ZrO_(2)-YO_(1.5)-TaO_(2.5)(ZYTO)is a promising top-coat material for thermal barrier coatings(TBCs).The bulk properties of ZYTO have been reported by several studies,but its performances as TBCs are less-well understo...ZrO_(2)-YO_(1.5)-TaO_(2.5)(ZYTO)is a promising top-coat material for thermal barrier coatings(TBCs).The bulk properties of ZYTO have been reported by several studies,but its performances as TBCs are less-well understood.In this work,ZYTO TBCs were prepared by air plasma spraying(APS)and their thermal cycling performances were investigated at 1150℃.Despite of the good bulk properties,APS ZYTO TBCs present an extremely short thermal fatigue life.This is attributed to the non-equilibrium grain-boundary segregation of TaO_(2.5) induced by limited solubility and rapid quenching during APS process,resulting in a tetragonal(t)to cubic(c)and metastable-tetragonal(tm)phase transformation in ZYTO TBCs.The volume shrinkage(~0.74vol%)of phase transformation leads to many cracks at the c/tm phase boundaries after deposition.On the other hand,the formation of cubic phase with massive grain-boundary Ta segregation induces a large intergranular embrittlement and a weak bonding strength(~5.3 MPa),resulting in the premature failure of the ZYTO TBCs.展开更多
基金financially supported by the National Natural Science Foundation of China (Nos. 51971139 and 51875341)the National Science and Technology Major Project of China (No. 2017-VI-0011-0083)
文摘ZrO_(2)-YO_(1.5)-TaO_(2.5)(ZYTO)is a promising top-coat material for thermal barrier coatings(TBCs).The bulk properties of ZYTO have been reported by several studies,but its performances as TBCs are less-well understood.In this work,ZYTO TBCs were prepared by air plasma spraying(APS)and their thermal cycling performances were investigated at 1150℃.Despite of the good bulk properties,APS ZYTO TBCs present an extremely short thermal fatigue life.This is attributed to the non-equilibrium grain-boundary segregation of TaO_(2.5) induced by limited solubility and rapid quenching during APS process,resulting in a tetragonal(t)to cubic(c)and metastable-tetragonal(tm)phase transformation in ZYTO TBCs.The volume shrinkage(~0.74vol%)of phase transformation leads to many cracks at the c/tm phase boundaries after deposition.On the other hand,the formation of cubic phase with massive grain-boundary Ta segregation induces a large intergranular embrittlement and a weak bonding strength(~5.3 MPa),resulting in the premature failure of the ZYTO TBCs.