Key technology and application of AB_(2) hydrogen storage alloy in fuel cell hydrogen supply system

At present,there is limited research on the application of fuel cell power generation system technology using solid hydrogen storage materials,especially in hydrogen-assisted two-wheelers.Considering the disadvantages of low hydrogen storage capacity and poor kinetics of hydrogen storage materials,our primary focus is to achieve smooth hydrogen ab-/desorption over a wide temperature range to meet the requirements of fuel cells and their integrated power generation systems.In this paper,the Ti_(0.9)Zr_(0.1)Mn_(1.45)V_(0.4)Fe_(0.15) hydrogen storage alloy was successfully prepared by arc melting.The maximum hydrogen storage capacity reaches 1.89 wt% at 318 K.The alloy has the capability to absorb 90% of hydrogen storage capacity within 50 s at 7 MPa and release 90% of hydrogen within 220 s.Comsol Multiphysics 6.0 software was used to simulate the hydrogen ab-/desorption processes of the tank.The flow rate of cooling water during hydrogen absorption varied in a gradient of(0.02 t x)m s^(-1)(x=0,0.02,0.04,0.06,0.08,0.1,0.12).Cooling water flow rate is positively correlated with the hydrogen absorption rate but negatively correlated with the cost.When the cooling rate is 0.06 m s^(-1),both simulation and experimentation have shown that the hydrogen storage tank is capable of steady hydrogen desorption for over 6 h at a flow rate of 2 L min^(-1).Based on the above conclusions,we have successfully developed a hydrogen-assisted two-wheeler with a range of 80 km and achieved regional demonstration operations in Changzhou and Shaoguan.This paper highlights the achievements of our team in the technological development of fuel cell power generation systems using solid hydrogen storage materials as hydrogen storage carriers and their application in twowheelers in recent years.

Properties of Ti-Based Hydrogen Storage Alloy

An efficient and safe hydrogen storage method is one of the important links for the large-scale development of hydrogen in the future. Because of its low price and simple design, Ti-based hydrogen storage alloys are considered to be suitable for practical applications. In this paper, we review the latest research on Ti-based hydrogen storage alloys. Firstly, the machine learning and density functional theory are introduced to provide theoretical guidance for the optimization of Ti-based hydrogen storage alloys. Then, in order to improve the hydrogen storage performance, we briefly introduce the research of AB type and AB2 type Ti-based alloys, focusing on doping elements and adaptive after treatment. Finally, suggestions for the future research and development of Ti-based hydrogen storage alloys are proposed. .

Editorial for the special issue“Hydrogen Energy Production,Storage and Utilization”

Hydrogen energy has emerged as a significant energy source for accomplishing energy transformation and achieving carbon neutrality.Hydrogen production,storage and transportation are the key technologies to realize hydrogen energy application and carbon neutralization goal.Apart from the mature technologies of fossil fuel reforming and water electrolysis,new hydrogen production methods(such as solar photolysis,biomass conversion,thermochemical circulation,etc.)have garnered widespread attention and research interest.The lack of safe and efficient hydrogen storage and utilization technology for hydrogen fuel cell systems is the major obstacle to achieving hydrogen economy.In the past decades,global researchers have conducted extensive studies on enhancing the hydrogen storage performance of materials,such as alloy,metal hydride,complex hydride,carbon-based materials,etc.,as well as the technological development of fuel cell power generation systems using solid hydrogen storage materials as hydrogen storage carriers.The themed issue entitled“Hydrogen Energy Production,Storage and Utilization”includes 10 carefully selected papers that address the most recent developments in hydrogen production and storage materials,involving catalyst design,structure characterization,hydrogen ab-/desorption performance and mechanism,and fuel cell coupling system exploit.

