To develop the microwave absorbing(MA)properties of cementitious material mixed with mine solid waste,the iron tailings cementitious microwave absorbing materials were prepared.The iron tailings was treated into diffe...To develop the microwave absorbing(MA)properties of cementitious material mixed with mine solid waste,the iron tailings cementitious microwave absorbing materials were prepared.The iron tailings was treated into different particle sizes by planetary ball mill,and the physicochemical properties of iron tailings were tested by laser particle size analyzer and scanning electron microscope(SEM).The electromagnetic parameters of iron tailings cementitious materials were characterized by a vector network analyzer and simulated MA properties,and the MA properties of iron tailings-cement composite system with steel fiber as absorber was studied.Based on the design of the single-layer structure,optimum mix ratio and thickness configuration method of double-layer structure were further studied,meanwhile,the mechanical properties and engineering application were analyzed and discussed.The results show that the particle size of iron tailings can afiect its electromagnetic behavior in cementitious materials,and the smaller particles lead the increase of demagnetisation efiect induced by domain wall motion and achieve better microwave absorbing properties in cementitious materials.When the thickness of matching layer and absorbing layer is 5 mm,the optimized microwave absorbing properties of C1/C3 double-layer cementitious material can obtain optimal RL value of-27.61 dB and efiective absorbing bandwidth of 0.97 GHz,which attributes to the synergistic efiect of impedance matching and attenuation characteristics.The double-layer microwave absorbing materials obtain excellent absorbing properties and show great design flexibility and diversity,which can be used as a suitable candidate for the preparation of favorable microwave absorbing cementitious materials.展开更多
Electronic devices have become ubiquitous in our daily lives,leading to a surge in the use of microwave absorbers and wearable sensor devices across various sectors.A prime example of this trend is the aramid nanofibe...Electronic devices have become ubiquitous in our daily lives,leading to a surge in the use of microwave absorbers and wearable sensor devices across various sectors.A prime example of this trend is the aramid nanofibers/polypyrrole/nickel(APN)aerogels,which serve dual roles as both microwave absorbers and pressure sensors.In this work,we focused on the preparation of aramid nanofibers/polypyrrole(AP15)aerogels,where the mass ratio of aramid nanofibers to pyrrole was 1:5.We employed the oxidative polymerization method for the preparation process.Following this,nickel was thermally evaporated onto the surface of the AP15 aerogels,resulting in the creation of an ultralight(9.35 mg·cm^(-3)).This aerogel exhibited a porous structure.The introduction of nickel into the aerogel aimed to enhance magnetic loss and adjust impedance matching,thereby improving electromagnetic wave absorption performance.The minimum reflection loss value achieved was-48.7 dB,and the maximum effective absorption bandwidth spanned 8.42 GHz with a thickness of 2.9 mm.These impressive metrics can be attributed to the three-dimensional network porous structure of the aerogel and perfect impedance matching.Moreover,the use of aramid nanofibers and a three-dimensional hole structure endowed the APN aerogels with good insulation,flame-retardant properties,and compression resilience.Even under a compression strain of 50%,the aerogel maintained its resilience over 500 cycles.The incorporation of polypyrrole and nickel particles further enhanced the conductivity of the aerogel.Consequently,the final APN aerogel sensor demonstrated high sensitivity(10.78 kPa-1)and thermal stability.In conclusion,the APN aerogels hold significant promise as ultra-broadband microwave absorbers and pressure sensors.展开更多
The electromagnetic and microwave absorbing properties of FeCoB powder composites prepared by sin- gle-roller melt-spinning and mechanical milling processes were investigated in this paper. The result indicates that t...The electromagnetic and microwave absorbing properties of FeCoB powder composites prepared by sin- gle-roller melt-spinning and mechanical milling processes were investigated in this paper. The result indicates that the flake-like powders are obtained. As milling time increases, the flake-like powder particles tend to agglomerate, causing the flake-like powders decrease gradually. The milling time plays an important role in the electromagnetic parameters which relates to the shape and size of the powder particles. The calculation shows that the sample milled for 6 h could achieve an optimal reflection loss of -11.5 dB at 5.8 GHz, with mass fraction of 83 % and a matching thickness of 1.8 mm. The result also indicates that the microwave absorbing properties of the FeCoB powder composites are adjustable by changing their thickness, and can be applied as a thinner microwave absorbing material in the range of 2-8 GHz.展开更多
The effects of types and amounts of silane coupling agent on mechanical properties of vuleanized rubber microwave absorbing patch (VRMAP) were studied. The mechanisms of silane coupling agent's effects on mechanica...The effects of types and amounts of silane coupling agent on mechanical properties of vuleanized rubber microwave absorbing patch (VRMAP) were studied. The mechanisms of silane coupling agent's effects on mechanical properties of rubber microwave absorbing patch ( RMAP ) and microvave absorbing patch's (MAP's) mierostrueture were also discussed by using SEM and FT-IR. The experimental results show that the tensile strength of RMAP could be increased through adding the filler of carbonyl iron powder (CIP) modified by silane coupling agent. RMAP fiUed with CIP, which was treated by silane coupling agent KH550, possessed a high tensile strength of 11.5 MPa, which was 448% more than that of MAP whose filler wus not modified by any coupling agent. It was found that the optimal amount of KH550 was 1.0 phr to 100.0 phr carbonyl iron powder. The effects of different modifying techniques on RMAP's mechanical properties were also inrestigated. It is indieated that MAP whose filler is modified by the wet process has the highest tensile strength, but it is not the optimal modiifying technique due to complieated wet process. On the contrary, the dry process was very simple, and VRMAP possessed fairly high mechanical properties, therefore, it was the perfect modifying process.展开更多
REI3Fes4Cr3(RE=Ce, Pr, Tb, Er) and Pr13_XFes4Cr3Ti(x=0, 2, 4, 6) alloy powders were prepared by are smelting method and high energy ball milling technique. The phase structure and the morphology of the alloy powde...REI3Fes4Cr3(RE=Ce, Pr, Tb, Er) and Pr13_XFes4Cr3Ti(x=0, 2, 4, 6) alloy powders were prepared by are smelting method and high energy ball milling technique. The phase structure and the morphology of the alloy powders were investigated by X-ray diffraction (XRD) and scanning electron microscopy (SEM), and their microwave absorbing properties were determined by a vector network analyzer. The results show that the alloys with light rare earths (Ce, Pr) have good low frequency absorbing property and those with heavy rare earths (Tb, Er) exhibit an improved high frequency absorbing property. The minimum refleetivity at the absorbing peak frequency of RE,FeuCr3(RE=Ce, Pr, Tb, Er) are -9.49 dB at 5.76 GHz, -22.38 dB at 7.92 GHz, -18.52 dB at 11.68 GHz and -17.59 dB at 10.24 GHz, respectively. The absorbing bandwidth under -10 dB of the Pr13FesaCr3 powder was widened from 1.91 GI-Iz to 3.89 GHz by adding 2% Ti, but the reflectivity of the alloy was increased from -22.38 dB to -14.91 riB.展开更多
