Fiber products for microwave kilns were prepared using alumina fibers with alumina contents of 72 mass%and 80 mass%,and calcined alumina powder(4-6μm)as the main raw materials,silica sol as the binder,and cationic st...Fiber products for microwave kilns were prepared using alumina fibers with alumina contents of 72 mass%and 80 mass%,and calcined alumina powder(4-6μm)as the main raw materials,silica sol as the binder,and cationic starch as the flocculant.Effects of different raw materials and their additions on the wave transparency of fiber products were researched.The results show that as the alumina fiber(72%)addition increases,the heating rate of the samples first decreases and then increases,and the corresponding wave transparency of the sample first increases and then decreases.When the alumina fibers addition is 40 mass%and the alumina powder addition is 30 mass%,the prepared microwave kiln lining material has a higher mullite content,which improves the wave transparency of the sample.The sample prepared from alumina fibers with an alumina content of 80%has a suitable glass-mullite phase ratio,performs lower overall dielectric constant and good wave transparency,and is a suitable lining material for microwave kilns.展开更多
Long alumina fibers were prepared by sol-gel method.The spinning sol was obtained by mixing aluminum nitrate,tartaric acid,and polyvinylpyrrolidone with a mass ratio of 10∶3∶1.5.Thermogravimetry-differential scannin...Long alumina fibers were prepared by sol-gel method.The spinning sol was obtained by mixing aluminum nitrate,tartaric acid,and polyvinylpyrrolidone with a mass ratio of 10∶3∶1.5.Thermogravimetry-differential scanning calorimetry （TG-DSC）,Fourier transform infrared （FT-IR） spectra,X-ray diffraction （XRD）,and scanning electron microscopy （SEM） were used to characterize the properties of the gel and ceramic fibers.A little of α-Al2O3 phase is observed in the alumina precursor gel fibers sintered at 1273 K.The fibers with a uniform diameter can be obtained when sintered at 1473 K,and its main phase is also indentified as α-Al2O3.展开更多
The specimens were prepared with high alumina fiber accounting for 0. 5% , 10% or 15% by mass of the total amount of amorphous silica and high alumina fiber, using phenolic resin as binder, and extra-adding 0 or 0. 5%...The specimens were prepared with high alumina fiber accounting for 0. 5% , 10% or 15% by mass of the total amount of amorphous silica and high alumina fiber, using phenolic resin as binder, and extra-adding 0 or 0. 5% ZnO as sunscreen to cut the cost of SiO2 nanoporous insulation board. The hot volume stability and thermal conductivity （flat plate method ） of the specimens were tested and multi-Jimetion simulation equipment was used to study the thermal insulation performante. The results show that： （1） with high alumina fiber addition increasing, the linear shrinkage rate decreases, but thermal eonductivity changes a little; （2） adding ZnO can decrease thermal conductivity obviously; （3）for the specimen with ZnO and 15% of high alumina fiber, its cold face temperature hardly rises during the simulation experiment at 1 000 ℃ for 2 h, and the cold face temperature of the specimen with the smallest thickness of 2 cm doesn＇t exceed 180 ℃.展开更多
Long alumina .fibers with 60 cm in length were pre- pared by sol - gel method. The spinning sol was ob- tained by mixing aluminum nitrate, oxalic acid, and polyvinylpyrrolidone with a mass ratio of 10： 3： 2. Fourier...Long alumina .fibers with 60 cm in length were pre- pared by sol - gel method. The spinning sol was ob- tained by mixing aluminum nitrate, oxalic acid, and polyvinylpyrrolidone with a mass ratio of 10： 3： 2. Fourier transform infrared （ FTIR ） spectra, X-ray diffraction （XRD） , and scanning electron microscopy （SEM） were used to characterize the properties of the gel and ce- ramic fibers. The fibers with uniform diameter and smooth surface were obtained by sintering at 1 200℃ for 1 h, and their main phase was indentified as α-Al2O3.展开更多
The swung gel fibers were hea, ted to 400 ℃ at 0. .5 ,1, 1.5,2,2.5,3and4 ℃ min^-1 of heating rate, respectivel, and soaked.for 1 h ; then heated to 600 ℃ at 3 ℃ min ^-1 of.heating rate amt soaked for 1 h at last ...The swung gel fibers were hea, ted to 400 ℃ at 0. .5 ,1, 1.5,2,2.5,3and4 ℃ min^-1 of heating rate, respectivel, and soaked.for 1 h ; then heated to 600 ℃ at 3 ℃ min ^-1 of.heating rate amt soaked for 1 h at last calcined m 1 000, 1 100, 1 200, 1 300, and 1 400 ℃.for 1 h, respectively.展开更多
