ni alloy of the same thickness. The possible reasons for the better protective performance of Zn-Ni/Zn CMM coatings were given on the basis of the analysis on the micrographic features of zinc and Zn-Ni alloy CMM eoatings after the corrosion test. A probable corrosion mechanism of zinc and Zn-Ni alloy CMM coatings was also proposed.

Developing high photocatalytic antibacterial Zn electrodeposited coatings through Schottky junction with Fe3+-doped alkalized g-C_(3)N_(4) photocatalysts

Pure Zn coatings easily lose their protective performance after biofouling because they have no antibacterial effect under visible light.In this study,we fabricate a new antibacterial Zn composite coating using electrodeposition to couple Fe3+-doped alkalized g-C_(3)N_(4)(AKCN-Fe)into an existing Zn coating and show that the AKCN-Fe enhances antibacterial property of the Zn coating under visible light.We attribute this enhancement to the high photocatalytic performance,high loading content,and good dispersion of AKCN-Fe.In addition,the photocatalytic antibacterial mechanism of the composite coating is supported by scavenger experiments and electron paramagnetic resonance(EPR)measurements,suggesting that superoxide(·O_(2)^(-))and hydroxyl radical(·OH)play main and secondary roles,respectively.

Effects of rare earth metal addition on microstructure of hot-dip 55%Al-Zn-Si coatings

Optical microscope(OM),scanning electron microscope(SEM),energy dispersive spectrometer (EDS) and X-ray Diffraction(XRD) were used to study the effects of rare earth on the microstructural characteristics of 55%Al-Zn-1.6%Si hot -dip coatings on steel.The results of OM,SEM and EDS showed that by adding RE into the 55%Al-Zn-1.6%Si bath,the saw-toothed shape of intermetallic reaction layer of coating became smooth,and the thickness of the overlay and intermetallic reaction layer decreased.The XRD results revealed that the intermetallic reaction layer was comprised of two different regions,a bright phase closest to the steel substrate with phases of Fe_2Al_3 and a dark phase closest to the metallic coating with phases of FeAl_3/α-Fe-Al-Si.

Corrosion-erosion resistance of Zn-Al co-cementation coatings on carbon steels in aqueous media

A novel Zn Al co cementation coating was obtained by a pack cementation method. This coating possesses a two layered structure. The outer layer is mainly composed of Fe 2Al 5 and FeAl intermetallics with a small amount of Zn, and the inner layer consists of Zn, Fe and a small amount of Al. The corrosion erosion resistance of Zn Al co cementation coatings on carbon steel was studied by a rotary corrosion method in various NaCl and H 2S containing solutions and relevant SiO 2 containing media. The experimental results are compared with those of carbon steels and the sherardizing and aluminizing coatings, showing that the Zn Al co cementation coatings have excellent corrosion erosion resistance in various aqueous media.

Corrosion behaviors of zinc and Zn-Ni alloy compositionally modulated multilayer coatings

Zinc and Zn-Ni alloy compositionally modulated multilayer （CMM） coatings were electrodeposited from dual baths. The coated samples were evaluated in terms of surface appearance, surface and cross-sectional morphologies, as well as corrosion resistance. The results obtained from the salt spray test show that the zinc and Zn-Ni alloy CMM coatings are more corrosion-resistant than the monolithic coatings of zinc or Zn-Ni alloy alone with a similar thickness. The corrosion potential measurement and anodic polarisation tests were undertaken to examine the probable corrosion mechanisms of zinc and Zn-Ni alloy CMM coatings. Analysis on the micrographic features of zinc and Zn-Ni alloy CMM coatings after the corrosion test explains the probable reasons why the Zn-Ni/Zn CMM coatings have a better protective performance. Surface morphologies and compositional analysis of the remaining coating material of Zn-Ni alloy deposit after the corrosion test confirms the dezincification mechanism of the Zn-Ni alloy deposit during the corrosion process.

