The effect of the parameters on the open-circuit voltage, V_(OC) of a-Si:H/c-Si heterojunction solar cells was explored by an analytical model. The analytical results show that V_(OC) increases linearly with the logar...The effect of the parameters on the open-circuit voltage, V_(OC) of a-Si:H/c-Si heterojunction solar cells was explored by an analytical model. The analytical results show that V_(OC) increases linearly with the logarithm of illumination intensity under usual illumination. There are two critical values of the interface state density(D_(it)) for the open-circuit voltage(V_(OC)), D_(it)^(crit,1) and D_(it)crit,2(a few 1010 cm^(-2)·e V^(-1)). V_(OC) decreases remarkably when D_(it) is higher than D_(it)^(crit,1). To achieve high V_(OC), the interface states should reduce down to a few 1010 cm^(-2)·e V^(-1). Due to the difference between the effective density of states in the conduction and valence band edges of c-Si, the open-circuit voltage of a-Si:H/c-Si heterojunction cells fabricated on n-type c-Si wafers is about 22 mV higher than that fabricated on p-type c-Si wafers at the same case. V_(OC) decreases with decreasing the a-Si:H doping concentration at low doping level since the electric field over the c-Si depletion region is reduced at low doping level. Therefore, the a-Si:H layer should be doped higher than a critical value of 5×10^(18) cm^(-3) to achieve high V_(OC).展开更多
This paper reports that a double N layer （a-Si：H/μc-Si：H） is used to substitute the single microcrystalline silicon n layer （n-μc-Si：H） in n/p tunnel recombination junction between subcells in a-Si：H/μc-Si...This paper reports that a double N layer （a-Si：H/μc-Si：H） is used to substitute the single microcrystalline silicon n layer （n-μc-Si：H） in n/p tunnel recombination junction between subcells in a-Si：H/μc-Si：H tandem solar cells. The electrical transport and optical properties of these tunnel recombination junctions are investigated by current voltage measurement and transmission measurement. The new n/p tunnel recombination junction shows a better ohmic contact. In addition, the n/p interface is exposed to the air to examine the effect of oxidation on the tunnel recombination junction performance. The open circuit voltage and FF of a-Si：H/μc-Si：H tandem solar cell are all improved and the current leakage of the subcells can be effectively prevented efficiently when the new n/p junction is implemented as tunnel recombination junction.展开更多
The intrinsic a-Si：H passivation layer inserted between the doped a-Si：H layer and the c-Si substrate is very crucial for improving the performance of the a-Si：H/c- Si heterojunction （SHJ） solar cell. The passiva...The intrinsic a-Si：H passivation layer inserted between the doped a-Si：H layer and the c-Si substrate is very crucial for improving the performance of the a-Si：H/c- Si heterojunction （SHJ） solar cell. The passivation performance of the a-Si：H layer is strongly dependent on its microstructure. Usually, the compact a-Si：H deposited near the transition from the amorphous phase to the nanocrystalline phase by plasma enhanced chemical vapor deposition （PECVD） can provide excellent passivation. However, at the low deposition pressure and low deposition power, such an a-Si：H layer can be only prepared in a narrow region. The deposition condition must be controlled very carefully. In this paper, intrinsic a- Si：H layers were prepared on n-type Cz c-Si substrates by 27.12 MHz PECVD at a high deposition pressure and high deposition power. The corresponding passivation perfor- mance on c-Si was investigated by minority carrier lifetime measurement. It was found that an excellent a-Si：H passivation layer could be obtained in a very wide deposition pressure and power region. Such wide process window would be very beneficial for improving the uniformity and the yield for the solar cell fabrication. The a-Si：H layer microstructure was further investigated by Raman and Fourier transform infrared （FTIR） spectro-scopy characterization. The correlation between the microstructure and the passivation performance was revealed. According to the above findings, the a-Si：H passivation performance was optimized more elaborately. Finally, a large-area SHJ solar cell with an efficiency of 22.25% was fabricated on the commercial 156 mm pseudo-square n-type Cz c-Si substrate with the opencircuit voltage （Voc） of up to 0.732 V.展开更多