Magnesium-substituted Mn0.8Zn0.2Fe2O4 ferrite is synthesized by the sol–gel combustion method using citrate acid as the complex agent. The electromagnetic absorbing behaviors of ferrite/polymer coatings fabricated by...Magnesium-substituted Mn0.8Zn0.2Fe2O4 ferrite is synthesized by the sol–gel combustion method using citrate acid as the complex agent. The electromagnetic absorbing behaviors of ferrite/polymer coatings fabricated by dispersing Mn–Zn ferrite into epoxy resin (EP) are studied. The microstructure and morphology are characterized by X-ray diffraction and scanning electron microscope. Complex permittivity, complex permeability, and reflection loss of ferrite/EP composite coating are investigated in a low frequency range. It is found that the prepared ferrite particles are traditional cubic spinel ferrite particles with an average size of 200 nm. The results reveal that the electromagnetic microwave absorbing properties are significantly influenced by the weight ratio of ferrite to polymer. The composites with a weight ratio of ferrite/polymer being 3:20 have a maximum reflection loss of –16 dB and wide absorbing band. Thus, the Mn–Zn ferrite is the potential candidate in electromagnetic absorbing application in the low frequency range (10 MHz–1 GHz).展开更多
A microwave absorbing sheet with a high complex permeability and a relatively low complex permittivity is obtained by molding of the densely coated flaky carbonyl iron particles(FCIPs)by styrenebutadiene-styrene block...A microwave absorbing sheet with a high complex permeability and a relatively low complex permittivity is obtained by molding of the densely coated flaky carbonyl iron particles(FCIPs)by styrenebutadiene-styrene block copolymer(SBS)in the assistance of coupling agent modification.Direct molding of the core-shell FCIPs without adding extra binder results in a large permeability due to the high filling ratio(55vol%)of absorbents.Importantly,the permittivity is well suppressed by the dense insulate polymer shell on the FCIPs,avoiding the severe impedance mismatch problem of the high filler content microwave absorbing materials.Investigations show that modifying the surface of FCIPs by proper amount of silane coupling agent is critical for the coating quality of the SBS shell,which is verified by resistivity and corrosion current density measurements,and can be interpreted by improved interfacial compatibility between the modified FCIPs and SBS.The obtained microwave absorbing sheet shows a minimum reflection loss of-38.74 dB at 1.57 GHz and has an effective absorption bandwidth from 1.1 to 2.3 GHz at a relatively small thickness of 2 mm.展开更多
In this paper,Fe-Al solid solution was prepared by mechanical alloying technology,and Fe-Al powder was dispersed into unsaturated polyester (UP) with different contents as absorber to form mixture Fe-Al-UP.The result...In this paper,Fe-Al solid solution was prepared by mechanical alloying technology,and Fe-Al powder was dispersed into unsaturated polyester (UP) with different contents as absorber to form mixture Fe-Al-UP.The results indicate that the alloying process is almost accomplished and most of the particles are nanometer.Meanwhile,the microwave absorbability of Fe-Al-UP samples in frequency from 0.3 MHz to 1.5 GHz was studied.The results indicate that the more the absorber,the better the absorbing property.The absorbing property of Fe-50Al-UP was slightly higher than Fe-28Al-UP.展开更多
The experiment samples of La1-xSrxMn1-y FeyO3(x = 0. 15, 0.20, 0.23; y = 0. 10, 0. 12, 0.14, 0.16) were prepared by sol-gel process, and the loss tangent and absorption coefficient in the range of 2 - 18 GHz were me...The experiment samples of La1-xSrxMn1-y FeyO3(x = 0. 15, 0.20, 0.23; y = 0. 10, 0. 12, 0.14, 0.16) were prepared by sol-gel process, and the loss tangent and absorption coefficient in the range of 2 - 18 GHz were measured by HP8722 net analyzing apparatus. It is found that changing the content of Sr or Fe would effect the microwave absorbing. When the thickness of La1-x SrxMn1-y FeyO3 is 2 mm and x =0.20, y = 0.14, the capability of microwave absorbing is the best one. There are two absorption peaks; the maximum is 34 dB and effective band width with 10 dB and more reaches 6.2 GHz.展开更多
The microwave absorbing behaviour of Mn-Zn ferrite sintered at 1100,1200,1300,1400 and 1500℃ has been investigated.The phase constitution of the ferrite was analyzed by X-ray diffraction.The results show that the fer...The microwave absorbing behaviour of Mn-Zn ferrite sintered at 1100,1200,1300,1400 and 1500℃ has been investigated.The phase constitution of the ferrite was analyzed by X-ray diffraction.The results show that the ferrite sintered at 1 500℃ has better microwave absorbing prop- erty than those prepared at other temperatures,due to the increase of turbulent loss generated by the formation of excessive Fe^(2+) in deoxidizing of Fe_2O_3 at high temperatures.展开更多
As a heat-resistant wave-absorbing material,silicon carbide(SiC)aerogel has become a research hotspot at present.However,the most common silicon sources are organosilanes,which are costly and toxic.In this work,SiC ae...As a heat-resistant wave-absorbing material,silicon carbide(SiC)aerogel has become a research hotspot at present.However,the most common silicon sources are organosilanes,which are costly and toxic.In this work,SiC aerogels were successfully prepared by using water glass as the silicon source.Specifically,the microstructure and chemical composition of SiC aerogels were controlled by adjusting the Si to C molar ratio during the sol–gel process,and the effect on SiC aerogel microwave absorption properties was investigated.The SiC aerogels prepared with Si:C molar ratio of 1:1 have an effective electromagnetic wave absorption capacity,with a minimum reflection loss value of-46.30 dB at 12.88 GHz and an effective frequency bandwidth of 4.02 GHz.They also have good physical properties,such as the density of0.0444 g/cm^(3),the thermal conductivity of 0.0621 W/(m·K),and the specific surface area of 1099 m^(2)/g.These lightweight composites with microwave-absorbing properties and low thermal conductivity can be used as thermal protection materials for space shuttles and reusable carriers.展开更多
