Dissimilar metal joining between 5A02 aluminum alloy and H62 brass sheets was conducted by gas tungsten arc welding with Zn-15% Al and Al-12% Si flux-cored filler wires. The microstructure in the weld and distribution...Dissimilar metal joining between 5A02 aluminum alloy and H62 brass sheets was conducted by gas tungsten arc welding with Zn-15% Al and Al-12% Si flux-cored filler wires. The microstructure in the weld and distribution of major alloying elements in the intelfacial layer were examined, and the tensile strength of the resultant joints was measured. Pores appeared in the weld made with Zn-15% Al flax-cored filler wire, the interracial layer mainly consisted of AlCu phase, and the specimens fractured through the weld with tensile strength of 129 MPa. When Al-12% Si flux-cored filler wire was used, Cu diffused into the weld and Al2 Cu phase formed, and the specimens fractured along the interfacial layer with tensile strength of 122 MPa.展开更多
基金Acknowledgements This work was financially supported by the National Natural Science Foundation of China （ Grant No. 50904012 ） and Natural Science Foundation of Liaoning Province （Grant No. 20092152）.
文摘Dissimilar metal joining between 5A02 aluminum alloy and H62 brass sheets was conducted by gas tungsten arc welding with Zn-15% Al and Al-12% Si flux-cored filler wires. The microstructure in the weld and distribution of major alloying elements in the intelfacial layer were examined, and the tensile strength of the resultant joints was measured. Pores appeared in the weld made with Zn-15% Al flax-cored filler wire, the interracial layer mainly consisted of AlCu phase, and the specimens fractured through the weld with tensile strength of 129 MPa. When Al-12% Si flux-cored filler wire was used, Cu diffused into the weld and Al2 Cu phase formed, and the specimens fractured along the interfacial layer with tensile strength of 122 MPa.