A review of classical hydrogen isotopes storage materials

Hydrogen storage alloys(HSAs)are attracting widespread interest in the nuclear industry because of the generation of stable metal hydrides after tritium absorption,thus effectively preventing the leakage of radioactive tritium.Commonly used HSAs in the hydrogen isotopes field are Zr2M(M=Co,Ni,Fe)alloys,metallic Pd,depleted U,and ZrCo alloy.Specifically,Zr2M(M=Co,Ni,Fe)alloys are considered promising tritium-getter materials,and metallic Pd is utilized to separate and purify hydrogen isotopes.Furthermore,depleted U and ZrCo alloy are well suited for storing and delivering hydrogen isotopes.Notably,all the aforementioned HSAs need to modulate their hydrogen storage properties for complex operating conditions.In this review,we present a comprehensive overview of the reported modification methods applied to the above alloys.Alloying is an effective amelioration method that mainly modulates the properties of HSAs by altering their local geometrical/electronic structures.Besides,microstructural modifications such as nano-sizing and nanopores have been used to increase the specific surface area and active sites of metallic Pd and ZrCo alloys for enhancing de-/hydrogenation kinetics.The combination of metallic Pd with support materials can significantly reduce the cost and enhance the pulverization resistance.Moreover,the poisoning resistance of ZrCo alloy is improved by constructing active surfaces with selective permeability.Overall,the review is constructive for better understanding the properties and mechanisms of hydrogen isotope storage alloys and provides effective guidance for future modification research.

Combined “Gateway” and “Spillover” effects originated from a CeNi_(5) alloy catalyst for hydrogen storage of MgH_(2)

Efficient catalysts enable MgH2 with superior hydrogen storage performance.Herein,we successfully synthesized a catalyst composed of Ce and Ni (i.e.CeNi_(5) alloy) with splendid catalytic action for boosting the hydrogen storage property of magnesium hydride (MgH_(2))The MgH2–5wt%CeNi_(5) composite’s initial hydrogen release temperature was reduced to 174℃ and approximately 6.4wt%H_(2) was released at 275℃ within 10 min.Besides,the dehydrogenation enthalpy of MgH_(2) was slightly decreased by adding CeNi_(5).For hydrogenation,the fully dehydrogenated sample absorbed 4.8wt%H_(2) at a low temperature of 175℃.The hydrogenation apparent activation energy was decreased from(73.60±1.79) to (46.12±7.33) kJ/mol.Microstructure analysis revealed that Mg_(2)Ni/Mg_(2)NiH_(4) and CeH_(2.73) were formed during the process of hydrogen absorption and desorption,exerted combined“Gateway”and“Spillover”effects to reduce the operating temperature and improve the hydrogen storage kinetics of MgH_(2).Our work provides an example of merging“Gateway”and“Spillover”effects in one catalyst and may shed light on designing novel highly-effective catalysts for MgH_(2) in near future.

FeCoNiCrMo high entropy alloy nanosheets catalyzed magnesium hydride for solid-state hydrogen storage

The catalytic effect of FeCoNiCrMo high entropy alloy nanosheets on the hydrogen storage performance of magnesium hydride(MgH_(2))was investigated for the first time in this paper.Experimental results demonstrated that 9wt%FeCoNiCrMo doped MgH_(2)started to dehydrogenate at 200℃and discharged up to 5.89wt%hydrogen within 60 min at 325℃.The fully dehydrogenated composite could absorb3.23wt%hydrogen in 50 min at a temperature as low as 100℃.The calculated de/hydrogenation activation energy values decreased by44.21%/55.22%compared with MgH_(2),respectively.Moreover,the composite’s hydrogen capacity dropped only 0.28wt%after 20 cycles,demonstrating remarkable cycling stability.The microstructure analysis verified that the five elements,Fe,Co,Ni,Cr,and Mo,remained stable in the form of high entropy alloy during the cycling process,and synergistically serving as a catalytic union to boost the de/hydrogenation reactions of MgH_(2).Besides,the FeCoNiCrMo nanosheets had close contact with MgH_(2),providing numerous non-homogeneous activation sites and diffusion channels for the rapid transfer of hydrogen,thus obtaining a superior catalytic effect.

