The aim of this pilot study was to evaluate the shear bond strength of superficial bovine incisor dentin in different crown regions. Bonding was performed to the incisal, middle and cervical thirds of superficial bovi...The aim of this pilot study was to evaluate the shear bond strength of superficial bovine incisor dentin in different crown regions. Bonding was performed to the incisal, middle and cervical thirds of superficial bovine coronal dentin (n = 20) with a two-step etch-and-rinse adhesive (Optibond Solo Plus) and resin composite (Z100). Shear bond strength was evaluated at 24 h and failure modes of representative specimens wereobserved with FE-SEM. Non-parametric Kruskal-Wallis test with a significance level of 0.05 was used for data analysis. Mean shear bond strength values for the incisal, middle, and cervical thirds were 36.9 (3.1), 42.6 (2.6), and 37.1 (2.1) respectively with no significant differences evidenced between the crown thirds (p = 0.19). Observation of the failure mode of representative specimens demonstrated that specimens with high bond strength values exhibited predominantly mixed-type failures whereas low strength specimens exhibited adhesive failures between the dentin and adhesive. The absence of significant differences in shear bond strength between crown thirds indicate that, regardless of tubule orientation, any crown region can be used when superficial bovine incisor dentin is used for shear bond strength testing.展开更多
Background: To date there is not a material considered ideal for the lased dentin. Objective: To compare the bond strength to human lased dentin of self-etch and etch-and-rinse adhesive systems, a self-adhesive resin ...Background: To date there is not a material considered ideal for the lased dentin. Objective: To compare the bond strength to human lased dentin of self-etch and etch-and-rinse adhesive systems, a self-adhesive resin composite and a glass-ionomer cement. Methods: Forty human molars were sectioned to obtain a 2 mm-thick slab of mid-coronal dentin. The occlusal surface of each slab was polished by SiC paper (P600) for 10 s. Then an half part of dentin slabs was randomly selected for receiving treatment with 2.94 μm Er:YAG laser (DEKA, Smart 2940D Plus) with 10 Hz at 100 mJ, pulse duration of 230 μs with contact tip. Dentin slabs were randomly divided into four groups (n = 10). Six conical frustum-shaped build-ups were constructed on the occlusal surface of each dentin slab using bonding agents (OptiBond Solo Plus Group 1;OptiBond All-in-one Group 2) combined with a resin composite (Premise Flow), self-adhesive resin composites (Vertise Flow Group 3) and a glass-ionomer cement (Ketac-Fil Group 4). Specimens were subjected to μSBS test. Data were analyzed by a mixed model and Tukey’s test. Results: Measured bond strengths were (mean ± standard deviation): 20.8 ± 5.5 MPa (laser treatment) and 15.6 ± 4.5 MPa (SiC paper) for Group 1, 18.9 ± 5.3 MPa (laser treatment) and 14.0 ± 4.3 MPa (SiC paper) for Group 2, 7.9 ± 2.8 MPa (laser treatment) and 4.3 ± 2.2 MPa (SiC paper) for Group 3, 4.7 ± 1.9 MPa (laser treatment) and 2.6 ± 1.2 MPa (SiC paper) for Group 4. The inferential analysis showed that the dentin laser treatment significantly affected the bond strength within each individual group. On dentin treated with laser the bond strengths recorded for build-ups constructed with etch and rinse and self-etch adhesive systems were significantly higher than those recorded for build-ups constructed with self-adhesive resin composite and glass-ionomer cement (p < 0.0001). Similarly, on dentin treated with SiC paper the bond strengths recorded for build-ups constructed with etch and rinse and self-etch adhesive systems were significantly higher than those recorded for build-ups constructed with self-adhesive resin composite and glass-ionomer cement (p < 0.0001). Conclusion: Er:YAG laser treatment has increased the shear bond strength of all the adhesive materials used.展开更多
