Development of graphene field effect transistors （GFETs） faces a serious challenge of graphene interface to the dielectric material. A single layer of intrinsic graphene has an average sheet resistance of the order ...Development of graphene field effect transistors （GFETs） faces a serious challenge of graphene interface to the dielectric material. A single layer of intrinsic graphene has an average sheet resistance of the order of 1-5 kΩ/□. The intrinsic nature of graphene leads to higher contact resistance yielding into the outstanding properties of the material. We design a graphene matrix with minimized sheet resistance of 0.185 kΩ/□ with Ag contacts. The developed matrices on silicon substrates provide a variety of transistor design options for subsequent fabrication. The graphene layer is developed over 400 nm nickel in such a way as to analyze hypersensitive electrical properties of the interface for exfoliation. This work identifies potential of the design in the applicability of few-layer GFETs with less process steps with the help of analyzing the effect of metal contact and post-process anneMing on its electrical fabrication.展开更多
Transmission spectra of triangular lattice photonic crystals milled in the top surface of an annealed proton- exchange waveguide are numerically simulated. The effects of the finite depth, conical shape, trapezoidal s...Transmission spectra of triangular lattice photonic crystals milled in the top surface of an annealed proton- exchange waveguide are numerically simulated. The effects of the finite depth, conical shape, trapezoidal shape and hybrid shape of holes are theoretically analyzed. Due to the difficulty of milling high aspect-ratio cylindrical holes in lithium niobate （LiNbO3 ）, a compromised solution is proposed to improve the overlap between shallow holes and the waveguide mode, and useful transmission spectra with strong contrast and sharp band edges are achieved.展开更多
The effects of Cr content and annealing temperature on abrasive wear characteristics of cast ausferrite nodular iron were investigated with Suga type abrasive wear tester. The surface morphology and Vickers hardness o...The effects of Cr content and annealing temperature on abrasive wear characteristics of cast ausferrite nodular iron were investigated with Suga type abrasive wear tester. The surface morphology and Vickers hardness of the tested samples were analyzed by scanning electron microscopy（SEM）, digital microscope and Vickers hardness tester. The results show that the cast ausferrite nodular iron could be obtained by alloying with Cr in the as-cast ductile cast iron and permanent mold casting, and the bainite content in the matrix increased with increasing Cr content. However, the decomposition of bainite took place during annealing at 500 °C to 800 °C; especially, at 800 °C, the bainite transformed into a mixture of fine lamellar pearlite and ferrite matrix structure. The wear loss of specimens was reduced with increasing Cr content in the cast ausferrite nodular iron. The wear loss of the sample cast ausferrite nodular iron with 0.4mass% Cr is the least. The wear loss began to increase while the Cr content is 0.6mass%. The wear loss of annealed ductile irons at different annealing temperatures was higher than that of as-cast samples. During the abrasive wear, the shear stress transformed austenite to martensite, and the hardness of specimens increased and the wear resistance of as-cast ductile cast iron was improved.展开更多
文摘Development of graphene field effect transistors （GFETs） faces a serious challenge of graphene interface to the dielectric material. A single layer of intrinsic graphene has an average sheet resistance of the order of 1-5 kΩ/□. The intrinsic nature of graphene leads to higher contact resistance yielding into the outstanding properties of the material. We design a graphene matrix with minimized sheet resistance of 0.185 kΩ/□ with Ag contacts. The developed matrices on silicon substrates provide a variety of transistor design options for subsequent fabrication. The graphene layer is developed over 400 nm nickel in such a way as to analyze hypersensitive electrical properties of the interface for exfoliation. This work identifies potential of the design in the applicability of few-layer GFETs with less process steps with the help of analyzing the effect of metal contact and post-process anneMing on its electrical fabrication.
基金Supported by the National Natural Science Foundation of China under Grant Nos 50872089,61077039 and 61377060the Research Grants Council of the Hong Kong Special Administrative Region of China under Grant No 11211014+1 种基金the Key Program for Research on Fundamental to Application and Leading Technology of Tianjin Science and Technology Commission of China under Grant No 11JCZDJC15500the Specialized Research Fund for the Doctoral Program of Higher Education of China under Grant No 20100032110052
文摘Transmission spectra of triangular lattice photonic crystals milled in the top surface of an annealed proton- exchange waveguide are numerically simulated. The effects of the finite depth, conical shape, trapezoidal shape and hybrid shape of holes are theoretically analyzed. Due to the difficulty of milling high aspect-ratio cylindrical holes in lithium niobate （LiNbO3 ）, a compromised solution is proposed to improve the overlap between shallow holes and the waveguide mode, and useful transmission spectra with strong contrast and sharp band edges are achieved.
基金Item Sponsored by Important National Science and Technology Specific Project of China(2012ZX04010-031)
文摘The effects of Cr content and annealing temperature on abrasive wear characteristics of cast ausferrite nodular iron were investigated with Suga type abrasive wear tester. The surface morphology and Vickers hardness of the tested samples were analyzed by scanning electron microscopy（SEM）, digital microscope and Vickers hardness tester. The results show that the cast ausferrite nodular iron could be obtained by alloying with Cr in the as-cast ductile cast iron and permanent mold casting, and the bainite content in the matrix increased with increasing Cr content. However, the decomposition of bainite took place during annealing at 500 °C to 800 °C; especially, at 800 °C, the bainite transformed into a mixture of fine lamellar pearlite and ferrite matrix structure. The wear loss of specimens was reduced with increasing Cr content in the cast ausferrite nodular iron. The wear loss of the sample cast ausferrite nodular iron with 0.4mass% Cr is the least. The wear loss began to increase while the Cr content is 0.6mass%. The wear loss of annealed ductile irons at different annealing temperatures was higher than that of as-cast samples. During the abrasive wear, the shear stress transformed austenite to martensite, and the hardness of specimens increased and the wear resistance of as-cast ductile cast iron was improved.