A novel method towards improving the hydrogen storage properties of hypoeutectic Mg-Ni alloy via ultrasonic treatment

Ultrasonic treatment has great contributions on modifying the morphology,dimension and distribution of constituent phases during solidification,which serve as dominate factors influencing the hydrogen storage performance of Mg-based alloys.In this research,ultrasonic treatment is utilized as a novel method to enhance the de-/hydriding properties of Mg-2Ni(at.%)alloy.Due to ultrasonic treatment,the microstructure of as-cast alloy is significantly refined and homogenized.Ascribing to the increased eutectic boundaries and shortened distance insideα-Mg for hydrogen atoms diffusion,the hydrogen uptake capacities and isothermal de-/hydriding rates improve effectively,especially at lower temperature.The peak desorption temperature reduces from 392.99°C to 345.56°C,and the dehydriding activation energy decreases from 101.93 k J mol^(-1)to 88.65 k J mol^(-1).Weakened hysteresis of plateau pressures and slightly optimized thermodynamics are determined from the pressure-composition isotherms.Owing to the refined primary Mg,a larger amount of hydrogen with the higher hydriding proportion is absorbed in the first stage when hydrides nucleate in eutectic region and grow on primary Mg periphery subsequently before MgH2colonies impinging,resulting in the enhancement of hydrogenation rates and capacities.

Effects of annealing treatment on the microstructure and electrochemical properties of low-Co hydrogen storage alloys containing Cu and Fe

The effects of annealing treatment on the microstructure and electrochemical properties of low-Co LaNi 3.55 Mn 0.35 Co 0.20 Al 0.20 Cu 0.75 Fe 0.10 hydrogen storage alloys were investigated. X-ray diffraction （XRD） analysis indicated that annealing treatment remarkably reduced the lattice strain and defects, and increased the unit-cell volume. The optical microscope analysis showed that the as-cast alloy had a crass dendrite microstructure with noticeable composition segregation, which gradually disappeared with increasing annealing temperature, and the micro-structure changed to an equiaxed structure after annealing the alloy at 1233 K. The electrochemical tests indicated that the annealed alloys demonstrated much better cycling stability compared with the as-cast one. The capacity retention at the 100th cycle increased from 90.0% （as-cast） to 94.7% （1273 K）. The annealing treatment also improved the discharge capacity. However, the high rate dischargeability （HRD） value of the annealed alloy slightly dropped, which was believed to be ascribed to the decreased exchange current density and the hydrogen diffusion coefficient in alloy bulk.

Study on Nanocrystalline Rare Earth Mg-Based System Hydrogen Storage Alloys with AB_3-Type

A sort of rare earth Mg-based system hydrogen storage alloys with AB3-type was prepared by double-roller rapid quenching method. The alloys were nanocrystalline multi-phase structures composed of LaNi3 phase and LaNi5 phase by X-ray diffraction and scanning electron microscopy analyses, and the suitable absorption/desorption plateau was revealed by the measurement of P-C-I curve. Electrochemical studies indicate that the alloys exhibit good electrochemical properties such as high capacity and stable cycle life, and the discharge capacity is 369 mAh·g-1 at 0.2 C (72 mA·g-1), after 460 cycles, the capacity decay was only 19.4% at 2 C (720 mA·g-1).

Effect of Heat-Treatment Process on Properties of Rare Earth Mg-Based System Hydrogen Storage Alloys with AB_3-Type

The effect of heat-treatment process on the properties of Mm0.8Mg0.2(NiCoAlMn)3.5 hydrogen storage alloy was discussed. The electrochemical properties such as cycling stability, activation property, and the plateau voltage of the alloy which was heat-treated in various temperatures and times had different changes during the cycle process, the optimum heat-treatment conditions of this alloy were determined by this work.