Al2O3(f)/TiAl composites were synthesized by an exothermic reaction method using Ti,Al and TiO2 powders doped with Nb2O5 and La2O3. The effect of Nb2O5 and La2O3 additives on the growth and morphology of the fibers, t...Al2O3(f)/TiAl composites were synthesized by an exothermic reaction method using Ti,Al and TiO2 powders doped with Nb2O5 and La2O3. The effect of Nb2O5 and La2O3 additives on the growth and morphology of the fibers, the phases and microstructure of the composites were investigated by means of XRD and SEM. The result indicates that the in situ alumina fiber can be developed in Ti-Al matrix with the Ti/Al mole ratio of 1:2-1:7, and the addition of rare earth powders can improve the dispersion of the fibers in the matrix and increase the length-to-diameter ratio of the fibers.展开更多
The morphology of the microstructure of Al-alloy composite with variousfiber contents was examined under optical microscope.The fracture of tension specimenwas studied under scanning electron microscope(SEM).The mecha...The morphology of the microstructure of Al-alloy composite with variousfiber contents was examined under optical microscope.The fracture of tension specimenwas studied under scanning electron microscope(SEM).The mechanical properties,wearresistance and coefficient of thermal linear expansion of the composite were measured.Theexperiment shows that the composite studied is suitable for engine pistons due to its goodwear resistance,higher elevated temperature mechanical properties and lower coefficient ofthermal linear expansion.展开更多
Among nitride fibers,aluminum nitride(AlN)fibers have been developed for various advanced applications due to their mechanical flexibility,high thermal conductivity,and excellent electrical insulation and chemical sta...Among nitride fibers,aluminum nitride(AlN)fibers have been developed for various advanced applications due to their mechanical flexibility,high thermal conductivity,and excellent electrical insulation and chemical stability.This article presents an overview on the recent progress of AlN fibers.The properties of AlN,particularly the thermal conductivity of AlN in polymer matrix composites are introduced.Afterward,two major approaches,carbothermal reduction and nitriding polycrystalline alumina fiber,for the preparation of AlN fibers are discussed.The carbothermal reduction includes electrospinning,solution blow spinning,and chemical vapor deposition.Furthermore,some perspectives on the future directions for the preparation and application of fibrous AlN are highlighted.This review is expected to provide readers with valuable guidance on the preparation of AlN fibers and inspire researchers to explore more potential applications.展开更多
The preparation and properties of ceramic short fiber reinforced Al-Si alloy matrix composite and it's application on the piston for internal combustion engines are presented. Alumina or aluminosilicatefiibers rei...The preparation and properties of ceramic short fiber reinforced Al-Si alloy matrix composite and it's application on the piston for internal combustion engines are presented. Alumina or aluminosilicatefiibers reinforced Al-Si alloy matrix composite has more excellent synthetical properties at elevated temperature than the matrix alloys. A partially reinforced Al-Si alloy matrix composite piston produced by squeeze casting technique has a firm interface between reinforced and unreinforced areas, low reject rate and good technical tolerance. As a new kind of piston material, it has been used for mass production of about 400,000 pieces of automobile engines piston. China has become one of a few countries in which aluminum alloy matrix composite materials have been used in automobile industry and attained industrialization.展开更多
MgO·Al 2O 3 spinel fibers may be obtained by thermal treatment of pressed specimens composed of Mg-Al-O materials with appropriate oxide-metal ratio at high temperature under controlled atmosphere. Their phase ...MgO·Al 2O 3 spinel fibers may be obtained by thermal treatment of pressed specimens composed of Mg-Al-O materials with appropriate oxide-metal ratio at high temperature under controlled atmosphere. Their phase composition and microstructure have been examined.展开更多