Effect of Pb content on the surface topography and corrosion resistance of hot dip Zn-Al-Mg coatings

In this study,the effect of Pb content on the surface morphology and salt spray corrosion resistance of hot dip Zn-AI-Mg coatings was investigated. The results showed that the coating surface easily formed small grains of zinc spangle structures and that the salt spray con＇osion resistance of the coating decreased when Pb content was greater than 0.01%. The microstructure and energy dispersive spectrum analysis of surface and cross-sectional areas was performed by scanning electron microscopy. Pb content present in the coating was analyzed by glow discharge spectrum. The results showed that the distribution of Pb in the coating was not uniform. The Pb content was segregated on the surface and at the cross-section of the Zn-A1-MgZn2 ternary eutectic structure,especially,on the surface of the Zn-A1-MgZn2 ternary eutectic structure.

Influence of pyrolytic carbon coatings on complex permittivity and microwave absorbing properties of Al_2O_3 fiber woven fabrics

The pyrolytic carbon （PyC） coatings were fabricated on A1203 fiber fabrics by the method of chemical vapor deposition （CVD）. The microstructures of A1203 fibers with and without PyC coatings were characterized by SEM and Raman spectroscopy. The influence of deposition time of PyC on the DC conductivity （ad） of A1203 filaments and complex permittivity of fabrics at X band （8.2-12.4 GHz） were investigated. The values of Crd and complex permittivity increase with increasing deposition time of PyC. The electron relaxation polarization and conductance loss were supposed to be contributed to the increase of ε＇ and ε＂, respectively. In addition, the reflection loss （RL） of fabrics was calculated. The results show that the microwave absorbing properties of Al2O3 fiber fabrics can be improved by PyC coatings. The best RL results are for 60 min-deposition sample, of which the minimum value is about -40.4 dB at about 9.5 GHz and the absorbing frequency band （AFB） is about 4 GHz.

Interface characteristics of Al_2O_3－13%TiO_2 ceramic coatings prepared by laser cladding

Al2O3-13%TiO2 （mass fraction） coatings, prepared by laser cladding on nickel-based alloy, were heated using high frequency induction sources. The coating microstructure and the interface between bond coating and ceramic coating were characterized by SEM, XRD and EDS. The results show that two-layer substructure exists in the ceramic coating： one layer evolving from fully melted region where the sintered grains grow fully; another layer resembling the liquid-phase-sintered structure consisting of three-dimensional net where the melted Al2O3 particles are embedded in the TiO2-rich matrix. The mechanism of the two-layer substructure formation is also explained in terms of the melting and flattening behavior of the powders during laser cladding processing. The spinel compounds NiAl2O4 and acicular compounds Cr2O3 are discovered in the interface between bond coating and ceramic coating. It proves that the chemical reactions in the laser cladding process will significantly enhance the coating adhesion.

电弧喷涂Zn-Al伪合金涂层耐腐蚀性能研究进展

通过在钢基体表面制备涂层可以很好地延长钢铁材料的服役时间,减少因腐蚀造成的重大事故和人员伤亡。相较于传统的纯Zn涂层、纯Al涂层以及Zn-Al合金涂层,Zn-Al伪合金涂层能够为基体材料提供长久有效的腐蚀防护,在钢铁材料的腐蚀防护中具有巨大的应用潜力。简述了Zn-Al伪合金涂层电弧喷涂制备工艺的特点;介绍了Zn、Al、Zn-Al合金及Zn-Al伪合金涂层在模拟海洋环境下的腐蚀防护原理;在此基础上从组分、喷涂工艺参数(喷涂距离、喷涂电流和喷涂电压)、元素掺杂(Mg、Si及Re)及后处理工艺(封孔、激光重熔)等角度,论述了其对Zn-Al伪合金涂层耐蚀性的影响;讨论了Zn-Al伪合金涂层防腐体系在桥梁、海洋钢结构件、地下运输管道中的应用现状;最后总结了目前研究工作中存在的挑战,提出了电弧喷涂Zn-Al伪合金涂层尚需深入研究的重点问题,为提高钢铁材料使用寿命提供了参考。

