The compressive strength and flexural strength with the same strength class cement mortar of the alkali-resistant glass fiber cement mortar were tested in standard and hot-water curing condition, and the damage mechan...The compressive strength and flexural strength with the same strength class cement mortar of the alkali-resistant glass fiber cement mortar were tested in standard and hot-water curing condition, and the damage mechanism of alkali-resistant glass fiber was studied. The interaction mechanisms of the chemical erosion and physical injury in different curing conditions were studied in order to summarize the damage mechanism of alkali-resistant glass fiber in cement-based materials, and chloride diffusivity coefficient and porosity of cement mortar were tested in the different curing conditions. The experimental results are that the strength of cement based materials and fiber cement slurry interface zone were closely related, and heat curing could accelerate the hydration of cement, but inevitably enlarge the defect.展开更多
Statement of problem: Many processes have been applied to improve the fracture resistance of acrylic resin dentures by reinforcing them. The maximum goal of any denture repair is to restore the main strength of the de...Statement of problem: Many processes have been applied to improve the fracture resistance of acrylic resin dentures by reinforcing them. The maximum goal of any denture repair is to restore the main strength of the denture and to avoid further fracture. Purpose: This study investigated the ability of self-curing acrylic resin to be strength and deflection of repaired acrylic resin joints reinforced with various reinforcement materials to resist fracture. Material and methods: Transverse strength of polymethyl methacrylate acrylic resin reinforced with glass fiber mesh, metal mesh, and metal wire was evaluated with a 3-point load test on 40 intact specimens (n = 10 for control group) (n = 10 per each reinforcement material group). Fractured joint margins were rounded, a 4-mm gap was placed between them, and then they were repaired with autopolymerizing acrylic resin and retested. Results: Transverse strength for the polymethyl methacrylate acrylic resin samples has showed fracture at the side of sample rather than in the middle area of reinforcement materials and some other samples showed bending statue rather than fracture. Conclusion: Reinforcement with glass fiber mesh, metal mesh, and metal wire produced transverse strength in the side area of resin denture base material rather than in the middle of reinforcement area with bending samples rather than fracture response.展开更多
基金Funded by the National Natural Science Foundation of China(Nos.51009015and50872015)the Education Foundation of Liaoning Province(No.L2010038)
文摘The compressive strength and flexural strength with the same strength class cement mortar of the alkali-resistant glass fiber cement mortar were tested in standard and hot-water curing condition, and the damage mechanism of alkali-resistant glass fiber was studied. The interaction mechanisms of the chemical erosion and physical injury in different curing conditions were studied in order to summarize the damage mechanism of alkali-resistant glass fiber in cement-based materials, and chloride diffusivity coefficient and porosity of cement mortar were tested in the different curing conditions. The experimental results are that the strength of cement based materials and fiber cement slurry interface zone were closely related, and heat curing could accelerate the hydration of cement, but inevitably enlarge the defect.
文摘Statement of problem: Many processes have been applied to improve the fracture resistance of acrylic resin dentures by reinforcing them. The maximum goal of any denture repair is to restore the main strength of the denture and to avoid further fracture. Purpose: This study investigated the ability of self-curing acrylic resin to be strength and deflection of repaired acrylic resin joints reinforced with various reinforcement materials to resist fracture. Material and methods: Transverse strength of polymethyl methacrylate acrylic resin reinforced with glass fiber mesh, metal mesh, and metal wire was evaluated with a 3-point load test on 40 intact specimens (n = 10 for control group) (n = 10 per each reinforcement material group). Fractured joint margins were rounded, a 4-mm gap was placed between them, and then they were repaired with autopolymerizing acrylic resin and retested. Results: Transverse strength for the polymethyl methacrylate acrylic resin samples has showed fracture at the side of sample rather than in the middle area of reinforcement materials and some other samples showed bending statue rather than fracture. Conclusion: Reinforcement with glass fiber mesh, metal mesh, and metal wire produced transverse strength in the side area of resin denture base material rather than in the middle of reinforcement area with bending samples rather than fracture response.