In order to obtain higher conversion efficiency and to reduce production cost for hydrogenated amorphous silicon/crystalline silicon(a-Si:H/c-Si) based heterojunction solar cells, an a-Si:H/c-Si heterojunction with lo...In order to obtain higher conversion efficiency and to reduce production cost for hydrogenated amorphous silicon/crystalline silicon(a-Si:H/c-Si) based heterojunction solar cells, an a-Si:H/c-Si heterojunction with localized p–n structure(HACL) is designed. A numerical simulation is performed with the ATLAS program. The effect of the a-Si:H layer on the performance of the HIT(heterojunction with intrinsic thin film) solar cell is investigated. The performance improvement mechanism for the HACL cell is explored. The potential performance of the HACL solar cell is compared with those of the HIT and HACD(heterojunction of amorphous silicon and crystalline silicon with diffused junction) solar cells.The simulated results indicate that the a-Si:H layer can bring about much absorption loss. The conversion efficiency and the short-circuit current density of the HACL cell can reach 28.18% and 43.06 m A/cm^2, respectively, and are higher than those of the HIT and HACD solar cells. The great improvement are attributed to(1) decrease of optical absorption loss of a-Si:H and(2) decrease of photocarrier recombination for the HACL cell. The double-side local junction is very suitable for the bifacial solar cells. For an HACL cell with n-type or p-type c-Si base, all n-type or p-type c-Si passivating layers are feasible for convenience of the double-side diffusion process. Moreover, the HACL structure can reduce the consumption of rare materials since the transparent conductive oxide(TCO) can be free in this structure. It is concluded that the HACL solar cell is a promising structure for high efficiency and low cost.展开更多
Silicon thin-film solar cells are considered to be one of the most promising cells in the future for their potential advantages, such as low cost, high efficiency, great stability, simple processing, and none-pollutio...Silicon thin-film solar cells are considered to be one of the most promising cells in the future for their potential advantages, such as low cost, high efficiency, great stability, simple processing, and none-pollution. In this paper, latest progress on poly-crystalline silicon solar cells on ceramic substrates achieved by our group was reported. Rapid thermal chemical vapor deposition (RTCVD) was used to deposited poly-crystalline silicon thin films, and the grains of as-grown film were enlarged by Zone-melting Recrystallization (ZMR). As a great change in cell′s structure, traditional diffused pn homojunction was replaced by a-Si/c-Si heterojunction, which lead is to distinct improvement in cell′s efficiency. A conversion efficiency of 3.42% has been achieved on 1 cm2 a-Si/c-Si heterojunction solar cell (Isc=16.93 mA, Voc=310.9 mV, FF=0.6493, AM=1.5 G, 24 ℃), while the cell with diffused homojunction only got an efficiency of 0.6%. It indicates that a-Si emitter formed at low temperature might be more suitable for thin film cell on ceramics.展开更多
基金Project(11374094)supported by the National Natural Science Foundation of ChinaProject(2013HZX23)supported by Natural Science Foundation of Hunan University of Technology,ChinaProject(2015JJ3060)supported by Natural Science Foundation of Hunan Province of China
文摘The effect of the parameters on the open-circuit voltage, V_(OC) of a-Si:H/c-Si heterojunction solar cells was explored by an analytical model. The analytical results show that V_(OC) increases linearly with the logarithm of illumination intensity under usual illumination. There are two critical values of the interface state density(D_(it)) for the open-circuit voltage(V_(OC)), D_(it)^(crit,1) and D_(it)crit,2(a few 1010 cm^(-2)·e V^(-1)). V_(OC) decreases remarkably when D_(it) is higher than D_(it)^(crit,1). To achieve high V_(OC), the interface states should reduce down to a few 1010 cm^(-2)·e V^(-1). Due to the difference between the effective density of states in the conduction and valence band edges of c-Si, the open-circuit voltage of a-Si:H/c-Si heterojunction cells fabricated on n-type c-Si wafers is about 22 mV higher than that fabricated on p-type c-Si wafers at the same case. V_(OC) decreases with decreasing the a-Si:H doping concentration at low doping level since the electric field over the c-Si depletion region is reduced at low doping level. Therefore, the a-Si:H layer should be doped higher than a critical value of 5×10^(18) cm^(-3) to achieve high V_(OC).
基金Project supported by the State Key Development Program for Basic Research of China (Grant Nos 2006CB202602 and2006CB202603)the National Natural Science Foundation of China (Grant No 60506003)
文摘This paper reports that a double N layer （a-Si：H/μc-Si：H） is used to substitute the single microcrystalline silicon n layer （n-μc-Si：H） in n/p tunnel recombination junction between subcells in a-Si：H/μc-Si：H tandem solar cells. The electrical transport and optical properties of these tunnel recombination junctions are investigated by current voltage measurement and transmission measurement. The new n/p tunnel recombination junction shows a better ohmic contact. In addition, the n/p interface is exposed to the air to examine the effect of oxidation on the tunnel recombination junction performance. The open circuit voltage and FF of a-Si：H/μc-Si：H tandem solar cell are all improved and the current leakage of the subcells can be effectively prevented efficiently when the new n/p junction is implemented as tunnel recombination junction.
