A novel technology which combined electrochemical process catalyzed by manganese mineral with electro-assisted coagulation process was proposed in this study. The mineralization of organic pollutant from simulated dye...A novel technology which combined electrochemical process catalyzed by manganese mineral with electro-assisted coagulation process was proposed in this study. The mineralization of organic pollutant from simulated dye wastewater containing an azo dye Acid Red B（ARB） was experimentally investigated using this method. It was found that the manganese mineral could catalyze the electrochemical process dramatically. The TOC removal percentage of electrochemical treatment catalyzed by manganese mineral was 43.6% while the TOC removal percentage of the process using the manganese mineral alone and using the electrolysis alone were 9.3% and 20.8%, respectively. Moreover, it was found that combined electroxidation with electro-assisted coagulation process could more effectively eliminate ARB. After a period of 180 min electrooxidation and 300 min electroreduction, almost 66.9% of TOC was removed, and the dissolved Mn^2＋. could be effectivly removed. The effects of the order of oxidation and reduction, the proper ratio electrooxidation/reduction time, and current density on the removal efficiency were investigated in detail. In addition, a proposed mechanism of manganese-mineral-catalyzed electrooxidation-reduction process was discussed in this paper.展开更多
Boron- and cerium-codoped TiO2 photocatalysts were synthesized using modified sol-gel reaction process and characterized by X- ray diffraction （XRD）, X-ray photoelectron spectroscopy （XPS）, particle size distribut...Boron- and cerium-codoped TiO2 photocatalysts were synthesized using modified sol-gel reaction process and characterized by X- ray diffraction （XRD）, X-ray photoelectron spectroscopy （XPS）, particle size distribution （PSD）, diffuse reflectance spectra （DRS）, and Brunauer-Emmett-Teller （BET）. The photocatalytic activities were evaluated by monitoring the degradation of dye Acid Red B （ARB）. The results showed that the prepared photocatalysts were mixed oxides mainly consisting of titania, ceria, and boron oxide. The structure of TiO2 could be transformed from amorphous to anatase and then to rutile by increasing calcination temperature; the transformation being accompanied by the growth of particle size without any obvious change in phase structure of CeO2. The XPS of B1.6Ce1.0-TiO2 prepared at 500℃ showed that a few boron atoms were incorporated into titania and ceria lattice, whereas others existed as B2O3. Cerium ions existed in two states, Ce^3＋ and Ce^4＋, and the atomic ratio of Ce^3＋/Ce^4＋ was 1.86. When boron and cerium were doped, the UV-Vis adsorption band wavelength showed an obvious shift toward the visible range （〈526 nm）. As the atomic ratio of Ce/Ti increased to 1.0, the absorbance edge wavelength increased to 481 nm. The absorbance edge wavelength decreased for higher cerium doping levels （Ce/Ti=2.0）. The particles size ranged from 122 to 255 nm with a domain at 168 nm （39.4%）. The degradation of ARB dye indicated that the photocatalytic activities of boron- and cerium-codoped TiO2 were much higher than those of P25 （a standard TiO2 powder）. The activities increased as the boron doping increased, whereas decreased when the Ce/Ti atomic ratio was greater than 0.5. The optimum atomic ratio of B/Ti and Ce/Ti was 1.6 and 0.5, respectively.展开更多
Pervoskite-type oxides LaFe_ 1-yCu_yO_3 was prepared by citrate method. Using a fluorescent Hg lamp as irradiator, the degradation experiments of acid red 3B were carried out in the suspension system of LaFe_ 1-yCu_yO...Pervoskite-type oxides LaFe_ 1-yCu_yO_3 was prepared by citrate method. Using a fluorescent Hg lamp as irradiator, the degradation experiments of acid red 3B were carried out in the suspension system of LaFe_ 1-yCu_yO_3. The results show that the doped oxides LaFe_ 1-yCu_yO_3 have good photocatalytic oxidation property. With the study of positron annihilation, its photocatalytic activity is mainly related with defect structures resulted by doping.展开更多
文摘A novel technology which combined electrochemical process catalyzed by manganese mineral with electro-assisted coagulation process was proposed in this study. The mineralization of organic pollutant from simulated dye wastewater containing an azo dye Acid Red B（ARB） was experimentally investigated using this method. It was found that the manganese mineral could catalyze the electrochemical process dramatically. The TOC removal percentage of electrochemical treatment catalyzed by manganese mineral was 43.6% while the TOC removal percentage of the process using the manganese mineral alone and using the electrolysis alone were 9.3% and 20.8%, respectively. Moreover, it was found that combined electroxidation with electro-assisted coagulation process could more effectively eliminate ARB. After a period of 180 min electrooxidation and 300 min electroreduction, almost 66.9% of TOC was removed, and the dissolved Mn^2＋. could be effectivly removed. The effects of the order of oxidation and reduction, the proper ratio electrooxidation/reduction time, and current density on the removal efficiency were investigated in detail. In addition, a proposed mechanism of manganese-mineral-catalyzed electrooxidation-reduction process was discussed in this paper.
基金Project supported by the National Natural Science Foundation of China (No. 20277010)
文摘Boron- and cerium-codoped TiO2 photocatalysts were synthesized using modified sol-gel reaction process and characterized by X- ray diffraction （XRD）, X-ray photoelectron spectroscopy （XPS）, particle size distribution （PSD）, diffuse reflectance spectra （DRS）, and Brunauer-Emmett-Teller （BET）. The photocatalytic activities were evaluated by monitoring the degradation of dye Acid Red B （ARB）. The results showed that the prepared photocatalysts were mixed oxides mainly consisting of titania, ceria, and boron oxide. The structure of TiO2 could be transformed from amorphous to anatase and then to rutile by increasing calcination temperature; the transformation being accompanied by the growth of particle size without any obvious change in phase structure of CeO2. The XPS of B1.6Ce1.0-TiO2 prepared at 500℃ showed that a few boron atoms were incorporated into titania and ceria lattice, whereas others existed as B2O3. Cerium ions existed in two states, Ce^3＋ and Ce^4＋, and the atomic ratio of Ce^3＋/Ce^4＋ was 1.86. When boron and cerium were doped, the UV-Vis adsorption band wavelength showed an obvious shift toward the visible range （〈526 nm）. As the atomic ratio of Ce/Ti increased to 1.0, the absorbance edge wavelength increased to 481 nm. The absorbance edge wavelength decreased for higher cerium doping levels （Ce/Ti=2.0）. The particles size ranged from 122 to 255 nm with a domain at 168 nm （39.4%）. The degradation of ARB dye indicated that the photocatalytic activities of boron- and cerium-codoped TiO2 were much higher than those of P25 （a standard TiO2 powder）. The activities increased as the boron doping increased, whereas decreased when the Ce/Ti atomic ratio was greater than 0.5. The optimum atomic ratio of B/Ti and Ce/Ti was 1.6 and 0.5, respectively.
文摘Pervoskite-type oxides LaFe_ 1-yCu_yO_3 was prepared by citrate method. Using a fluorescent Hg lamp as irradiator, the degradation experiments of acid red 3B were carried out in the suspension system of LaFe_ 1-yCu_yO_3. The results show that the doped oxides LaFe_ 1-yCu_yO_3 have good photocatalytic oxidation property. With the study of positron annihilation, its photocatalytic activity is mainly related with defect structures resulted by doping.