Large magnetic entropy change and adiabatic temperature rise of a ternary Gd_(34)Ni_(33)Al_(33) metallic glass

A low cost Gd_(34)Ni_(33)Al_(33) metallic glass with excellent magnetocaloric properties was successfully prepared in the present work.The magnetic properties of the ribbons were measured by constructing the relationship of magnetic entropy change(-ΔS_(m)) on temperature as well as magnetic field.The amorphous alloy shows typical magnetocaloric behaviors,large maximum-ΔS_(m)(11.06 J/(kg·K) under 5 T)and adiabatic temperature rise(4.3 K under 5 T) near 40 K,indicating that the low cost Gd_(34)Ni_(33)Al_(33) metallic glass is a good candidate material for low temperature magnetic refrigeration.

Design and Preparation of High Elastic Modulus Self-compacting Concrete for Pre-stressed Mass Concrete Structures

Requirements of self-compacting concrete （SCC） applied in pre-stressed mass concrete structures include high fluidity, high elastic modulus, low adiabatic temperature rise and low drying shrinkage, which cannot be satisfied by ordinary SCC. In this study, in order to solve the problem, a few principles of SCC design were proposed and the effects of binder amount, fly ash （FA） substitution, aggregate content and gradation on the workability, temperature rise, drying shrinkage and elastic modulus of SCC were investigated. The results and analysis indicate that the primary factor influencing the fluidity was paste content, and the main methods improving the elastic modulusof SCC were a lower sand ratio and an optimized coarse aggregate gradation. Lower adiabatic temperature rise and drying shrinkage were beneficial for decreasing the cement content. Further, based on the optimization of mixture, a C50 grade SCC （with binder amount of only 480 kg/ m3, fly ash substitution of 40%, sand ratio of 51% and proper coarse aggregate gradation （Vs.~0 mm： V10-16 ram： V16.20 mm= 30%： 30%：40%）） with superior workability was successfully prepared. The temperature rise and drying shrinkage of the prepared SCC were significantly reduced, and the elastic modulus reached 37.6 GPa at 28 d.

Effect of Ni substitution on the formability and magnetic properties of Gd50Co50 amorphous alloy

A small amount of Ni was added into the binary Gd50Co50 amorphous alloy to replace Gd in order to obtain ternary Co50Gd50-xNx(x=1,2,and 3)amorphous alloys.Compared to the binary Gd50Co50 amorphous alloy,the Co50Gd50-xNx amorphous alloys show an enhanced Curie temperature(TC)with a weakened formability.The maximum magnetic entropy change(-Δ^Smpeak)of the Co50Gd50-xNx amorphous alloys is found to decrease with the increasing TC.The adiabatic temperature rise(ΔTad)of the Co50Gd47Ni3 amorphous alloy is superior to that of the Fe-based metallic glasses at room temperature.The variation of the TC and-Δ^Smpeak of the Gd50Co50 amorphous alloy with Ni addition,and the mechanism involved,were discussed.