The graft polymerization of acrylic acid(A) and acrylamide(B) was carried out onto bi-oriented polyester BOPET corona film.The influence of monomer concentration,reducer concentration and reaction time on the graft po...The graft polymerization of acrylic acid(A) and acrylamide(B) was carried out onto bi-oriented polyester BOPET corona film.The influence of monomer concentration,reducer concentration and reaction time on the graft polymerization was investigated.The surface tension of the films increased with an increase of monomer concentration,till the concentration of monomer A reached 1.5×10^(-2)g/mL and the concentration of monomer B reached 4.0×10^(-2)g/mL.The surface tension of the films reached a maximum value at 7×10^(-4)M of reducer concentration and subsequently decreased with further increase in reducer concentration.The surface tension of the films increased with the increase of the reaction time apparently within 50min.The grafted corona BOPET films were characterized with IR and XPS.The presence of graft on the film surface was confirmed.The attenuation experiments on grafted corona BOPET films in air at 50℃ and in water were carried out to investigate the persistence of graft polymerization of acrylic acid and arylamide onto BOPET corona films.展开更多
In this article,alkali lignin separated from paper pulp waste was grafted into a novel copolymer LSAA (a copolymer of lignin,starch, acrylamide,and acrylic acid).Its practical application effect and environmental safe...In this article,alkali lignin separated from paper pulp waste was grafted into a novel copolymer LSAA (a copolymer of lignin,starch, acrylamide,and acrylic acid).Its practical application effect and environmental safety were studied.The results of field simulation experiment indicated that the application of LSAA significantly affected the output of the runoff and pollutants.The runoff quantity was decreased by 16.67%-47.00%and the loads of total suspended solids (TSS),chemical oxygen demand (COD),total nit...展开更多
文摘The graft polymerization of acrylic acid(A) and acrylamide(B) was carried out onto bi-oriented polyester BOPET corona film.The influence of monomer concentration,reducer concentration and reaction time on the graft polymerization was investigated.The surface tension of the films increased with an increase of monomer concentration,till the concentration of monomer A reached 1.5×10^(-2)g/mL and the concentration of monomer B reached 4.0×10^(-2)g/mL.The surface tension of the films reached a maximum value at 7×10^(-4)M of reducer concentration and subsequently decreased with further increase in reducer concentration.The surface tension of the films increased with the increase of the reaction time apparently within 50min.The grafted corona BOPET films were characterized with IR and XPS.The presence of graft on the film surface was confirmed.The attenuation experiments on grafted corona BOPET films in air at 50℃ and in water were carried out to investigate the persistence of graft polymerization of acrylic acid and arylamide onto BOPET corona films.
文摘In this article,alkali lignin separated from paper pulp waste was grafted into a novel copolymer LSAA (a copolymer of lignin,starch, acrylamide,and acrylic acid).Its practical application effect and environmental safety were studied.The results of field simulation experiment indicated that the application of LSAA significantly affected the output of the runoff and pollutants.The runoff quantity was decreased by 16.67%-47.00%and the loads of total suspended solids (TSS),chemical oxygen demand (COD),total nit...