通过不同热挤压方式制备具有较优强塑性组合的新型Mg-5Sn-2Al-1Zn合金

制备新型Mg-5Sn-2Al-1Zn(TAZ521)合金。为提高合金的强度与塑性,采用正挤压(DE)和挤压-剪切(ES)两种工艺对该合金进行变形处理。通过XRD、SEM、TEM、EBSD和拉伸试验等方法研究均匀态和挤压态合金的显微组织演变、织构演变及强化机制。结果表明,正挤压态合金的力学性能得到改善;然而,合金表现出由粗晶和细小动态再结晶(DRXed)晶粒组成的双峰组织。经过挤压-剪切变形后的合金组织变得更加均匀,并且实现更好的强韧性结合,变形后合金的屈服强度(YS)、极限抗拉强度(UTS)和伸长率(EL)分别达到212 MPa、303 MPa和21.7%。晶粒细化和Mg2Sn析出物的钉扎效应对强度的提高起到重要作用,此外,延展性的提高归因于基面纤维织构的弱化和非基面滑移系的激活。

Preparation of Al_2O_3/Au nano-laminated composite coatings and their oxidation resistance on stainless steel

Al2O3/Au nano-laminated composite coatings were prepared by means of magnetron sputtering. The coating was compact and comprised of nano-laminated Al2O3 and Au layers. High temperature cyclic oxidation test was employed to investigate the oxidation resistance of the composite coatings. The results revealed that the applied Al2O3/Au nano-laminated composite coatings improved the oxidation and spallation resistance of the stainless steel substrate significantly. The mechanism accounting for oxidation resistance was related with the suppression of inward oxygen diffusion and selective oxidation of Cr in the substrate. The mechanism accounting for spallation resistance was attributed to the relaxation of thermal stress by the nano-laminated structure.

基于冷喷涂工艺的Mg-Zn-Al-Sn-Mn合金防腐Al涂层制备

采用冷喷涂技术在Mg-Zn-Al-Sn-Mn合金表面制备Al涂层,以提高其耐腐蚀性能。研究工作气体温度和压力对Al涂层显微组织和腐蚀行为的影响。结果表明,随着气体温度和压力的升高,Al涂层的致密度和厚度均明显增加。高的气体温度能降低颗粒沉积的临界速度,并提高沉积效率。高的气体压力不仅提升机械结合质量,而且对沉积的涂层具有较强的夯实作用。由于孔隙的减少,Al涂层的耐蚀性随着气体温度和压力的升高而提高。Al(OH)_(3)和Al_(2)O_(3)等腐蚀产物可以堵塞涂层中的孔隙,并作为阻碍腐蚀的物理屏障,从而有效保护Mg合金免受腐蚀。

高强Al-Zn-Mg-Cu合金静态再结晶模型及组织演变

采用Gleeble 3800热模拟试验机对航空用Al-Zn-Mg-Cu合金的热变形行为进行了测试,对变形后的微观组织进行了表征,系统分析了静态软化行为,建立了静态再结晶动力学模型。结果表明:实验用航空Al-Zn-Mg-Cu合金的静态再结晶激活能为129162 J·mol^(-1),静态再结晶体积分数受变形温度、变形程度、变形速率的影响,且变形温度对静态再结晶影响最明显;变形速率一定时,变形温度越高,道次停留时间的影响越不明显;350℃低温变形后,α-Al基体晶粒内部仍存在大量的位错缠结;400℃中温变形后,位错运动能够充分进行,部分晶粒发生了再结晶;450℃高温变形后,基体晶粒基本全部完成了再结晶,基体晶粒内部发现5~25 nm尺寸范围的Al-Zn-Mg-Cu四元相粒子;对于不同热变形条件,模型预测值的误差在0.008~0.0625范围内,动力学模型的计算结果精确度较高。

国产Zn-5%Al-混合稀土合金镀层高钒封闭索丝耐久性研究

以国家速滑馆首次应用的国产Zn-5%Al-混合稀土合金镀层高钒封闭索丝为研究对象,对其使用性能、基本特性及耐久性等进行研究。采用了国家速滑馆内部高空索体实际服役环境处的大气暴露试验方式,综合考虑索在加工安装过程中易产生的损伤,对索丝试件进行了划痕、刮擦、焊点的预制缺陷设计,研究了含预制缺陷的国产Zn-5%Al-稀土合金镀层高钒封闭索丝在真实使用环境中的大气腐蚀行为规律,并采用力学性能测试研究了索丝在服役环境大气腐蚀作用下的力学性能变化规律及不同缺陷对力学性能的影响。结果表明,加工安装过程中在索丝表面合金镀层产生的划痕、刮擦、焊点等损伤,会破坏合金镀层的完整性。大气暴露试验和力学性能试验中,三类缺陷对索丝金属镀层防大气腐蚀性能和单丝抗拉强度均有负面影响,其中焊点缺陷影响最大,单丝抗拉强度下降约40%。