Face centred cubic（FCC） TiB ceramic powder synthesized by Ti-boronizing method was used as conductive filler to make ceramic electrically conductive adhesives（ECAs） with the polymer matrix.Electrically conductive ...Face centred cubic（FCC） TiB ceramic powder synthesized by Ti-boronizing method was used as conductive filler to make ceramic electrically conductive adhesives（ECAs） with the polymer matrix.Electrically conductive properties of the ceramic ECAs were studied.The bulk electrical resistivity varied with the powder content of the FCC-TiB in ECAs.The FCC-TiB filled ECAs also showed the percolation behavior that usually occurred for the metal-filled ECAs,the percolation threshold was located at the content of 60%FCC-TiB.A minimum value of 0.1 Ω·cm was obtained at a content of 75%FCC-TiB.In order to check the reliability of mechanical property,tensile test was done to measure the shear strength,and the shear strength dropped with increasing the content of FCC-TiB powders.It is about 12.26 MPa at the content of 70%TiB powders.The Cu filled ECAs were also prepared for comparison.The properties of the oxidation resistance of the two ECAs were evaluated.The results show that the ceramic ECAs have excellent oxidation resistance and better stability compared with the Cu filled ECAs.展开更多
目的:研究3种粘接剂对抛光及上釉锆瓷与正畸金属托槽粘接强度和耐久性的影响。方法:选用2种通用型粘接剂Single Bond Universal(SBU)和Prime&Bond Universal(PBU),以TransbondTMMIP(TM)为对照分别将抛光组、上釉组锆瓷与上颌中切牙...目的:研究3种粘接剂对抛光及上釉锆瓷与正畸金属托槽粘接强度和耐久性的影响。方法:选用2种通用型粘接剂Single Bond Universal(SBU)和Prime&Bond Universal(PBU),以TransbondTMMIP(TM)为对照分别将抛光组、上釉组锆瓷与上颌中切牙金属托槽粘接,试样共6组(n=20)。水浴或水浴+冷热循环储存后测试全部试件剪切粘接强度(SBS),分析断裂形态以及粘接剂残留指数(ARI)。结果:粘接剂(P<0.001)和储存条件(P<0.001)显著影响锆瓷与托槽的剪切粘接强度;抛光或上釉(P=0.09)组间无统计学差异。SBU在各组中都表现出较强的粘接强度和较低的ARI,3种粘接剂间的ARI分数存在显著差异(P<0.001)。结论:粘接金属托槽与抛光及上釉锆瓷时,SBU较PBU和TM有更好的粘接性能。展开更多
文摘The aim of this pilot study was to evaluate the shear bond strength of superficial bovine incisor dentin in different crown regions. Bonding was performed to the incisal, middle and cervical thirds of superficial bovine coronal dentin (n = 20) with a two-step etch-and-rinse adhesive (Optibond Solo Plus) and resin composite (Z100). Shear bond strength was evaluated at 24 h and failure modes of representative specimens wereobserved with FE-SEM. Non-parametric Kruskal-Wallis test with a significance level of 0.05 was used for data analysis. Mean shear bond strength values for the incisal, middle, and cervical thirds were 36.9 (3.1), 42.6 (2.6), and 37.1 (2.1) respectively with no significant differences evidenced between the crown thirds (p = 0.19). Observation of the failure mode of representative specimens demonstrated that specimens with high bond strength values exhibited predominantly mixed-type failures whereas low strength specimens exhibited adhesive failures between the dentin and adhesive. The absence of significant differences in shear bond strength between crown thirds indicate that, regardless of tubule orientation, any crown region can be used when superficial bovine incisor dentin is used for shear bond strength testing.