Transparent microwave absorbers that exhibit high optical transmittance and microwave absorption capability are ideal,although having a fixed absorption performance limits their applicability.Here,a simple,transparent...Transparent microwave absorbers that exhibit high optical transmittance and microwave absorption capability are ideal,although having a fixed absorption performance limits their applicability.Here,a simple,transparent,and thermally tunable microwave absorber is proposed,based on a patterned vanadium dioxide(VO_(2))film.Numerical calculations and experiments demonstrate that the proposed VO_(2)absorber has a high optical transmittance of 84.9%at 620 nm;its reflection loss at 15.06 GHz can be thermally tuned from–4.257 to–60.179 dB,and near-unity absorption is achieved at 523.750 K.Adjusting only the patterned VO_(2)film duty cycle can change the temperature of near-unity absorption.Our VO_(2)absorber has a simple composition,a high optical transmittance,a thermally tunable microwave absorption performance,a large modulation depth,and an adjustable temperature tuning range,making it promising for application in tunable sensors,thermal emitters,modulators,thermal imaging,bolometers,and photovoltaic devices.展开更多
A Y-type hexaferrite rod with the composition of Ba2COl.8Cuo.2Fe12022 was presented as an absorbing material with high absorb- anee. Its high absorbance and wide absorption band result from ferromagnetic resonance (...A Y-type hexaferrite rod with the composition of Ba2COl.8Cuo.2Fe12022 was presented as an absorbing material with high absorb- anee. Its high absorbance and wide absorption band result from ferromagnetic resonance (FMR) that is self-biased by strong shape and mag- netocrystaUine anisotropy fields. Around the FMR frequency the specimen of the ferrite rods exhibits very high absorbance and the FMR frequency can be tuned by the rod dimension. In addition to the high absorbance and the wide tunable absorption band, the microwave ab- sorber has another advantage of light weight due to the use of the ferrite rods instead of ferrite slabs.展开更多
This paper reports that amorphous magnetic microwires (Fe79Si16Bs) have been fabricated by a melt-extraction technique and have been annealed at 600℃ and 750℃ respectively. Differential scanning calorimeter measur...This paper reports that amorphous magnetic microwires (Fe79Si16Bs) have been fabricated by a melt-extraction technique and have been annealed at 600℃ and 750℃ respectively. Differential scanning calorimeter measurements show that nanocrystalline magnetic phase (α-Fe) has been formed in the amorphous matrix when it was annealed at 600℃. Hard magnetic phase (Fe2B) was formed in the microwires annealed at 750℃, which increases the magnetic coercivity. Microwave permittivity and permeability are found to be dependent on the microstruetures. The permittivity fitting results show that multi Lorentzian dispersion processes exist. For microwires annealed at 750℃, their resonance peaks due to the domain wall movements and natural resonance are found higher than those of microwires annealed at 600℃. The microwave absorption performance of microwires annealed at 600℃ is found better than microwires annealed at 750℃.展开更多
Using lignite-based hypercoal as raw material, KOH as activator and CuO as microwave absorber, we prepared hypercoal-based activated carbons by microwave-assisted activation. The pore structure and the electrochemical...Using lignite-based hypercoal as raw material, KOH as activator and CuO as microwave absorber, we prepared hypercoal-based activated carbons by microwave-assisted activation. The pore structure and the electrochemical performance of the activated carbons were tested, and the effects of adding CuO in the activation reaction process were also investigated. The activated carbons prepared were characterized by nitrogen adsorption-desorption, X-ray diffraction (XRD) and scanning electron microscopy (SEM). The specific surface area and mesoporous ratio of the hypercoal-based activated carbon are 1257 m2/g and 55.4%, respectively. When the activated carbons are used as the electrode materials, the specific capacitance reaches 309 F/g in 3 M KOH electrolyte. In comparison with those prepared without CuO absorber, the specific capacitance increases by 11.6%. It was proved that the addition of microwave absorber in microwave-assisted activation was a low-cost method for rapidly preparing activated carbon, and it could effectively promote the development of the pore structure and improve its electrochemical performance.展开更多
Metallic flaky sendust particles are prepared for use as fillers in electromagnetic attenuation composites. We report the interface reflection model to divide the broad bandwidth into electromagnetic loss and quarter-...Metallic flaky sendust particles are prepared for use as fillers in electromagnetic attenuation composites. We report the interface reflection model to divide the broad bandwidth into electromagnetic loss and quarter-wavelength (λ/4) cancelation. Combining with the face reflection calculation, we identify the electromagnetic loss originated from skin effect, which is used to explain over half of the absorbed energy in high frequency band. Most impor- tantly, the unique electromagnetic loss cannot generate the reflection loss (RL) peak. Using the phase relation of face reflection, we show evidence that the λ/4 cancelation is vital to generate the RL peak. The calculated energy loss agrees well with the experimental data and lays the foundation for further research.展开更多
Nanocomposite BaFe12019/a-Fe microfibers with diameters of about 1-5 μm are prepared by the organic gel- thermal selective reduction process. The binary phase of BaFe12019 and a-Fe is formed after reduction of the pr...Nanocomposite BaFe12019/a-Fe microfibers with diameters of about 1-5 μm are prepared by the organic gel- thermal selective reduction process. The binary phase of BaFe12019 and a-Fe is formed after reduction of the precursor BaFel2019/a-Fe203 microfibers at 350 ℃ for 1 h. These nanocomposite microfibers are fabricated from a-Fe (16-22 nm in diameter) and BaFe12019 particles (36--42 nm in diameter) and basically exhibit a single-phase-like magnetization be- havior, with a high saturation magnetization and coercive force arising from the exchange--coupling interactions of soft a-Fe and hard BaFe12019. The microwave absorption characteristics in a 2-18 GHz frequency range of the nanocomposite BaFe12O19/a-Fe microfibers are mainly influenced by their mass ratio of a-Fe/BaFe12019 and specimen thickness. It is found that the nanocomposite BaFelzO19/a-Fe microfibers with a mass ratio of 1:6 and specimen thickness of 2.5 mm show an optimal reflection loss (RL) of -29.7 dB at 13.5 GHz and the bandwidth with RL exceeding -10 dB covers the whole Ku-band (12.4-18.0 GHz). This enhancement of microwave absorption can be attributed to the heterostruc- ture of soft, nano, conducting a-Fe particles embedded in hard, nano, semiconducting barium ferrite, which improves the dipolar polarization, interfacial polarization, exchange--coupling interaction, and anisotropic energy in the nanocomposite BaFe12O19/a-Fe microfibers.展开更多
