Acrylate latex modified by vinyl triisopropoxy silane (C-1706) was synthesized by seeded emulsion polymerization with anionic emulsifier sodium dodecyl sulphonate(SDS) and nonionic emulsifier OP-10 as the multiple emu...Acrylate latex modified by vinyl triisopropoxy silane (C-1706) was synthesized by seeded emulsion polymerization with anionic emulsifier sodium dodecyl sulphonate(SDS) and nonionic emulsifier OP-10 as the multiple emulsifiers at (78±2) ℃. The effects of different factors, such as the emulsifier, C-1706 monomer and its feeding manner on the properties of acrylate latex modified by C-1706 were investigated. The particle size distribution and the structure, the configuration, the weather durability and stain resistance of copolymer latex were characterized by particle size analyzer, Fourier transform infrared spectroscopy (FT-IR), transmission electron microscope(TEM), scanning electron microscope(SEM) and ultraviolet aging instrument respectively. The results show that SDS to OP-10 as multiple emulsifiers can lead to coordinated efficiency, the optimal emulsifier dosage is 2.4%?3.2%(mass fraction), and the mass ratio of SDS to OP-10 is 1?1? 1?2. The seeded emulsion polymerization can effectively introduce a organic-siloxane bonding in a macromolecule inter polymer, and the obtained acrylate latex modified by organic-siloxane possesses narrow distribution of particle size with mean diameter of 51.8?76.6 nm and has the excellent properties in weather durability and stain-resistance especially.展开更多
Novel self cross-linking fluorinated acrylic latex(SCLFAL) has been successfully prepared via starved seeded semi-batch emulsion polymerization.The resultant SCLFAL is characterized by Fourier transform infrared(F...Novel self cross-linking fluorinated acrylic latex(SCLFAL) has been successfully prepared via starved seeded semi-batch emulsion polymerization.The resultant SCLFAL is characterized by Fourier transform infrared(FTIR) spectrometry.Contact angle (CA) and glass transition temperature(T_g) of the film are investigated.Results show that CA and T_g of the film can be improved when the moderate amount of HPMA is introduced into the mixed monomers.展开更多
Cationic fluorinated acrylate latex was prepared via semi-continuous emulsion copolymerization of cationic monomer and other monomers. The resultant latex and its film were characterized with dynamic light scattering ...Cationic fluorinated acrylate latex was prepared via semi-continuous emulsion copolymerization of cationic monomer and other monomers. The resultant latex and its film were characterized with dynamic light scattering detector and contact angle meter. Influences of amount of DMDAAC on the properties of resultant latex and its film were investigated in detail. Results show that the particle size of the latex has the minimum value knd the zeta potential of the latex is increased when the amount of DMDAAC is increased. In addition, the particle size of the latex is unimodal distribution when the amount of DMDAAC is not more than 2.5%. However, the particle size of the latex is bimodal distribution when the amount of DMDAAC is more than 2.5%. The contact angle is varied slightly with the increase of amount of DMDAAC when it is not more than 2.5%. Nevertheless, the contact angle is decreased with the increase of the amount of DMDAAC when it is more than 2.5%.展开更多
基金Project(2003B10506) supported by Science and Technology Department of Guangdong Province, China
文摘Acrylate latex modified by vinyl triisopropoxy silane (C-1706) was synthesized by seeded emulsion polymerization with anionic emulsifier sodium dodecyl sulphonate(SDS) and nonionic emulsifier OP-10 as the multiple emulsifiers at (78±2) ℃. The effects of different factors, such as the emulsifier, C-1706 monomer and its feeding manner on the properties of acrylate latex modified by C-1706 were investigated. The particle size distribution and the structure, the configuration, the weather durability and stain resistance of copolymer latex were characterized by particle size analyzer, Fourier transform infrared spectroscopy (FT-IR), transmission electron microscope(TEM), scanning electron microscope(SEM) and ultraviolet aging instrument respectively. The results show that SDS to OP-10 as multiple emulsifiers can lead to coordinated efficiency, the optimal emulsifier dosage is 2.4%?3.2%(mass fraction), and the mass ratio of SDS to OP-10 is 1?1? 1?2. The seeded emulsion polymerization can effectively introduce a organic-siloxane bonding in a macromolecule inter polymer, and the obtained acrylate latex modified by organic-siloxane possesses narrow distribution of particle size with mean diameter of 51.8?76.6 nm and has the excellent properties in weather durability and stain-resistance especially.
基金supported by the Science and Technology Department of Zhejiang Province under Grant No. 2010C31040.In additionthe financial support of Zhejiang Provincial Natural Science Foundation of China(No. Y4100152)
文摘Novel self cross-linking fluorinated acrylic latex(SCLFAL) has been successfully prepared via starved seeded semi-batch emulsion polymerization.The resultant SCLFAL is characterized by Fourier transform infrared(FTIR) spectrometry.Contact angle (CA) and glass transition temperature(T_g) of the film are investigated.Results show that CA and T_g of the film can be improved when the moderate amount of HPMA is introduced into the mixed monomers.
基金supported by the Science and Technology Department of Zhejiang Province under Grant No. 2010C31040the financial support of Zhejiang Provincial Natural Science Foundation of China(No. Y4100152)Zhejiang University of Technology Natural Science Foundation(No.20100202)
文摘Cationic fluorinated acrylate latex was prepared via semi-continuous emulsion copolymerization of cationic monomer and other monomers. The resultant latex and its film were characterized with dynamic light scattering detector and contact angle meter. Influences of amount of DMDAAC on the properties of resultant latex and its film were investigated in detail. Results show that the particle size of the latex has the minimum value knd the zeta potential of the latex is increased when the amount of DMDAAC is increased. In addition, the particle size of the latex is unimodal distribution when the amount of DMDAAC is not more than 2.5%. However, the particle size of the latex is bimodal distribution when the amount of DMDAAC is more than 2.5%. The contact angle is varied slightly with the increase of amount of DMDAAC when it is not more than 2.5%. Nevertheless, the contact angle is decreased with the increase of the amount of DMDAAC when it is more than 2.5%.