The effect of processing parameters such as hot rolling and heat treatment on microstructure and mechanical properties was investigated for a new 0.27mass% C and Ni, Mo-free low alloy martensitic abrasion resistant st...The effect of processing parameters such as hot rolling and heat treatment on microstructure and mechanical properties was investigated for a new 0.27mass% C and Ni, Mo-free low alloy martensitic abrasion resistant steel. The three-body impact abrasive wear behavior was also analyzed. The results showed that two-step controlled rolling besides quenching at 880 ℃ and tempering at 170 ℃ could result in optimal mechanical property., the Brinell hardness, tensile strength, elongation and --40 ℃ impact toughness were 531, 1530 MPa, 11.8% and 58 J, re- spectively. The microstructure was of fine lath martensite with little retained austenite. Three-body impact abrasive wear results showed that wear mechanism was mainly of plastic deformation fatigue when the impact energy was 2 J, and the relative wear resistance was 1.04 times higher than that of the same grade compared steel under the same working condition. The optimal hardness and toughness match was the main reason of higher wear resistance.展开更多
High strength abrasion resistant steel plates are widely used in mining,construction and agricultural machineries.The plates are,however,usually poor in impact toughness.An attempt is made to improve the impact toughn...High strength abrasion resistant steel plates are widely used in mining,construction and agricultural machineries.The plates are,however,usually poor in impact toughness.An attempt is made to improve the impact toughness of HB400 grade abrasion resistant steel by controlling quenching and tempering of the plates.Optimized combination of the strength and the toughness has been achieved by choosing best fit set of quenching and tempering condition.Mechanism underlying the achievement has been investigated in terms of the microstructure consisting of tempered lath martensite,retained austenite and precipitated carbides.展开更多
基金Item Sponsored by National Basic Research Program of China(2010CB630801)
文摘The effect of processing parameters such as hot rolling and heat treatment on microstructure and mechanical properties was investigated for a new 0.27mass% C and Ni, Mo-free low alloy martensitic abrasion resistant steel. The three-body impact abrasive wear behavior was also analyzed. The results showed that two-step controlled rolling besides quenching at 880 ℃ and tempering at 170 ℃ could result in optimal mechanical property., the Brinell hardness, tensile strength, elongation and --40 ℃ impact toughness were 531, 1530 MPa, 11.8% and 58 J, re- spectively. The microstructure was of fine lath martensite with little retained austenite. Three-body impact abrasive wear results showed that wear mechanism was mainly of plastic deformation fatigue when the impact energy was 2 J, and the relative wear resistance was 1.04 times higher than that of the same grade compared steel under the same working condition. The optimal hardness and toughness match was the main reason of higher wear resistance.
文摘High strength abrasion resistant steel plates are widely used in mining,construction and agricultural machineries.The plates are,however,usually poor in impact toughness.An attempt is made to improve the impact toughness of HB400 grade abrasion resistant steel by controlling quenching and tempering of the plates.Optimized combination of the strength and the toughness has been achieved by choosing best fit set of quenching and tempering condition.Mechanism underlying the achievement has been investigated in terms of the microstructure consisting of tempered lath martensite,retained austenite and precipitated carbides.