Microwave absorption properties of the nanocrystalline strontium ferrite (SrFe12O19) and iron (α-Fe) microfibers for single-layer and double-layer structures are investigated in a frequency range of 2 GHz 18 GHz....Microwave absorption properties of the nanocrystalline strontium ferrite (SrFe12O19) and iron (α-Fe) microfibers for single-layer and double-layer structures are investigated in a frequency range of 2 GHz 18 GHz. For the singlelayer absorbers, the nanocrystalline SrFe12O19 microfibers show some microwave absorptions at 6 GHz 18 GHz, with a minimum reflection loss (RL) value of -11.9 dB at 14.1 GHz for a specimen thickness of 3.0 mm, while for the nanocrystalline α-Fe microfibers, their absorptions largely take place at 15 GHz-18 GHz with the RL value exceeding -10 dB, with a minimum .RL value of about -24 dB at 17.5 GHz for a specimen thickness of 0.7 mm. For the doublelayer absorber with an absorbing layer of α-Fe microfibers with a thickness of 0.7 mm and matching layer of SrFe12O19 microfibers with a thickness of 1.3 ram, the minimum RL value is about -63 dB at 16.4 GHz and the absorption band width is about 6.7 GHz ranging from 11.3 GHz to 18 GHz with the RL value exceeding -10 dB which covers the whole Ku-band (12.4 GHz 18 GHz) and 27% of X-band (8.2 GHz 12.4 GHz).展开更多
An Fe-based nanocrystalline alloy powder is important for application in microwave absorption,and the particle size has a critical impact on the electromagnetic microwave parameters.Therefore,it is necessary to study ...An Fe-based nanocrystalline alloy powder is important for application in microwave absorption,and the particle size has a critical impact on the electromagnetic microwave parameters.Therefore,it is necessary to study further the effects of the particle size on such parameters and improve the microwave absorption performance of Febased nanocrystalline powers.In this study,Fe-B-P particles were prepared through a synthetic approach consisting of an aqueous chemical reduction and a ball milling treatment.We investigated the effects of ball milling on the microstructure and electromagnetic properties of Fe-B-P particles.The experimental results indicate that the Fe-B-P particles synthesized through an aqueous chemical reduction are amorphous spheres.Fe-B-P particles with an original particle size of 200-1200 nm can be milled into an irregular shape with the size reduced to\500 nm after 0.5 h of ball milling,and subsequently,the particles become smaller with increases in the milling time,with traces of Fe2O3 generated on the particle surface.The results of the Mo¨ssbauer spectra show that a portion of the small particles demonstrate a superparamagnetic property.The volume proportions of the superparamagnetic component increase from 13.1 to 15.8%as the treatment time increases.We measured the permittivity and permeability spectra of Fe-B-P particles within the frequency range of 2-18 GHz.The reflection loss(RL)is-10 dB for an absorber thickness of 1.7-5.0 mm.The RL is-20 dB for an absorber thickness of 1.9-2.7 mm.The microwave absorption properties of samples with the same thickness are improved with an increase in the treatment time and are shifted to a higher frequency,which will broaden the bandwidth of the absorption as well.展开更多
Synthesis and characterization of lanthanum-doped yttrium iro n garnet(YIG)in the compositional se ries of Y_(3-x)La_(x)Fe_(5)O_(12)(x=0.0,0.1,0.3,and 0.5)were carried out.All compositions were made by using solid sta...Synthesis and characterization of lanthanum-doped yttrium iro n garnet(YIG)in the compositional se ries of Y_(3-x)La_(x)Fe_(5)O_(12)(x=0.0,0.1,0.3,and 0.5)were carried out.All compositions were made by using solid state reaction method with ball-milling technique.The phase formation,surface morphology,magnetic properties,and microwave absorbing ability of all compositions were characterized by using an X-ray diffractometer,a scanning electron microscope,a vibrating sample magnetometer,and a Vector network analyzer.The results reveal that all compositions are crystallized into Y_(3)Fe_(5)O_(12)phase(space group la-3d(230).It was observed that the lattice constant is increased from 1.2373 to 1.2421 nm with the increase of lanthanum substitution level from x=0.0-0.5.The crystallite size of Y_(3-x)La_(x)Fe_(5)O_(12)series calculated by Scherrer method is found to decrease from 78 nm in x=0.0-63 nm in x=0.5.The particle size distribution from the surface morphology image analysis is shifted to lower-range number with the increase of lanthanum substitution level from x=0.0 to 0.5.The substitution process also affects the lattice distortion in La-doped samples and changes the bond angles and bond lengths of the YIG structure.As the results,a linear correlation between the Fe'-O-Fe bond angle with magnetic properties parameters of saturation magnetization(M_(s))and remanence magnetization(M_(r))was studied.Due to the lanthanum substitution process,all La^(3+)-doped samples possess higher M_(s)and M_(r)values compared to the original composition.The results of Vector network analyzer show that the improvement of the M_(s)and M_(r)plays an important role in enhancing the microwave absorbing ability of the materials.The minimum RL changes from-8.22 dB(~85.22%microwave absorption)in x=0.0 to-14.21 dB(~96.25%microwave absorption)in x=0.5.The enhancement is mainly ascribed to the natural magnetic resonance loss and dipoIe-polarization loss due to the substitution process.The decreasing particle size also enhances the microwave absorbing ability of the La-doped samples via multiple-reflections mechanism.展开更多
基金Funded by the Natural Science Foundation of Nanping of China(No.N2021J002)Guangdong Basic and Applied Basic Research Foundation(No.2020A1515110304)+3 种基金Guangzhou Science and Technology Plan(No.202102020224)Natural Science Foundation of Fujian Province(No.2020Y0092)Natural Science Foundation of Fujian Province(No.2023J011044)Resource Chemical Industry and Technology Foundation of Nanping(No.N2020Z003)。
文摘To develop the microwave absorbing(MA)properties of cementitious material mixed with mine solid waste,the iron tailings cementitious microwave absorbing materials were prepared.The iron tailings was treated into different particle sizes by planetary ball mill,and the physicochemical properties of iron tailings were tested by laser particle size analyzer and scanning electron microscope(SEM).The electromagnetic parameters of iron tailings cementitious materials were characterized by a vector network analyzer and simulated MA properties,and the MA properties of iron tailings-cement composite system with steel fiber as absorber was studied.Based on the design of the single-layer structure,optimum mix ratio and thickness configuration method of double-layer structure were further studied,meanwhile,the mechanical properties and engineering application were analyzed and discussed.The results show that the particle size of iron tailings can afiect its electromagnetic behavior in cementitious materials,and the smaller particles lead the increase of demagnetisation efiect induced by domain wall motion and achieve better microwave absorbing properties in cementitious materials.When the thickness of matching layer and absorbing layer is 5 mm,the optimized microwave absorbing properties of C1/C3 double-layer cementitious material can obtain optimal RL value of-27.61 dB and efiective absorbing bandwidth of 0.97 GHz,which attributes to the synergistic efiect of impedance matching and attenuation characteristics.The double-layer microwave absorbing materials obtain excellent absorbing properties and show great design flexibility and diversity,which can be used as a suitable candidate for the preparation of favorable microwave absorbing cementitious materials.