基于机器学习的Al-Zn-Mg-Cu合金快速设计

提出一种基于机器学习的合金快速设计系统(ARDS),以定制所需性能的合金制备策略或预测制备策略所对应的合金性能。为此,分别对3种回归算法:线性回归(LR)、支持向量回归(SVR)和人工神经网络(BPNN)进行建模和比较以训练多性能预测模型。其中,应用SVR构建的机器学习模型被证明是最佳的。然后,基于生成对抗网络(GAN)模型原理,构建Al-Zn-Mg-Cu系铝合金快速设计系统(ARDS)。对ARDS的预测可靠性进行验证。结果表明,为了能够获得准确的制备策略,系统中极限抗拉强度(UTS)、屈服强度(YS)和伸长率(EL)的输入上限分别约为790 MPa、730 MPa和28%。此外,基于ARDS预测结果,制备了一种性能优异的新型铝合金材料,其UTS为764 MPa、YS为732 MPa、EL为10.1%,进一步验证了ARDS的可靠性。

锌镁比对Al-Zn-Mg-Cu-Er-Sc-Zr合金显微组织与耐腐蚀性能影响的研究

通过调整Al-Zn-Mg-Cu-Er-Sc-Zr合金中的Mg元素含量,研究了Zn/Mg比的变化对合金相演变以及腐蚀性能的影响规律。结果表明:Al_(8)Cu_(4)Er相、Al_(3)(Er,Sc)相与含Fe相存在明显的伴生关系,二者依附于含Fe相生长。Zn/Mg比的变化可显著改变三者间的交互形式,高的Zn/Mg比例有利于稀土相独立生长,且在比值为4.18的条件下,Al_(8)Cu_(4)Er相与含Fe相均得到了显著细化。细化的晶界第二相使腐蚀坑深度仅为82μm,而连续的伴生混合相、粗大稀土相等均会不同程度降低合金的耐蚀性能。

烧结NdFeB磁体表面Zn-Al/T8超疏水复合涂层的显微组织及耐蚀性

为提升烧结NdFeB磁体的耐蚀性,采用旋涂法和等离子体增强化学气相沉积技术在其表面制备Zn-Al/T8(2-全氟辛基乙基丙烯酸酯)超疏水复合涂层。结果表明,Zn-Al涂层主要由片层状的Zn和Al相组成,厚度大约为28μm。Zn-Al/T8复合涂层的接触角达到151.78°,而滚动角仅为5.13°,说明Zn-Al/T8复合涂层可提供一个超疏水表面。Zn-Al涂层和Zn-Al/T8复合涂层对烧结NdFeB的磁性能均无显著影响。Zn-Al涂层通过牺牲阳极来提高NdFeB磁体的耐蚀性,而Zn-Al/T8复合涂层通过超疏水表面进一步提升耐蚀性。Zn-Al/T8复合涂层较Zn-Al涂层具有更好的耐盐雾性能。Zn-Al/T8超疏水复合涂层是一种非常有前途的烧结NdFeB磁体保护涂层。

Mg-Al-Zn合金激光填丝焊接接头的显微组织与力学性能

采用激光填丝焊方法对4 mm厚的Mg-Al-Zn系镁合金进行焊接,采用金相显微镜、扫描电镜、透射电镜和X射线衍射仪对接头的微观组织进行分析,并对接头的拉伸性能和显微硬度进行测试。结果表明,接头焊缝区主要由α-Mg基体相和β-Mg17Al_(12)强化相组成。与母材区相比,接头热影响区的硬度有所降低,与该区域的晶粒粗化有关。在激光功率3.0 kW,焊接速度1.5 m/min,送丝速度2.1 m/min的工艺条件下获得的接头,焊缝成形良好,其抗拉强度为315 MPa,与母材的抗拉强度接近。接头拉伸断口上分布着一定数量的韧窝和河流花样,总体呈韧-脆混合型断裂特征。