A new organic/inorganic hybrid nonlinear optical (NLO) material was developed by the sol-gel process of an alkoxysilane dye with tetraethoxysilane. A NLO moiety based on 4-nitro-4 ' -hydroxy azobenzene was covalen...A new organic/inorganic hybrid nonlinear optical (NLO) material was developed by the sol-gel process of an alkoxysilane dye with tetraethoxysilane. A NLO moiety based on 4-nitro-4 ' -hydroxy azobenzene was covalently bonded to the triethoxysilane derivative, i.e, gamma -isocyanatopropyl triethoxysilane. The preparation process and properties of the sol-gel derived NLO polymer were studied and characterized by SEM, FTIR,H-1-NMR, UV-Vis, DSC and second harmonic generation (SHG) measurement. The results indicated that the chemical bonding of the chromophores to the inorganic SiO2 networks induces low dipole alignment relaxation and preferable orientational stability. The SHG measurements also showed that the bonded polymer film containing 75 wt% of the akoxysilane dye has a high electro-optic coefficient (r(33)) of 7.1 pm/V at 1.1 mum wavelength, and exhibit good SHG stability, the r(33) values can maintain about 92.7% of its initial value at room temperature for 90 days, and can maintain about 59.3% at 100 degreesC for 300 min.展开更多
基金This work was supported by the Postdoctoral Science Foundation of Guangdong Province (No. 9644) and the Natural Science Fund of Guangdong Province(No. 990629).
文摘A new organic/inorganic hybrid nonlinear optical (NLO) material was developed by the sol-gel process of an alkoxysilane dye with tetraethoxysilane. A NLO moiety based on 4-nitro-4 ' -hydroxy azobenzene was covalently bonded to the triethoxysilane derivative, i.e, gamma -isocyanatopropyl triethoxysilane. The preparation process and properties of the sol-gel derived NLO polymer were studied and characterized by SEM, FTIR,H-1-NMR, UV-Vis, DSC and second harmonic generation (SHG) measurement. The results indicated that the chemical bonding of the chromophores to the inorganic SiO2 networks induces low dipole alignment relaxation and preferable orientational stability. The SHG measurements also showed that the bonded polymer film containing 75 wt% of the akoxysilane dye has a high electro-optic coefficient (r(33)) of 7.1 pm/V at 1.1 mum wavelength, and exhibit good SHG stability, the r(33) values can maintain about 92.7% of its initial value at room temperature for 90 days, and can maintain about 59.3% at 100 degreesC for 300 min.