基金The authors acknowledge the financial support from the National Natural Science Foundation of China(Nos.52071280 and 51972280)the Natural Science Foundation of Hebei Province,China(Nos.E2020203151 and E2022203208)+1 种基金the Research Program of the College Science&Technology of Hebei Province,China(No.ZD2020121)the Cultivation Project for Basic Research and Innovation of Yanshan University,China(No.2021LGZD016).
文摘Electronic devices have become ubiquitous in our daily lives,leading to a surge in the use of microwave absorbers and wearable sensor devices across various sectors.A prime example of this trend is the aramid nanofibers/polypyrrole/nickel(APN)aerogels,which serve dual roles as both microwave absorbers and pressure sensors.In this work,we focused on the preparation of aramid nanofibers/polypyrrole(AP15)aerogels,where the mass ratio of aramid nanofibers to pyrrole was 1:5.We employed the oxidative polymerization method for the preparation process.Following this,nickel was thermally evaporated onto the surface of the AP15 aerogels,resulting in the creation of an ultralight(9.35 mg·cm^(-3)).This aerogel exhibited a porous structure.The introduction of nickel into the aerogel aimed to enhance magnetic loss and adjust impedance matching,thereby improving electromagnetic wave absorption performance.The minimum reflection loss value achieved was-48.7 dB,and the maximum effective absorption bandwidth spanned 8.42 GHz with a thickness of 2.9 mm.These impressive metrics can be attributed to the three-dimensional network porous structure of the aerogel and perfect impedance matching.Moreover,the use of aramid nanofibers and a three-dimensional hole structure endowed the APN aerogels with good insulation,flame-retardant properties,and compression resilience.Even under a compression strain of 50%,the aerogel maintained its resilience over 500 cycles.The incorporation of polypyrrole and nickel particles further enhanced the conductivity of the aerogel.Consequently,the final APN aerogel sensor demonstrated high sensitivity(10.78 kPa-1)and thermal stability.In conclusion,the APN aerogels hold significant promise as ultra-broadband microwave absorbers and pressure sensors.
基金financially supported by the National Hi-tech R&D Project Supporting Programs Funded by Ministry of Science&Technology of China(No.2012AA063202)the National Natural Science Foundation of China(Nos.50972013,50802008,and 51004011)+1 种基金the National Key Project of Scientific and Technical Supporting Programs Funded by Ministry of Science&Technology of China(Nos.2012BAC02B01,2012BAC12B05,2011BAE13B07,and 2011BAC10B02)the Guangdong Province&Ministry of Education Industry-Study-Research United Project(No.2009A090100017)
文摘The electromagnetic and microwave absorbing properties of FeCoB powder composites prepared by sin- gle-roller melt-spinning and mechanical milling processes were investigated in this paper. The result indicates that the flake-like powders are obtained. As milling time increases, the flake-like powder particles tend to agglomerate, causing the flake-like powders decrease gradually. The milling time plays an important role in the electromagnetic parameters which relates to the shape and size of the powder particles. The calculation shows that the sample milled for 6 h could achieve an optimal reflection loss of -11.5 dB at 5.8 GHz, with mass fraction of 83 % and a matching thickness of 1.8 mm. The result also indicates that the microwave absorbing properties of the FeCoB powder composites are adjustable by changing their thickness, and can be applied as a thinner microwave absorbing material in the range of 2-8 GHz.
文摘The effects of types and amounts of silane coupling agent on mechanical properties of vuleanized rubber microwave absorbing patch (VRMAP) were studied. The mechanisms of silane coupling agent's effects on mechanical properties of rubber microwave absorbing patch ( RMAP ) and microvave absorbing patch's (MAP's) mierostrueture were also discussed by using SEM and FT-IR. The experimental results show that the tensile strength of RMAP could be increased through adding the filler of carbonyl iron powder (CIP) modified by silane coupling agent. RMAP fiUed with CIP, which was treated by silane coupling agent KH550, possessed a high tensile strength of 11.5 MPa, which was 448% more than that of MAP whose filler wus not modified by any coupling agent. It was found that the optimal amount of KH550 was 1.0 phr to 100.0 phr carbonyl iron powder. The effects of different modifying techniques on RMAP's mechanical properties were also inrestigated. It is indieated that MAP whose filler is modified by the wet process has the highest tensile strength, but it is not the optimal modiifying technique due to complieated wet process. On the contrary, the dry process was very simple, and VRMAP possessed fairly high mechanical properties, therefore, it was the perfect modifying process.