Study on High Rate Discharge Performance and Mechanism of AB_5 Type Hydrogen Storage Alloys

The effects of surface treatment, particle size distribution,rare earth composition and B additive on the high rate discharge performance of hydrogen storage alloys were investigated. It is found that the activity, discharge capacity and high rate dischargeability of the alloys are improved after physical and chemical modification as a result of the increase of the surface area and formation of the electrocatalysis layers, which increase both the electrochemical reaction rate on the alloy surface and H diffusion rate in the alloy bulk. It is also found that both the over-coarse and over-fine particle size increase the contact resistance of the electrode, resulting in a decrease of discharge capacity, deterioration of high rate dischargeability and lower discharge plateau. In another word, a suitable particle size distribution can enhance the alloy activity, discharge capacity and high rate dischargeability. In addition, the high rate dischargeability is enhanced by increasing La content and decreasing Ce content of the alloy composition because of enlargement of the unit cell volume and the improvement of the surface activity. Moreover, B additive resultes in the formation of the second phase, and makes the alloys easier pulverization, which greatly improves the activity, discharge capacity and high rate dischargeability.

Effect of stoichiometry and Cu-substitution on the phase structure and hydrogen storage properties of Ml-Mg-Ni-based alloys

To improve the electrochemical properties of rare-earth-Mg-Ni-based hydrogen storage alloys, the effects of stoichiometry and Cu-substitution on the phase structure and thermodynamic properties of the alloys were studied. Nonsubstituted Ml0.80Mg0.20（Ni2.90Co0.50-Mn0.30Al0.30）x （x=0.68, 0.70, 0.72, 0.74, 0.76） alloys and Cu-substituted Ml0.80Mg0.20（Ni2.90Co0.50-yCuyMn0.30Al0.30）0.70 （y=0, 0.10, 0.30, 0.50） alloys were prepared by induction melting. Phase structure analysis shows that the nonsubstituted alloys consist of a LaNi5 phase, a LaNi3 phase, and a minor La2Ni7 phase;in addition, in the case of Cu-substitution, the Nd2Ni7 phase appears and the LaNi3 phase vanishes. Ther-modynamic tests show that the enthalpy change in the dehydriding process decreases, indicating that hydride stability decreases with in-creasing stoichiometry and increasing Cu content. The maximum discharge capacity, kinetic properties, and cycling stability of the alloy electrodes all increase and then decrease with increasing stoichiometry or increasing Cu content. Furthermore, Cu substitution for Co ame-liorates the discharge capacity, kinetics, and cycling stability of the alloy electrodes.

Research of heat treatment of low-Co AB_5 type hydrogen storage alloys for MH-Ni batteries

The effects of low-Co AB_5 type hydrogen storage alloys prepared by quenchingand annealing on the performances of MH-Ni batteries were investigated, and the characteristics ofthe low-Co AB_5 type hydrogen storage alloys were compared with those of the high-Co AB_5 typehydrogen storage alloy as well. The results showed that the faster the cooling of the low-Cohydrogen storage alloy is, the better homogeneity of the chemical composition for the alloy and thelonger cycle life of the battery are, but the electrochemical discharge capacity and high-ratedischarge ability are reduced. The high-rate discharge ability and charge retention of MH-Nibatteries for the conventional as-cast annealed low-Co hydrogen storage alloy were superior to thosefor the rapidly quenched low-Co hydrogen storage alloy and the high-Co hydrogen storage alloy, buta little inferior in the cycle life.

Kinetics of Hydrogen Absorption in Hydrogen Storage Alloy

Hydrogenation kinetics of MLNi3.8(Co,Mn,Al)1.2 and MLNi3.7(Co,Mn,Al)1.2Cu0.1 alloy in α + β phase at the temperatUre range of 30 ～70 ℃ has been studied. The kinetic mechanism of hydrogen absorption is not affected by initial hydrogen pressure. Temperature does not influence the rate of hydrogen absorption obviously. In the prior and later period of hydrogen absorption the rate-controlling step is chemical reaction and hydrogen diffusion in the hydride phase respectively for MLNi3.8(Co,Mn,Al)1.2 alloy. Adding Cu, the rate-controlling step changes from chemical reaction to the nucleation and growth of β phase in the prior period and the process of hydrogen absorption still controlled by diffusion in the later period.

