The La0.8Mg0.2Ni2.4Mn0.10Co0.55Al0.10 alloy was prepared by induction melting. The structural and morphological characterizations were performed by means of X-ray powder diffraction （XRD） and scanning electron micro...The La0.8Mg0.2Ni2.4Mn0.10Co0.55Al0.10 alloy was prepared by induction melting. The structural and morphological characterizations were performed by means of X-ray powder diffraction （XRD） and scanning electron microscopy （SEM）. The electrochemical measurements were performed using LAND and CH/660b electrochemical workstation. The main phases of the alloy were LaNi5 and （La,Mg）Ni3. After annealing, the maximum discharge capacity, cycle stability and high rate dischargeability （HRD） were improved obviously. The maximum discharge capacity reached 373.80 mAh/g （T=1173 K）, the C100/Cmax（%） was 72.63% （T=1173 K）, and the value of HRD reached 51.8% at a discharge current density of 1150 mA/g （T=1173 K）. The cyclic voltammetry （CV） and potentiodynamic polarization were also studied.展开更多
基金the National Natural Science Foundation of China (50571046, 20573058, 50631020)TJNFS (07JCYBJC03500)+1 种基金863 Pro-gram (2007AA05Z149, 2007AA05Z108, 2006AA05Z110)SRF for ROCS
文摘The La0.8Mg0.2Ni2.4Mn0.10Co0.55Al0.10 alloy was prepared by induction melting. The structural and morphological characterizations were performed by means of X-ray powder diffraction （XRD） and scanning electron microscopy （SEM）. The electrochemical measurements were performed using LAND and CH/660b electrochemical workstation. The main phases of the alloy were LaNi5 and （La,Mg）Ni3. After annealing, the maximum discharge capacity, cycle stability and high rate dischargeability （HRD） were improved obviously. The maximum discharge capacity reached 373.80 mAh/g （T=1173 K）, the C100/Cmax（%） was 72.63% （T=1173 K）, and the value of HRD reached 51.8% at a discharge current density of 1150 mA/g （T=1173 K）. The cyclic voltammetry （CV） and potentiodynamic polarization were also studied.