An optical sensing system was constructed to study the coating when joining ahtminium alloy to zinc-coated steel by MIG welding-brazing process. The results showed that the coating fused to form a liquid zinc film on ...An optical sensing system was constructed to study the coating when joining ahtminium alloy to zinc-coated steel by MIG welding-brazing process. The results showed that the coating fused to form a liquid zinc film on surface during process. The Al-Si filler metal reacted with the liquid zinc film to improve the spreadability of filler metal and thus a new method was established to join aluminium alloy and uncoated steel by depositing a mixed layer on steel surface.展开更多
从材料保护的角度出发,在分析了Nd Fe B永磁材料的氢脆过程及氢脆的特点后,用RF磁控溅射制备一定厚度的Al薄膜并在一定条件下进行氧化处理,得到了Al+Al2O3复合涂层。用SEM和XRD分析了涂层形貌和组成,并用高压气相充氢的方式测试了涂层...从材料保护的角度出发,在分析了Nd Fe B永磁材料的氢脆过程及氢脆的特点后,用RF磁控溅射制备一定厚度的Al薄膜并在一定条件下进行氧化处理,得到了Al+Al2O3复合涂层。用SEM和XRD分析了涂层形貌和组成,并用高压气相充氢的方式测试了涂层的阻氢性能。研究表明,厚度为8.0μm复合涂层的阻氢性能为:在10MPa的H2环境中(25℃),阻氢时间达65min,且对磁体的磁性能无不良影响。展开更多
After analyzing the phenomena and processes of hydrogen embrittlement of NdFeB permanent magnets, RF magnetron sputtering was used to fabricate Al thin films and then oxidized to form the Al/Al_2O_3 composite films on...After analyzing the phenomena and processes of hydrogen embrittlement of NdFeB permanent magnets, RF magnetron sputtering was used to fabricate Al thin films and then oxidized to form the Al/Al_2O_3 composite films on the magnets as the hydrogen resistance coatings. SEM and EDS were used to examine the morphology and composition respectively. Hydrogen resistance performance was tested by exposing the magnets in 10 MPa hydrogen gas at room temperature. The results show that the magnets with 8 μm Al/Al_2O_3 coatings can withstand hydrogen of 10 MPa for 65 min without being embrittled into powder. The samples with and without hydrogen resistance coatings have almost the same magnetic properties.展开更多
基金Acknowledgements The research was sponsored by Project 50905045 supported by the National Natural Science Foundation of China and State Key Laboratory of Advanced Welding and Joining, Harbin Institute of Technology.
文摘An optical sensing system was constructed to study the coating when joining ahtminium alloy to zinc-coated steel by MIG welding-brazing process. The results showed that the coating fused to form a liquid zinc film on surface during process. The Al-Si filler metal reacted with the liquid zinc film to improve the spreadability of filler metal and thus a new method was established to join aluminium alloy and uncoated steel by depositing a mixed layer on steel surface.
文摘从材料保护的角度出发,在分析了Nd Fe B永磁材料的氢脆过程及氢脆的特点后,用RF磁控溅射制备一定厚度的Al薄膜并在一定条件下进行氧化处理,得到了Al+Al2O3复合涂层。用SEM和XRD分析了涂层形貌和组成,并用高压气相充氢的方式测试了涂层的阻氢性能。研究表明,厚度为8.0μm复合涂层的阻氢性能为:在10MPa的H2环境中(25℃),阻氢时间达65min,且对磁体的磁性能无不良影响。
文摘After analyzing the phenomena and processes of hydrogen embrittlement of NdFeB permanent magnets, RF magnetron sputtering was used to fabricate Al thin films and then oxidized to form the Al/Al_2O_3 composite films on the magnets as the hydrogen resistance coatings. SEM and EDS were used to examine the morphology and composition respectively. Hydrogen resistance performance was tested by exposing the magnets in 10 MPa hydrogen gas at room temperature. The results show that the magnets with 8 μm Al/Al_2O_3 coatings can withstand hydrogen of 10 MPa for 65 min without being embrittled into powder. The samples with and without hydrogen resistance coatings have almost the same magnetic properties.