A new corona protection varnish was prepared by using epoxy/montmorillonite nanocomposite and pure epoxy resin as adhesives respectively.The adhesive with different amounts of organic montmorillonite（OMMT） was mixed...A new corona protection varnish was prepared by using epoxy/montmorillonite nanocomposite and pure epoxy resin as adhesives respectively.The adhesive with different amounts of organic montmorillonite（OMMT） was mixed with 1200 mesh silicon carbide（Si C） by different weight ratios.The surface states of the varnishes with various adhesives were observed by powerful optical microscope.Some properties of the varnishes were analyzed during the enduring time under 5kV/cm DC,such as the relation of change in nonlinear coefficient,natural surface resistivity,and surface temperature variation.The results showed that the amounts of OMMT had little effect on the natural surface resistance of the varnish but had important influence on the nonlinear property of the varnish.When the range of the OMMT content was 2wt% to 6wt%,the nonlinear coefficient of all materials with epoxy/OMMT nano-composite adhesive was higher than that with pure epoxy resin adhesive.The surface temperature of the varnish with epoxy/OMMT nanocomposite adhesive was all lower than that with the pure epoxy resin adhesive under high electrical field strength.展开更多
基金Funded by the Major State Basic Research Development Program of China(No.2010CB736208)the Planning Project of Hei Longjiang Province for Science and Technology(No.GC10A203)
文摘A new corona protection varnish was prepared by using epoxy/montmorillonite nanocomposite and pure epoxy resin as adhesives respectively.The adhesive with different amounts of organic montmorillonite（OMMT） was mixed with 1200 mesh silicon carbide（Si C） by different weight ratios.The surface states of the varnishes with various adhesives were observed by powerful optical microscope.Some properties of the varnishes were analyzed during the enduring time under 5kV/cm DC,such as the relation of change in nonlinear coefficient,natural surface resistivity,and surface temperature variation.The results showed that the amounts of OMMT had little effect on the natural surface resistance of the varnish but had important influence on the nonlinear property of the varnish.When the range of the OMMT content was 2wt% to 6wt%,the nonlinear coefficient of all materials with epoxy/OMMT nano-composite adhesive was higher than that with pure epoxy resin adhesive.The surface temperature of the varnish with epoxy/OMMT nanocomposite adhesive was all lower than that with the pure epoxy resin adhesive under high electrical field strength.