Effect of Ti substitution on hydrogen storage properties of Zr_(1-x)Ti_xCo (x = 0, 0.1, 0.2, 0.3) alloys

Zr1-xTixCo(x = 0, 0.1, 0.2, 0.3) alloys were prepared by arc-melting method and the effect of Ti substitution on hydrogen storage properties was studied systematically. Hydrogen desorption pressure-composition-temperature(PCT) measurements were carried out using Sievert’s type volumetric apparatus for ZrCo(at 473 K, 573 K and 673 K) and Zr1-xTixCo alloys(at 673 K), respectively. Products after dehydrogenation were characterized by X-ray diffraction(XRD). In addition, the kinetics of Zr1-xTixCo hydride was investigated at 473 K and 673 K,respectively, under hydrogen pressure of 5 MPa. Results showed that Ti substitution for Zr did not change the crystal structure of ZrCo phase.With the increase of temperature from 473 K to 673 K, the extent of disproportionation for ZrCo alloy increased. With Ti content increasing at 673 K, the desorption equilibrium pressure of Zr1-xTixCo-H2 systems elevated and the disproportionation reaction of Zr1-xTixCo alloys was inhibited effectively. Ti substitution decreased the kinetics rate and the effective hydrogen storage capacity of Zr1-xTixCo alloys slightly.Generally speaking, it was found that Zr0.8Ti0.2Co alloy had better anti-disproportionation property with less decrease of effective hydrogen storage capacity which was beneficial to tritium application in the International Thermonuclear Experimental Reactor(ITER).

Hydrogen storage properties of Laves phase Ti_(1-x)Zr_x(Mn_(0.5)Cr_(0.5))_2 alloys

The activation behaviors and hydrogen storage properties of the Laves phase Ti1-xZrx(Mn0.5Cr0.5)2 (x=0, 0.1, 0.2, 0.32, 0.5) alloys were investigated by the pressure-composition-temperature (P-C-T) measurements. All the studied alloys show the single C14-type Laves phase structure based on the XRD data. Except for the alloys with very low Zr content of x=0 and x=0.1, all these alloys can be fully activated. The P-C isotherms of the activated alloys show that, the introduction of Zr induces the decrease of the equilibrium pressures and the steeper plateaus. As the x increases, the maximum hydrogen absorption also increases, whereas the desorption of hydrogen decreases. These two effects result in a maximum reversible hydrogen storage capacity of H/M=3.03 for the alloy at x=0.32. Furthermore, the well-defined plateau associated with the smallest hysteresis also appears at x=0.32.

Hydrogen Storage Properties of Ti_(1.2)Fe+xCa Hydrogen Storage Alloys

The hydrogen storage properties of Ti1.2Fe+xCa (x=1%, 3% and 5% in mass fraction) alloys was investigated. Results stow that the modified alloys can be activated without any thermal treatment at room temperature due to the addition of Ca and excess Ti in (lie alloys. Hydrogen storage properties of these modified alloys vary with Ca amount and reaction temperature. In addition, the influence mechanism of the addition of Ca and excessive Ti on the activation behavior and hydrogen storage capacity of the alloys was discussed.