基金Funded by National Natural Science Foundation of China(Nos.50961005 and 51361007)National Natural Science Foundation of Guangxi(Nos.2012 GXNSFGA06002 and 2013GXNSFAA019295)
文摘REI3Fes4Cr3(RE=Ce, Pr, Tb, Er) and Pr13_XFes4Cr3Ti(x=0, 2, 4, 6) alloy powders were prepared by are smelting method and high energy ball milling technique. The phase structure and the morphology of the alloy powders were investigated by X-ray diffraction (XRD) and scanning electron microscopy (SEM), and their microwave absorbing properties were determined by a vector network analyzer. The results show that the alloys with light rare earths (Ce, Pr) have good low frequency absorbing property and those with heavy rare earths (Tb, Er) exhibit an improved high frequency absorbing property. The minimum refleetivity at the absorbing peak frequency of RE,FeuCr3(RE=Ce, Pr, Tb, Er) are -9.49 dB at 5.76 GHz, -22.38 dB at 7.92 GHz, -18.52 dB at 11.68 GHz and -17.59 dB at 10.24 GHz, respectively. The absorbing bandwidth under -10 dB of the Pr13FesaCr3 powder was widened from 1.91 GI-Iz to 3.89 GHz by adding 2% Ti, but the reflectivity of the alloy was increased from -22.38 dB to -14.91 riB.
基金Project supported by the Specialized Research Fund for the Doctoral Program of Higher Education of China(Grant No.20121101110014)
文摘Magnesium-substituted Mn0.8Zn0.2Fe2O4 ferrite is synthesized by the sol–gel combustion method using citrate acid as the complex agent. The electromagnetic absorbing behaviors of ferrite/polymer coatings fabricated by dispersing Mn–Zn ferrite into epoxy resin (EP) are studied. The microstructure and morphology are characterized by X-ray diffraction and scanning electron microscope. Complex permittivity, complex permeability, and reflection loss of ferrite/EP composite coating are investigated in a low frequency range. It is found that the prepared ferrite particles are traditional cubic spinel ferrite particles with an average size of 200 nm. The results reveal that the electromagnetic microwave absorbing properties are significantly influenced by the weight ratio of ferrite to polymer. The composites with a weight ratio of ferrite/polymer being 3:20 have a maximum reflection loss of –16 dB and wide absorbing band. Thus, the Mn–Zn ferrite is the potential candidate in electromagnetic absorbing application in the low frequency range (10 MHz–1 GHz).
基金Funded by the Young Top-notch Talent Cultivation Program of Hubei Provincethe National Natural Science Foundation of China(Nos.52071239,51521001)Fundamental Research Funds for the Central Universities(Nos.WUT:2021IVA116 and WUT:2021CG015)。
文摘A microwave absorbing sheet with a high complex permeability and a relatively low complex permittivity is obtained by molding of the densely coated flaky carbonyl iron particles(FCIPs)by styrenebutadiene-styrene block copolymer(SBS)in the assistance of coupling agent modification.Direct molding of the core-shell FCIPs without adding extra binder results in a large permeability due to the high filling ratio(55vol%)of absorbents.Importantly,the permittivity is well suppressed by the dense insulate polymer shell on the FCIPs,avoiding the severe impedance mismatch problem of the high filler content microwave absorbing materials.Investigations show that modifying the surface of FCIPs by proper amount of silane coupling agent is critical for the coating quality of the SBS shell,which is verified by resistivity and corrosion current density measurements,and can be interpreted by improved interfacial compatibility between the modified FCIPs and SBS.The obtained microwave absorbing sheet shows a minimum reflection loss of-38.74 dB at 1.57 GHz and has an effective absorption bandwidth from 1.1 to 2.3 GHz at a relatively small thickness of 2 mm.
文摘In this paper,Fe-Al solid solution was prepared by mechanical alloying technology,and Fe-Al powder was dispersed into unsaturated polyester (UP) with different contents as absorber to form mixture Fe-Al-UP.The results indicate that the alloying process is almost accomplished and most of the particles are nanometer.Meanwhile,the microwave absorbability of Fe-Al-UP samples in frequency from 0.3 MHz to 1.5 GHz was studied.The results indicate that the more the absorber,the better the absorbing property.The absorbing property of Fe-50Al-UP was slightly higher than Fe-28Al-UP.
文摘The experiment samples of La1-xSrxMn1-y FeyO3(x = 0. 15, 0.20, 0.23; y = 0. 10, 0. 12, 0.14, 0.16) were prepared by sol-gel process, and the loss tangent and absorption coefficient in the range of 2 - 18 GHz were measured by HP8722 net analyzing apparatus. It is found that changing the content of Sr or Fe would effect the microwave absorbing. When the thickness of La1-x SrxMn1-y FeyO3 is 2 mm and x =0.20, y = 0.14, the capability of microwave absorbing is the best one. There are two absorption peaks; the maximum is 34 dB and effective band width with 10 dB and more reaches 6.2 GHz.
文摘The microwave absorbing behaviour of Mn-Zn ferrite sintered at 1100,1200,1300,1400 and 1500℃ has been investigated.The phase constitution of the ferrite was analyzed by X-ray diffraction.The results show that the ferrite sintered at 1 500℃ has better microwave absorbing prop- erty than those prepared at other temperatures,due to the increase of turbulent loss generated by the formation of excessive Fe^(2+) in deoxidizing of Fe_2O_3 at high temperatures.
基金supported by the Program of Applied Basic Research Program of Shanxi Province,China (No.202103021223055)the Shanxi Scholarship Council of Chinathe Key R&D program of Shanxi Province,China (No.202102030201006)。
文摘As a heat-resistant wave-absorbing material,silicon carbide(SiC)aerogel has become a research hotspot at present.However,the most common silicon sources are organosilanes,which are costly and toxic.In this work,SiC aerogels were successfully prepared by using water glass as the silicon source.Specifically,the microstructure and chemical composition of SiC aerogels were controlled by adjusting the Si to C molar ratio during the sol–gel process,and the effect on SiC aerogel microwave absorption properties was investigated.The SiC aerogels prepared with Si:C molar ratio of 1:1 have an effective electromagnetic wave absorption capacity,with a minimum reflection loss value of-46.30 dB at 12.88 GHz and an effective frequency bandwidth of 4.02 GHz.They also have good physical properties,such as the density of0.0444 g/cm^(3),the thermal conductivity of 0.0621 W/(m·K),and the specific surface area of 1099 m^(2)/g.These lightweight composites with microwave-absorbing properties and low thermal conductivity can be used as thermal protection materials for space shuttles and reusable carriers.