基金Acknowledgements This work was supported by the National High Technology Research and Development Program of China （863 Program） （Grant No. 2011AA050502） and the National Natural Science Foundation of China （Grant No. 61274061）.
文摘The intrinsic a-Si：H passivation layer inserted between the doped a-Si：H layer and the c-Si substrate is very crucial for improving the performance of the a-Si：H/c- Si heterojunction （SHJ） solar cell. The passivation performance of the a-Si：H layer is strongly dependent on its microstructure. Usually, the compact a-Si：H deposited near the transition from the amorphous phase to the nanocrystalline phase by plasma enhanced chemical vapor deposition （PECVD） can provide excellent passivation. However, at the low deposition pressure and low deposition power, such an a-Si：H layer can be only prepared in a narrow region. The deposition condition must be controlled very carefully. In this paper, intrinsic a- Si：H layers were prepared on n-type Cz c-Si substrates by 27.12 MHz PECVD at a high deposition pressure and high deposition power. The corresponding passivation perfor- mance on c-Si was investigated by minority carrier lifetime measurement. It was found that an excellent a-Si：H passivation layer could be obtained in a very wide deposition pressure and power region. Such wide process window would be very beneficial for improving the uniformity and the yield for the solar cell fabrication. The a-Si：H layer microstructure was further investigated by Raman and Fourier transform infrared （FTIR） spectro-scopy characterization. The correlation between the microstructure and the passivation performance was revealed. According to the above findings, the a-Si：H passivation performance was optimized more elaborately. Finally, a large-area SHJ solar cell with an efficiency of 22.25% was fabricated on the commercial 156 mm pseudo-square n-type Cz c-Si substrate with the opencircuit voltage （Voc） of up to 0.732 V.
基金Project supported by the National Key R&D Program of China(Grant No.2018YFB1500403)the National Natural Science Foundation of China(Grant Nos.11964018,61741404,and 61464007)the Natural Science Foundation of Jiangxi Province of China(Grant No.20181BAB202027)
文摘In order to obtain higher conversion efficiency and to reduce production cost for hydrogenated amorphous silicon/crystalline silicon(a-Si:H/c-Si) based heterojunction solar cells, an a-Si:H/c-Si heterojunction with localized p–n structure(HACL) is designed. A numerical simulation is performed with the ATLAS program. The effect of the a-Si:H layer on the performance of the HIT(heterojunction with intrinsic thin film) solar cell is investigated. The performance improvement mechanism for the HACL cell is explored. The potential performance of the HACL solar cell is compared with those of the HIT and HACD(heterojunction of amorphous silicon and crystalline silicon with diffused junction) solar cells.The simulated results indicate that the a-Si:H layer can bring about much absorption loss. The conversion efficiency and the short-circuit current density of the HACL cell can reach 28.18% and 43.06 m A/cm^2, respectively, and are higher than those of the HIT and HACD solar cells. The great improvement are attributed to(1) decrease of optical absorption loss of a-Si:H and(2) decrease of photocarrier recombination for the HACL cell. The double-side local junction is very suitable for the bifacial solar cells. For an HACL cell with n-type or p-type c-Si base, all n-type or p-type c-Si passivating layers are feasible for convenience of the double-side diffusion process. Moreover, the HACL structure can reduce the consumption of rare materials since the transparent conductive oxide(TCO) can be free in this structure. It is concluded that the HACL solar cell is a promising structure for high efficiency and low cost.
文摘Silicon thin-film solar cells are considered to be one of the most promising cells in the future for their potential advantages, such as low cost, high efficiency, great stability, simple processing, and none-pollution. In this paper, latest progress on poly-crystalline silicon solar cells on ceramic substrates achieved by our group was reported. Rapid thermal chemical vapor deposition (RTCVD) was used to deposited poly-crystalline silicon thin films, and the grains of as-grown film were enlarged by Zone-melting Recrystallization (ZMR). As a great change in cell′s structure, traditional diffused pn homojunction was replaced by a-Si/c-Si heterojunction, which lead is to distinct improvement in cell′s efficiency. A conversion efficiency of 3.42% has been achieved on 1 cm2 a-Si/c-Si heterojunction solar cell (Isc=16.93 mA, Voc=310.9 mV, FF=0.6493, AM=1.5 G, 24 ℃), while the cell with diffused homojunction only got an efficiency of 0.6%. It indicates that a-Si emitter formed at low temperature might be more suitable for thin film cell on ceramics.