Porous polypropylene hollow fiber(PPHF) membranes are widely used in liquid purification. However, the hydrophobicity of polypropylene(PP) has limited its applications in water treatment. Herein, we demonstrate that, ...Porous polypropylene hollow fiber(PPHF) membranes are widely used in liquid purification. However, the hydrophobicity of polypropylene(PP) has limited its applications in water treatment. Herein, we demonstrate that, for the first time, atomic layer deposition(ALD) is an effective strategy to conveniently upgrade the filtration performances of PPHF membranes. The chemical and morphological changes of the deposited PPHF membranes are characterized by spectral, compositional, microscopic characterizations and protein adsorption measurements. Al_2O_3 is distributed along the cross section of the PP hollow fibers, with decreasing concentration from the outer surface to the inner surface. The pore size of the outer surface can be easily turned by altering the ALD cycles. Interestingly, the hollow fibers become much more ductile after deposition as their elongation at break is increased more than six times after deposition with 100 cycles. The deposited membranes show simultaneously enhanced water permeance and retention after deposition with moderate ALD cycle numbers.For instance, after 50 ALD cycles a 17% increase in water permeance and one-fold increase in BSA rejection are observed. Moreover, the PP membranes exhibit improved fouling-resistance after ALD deposition.展开更多
文摘Fiber products for microwave kilns were prepared using alumina fibers with alumina contents of 72 mass%and 80 mass%,and calcined alumina powder(4-6μm)as the main raw materials,silica sol as the binder,and cationic starch as the flocculant.Effects of different raw materials and their additions on the wave transparency of fiber products were researched.The results show that as the alumina fiber(72%)addition increases,the heating rate of the samples first decreases and then increases,and the corresponding wave transparency of the sample first increases and then decreases.When the alumina fibers addition is 40 mass%and the alumina powder addition is 30 mass%,the prepared microwave kiln lining material has a higher mullite content,which improves the wave transparency of the sample.The sample prepared from alumina fibers with an alumina content of 80%has a suitable glass-mullite phase ratio,performs lower overall dielectric constant and good wave transparency,and is a suitable lining material for microwave kilns.
基金supported by the Natural Science Foundation of Shaanxi Province,China (No.2010K10-21)
文摘Long alumina fibers were prepared by sol-gel method.The spinning sol was obtained by mixing aluminum nitrate,tartaric acid,and polyvinylpyrrolidone with a mass ratio of 10∶3∶1.5.Thermogravimetry-differential scanning calorimetry （TG-DSC）,Fourier transform infrared （FT-IR） spectra,X-ray diffraction （XRD）,and scanning electron microscopy （SEM） were used to characterize the properties of the gel and ceramic fibers.A little of α-Al2O3 phase is observed in the alumina precursor gel fibers sintered at 1273 K.The fibers with a uniform diameter can be obtained when sintered at 1473 K,and its main phase is also indentified as α-Al2O3.
基金support of the National Natural Science Foundation of China(No.51402265,51202225,and 51272240)
文摘The specimens were prepared with high alumina fiber accounting for 0. 5% , 10% or 15% by mass of the total amount of amorphous silica and high alumina fiber, using phenolic resin as binder, and extra-adding 0 or 0. 5% ZnO as sunscreen to cut the cost of SiO2 nanoporous insulation board. The hot volume stability and thermal conductivity （flat plate method ） of the specimens were tested and multi-Jimetion simulation equipment was used to study the thermal insulation performante. The results show that： （1） with high alumina fiber addition increasing, the linear shrinkage rate decreases, but thermal eonductivity changes a little; （2） adding ZnO can decrease thermal conductivity obviously; （3）for the specimen with ZnO and 15% of high alumina fiber, its cold face temperature hardly rises during the simulation experiment at 1 000 ℃ for 2 h, and the cold face temperature of the specimen with the smallest thickness of 2 cm doesn＇t exceed 180 ℃.
基金supported by the Natural Science Foundation of Shaanxi in China ( No. 2010K10 - 21)
文摘Long alumina .fibers with 60 cm in length were pre- pared by sol - gel method. The spinning sol was ob- tained by mixing aluminum nitrate, oxalic acid, and polyvinylpyrrolidone with a mass ratio of 10： 3： 2. Fourier transform infrared （ FTIR ） spectra, X-ray diffraction （XRD） , and scanning electron microscopy （SEM） were used to characterize the properties of the gel and ce- ramic fibers. The fibers with uniform diameter and smooth surface were obtained by sintering at 1 200℃ for 1 h, and their main phase was indentified as α-Al2O3.
文摘The swung gel fibers were hea, ted to 400 ℃ at 0. .5 ,1, 1.5,2,2.5,3and4 ℃ min^-1 of heating rate, respectivel, and soaked.for 1 h ; then heated to 600 ℃ at 3 ℃ min ^-1 of.heating rate amt soaked for 1 h at last calcined m 1 000, 1 100, 1 200, 1 300, and 1 400 ℃.for 1 h, respectively.
