The inhibitive action of CaSO_4 towards corrosion of aluminium in 1 mol/L HCl has been inveetigated by using fluorometrio and weight loss techniques.The results show that the inhibitor exhibits an outstanding function...The inhibitive action of CaSO_4 towards corrosion of aluminium in 1 mol/L HCl has been inveetigated by using fluorometrio and weight loss techniques.The results show that the inhibitor exhibits an outstanding function of inhibition,especially at higher tempe- ratures,and it was found to be predomiantly of cathodic rate control.Ths mechanism of inhibition and the effect of CdSO_4 on the corrosion kinetics are also discussed.展开更多
The coarse blocky compounds in the as-cast 7075 aluminium alloys containing rare earth elements, neodymium, cerium or mischmetal were investigated by means of transmission electron microscope with EDX and scanning ele...The coarse blocky compounds in the as-cast 7075 aluminium alloys containing rare earth elements, neodymium, cerium or mischmetal were investigated by means of transmission electron microscope with EDX and scanning electron microscope. The blocky compounds in these alloys were identified as rare earth compounds, (Cr, Ti)2 RE (Al, X)20 (X is magnesium, copper and zinc),body-centred cubic, with 184 atoms to the unit cell , lattice parameter 1.453￣1. 458 nm, Vickers hardness 4000￣5600 MPa and calculated density 3400 kg/m3. The results show that the amount of blocky compounds in the alloys decreases with decreasing of Ti and Cr content or with increasing of cooling rate during solidification.展开更多
文摘The inhibitive action of CaSO_4 towards corrosion of aluminium in 1 mol/L HCl has been inveetigated by using fluorometrio and weight loss techniques.The results show that the inhibitor exhibits an outstanding function of inhibition,especially at higher tempe- ratures,and it was found to be predomiantly of cathodic rate control.Ths mechanism of inhibition and the effect of CdSO_4 on the corrosion kinetics are also discussed.
文摘The coarse blocky compounds in the as-cast 7075 aluminium alloys containing rare earth elements, neodymium, cerium or mischmetal were investigated by means of transmission electron microscope with EDX and scanning electron microscope. The blocky compounds in these alloys were identified as rare earth compounds, (Cr, Ti)2 RE (Al, X)20 (X is magnesium, copper and zinc),body-centred cubic, with 184 atoms to the unit cell , lattice parameter 1.453￣1. 458 nm, Vickers hardness 4000￣5600 MPa and calculated density 3400 kg/m3. The results show that the amount of blocky compounds in the alloys decreases with decreasing of Ti and Cr content or with increasing of cooling rate during solidification.