Effect of praseodymium substitution for lanthanum on structure and properties of La_(0.65-x)Pr_xNd_(0.12)Mg_(0.23)Ni_(3.4)Al_(0.1)(x=0.00–0.20) hydrogen storage alloys

In order to investigate the effect of substituting La with Pr on structural and hydrogen storage properties of La-Mg-Ni system （AB3.5-type） hydrogen storage alloys, a series of La0.65-xPrxNd0.12Mg0.23Ni3.4Al0.1（x=0, 0.10, 0.15, 0.2） hydrogen storage alloys were prepared. X-ray diffraction （XRD）, scanning electron microscopy （SEM） and energy dispersive spectrometer （EDS） analyses revealed that two alloys （x=0.0 and 0.10） were composed of （La,Mg）2（Ni,Al）7 phase, La（Ni,A1）5 phase and （La,Mg）Ni2 phase, while other alloys （x=0.15 and 0.20） consisted of （La,Mg）2（Ni,A1）7 phase, La（Ni,A1）5 phase, （La,Mg）Ni2 phase and （La,Mg）（Ni,A1）3 phase. All alloys showed, however, only one pressure plateau in P-C isotherms. The Pr/La ratio in alloy composition influenced hydrogen storage capacity and kinetics properties. Electrochemical studies showed that the discharge capacity decreased from 360 mAh/g （x=-0.00） to 335 mAh/g （x=-0.20） as x increased. But the high-rate dischargeability （HRD） of alloy electrodes increased from 26% （x=0.00） to 56% （x=-0.20） at a discharge current density of Id=1800 mA/g. Anode polarization measurements were done to further understand the electrochemical kinetics properties after Pr substitution.

Effect of Ni,Fe and Fe-Ni alloy catalysts on the synthesis of metal contained carbon nano-onions and studies of their electrochemical hydrogen storage properties

Three types of carbon nano-onions（CNOs） including Ni@CNOs.Fe3C@CNOs and Fe0.64Ni0.36@CNOs nanoparticles have been synthesized by catalytic decomposition of methane at 850 ℃ using nickel,iron and iron-nickel alloy catalysts.Comparative and systematic studies have been carried out on the morphology,structural characteristics and graphitic crystallinity of these CNOs products.Furthermore,the electrochemical hydrogen storage properties of three types of CNOs have been investigated.Measurements show that the Ni@CNOs have the highest discharge capacity of 387.2 mAh/g,coiTesponding to a hydrogen storage of 1.42%.This comparison study shows the advantages of each catalyst in the growth of CNOs.enabling the controllable synthesis and tuning the properties of CNOs by mediating different metals and their alloy for using in the fuel cell system.

Phase structure and hydrogen storage properties of LaMg_(3.70)Ni_(1.18) alloy

The phase structure and hydrogen storage properties of LaMg 3.70 Ni 1.18 alloy were investigated. The LaMg 3.70 Ni 1.18 alloy consists of main LaMg 2 Ni phase, minor La 2 Mg 17 and LaMg 3 phases. The alloy can be activated in the first hydriding/dehydriding process, and initial LaMg 2 Ni, La 2 Mg 17 , and LaMg 3 phases transfer to LaH 2.34 , Mg, and Mg 2 Ni phases after activation. The reversible hydrogen storage capacity of the LaMg 3.70 Ni 1.18 alloy is 2.47 wt.% at 558 K, which is higher than that of the LaMg 2 Ni alloy. The pressure-composition-temperature （PCT） curves display two hydriding plateaus, corresponding to the formation of MgH 2 and Mg 2 NiH 4 . However, only one dehydriding plateau is observed, owing to the synergetic effect of hydrogen desorption between MgH 2 and Mg 2 NiH 4 . The uptake time for hydrogen content to reach 99% of saturated state is less than 250 s, and 90% hydrogen can be released in 1200 s in the experimental conditions, showing fast kinetics in hydriding and dehydriding. The activation energies of the LaMg 3.70 Ni 1.18 alloy are –51.5 ± 1.1 kJ/mol and –57.0 ± 0.6 kJ/mol for hydriding and dehydriding, respectively. The hydriding/dehydriding kinetics of the LaMg 3.70 Ni 1.18 alloy is better than that of the Mg 2 Ni alloy, owing to the lower activation energy values.