Effect of SiO2 Micropowder Addition on Properties of Alumina-magnesia Based Wet Gunning Mix for Working Layer

The magnesia - alumina based wet gunning mix was prepared using tabular corundum aggregates,fused mag- nesia aggregates, tabular corundum micropowder, silica mieropowder and pure calcium ahuninate cement as the main starting materials. Effects of silica micropowder ad- ditions （0, 0. 2% , 0. 5% , 1.0% , 1.5% , 2. 0% , and 2.5%, by mass, the same hewinafier） on properties oJ the gunning mix were researched. The results show that when ttze silica micropowder addition is i. 0% -2. 0% , the gunning mix has good .flou,ability and pumpability. Adding 2.5% silica micropowder, the nepheline forms at 1 600 ℃, which will reduce the high. temperature proper- ties of ntagnesia -ahtmina wet gunning mix. The intro- duction qf silica micropowder has obvious effects on cold mechanical properties of the gunning mix. For the speci- tnens dried at 110 ℃ , the strength increases slightly with the silica micropowder addition increasing. For the specimens heat-treated at 1 600 ℃ for 3 h, the strength in- creases nutrkedlv with the silica micropowder addition in- creasing. When keeping the water addition and particle size di, stribution constant, the residual linear expansion rate qf the specimen with 1.5% of silica micropowder is the lowest, ltot modulus tf rupture at 1 450 ℃ .for 0. 5 h oJ the specimens decreases gradually with the increase of silica fame addition. A small amount of silica micropow- der is beneficial for the slag penetration resistance.

SiO_2微粉加入量对铝镁质湿法喷补料性能的影响

为改善铝镁质喷补料的施工流动性,以72%(w)的板状刚玉,6%(w)的电熔镁砂,以及总量为22%(w)的氧化铝微粉、板状刚玉微粉和纯铝酸钙水泥制备了铝镁质湿法喷补料,并研究了SiO_2微粉加入量(外加质量分数分别为0、0.2%、0.5%、1.0%、1.5%、2.0%和2.5%)对其性能的影响。结果表明:1)当SiO_2微粉加入量为1%~2%(w)时,喷补料具有较好的流动性和泵送性能;2)添加2.5%(w)SiO_2微粉的试样经1 600℃热处理后生成少量霞石,将会降低材料的高温性能;3)110℃烘干后试样的强度随SiO_2微粉加入量的增加而升高,1 600℃处理后的试样强度随SiO_2微粉的增加而显著增大;4)当SiO_2微粉加入量为1.5%(w)时,试样1 600℃烧后的线膨胀率最小;5)试样的高温抗折强度随着SiO_2微粉加入量的增加逐渐下降,少量SiO_2微粉的加入对抗渣渗透有利。综合考虑,铝镁质湿法喷补料中SiO_2微粉加入1.5%(w)最佳。