基金support from the National Natural Science Foundation of China(61975046)。
文摘Transparent microwave absorbers that exhibit high optical transmittance and microwave absorption capability are ideal,although having a fixed absorption performance limits their applicability.Here,a simple,transparent,and thermally tunable microwave absorber is proposed,based on a patterned vanadium dioxide(VO_(2))film.Numerical calculations and experiments demonstrate that the proposed VO_(2)absorber has a high optical transmittance of 84.9%at 620 nm;its reflection loss at 15.06 GHz can be thermally tuned from–4.257 to–60.179 dB,and near-unity absorption is achieved at 523.750 K.Adjusting only the patterned VO_(2)film duty cycle can change the temperature of near-unity absorption.Our VO_(2)absorber has a simple composition,a high optical transmittance,a thermally tunable microwave absorption performance,a large modulation depth,and an adjustable temperature tuning range,making it promising for application in tunable sensors,thermal emitters,modulators,thermal imaging,bolometers,and photovoltaic devices.
基金supported by the National Natural Science Foundation of China (No.50702005)the Natural Science Foundation of the Education Department of Henan Province,China (No.2010A430012)
文摘A Y-type hexaferrite rod with the composition of Ba2COl.8Cuo.2Fe12022 was presented as an absorbing material with high absorb- anee. Its high absorbance and wide absorption band result from ferromagnetic resonance (FMR) that is self-biased by strong shape and mag- netocrystaUine anisotropy fields. Around the FMR frequency the specimen of the ferrite rods exhibits very high absorbance and the FMR frequency can be tuned by the rod dimension. In addition to the high absorbance and the wide tunable absorption band, the microwave ab- sorber has another advantage of light weight due to the use of the ferrite rods instead of ferrite slabs.
基金supported by the National Natural Science Foundation of China (Grant No 60701016)the Science Foundation for Young Faculties of UESTC (Grant Nos L08010301JX0618 and L08010301JX05013)
文摘This paper reports that amorphous magnetic microwires (Fe79Si16Bs) have been fabricated by a melt-extraction technique and have been annealed at 600℃ and 750℃ respectively. Differential scanning calorimeter measurements show that nanocrystalline magnetic phase (α-Fe) has been formed in the amorphous matrix when it was annealed at 600℃. Hard magnetic phase (Fe2B) was formed in the microwires annealed at 750℃, which increases the magnetic coercivity. Microwave permittivity and permeability are found to be dependent on the microstruetures. The permittivity fitting results show that multi Lorentzian dispersion processes exist. For microwires annealed at 750℃, their resonance peaks due to the domain wall movements and natural resonance are found higher than those of microwires annealed at 600℃. The microwave absorption performance of microwires annealed at 600℃ is found better than microwires annealed at 750℃.
基金Funded by the National Natural Science Foundation of China(No.51874136)Natural Science Foundation of Hebei Province(No.B2017209240)。
文摘Using lignite-based hypercoal as raw material, KOH as activator and CuO as microwave absorber, we prepared hypercoal-based activated carbons by microwave-assisted activation. The pore structure and the electrochemical performance of the activated carbons were tested, and the effects of adding CuO in the activation reaction process were also investigated. The activated carbons prepared were characterized by nitrogen adsorption-desorption, X-ray diffraction (XRD) and scanning electron microscopy (SEM). The specific surface area and mesoporous ratio of the hypercoal-based activated carbon are 1257 m2/g and 55.4%, respectively. When the activated carbons are used as the electrode materials, the specific capacitance reaches 309 F/g in 3 M KOH electrolyte. In comparison with those prepared without CuO absorber, the specific capacitance increases by 11.6%. It was proved that the addition of microwave absorber in microwave-assisted activation was a low-cost method for rapidly preparing activated carbon, and it could effectively promote the development of the pore structure and improve its electrochemical performance.
基金Supported by the Fundamental Research Fund for the Central Universities under Grant No LZUJBKY-2015-121the National Natural Science Foundations of China under Grant Nos 11574122 and 51102124the National Science Foundation for Fostering Talents in Basic Research of the National Natural Science Foundation of China
文摘Metallic flaky sendust particles are prepared for use as fillers in electromagnetic attenuation composites. We report the interface reflection model to divide the broad bandwidth into electromagnetic loss and quarter-wavelength (λ/4) cancelation. Combining with the face reflection calculation, we identify the electromagnetic loss originated from skin effect, which is used to explain over half of the absorbed energy in high frequency band. Most impor- tantly, the unique electromagnetic loss cannot generate the reflection loss (RL) peak. Using the phase relation of face reflection, we show evidence that the λ/4 cancelation is vital to generate the RL peak. The calculated energy loss agrees well with the experimental data and lays the foundation for further research.
基金Project supported by the National Natural Science Foundation of China (Grant Nos. 51274106 and 51202091)the Natural Science Foundation of Higher Education of Jiangsu Province, China (Grant No. 12KJA430001)+2 种基金the Research Fund for the Doctoral Program of Higher Education of China (Grant No. 20103227110006)the Science and Technology Support Program of Jiangsu Province, China (Grant No. BE2012143)the Postgraduate Cultivation and Innovation Project of Jiangsu Province, China (Grant No. CXZZ11 0557)
文摘Nanocomposite BaFe12019/a-Fe microfibers with diameters of about 1-5 μm are prepared by the organic gel- thermal selective reduction process. The binary phase of BaFe12019 and a-Fe is formed after reduction of the precursor BaFel2019/a-Fe203 microfibers at 350 ℃ for 1 h. These nanocomposite microfibers are fabricated from a-Fe (16-22 nm in diameter) and BaFe12019 particles (36--42 nm in diameter) and basically exhibit a single-phase-like magnetization be- havior, with a high saturation magnetization and coercive force arising from the exchange--coupling interactions of soft a-Fe and hard BaFe12019. The microwave absorption characteristics in a 2-18 GHz frequency range of the nanocomposite BaFe12O19/a-Fe microfibers are mainly influenced by their mass ratio of a-Fe/BaFe12019 and specimen thickness. It is found that the nanocomposite BaFelzO19/a-Fe microfibers with a mass ratio of 1:6 and specimen thickness of 2.5 mm show an optimal reflection loss (RL) of -29.7 dB at 13.5 GHz and the bandwidth with RL exceeding -10 dB covers the whole Ku-band (12.4-18.0 GHz). This enhancement of microwave absorption can be attributed to the heterostruc- ture of soft, nano, conducting a-Fe particles embedded in hard, nano, semiconducting barium ferrite, which improves the dipolar polarization, interfacial polarization, exchange--coupling interaction, and anisotropic energy in the nanocomposite BaFe12O19/a-Fe microfibers.
