The effects of the addition of rare earth （RE） elements on the void band in the diffusion layer, and the re sistances to both oxidation and spalling of aluminized steel were investigated through high temperature oxi...The effects of the addition of rare earth （RE） elements on the void band in the diffusion layer, and the re sistances to both oxidation and spalling of aluminized steel were investigated through high temperature oxidation and spalling tests. The results showed that RE had significant effects on the void band in the diffusion layer and the properties of aluminized steel. After diffusion treatment, a considerable number of the voids between the middle layer and transitional layer of pure aluminized coating, aggregated into wavy-line-shaped void bands parallel to the outer surface. For the RE added aluminized coating, only a few voids aggregated into intermittent block shapes. During high temperature oxidation at 800 ℃ for 200 h, the wavy void band of pure aluminized coating aggregated further into a linear crack parallel to the outer surface, and the internal oxidation occurred within them; the open cracks perpendicular to the surface penetrated through the diffusion layer. For the RE added aluminized coating, only a few voids aggregated into intermittent meniscus shapes. During cyclic spalling tests, the peeling, spallation, and pulver ulent cracking occurred along the void band in the diffusion layer of pure aluminized coating, but only a little spallation occurred in the diffusion layer of the RE-added aluminized coating, in which cracks perpendicular to the surface were much smaller than those of pure aluminized coating and did not penetrate through the diffusion layer. It is evident that RE addition can restrain the formation and aggregation of voids and subsequently improve the resistances to oxidation and spalling. The mechanism of the RE effect on the void band in the diffusion layer is also discussed.展开更多
Hot-dip aluminizing（HDA） is a proven surface coating technique for improving the oxidation and corrosion resistance of ferrous substrates. Although extensive studies on the HDA of plain carbon steels have been repor...Hot-dip aluminizing（HDA） is a proven surface coating technique for improving the oxidation and corrosion resistance of ferrous substrates. Although extensive studies on the HDA of plain carbon steels have been reported, studies on the HDA of stainless steels are limited. Because of the technological importance of stainless steels in high-temperature applications, studies of their microstructural development during HDA are needed. In the present investigation, the HDA of AISI 321 stainless steel was carried out in a pure Al bath. The microstructural features of the coating were studied using scanning electron microscopy and transmission electron microscopy. These studies revealed that the coating consists of two regions： an Al top coat and an aluminide layer at the interface between the steel and Al. The Al top coat was found to consist of intermetallic phases such as Al_7Cr and Al_3Fe dispersed in an Al matrix. Twinning was observed in both the Al_7Cr and the Al_3Fe phases. Furthermore, the aluminide layer comprised a mixture of nanocrystalline Fe_2Al_5, Al_7Cr, and Al. Details of the microstructural features are presented, and their formation mechanisms are discussed.展开更多
基金Item Sponsored by Key Science and Technology Plan Foundation of Henan of China (0423023500) and Natural ScienceFoundation of Henan Province (0511021600)
文摘The effects of the addition of rare earth （RE） elements on the void band in the diffusion layer, and the re sistances to both oxidation and spalling of aluminized steel were investigated through high temperature oxidation and spalling tests. The results showed that RE had significant effects on the void band in the diffusion layer and the properties of aluminized steel. After diffusion treatment, a considerable number of the voids between the middle layer and transitional layer of pure aluminized coating, aggregated into wavy-line-shaped void bands parallel to the outer surface. For the RE added aluminized coating, only a few voids aggregated into intermittent block shapes. During high temperature oxidation at 800 ℃ for 200 h, the wavy void band of pure aluminized coating aggregated further into a linear crack parallel to the outer surface, and the internal oxidation occurred within them; the open cracks perpendicular to the surface penetrated through the diffusion layer. For the RE added aluminized coating, only a few voids aggregated into intermittent meniscus shapes. During cyclic spalling tests, the peeling, spallation, and pulver ulent cracking occurred along the void band in the diffusion layer of pure aluminized coating, but only a little spallation occurred in the diffusion layer of the RE-added aluminized coating, in which cracks perpendicular to the surface were much smaller than those of pure aluminized coating and did not penetrate through the diffusion layer. It is evident that RE addition can restrain the formation and aggregation of voids and subsequently improve the resistances to oxidation and spalling. The mechanism of the RE effect on the void band in the diffusion layer is also discussed.
文摘Hot-dip aluminizing（HDA） is a proven surface coating technique for improving the oxidation and corrosion resistance of ferrous substrates. Although extensive studies on the HDA of plain carbon steels have been reported, studies on the HDA of stainless steels are limited. Because of the technological importance of stainless steels in high-temperature applications, studies of their microstructural development during HDA are needed. In the present investigation, the HDA of AISI 321 stainless steel was carried out in a pure Al bath. The microstructural features of the coating were studied using scanning electron microscopy and transmission electron microscopy. These studies revealed that the coating consists of two regions： an Al top coat and an aluminide layer at the interface between the steel and Al. The Al top coat was found to consist of intermetallic phases such as Al_7Cr and Al_3Fe dispersed in an Al matrix. Twinning was observed in both the Al_7Cr and the Al_3Fe phases. Furthermore, the aluminide layer comprised a mixture of nanocrystalline Fe_2Al_5, Al_7Cr, and Al. Details of the microstructural features are presented, and their formation mechanisms are discussed.