文摘Background: To date there is not a material considered ideal for the lased dentin. Objective: To compare the bond strength to human lased dentin of self-etch and etch-and-rinse adhesive systems, a self-adhesive resin composite and a glass-ionomer cement. Methods: Forty human molars were sectioned to obtain a 2 mm-thick slab of mid-coronal dentin. The occlusal surface of each slab was polished by SiC paper (P600) for 10 s. Then an half part of dentin slabs was randomly selected for receiving treatment with 2.94 μm Er:YAG laser (DEKA, Smart 2940D Plus) with 10 Hz at 100 mJ, pulse duration of 230 μs with contact tip. Dentin slabs were randomly divided into four groups (n = 10). Six conical frustum-shaped build-ups were constructed on the occlusal surface of each dentin slab using bonding agents (OptiBond Solo Plus Group 1;OptiBond All-in-one Group 2) combined with a resin composite (Premise Flow), self-adhesive resin composites (Vertise Flow Group 3) and a glass-ionomer cement (Ketac-Fil Group 4). Specimens were subjected to μSBS test. Data were analyzed by a mixed model and Tukey’s test. Results: Measured bond strengths were (mean ± standard deviation): 20.8 ± 5.5 MPa (laser treatment) and 15.6 ± 4.5 MPa (SiC paper) for Group 1, 18.9 ± 5.3 MPa (laser treatment) and 14.0 ± 4.3 MPa (SiC paper) for Group 2, 7.9 ± 2.8 MPa (laser treatment) and 4.3 ± 2.2 MPa (SiC paper) for Group 3, 4.7 ± 1.9 MPa (laser treatment) and 2.6 ± 1.2 MPa (SiC paper) for Group 4. The inferential analysis showed that the dentin laser treatment significantly affected the bond strength within each individual group. On dentin treated with laser the bond strengths recorded for build-ups constructed with etch and rinse and self-etch adhesive systems were significantly higher than those recorded for build-ups constructed with self-adhesive resin composite and glass-ionomer cement (p < 0.0001). Similarly, on dentin treated with SiC paper the bond strengths recorded for build-ups constructed with etch and rinse and self-etch adhesive systems were significantly higher than those recorded for build-ups constructed with self-adhesive resin composite and glass-ionomer cement (p < 0.0001). Conclusion: Er:YAG laser treatment has increased the shear bond strength of all the adhesive materials used.
基金Project (51172088) supported by the National Natural Science Foundation of China
文摘Face centred cubic（FCC） TiB ceramic powder synthesized by Ti-boronizing method was used as conductive filler to make ceramic electrically conductive adhesives（ECAs） with the polymer matrix.Electrically conductive properties of the ceramic ECAs were studied.The bulk electrical resistivity varied with the powder content of the FCC-TiB in ECAs.The FCC-TiB filled ECAs also showed the percolation behavior that usually occurred for the metal-filled ECAs,the percolation threshold was located at the content of 60%FCC-TiB.A minimum value of 0.1 Ω·cm was obtained at a content of 75%FCC-TiB.In order to check the reliability of mechanical property,tensile test was done to measure the shear strength,and the shear strength dropped with increasing the content of FCC-TiB powders.It is about 12.26 MPa at the content of 70%TiB powders.The Cu filled ECAs were also prepared for comparison.The properties of the oxidation resistance of the two ECAs were evaluated.The results show that the ceramic ECAs have excellent oxidation resistance and better stability compared with the Cu filled ECAs.
文摘目的:研究3种粘接剂对抛光及上釉锆瓷与正畸金属托槽粘接强度和耐久性的影响。方法:选用2种通用型粘接剂Single Bond Universal(SBU)和Prime&Bond Universal(PBU),以TransbondTMMIP(TM)为对照分别将抛光组、上釉组锆瓷与上颌中切牙金属托槽粘接,试样共6组(n=20)。水浴或水浴+冷热循环储存后测试全部试件剪切粘接强度(SBS),分析断裂形态以及粘接剂残留指数(ARI)。结果:粘接剂(P<0.001)和储存条件(P<0.001)显著影响锆瓷与托槽的剪切粘接强度;抛光或上釉(P=0.09)组间无统计学差异。SBU在各组中都表现出较强的粘接强度和较低的ARI,3种粘接剂间的ARI分数存在显著差异(P<0.001)。结论:粘接金属托槽与抛光及上釉锆瓷时,SBU较PBU和TM有更好的粘接性能。