基金supported by the Aviation Science Foundation,China (Grant No.2009ZF52063)the Research Fund for the Doctoral Program of Higher Education of China (Grant No.20103227110006)the Jiangsu Provincial Postgraduate Cultivation and Innovation Project,China (Grant No.CX10B-257Z)
文摘Microwave absorption properties of the nanocrystalline strontium ferrite (SrFe12O19) and iron (α-Fe) microfibers for single-layer and double-layer structures are investigated in a frequency range of 2 GHz 18 GHz. For the singlelayer absorbers, the nanocrystalline SrFe12O19 microfibers show some microwave absorptions at 6 GHz 18 GHz, with a minimum reflection loss (RL) value of -11.9 dB at 14.1 GHz for a specimen thickness of 3.0 mm, while for the nanocrystalline α-Fe microfibers, their absorptions largely take place at 15 GHz-18 GHz with the RL value exceeding -10 dB, with a minimum .RL value of about -24 dB at 17.5 GHz for a specimen thickness of 0.7 mm. For the doublelayer absorber with an absorbing layer of α-Fe microfibers with a thickness of 0.7 mm and matching layer of SrFe12O19 microfibers with a thickness of 1.3 ram, the minimum RL value is about -63 dB at 16.4 GHz and the absorption band width is about 6.7 GHz ranging from 11.3 GHz to 18 GHz with the RL value exceeding -10 dB which covers the whole Ku-band (12.4 GHz 18 GHz) and 27% of X-band (8.2 GHz 12.4 GHz).
基金supported by the National Natural Science Foundation of China (Nos. 51401049, U1704253)Natural Science Foundation of Zhejiang Province (No. LR18E010001)Key Research and Development Program of Zhejiang Province (No. 2019C01121)
文摘An Fe-based nanocrystalline alloy powder is important for application in microwave absorption,and the particle size has a critical impact on the electromagnetic microwave parameters.Therefore,it is necessary to study further the effects of the particle size on such parameters and improve the microwave absorption performance of Febased nanocrystalline powers.In this study,Fe-B-P particles were prepared through a synthetic approach consisting of an aqueous chemical reduction and a ball milling treatment.We investigated the effects of ball milling on the microstructure and electromagnetic properties of Fe-B-P particles.The experimental results indicate that the Fe-B-P particles synthesized through an aqueous chemical reduction are amorphous spheres.Fe-B-P particles with an original particle size of 200-1200 nm can be milled into an irregular shape with the size reduced to\500 nm after 0.5 h of ball milling,and subsequently,the particles become smaller with increases in the milling time,with traces of Fe2O3 generated on the particle surface.The results of the Mo¨ssbauer spectra show that a portion of the small particles demonstrate a superparamagnetic property.The volume proportions of the superparamagnetic component increase from 13.1 to 15.8%as the treatment time increases.We measured the permittivity and permeability spectra of Fe-B-P particles within the frequency range of 2-18 GHz.The reflection loss(RL)is-10 dB for an absorber thickness of 1.7-5.0 mm.The RL is-20 dB for an absorber thickness of 1.9-2.7 mm.The microwave absorption properties of samples with the same thickness are improved with an increase in the treatment time and are shifted to a higher frequency,which will broaden the bandwidth of the absorption as well.
基金Project supported by the Ministry of Finance Indonesia for the research grant through the competitive research program of RISPRO Kompetisi(PRJ-45/LPDP/2020)。
文摘Synthesis and characterization of lanthanum-doped yttrium iro n garnet(YIG)in the compositional se ries of Y_(3-x)La_(x)Fe_(5)O_(12)(x=0.0,0.1,0.3,and 0.5)were carried out.All compositions were made by using solid state reaction method with ball-milling technique.The phase formation,surface morphology,magnetic properties,and microwave absorbing ability of all compositions were characterized by using an X-ray diffractometer,a scanning electron microscope,a vibrating sample magnetometer,and a Vector network analyzer.The results reveal that all compositions are crystallized into Y_(3)Fe_(5)O_(12)phase(space group la-3d(230).It was observed that the lattice constant is increased from 1.2373 to 1.2421 nm with the increase of lanthanum substitution level from x=0.0-0.5.The crystallite size of Y_(3-x)La_(x)Fe_(5)O_(12)series calculated by Scherrer method is found to decrease from 78 nm in x=0.0-63 nm in x=0.5.The particle size distribution from the surface morphology image analysis is shifted to lower-range number with the increase of lanthanum substitution level from x=0.0 to 0.5.The substitution process also affects the lattice distortion in La-doped samples and changes the bond angles and bond lengths of the YIG structure.As the results,a linear correlation between the Fe'-O-Fe bond angle with magnetic properties parameters of saturation magnetization(M_(s))and remanence magnetization(M_(r))was studied.Due to the lanthanum substitution process,all La^(3+)-doped samples possess higher M_(s)and M_(r)values compared to the original composition.The results of Vector network analyzer show that the improvement of the M_(s)and M_(r)plays an important role in enhancing the microwave absorbing ability of the materials.The minimum RL changes from-8.22 dB(~85.22%microwave absorption)in x=0.0 to-14.21 dB(~96.25%microwave absorption)in x=0.5.The enhancement is mainly ascribed to the natural magnetic resonance loss and dipoIe-polarization loss due to the substitution process.The decreasing particle size also enhances the microwave absorbing ability of the La-doped samples via multiple-reflections mechanism.