Aluminizing coating and aluminizing-dispersed Y 2O 3 composite coating were prepared on 20 steel specimens by pulsed spark technique, which exhibited a micro-crystallized structure with grain size in the range of se...Aluminizing coating and aluminizing-dispersed Y 2O 3 composite coating were prepared on 20 steel specimens by pulsed spark technique, which exhibited a micro-crystallized structure with grain size in the range of several ten to several hundred nanometers. It is shown that, after oxidation at 600 ℃ in air for 100 h, these two kinds of coatings have excellent resistance to high temperature oxidation and scale spallation, and the aluminizing-dispersed Y 2O 3 composite coating has even better property than the aluminizing coating. AFM, SEM, EDS and XRD were applied to analyze the surface morphology, composition and phases structure of these coatings and the oxide scale formed in oxidation. The mechanism for these coatings that how to enhance the oxidation resistance and scale spallation resistance was discussed by considering the factors, such as Al concentration on the selective oxidation of Fe-Al alloy, the effect of micro-crystallization, reactive element effect (REE) caused by dispersed Y 2O 3, etc.展开更多
A Cr-modified aluminide coating is prepared on a Ni-based superalloy using arc ion plating and subsequent pack cementation aluminizing.Hot corrosion behavior of the Cr-modified aluminide coating exposed to molten Na2S...A Cr-modified aluminide coating is prepared on a Ni-based superalloy using arc ion plating and subsequent pack cementation aluminizing.Hot corrosion behavior of the Cr-modified aluminide coating exposed to molten Na2SO4/K2SO4（3：1） or Na2SO4/NaCl（3：1） salts at 900 °C in static air are evaluated as well as the aluminide coating.The results indicate that compared with the aluminide coating,the anti-corrosion properties of the Cr-modified aluminide coating in the both salts are improved,which should be attributed to the beneficial effect of the Cr in the coating.The corrosion mechanism of the Cr-modified aluminide coating,especially the role of Cr in the mixture salt corrosion,is discussed.展开更多
文摘Aluminizing coating and aluminizing-dispersed Y 2O 3 composite coating were prepared on 20 steel specimens by pulsed spark technique, which exhibited a micro-crystallized structure with grain size in the range of several ten to several hundred nanometers. It is shown that, after oxidation at 600 ℃ in air for 100 h, these two kinds of coatings have excellent resistance to high temperature oxidation and scale spallation, and the aluminizing-dispersed Y 2O 3 composite coating has even better property than the aluminizing coating. AFM, SEM, EDS and XRD were applied to analyze the surface morphology, composition and phases structure of these coatings and the oxide scale formed in oxidation. The mechanism for these coatings that how to enhance the oxidation resistance and scale spallation resistance was discussed by considering the factors, such as Al concentration on the selective oxidation of Fe-Al alloy, the effect of micro-crystallization, reactive element effect (REE) caused by dispersed Y 2O 3, etc.
基金financially supported by the National Natural Science Foundation of China (No.51001106)National Basic Research Program of China (No.2012CB625100)
文摘A Cr-modified aluminide coating is prepared on a Ni-based superalloy using arc ion plating and subsequent pack cementation aluminizing.Hot corrosion behavior of the Cr-modified aluminide coating exposed to molten Na2SO4/K2SO4（3：1） or Na2SO4/NaCl（3：1） salts at 900 °C in static air are evaluated as well as the aluminide coating.The results indicate that compared with the aluminide coating,the anti-corrosion properties of the Cr-modified aluminide coating in the both salts are improved,which should be attributed to the beneficial effect of the Cr in the coating.The corrosion mechanism of the Cr-modified aluminide coating,especially the role of Cr in the mixture salt corrosion,is discussed.