Influence of aluminum addition on the structures and properties of SiO_2-B_2O_3-Al_2O_3-CaO vitrified bond at low sintering temperature and high strength was discussed. FTIR and XRD analyses were used to characterize ...Influence of aluminum addition on the structures and properties of SiO_2-B_2O_3-Al_2O_3-CaO vitrified bond at low sintering temperature and high strength was discussed. FTIR and XRD analyses were used to characterize the structures of the basic vitrified bond with different contents of aluminum. The bending strength and the thermal expansion coefficients were also tested. Meanwhile, the microstructures of composite specimens at sintering temperature of 660 ℃ were observed by scanning electron microscope（SEM）. The experimental results showed that the properties of vitrified bond with 1wt% aluminum were improved significantly, where the bending strength, Rockwell hardness, and thermal expansion coefficient of the vitrified bond reached 132 MPa, 63 HRB, and 6.73×10^（-6） ℃^（-1）, respectively.展开更多
To investigate the differences and the development trends of the 400 kA aluminum reduction cell, four representative cells were deeply analyzed. By using numerical simulation methods in ANSYS software, the structure p...To investigate the differences and the development trends of the 400 kA aluminum reduction cell, four representative cells were deeply analyzed. By using numerical simulation methods in ANSYS software, the structure parameters were firstly compared, and then three-dimensional models of electric-magnetic-flow field were built and solved with finite element method(FEM). The comparison of the structures reveals that the cell bodies are similar while the current flow path and distribution ratio of bus bars are different. It appears that most of the current(70%-80%) in side A are used as the magnetic field compensation current and flow through two ends. The numerical simulation results indicate that the distributions of magnetic fields are different but all satisfy with the magnetohydrodynamics(MHD) stabilization, and the flow patterns are all two or multi vortexes with appropriate velocities. The comparison shows that all studied cells can satisfy with the physical field requirement, and the commercial applications also verify that the 400 kA cells have become the product of the mature and world's leading technology.展开更多
Substrate, a typical ultra-slender aluminum alloy structural components with a large aspect ratio and complex internal structure, was traditionally manufactured by re-assembly and sub-welding. In order to realize the ...Substrate, a typical ultra-slender aluminum alloy structural components with a large aspect ratio and complex internal structure, was traditionally manufactured by re-assembly and sub-welding. In order to realize the monoblock casting of the substrate, the Pro/E software was utilized to carry out three-dimensional(3D) modeling of the substrate casting, and the filling and solidification processes were calculated, as well as the location and types of casting defects were predicted by the casting simulation software Anycasting. Results of the filling process simulation show that the metal liquid is distributed into each gap runner evenly and smoothly. There is no serious vortex phenomenon in the mold cavity, and the trajectory of the virtual particles is clear. Results of the solidification process simulation show that shrinkage cavities mainly appear at the junction of gap runners and the rail surface of the substrate. The average deformation is 0.6 mm in X direction, 3.8 mm in Y direction, and 8.2 mm in Z direction. Based on the simulation results, the casting process of the substrate was optimized, and qualified castings were successfully produced, which will provide a reference for the casting process design of other ultraslender aluminum alloy structural components.展开更多
基金Funded by the National“Twelfth Five-Year”Plan for Science&Technology Support of China(2012BAA08B00)
文摘Influence of aluminum addition on the structures and properties of SiO_2-B_2O_3-Al_2O_3-CaO vitrified bond at low sintering temperature and high strength was discussed. FTIR and XRD analyses were used to characterize the structures of the basic vitrified bond with different contents of aluminum. The bending strength and the thermal expansion coefficients were also tested. Meanwhile, the microstructures of composite specimens at sintering temperature of 660 ℃ were observed by scanning electron microscope（SEM）. The experimental results showed that the properties of vitrified bond with 1wt% aluminum were improved significantly, where the bending strength, Rockwell hardness, and thermal expansion coefficient of the vitrified bond reached 132 MPa, 63 HRB, and 6.73×10^（-6） ℃^（-1）, respectively.
基金Projects(51104187,51274241,61321003) supported by the National Natural Science Foundation of ChinaProject(20100162120008) supported by Doctoral Fund of Ministry of Education of China
文摘To investigate the differences and the development trends of the 400 kA aluminum reduction cell, four representative cells were deeply analyzed. By using numerical simulation methods in ANSYS software, the structure parameters were firstly compared, and then three-dimensional models of electric-magnetic-flow field were built and solved with finite element method(FEM). The comparison of the structures reveals that the cell bodies are similar while the current flow path and distribution ratio of bus bars are different. It appears that most of the current(70%-80%) in side A are used as the magnetic field compensation current and flow through two ends. The numerical simulation results indicate that the distributions of magnetic fields are different but all satisfy with the magnetohydrodynamics(MHD) stabilization, and the flow patterns are all two or multi vortexes with appropriate velocities. The comparison shows that all studied cells can satisfy with the physical field requirement, and the commercial applications also verify that the 400 kA cells have become the product of the mature and world's leading technology.
文摘Substrate, a typical ultra-slender aluminum alloy structural components with a large aspect ratio and complex internal structure, was traditionally manufactured by re-assembly and sub-welding. In order to realize the monoblock casting of the substrate, the Pro/E software was utilized to carry out three-dimensional(3D) modeling of the substrate casting, and the filling and solidification processes were calculated, as well as the location and types of casting defects were predicted by the casting simulation software Anycasting. Results of the filling process simulation show that the metal liquid is distributed into each gap runner evenly and smoothly. There is no serious vortex phenomenon in the mold cavity, and the trajectory of the virtual particles is clear. Results of the solidification process simulation show that shrinkage cavities mainly appear at the junction of gap runners and the rail surface of the substrate. The average deformation is 0.6 mm in X direction, 3.8 mm in Y direction, and 8.2 mm in Z direction. Based on the simulation results, the casting process of the substrate was optimized, and qualified castings were successfully produced, which will provide a reference for the casting process design of other ultraslender aluminum alloy structural components.