基金Projects(50432010 50372037) supported by the National Natural Science Foundation of China
文摘Al2O3(f)/TiAl composites were synthesized by an exothermic reaction method using Ti,Al and TiO2 powders doped with Nb2O5 and La2O3. The effect of Nb2O5 and La2O3 additives on the growth and morphology of the fibers, the phases and microstructure of the composites were investigated by means of XRD and SEM. The result indicates that the in situ alumina fiber can be developed in Ti-Al matrix with the Ti/Al mole ratio of 1:2-1:7, and the addition of rare earth powders can improve the dispersion of the fibers in the matrix and increase the length-to-diameter ratio of the fibers.
文摘The morphology of the microstructure of Al-alloy composite with variousfiber contents was examined under optical microscope.The fracture of tension specimenwas studied under scanning electron microscope(SEM).The mechanical properties,wearresistance and coefficient of thermal linear expansion of the composite were measured.Theexperiment shows that the composite studied is suitable for engine pistons due to its goodwear resistance,higher elevated temperature mechanical properties and lower coefficient ofthermal linear expansion.
基金National Natural Science Foundation of China(No.52173059)。
文摘Among nitride fibers,aluminum nitride(AlN)fibers have been developed for various advanced applications due to their mechanical flexibility,high thermal conductivity,and excellent electrical insulation and chemical stability.This article presents an overview on the recent progress of AlN fibers.The properties of AlN,particularly the thermal conductivity of AlN in polymer matrix composites are introduced.Afterward,two major approaches,carbothermal reduction and nitriding polycrystalline alumina fiber,for the preparation of AlN fibers are discussed.The carbothermal reduction includes electrospinning,solution blow spinning,and chemical vapor deposition.Furthermore,some perspectives on the future directions for the preparation and application of fibrous AlN are highlighted.This review is expected to provide readers with valuable guidance on the preparation of AlN fibers and inspire researchers to explore more potential applications.
文摘The preparation and properties of ceramic short fiber reinforced Al-Si alloy matrix composite and it's application on the piston for internal combustion engines are presented. Alumina or aluminosilicatefiibers reinforced Al-Si alloy matrix composite has more excellent synthetical properties at elevated temperature than the matrix alloys. A partially reinforced Al-Si alloy matrix composite piston produced by squeeze casting technique has a firm interface between reinforced and unreinforced areas, low reject rate and good technical tolerance. As a new kind of piston material, it has been used for mass production of about 400,000 pieces of automobile engines piston. China has become one of a few countries in which aluminum alloy matrix composite materials have been used in automobile industry and attained industrialization.
文摘MgO·Al 2O 3 spinel fibers may be obtained by thermal treatment of pressed specimens composed of Mg-Al-O materials with appropriate oxide-metal ratio at high temperature under controlled atmosphere. Their phase composition and microstructure have been examined.
基金Supported by the National Basic Research Program of China(2015CB655301)the Natural Science Foundation of Jiangsu Province(BK20150063)+1 种基金the Program of Excellent Innovation Teams of Jiangsu Higher Education Institutionsthe Project of Priority Academic Program Development of Jiangsu Higher Education Institutions(PAPD)
文摘Porous polypropylene hollow fiber(PPHF) membranes are widely used in liquid purification. However, the hydrophobicity of polypropylene(PP) has limited its applications in water treatment. Herein, we demonstrate that, for the first time, atomic layer deposition(ALD) is an effective strategy to conveniently upgrade the filtration performances of PPHF membranes. The chemical and morphological changes of the deposited PPHF membranes are characterized by spectral, compositional, microscopic characterizations and protein adsorption measurements. Al_2O_3 is distributed along the cross section of the PP hollow fibers, with decreasing concentration from the outer surface to the inner surface. The pore size of the outer surface can be easily turned by altering the ALD cycles. Interestingly, the hollow fibers become much more ductile after deposition as their elongation at break is increased more than six times after deposition with 100 cycles. The deposited membranes show simultaneously enhanced water permeance and retention after deposition with moderate ALD cycle numbers.For instance, after 50 ALD cycles a 17% increase in water permeance and one-fold increase in BSA rejection are observed. Moreover, the PP membranes exhibit improved fouling-resistance after ALD deposition.