AlxOy films by DC reactive magnetron sputtering were annealed in air ambient at 500 ℃for 1 h with different heating rates of 5,15,and 25 ℃/min.Then heat treatments at 900 ℃ were carried out on these 500 ℃-annealed...AlxOy films by DC reactive magnetron sputtering were annealed in air ambient at 500 ℃for 1 h with different heating rates of 5,15,and 25 ℃/min.Then heat treatments at 900 ℃ were carried out on these 500 ℃-annealed films to simulate the high-temperature application environment.Effects of the annealing heating rate on structure and properties of both 500 ℃-annealed and 900 ℃-heated films were investigated systematically.It was found that distinct γ-Al2O3 crystallization was observed in the 900 ℃-heated films only when the annealing heating rates are 15 and 25 ℃/min.The 500 ℃-annealed film possessed the most compact surface morphology in the case of 25 ℃/min.The highest microhardness of both 500 ℃-annealed and 900℃-heated films were obtained when the annealing heating rate was 15 ℃/min.展开更多
We investigated the effects of heating rate on the process parameters of superplastic forming for Zr55Cu30Al10Ni5 by differential scanning calorimetry. The continuous heating and isothermal annealing analyses suggeste...We investigated the effects of heating rate on the process parameters of superplastic forming for Zr55Cu30Al10Ni5 by differential scanning calorimetry. The continuous heating and isothermal annealing analyses suggested that the temperatures of glass transition and onset crystallization are heating rate-dependent in the supercooled liquid region. Then, the time-temperature-transformation diagram under different heating rates indicates that increasing the heating rate can lead to an increase of the incubation time at the same anneal temperature in the supercooled liquid region. Based on the Arrhenius relationship, we discovered that the incubation time increases by 1.08-1.11 times with double increase of the heating rate at the same anneal temperature, and then verified it by the data of literatures and the experimental results. The obtained curve of the max available incubation time reveals that the incubation time at a certain anneal temperature in the supercooled liquid region is not infinite, and will increase with increasing heating rate until this temperature shifts out of the supercooled liquid region because of exceeding critical heating rate. It is concluded that heating rate must be an important processing parameter of superplastic forming for Zr55Cu30Al10Ni5.展开更多
文摘AlxOy films by DC reactive magnetron sputtering were annealed in air ambient at 500 ℃for 1 h with different heating rates of 5,15,and 25 ℃/min.Then heat treatments at 900 ℃ were carried out on these 500 ℃-annealed films to simulate the high-temperature application environment.Effects of the annealing heating rate on structure and properties of both 500 ℃-annealed and 900 ℃-heated films were investigated systematically.It was found that distinct γ-Al2O3 crystallization was observed in the 900 ℃-heated films only when the annealing heating rates are 15 and 25 ℃/min.The 500 ℃-annealed film possessed the most compact surface morphology in the case of 25 ℃/min.The highest microhardness of both 500 ℃-annealed and 900℃-heated films were obtained when the annealing heating rate was 15 ℃/min.
基金Funded by the National Natural Science Foundation of China(Nos.51175210 and 51175211)
文摘We investigated the effects of heating rate on the process parameters of superplastic forming for Zr55Cu30Al10Ni5 by differential scanning calorimetry. The continuous heating and isothermal annealing analyses suggested that the temperatures of glass transition and onset crystallization are heating rate-dependent in the supercooled liquid region. Then, the time-temperature-transformation diagram under different heating rates indicates that increasing the heating rate can lead to an increase of the incubation time at the same anneal temperature in the supercooled liquid region. Based on the Arrhenius relationship, we discovered that the incubation time increases by 1.08-1.11 times with double increase of the heating rate at the same anneal temperature, and then verified it by the data of literatures and the experimental results. The obtained curve of the max available incubation time reveals that the incubation time at a certain anneal temperature in the supercooled liquid region is not infinite, and will increase with increasing heating rate until this temperature shifts out of the supercooled liquid region because of exceeding critical heating rate. It is concluded that heating rate must be an important processing parameter of superplastic forming for Zr55Cu30Al10Ni5.