Effects of Atmospheric Pressure on Developmental Characteristics and the Stability of Air Entraining Agent for Concrete

In order to ascertain the effects of atmospheric pressure on developmental characteristics and the stability of AEA(air-entraining agent)solution bubbles,AEA solution experiments and AEA solution bubble experiments were,respectively,conducted in Peking(50 m,101.2 kPa)and Lhasa(3,650 m,63.1 kPa).Surface tensions and inflection-point concentrations were tested based on AEA solutions,whilst developmental characteristics,thicknesses and elastic coefficients of liquid films were tested based on air bubbles of AEA solutions.The study involved three types of AEAs,which were TM-O,226A,and 226S.The experimental results show that initial sizes of TM-O,226A,and 226S are,respectively,increased by 43.5%,17.5%,and 3.8%.With the decrease of ambient pressure,the drainage rate and the drainage index of AEA solution bubbles increase.Interference experiments show that the liquid film thicknesses of all tested AEA solution bubbles are in micron scales.When the atmospheric pressure decreases from 101.2 to 63.1 kPa,the liquid film thicknesses of three types of AEA solutions decrease in various degrees;and film elasticities at critical thicknesses increase.Liquid film of 226S solution bubbles is the most stable,presenting as a minimum thickness variation.It should be noted that elastic coefficient of liquid film only represents the level at critical thickness,thus it can not be applied as the only evaluating indicator of bubble stability.For a type of AEA,factors affecting the stability of its bubbles under low atmospheric pressure include initial bubbles size,liquid film thickness,liquid film elasticity,ambient temperature,etc.

The Influence of Chemical Admixtures on the Fluidity,Viscosity and Rheological Properties of Ultra-High Performance Concrete

To achieve higher strength and better durability,ultra-high performance concrete(UHPC)typically employs a relatively small water-binder ratio.However,this generally leads to an undesired increase in the paste viscosity.In this study,the effects of liquid and powder polycarboxylate superplasticizers(PCE)on UHPC are compared and critically discussed.Moreover,the following influential factors are considered:air-entraining agents(AE),slump retaining agents(SA),and defoaming agents(DF)and the resulting flow characteristics,mechanical properties,and hydration properties are evaluated assuming UHPC containing 8‰powder PCE(PCE-based UHPC).It is found that the spread diameter of powder PCE is 5%higher than that of liquid PCE.Among the chemical admixtures studied,AEs have the best effect on improving UHPC workability,while DFs have the worst effect.When the addition of AE and SA is 1.25‰and 14.7%of PCE,paste viscosity reduces by 35%and 19%,respectively compared to the paste with only 8‰PCE.A low AE dosage(1.25‰)decreases compressive strength by 4.1%,while SA(8.1%)increases UHPC compressive strength by 9.1%.Both AE and SA significantly delay the UHPC hydration process,reducing the hydration heat release peaks by 76%and 27%,respectively.

Rheological Properties of Self-compacting Concrete Paste Containing Chemical Admixtures

Self-compacting concrete （SCC） was used for the filling layer of CRTSⅢ plate ballastless track, which needs excellent workability. The rheological properties of SCC cement paste containing chemical admixtures （CA） such as polycarboxylate-based superplasticizer （PCE）, air-entraining agent （AE） and defoamer （DF） were investigated using a Brookfield R/S SST2000 soft solid tester with a vane geometry spindle. The cementitious materials were designed as one, two and, three components systems by addition of ordinary portland cement （OPC） with these chemical admixtures. The rheological properties of one-component system （PCE paste） were improved with increasing the content of PCE. For two components systems of PCE-AE and PCE-DF, yield stress and plastic viscosity reduced firstly and increased afterward with the increasing of AE content. And the plastic viscosity reached the optimum when the content of AE is 0.004wt%. In general, the trend of yield stress and plastic viscosity decreased with the increasing of the DF content. For three components systems, PCE-AE-DF systems, the rheological properties were improved compared with the sample with AE or DF, which attributed to mixes of the active components mentioned above （CA） which could have a synergetic effect.